Dielectric material with low temperature coefficient and high quality
Assignee: Niterra Co Ltd
•
Filing: 1997-09-26
•
Granted: 2000-09-19
•
Expires: 2017-09-26
Abstract
Abstract A dielectric material is disclosed which has a small absolute value of the temperature coefficient of resonance frequency and a high coefficient of unloaded quality. Also disclosed are a process for producing the dielectric material and multilayer and other circuit boards containing the dielectric material. The dielectric material is a highly densified material having a water absorption lower than 0.1%, which is obtained by mixing 95.5 to 99.5 percent by weight mixture of a glass frit and a strontium compound with 0.5 to 4.5 percent by weight titanium dioxide, compacting the resultant mixture, and sintering the compact at a relatively low temperature around 930 DEG C. This dielectric material is a glass ceramic containing strontium anorthite (SrAl2Si2O8) as the main crystalline phase, and may contain the TiO2, which remains unchanged after sintering. The absolute value of the temperature coefficient of resonance frequency of the dielectric material is 20 ppm/ DEG C. or lower, preferably 10 ppm/ DEG C. or lower, more preferably 5 ppm/ DEG C. or lower. The product of the unloaded quality coefficient and resonance frequency is 1,800 GHz or larger, preferably 2,500 GHz or larger. This material therefore has excellent dielectric properties.
Inventors
- 👤 Hitoshi Yokoi
- 👤 Hidetoshi Mizutani
- 👤 Motohiko Sato
- 👤 Kazushige Ohbayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 16:53
CPC Classifications
H; H01; H01P; H01P7/00; H01P7/08; H01P7/082; C; C03; C03C; C03C10/00; C03C10/0036; C03C10/0045; H01P7/084; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
40 words
A dielectric material comprising between 95.5 and 99.5 percent by weight crystallized glass, the crystallized glass comprising strontium anorthite as a main crystalline phase; and the dielectric material further comprising between 0.5 and 4.5 percent by weight TiO 2 .
Claim 2
Dependent Claim
40 words
A dielectric material comprising between 95.5 and 99.5 percent by weight crystallized glass, the crystallized glass comprising strontium anorthite as a main crystalline phase; and the dielectric material further comprising between 0.5 and 4.5 percent by weight TiO 2 .
Claim 3
Dependent Claim
31 words
The dielectric material of claim 1, wherein the crystallized glass is free of strontium titanate as a crystalline phase; and the crystallized glass further comprising magnesium titanate as another crystalline phase.
Claim 4
Dependent Claim
31 words
The dielectric material of either claim 1 or 2, wherein an amount of the strontium anorthite is not less than 40 percent by weight based on amount of the crystallized glass.
Claim 5
Dependent Claim
139 words
A dielectric material comprising a glass ceramic, the glass ceramic comprising strontium anorthite as a main crystalline phase and TiO 2 as another crystalline phase, wherein the strontium anorthite is a product of a reaction of a glass frit with a strontium compound, the strontium compound having at least one member selected from the group consisting Sr 3 Ti 2 O 7 , Sr 2 TiO 4 , SrSnO 3 and SrTiO 3 , wherein the glass frit comprises between 40 and 52 percent by weight SiO 2 , between 27 and 37 percent by weight Al 2 O 3 , between 11 and 13 percent by weight MgO, between 2 and 8 percent by weight B 2 O 3 , and between 2 and 8 percent by weight CaO, the percentages based on amount of the glass frit.
Claim 6
Dependent Claim
139 words
A dielectric material comprising a glass ceramic, the glass ceramic comprising strontium anorthite as a main crystalline phase and TiO 2 as another crystalline phase, wherein the strontium anorthite is a product of a reaction of a glass frit with a strontium compound, the strontium compound having at least one member selected from the group consisting Sr 3 Ti 2 O 7 , Sr 2 TiO 4 , SrSnO 3 and SrTiO 3 , wherein the glass frit comprises between 40 and 52 percent by weight SiO 2 , between 27 and 37 percent by weight Al 2 O 3 , between 11 and 13 percent by weight MgO, between 2 and 8 percent by weight B 2 O 3 , and between 2 and 8 percent by weight CaO, the percentages based on amount of the glass frit.
Claim 7
Dependent Claim
28 words
The dielectric material of claim 4, wherein the glass frit further comprises between 0.1 and 3 percent by weight ZrO 2 based on amount of the glass frit.
Claim 8
Dependent Claim
22 words
The dielectric material of claim 3, wherein the dielectric material contains no crystalline phase comprising any strontium compound other than strontium anorthite.
Claim 9
Dependent Claim
27 words
The dielectric material of claim 2, wherein the strontium anorthite comprises between 50 and 85 percent by weight based on a total amount of all crystalline phases.
Claim 10
Dependent Claim
20 words
The dielectric material of claim 1, wherein the strontium compound has an average particle diameter of 2 μm or smaller.
Claim 11
Dependent Claim
59 words
The dielectric material of claim 4, wherein the smaller of a number of moles of silicon of the SiO 2 contained in the glass frit and a number of moles of the aluminum of the Al 2 O 3 contained in the glass frit is more than two times the number of moles of strontium of the strontium compound.
Claim 12
Dependent Claim
45 words
The dielectric material of claim 1, wherein the dielectric material has a temperature coefficient of resonance frequency of between -20 and +20 ppm/° C., the dielectric material further having a product of an unloaded quality coefficient and the resonance frequency of 1,800 GHz or larger.
Claim 13
Dependent Claim
52 words
The dielectric material of claim 1, wherein the dielectric material is shaped into a substrate comprising at least one surface; the substrate further having at least one wiring pattern made of a conductive material, the at least one wiring pattern made of a conductive material located on the at least one surface.
Claim 14
Dependent Claim
60 words
The dielectric material of claim 1, wherein the dielectric material is shaped into a plurality of substrates, the plurality of substrates stacked co-planarly to comprise a multilayer circuit board; the substrates further comprising surfaces; the multilayer circuit board further comprising at least one wiring pattern made of a conductive material, the wiring patterns located on the surfaces of the substrates.
Claim 15
Dependent Claim
32 words
The dielectric material of claim 4, wherein the glass frit comprises between 2 and 7.9 percent by weight B 2 O 3 , the percentages based on amount of the glass frit.
Claim 16
Dependent Claim
30 words
The dielectric material of claim 4, wherein the glass frit comprises between 45.1 and 52 percent by weight SiO 2 , the percentages based on amount of the glass frit.
Claim 17
Dependent Claim
31 words
The dielectric material of claim 4, wherein the one member of the strontium compound is selected from the group consisting of Sr 3 Ti 2 O 7 and SrTiO 3 .
Claim 18
Dependent Claim
141 words
A dielectric material comprising a glass ceramic, the glass ceramic comprising strontium anorthite as a main crystalline phase and TiO 2 as another crystalline phase, wherein the strontium anorthite is a product of a reaction of a glass frit with a strontium compound, the strontium compound having at least one member selected from the group consisting of Sr 3 Ti 2 O 7 , Sr 2 TiO 4 , SrSnO 3 and SrTiO 3 , and wherein the glass frit comprises between 40 and 52 percent by weight SiO 2 , between 27 and 37 percent by weight Al 2 O 3 , between 11 and 13 percent by weight MgO, between 2 and 8 percent by weight B 2 O 3 , and between 2 and 4.9 percent by weight CaO, the percentages based on amount of the glass frit.
Claim 19
Dependent Claim
141 words
A dielectric material comprising a glass ceramic, the glass ceramic comprising strontium anorthite as a main crystalline phase and TiO 2 as another crystalline phase, wherein the strontium anorthite is a product of a reaction of a glass frit with a strontium compound, the strontium compound having at least one member selected from the group consisting of Sr 3 Ti 2 O 7 , Sr 2 TiO 4 , SrSnO 3 and SrTiO 3 , and wherein the glass frit comprises between 40 and 52 percent by weight SiO 2 , between 27 and 37 percent by weight Al 2 O 3 , between 11 and 13 percent by weight MgO, between 2 and 8 percent by weight B 2 O 3 , and between 2 and 4.9 percent by weight CaO, the percentages based on amount of the glass frit.
Claim 20
Dependent Claim
31 words
The dielectric material of claim 16, wherein the one member of the strontium compound is selected from the group consisting of Sr 3 Ti 2 O 7 and SrTiO 3 .
Claim 21
Dependent Claim
97 words
A process for producing a dielectric material comprising: material between 95.5 and 99.5 percent by weight comprising a glass frit and a strontium compound with between 0.5 and 4.5 percent by weight TiO 2 , the mixing producing a resultant mixture; compacting the resultant mixture to produce a compact; burning the compact at a temperature of between 850 and 1,000° C. in order to densify the compact until the compact attains a water absorption lower than 0.1 percent; and simultaneously reacting the glass frit with the strontium compound to yield stronium anorthite as a main crystalline phase.
Claim 22
Dependent Claim
97 words
A process for producing a dielectric material comprising: material between 95.5 and 99.5 percent by weight comprising a glass frit and a strontium compound with between 0.5 and 4.5 percent by weight TiO 2 , the mixing producing a resultant mixture; compacting the resultant mixture to produce a compact; burning the compact at a temperature of between 850 and 1,000° C. in order to densify the compact until the compact attains a water absorption lower than 0.1 percent; and simultaneously reacting the glass frit with the strontium compound to yield stronium anorthite as a main crystalline phase.
Claim 23
Dependent Claim
70 words
The process of claim 18, wherein the glass frit comprises between 40 and 52 percent by weight SiO 2 , between 27 and 37 percent by weight Al 2 O 3 , between 11 and 13 percent by weight MgO, between 2 and 8 percent by weight B 2 O 3 , and between 2 and 8 percent by weight CaO, the percentages based on amount of the glass frit.
Claim 24
Dependent Claim
27 words
The process of claim 19, wherein the glass frit further comprises between 0.1 and 3 percent by weight ZrO 2 based on amount of the glass frit.
Claim 25
Dependent Claim
25 words
The process of claim 18, wherein the strontium anorthite comprises between 50 and 85 percent weight based on a total amount of all crystalline phases.
Claim 26
Dependent Claim
38 words
The process of claim 18, wherein the strontium compound is atleast one member selected from a group consisting of SrTio 3 , Sr 3 Ti 2 O 7 , Sr 2 TiO 4 , and SrSnO 3 .
Claim 27
Dependent Claim
19 words
The process of claim 18, wherein the strontium compound has an average particle diameter of 2 μm or smaller.
Claim 28
Dependent Claim
58 words
The process of claim 19, wherein the smaller of the number of moles of silicon of the SiO 2 contained in the glass frit and the number of moles of the aluminum of the Al 2 O 3 contained in the glass frit is more than two times the number of moles of strontium of the strontium compound.
Claim 29
Dependent Claim
42 words
The process of claim 18, wherein the process further comprises the steps of: shaping the dielectric material into a substrate comprising at least one surface; and forming at least one wiring pattern made of conductive material on the at least one surface.
Claim 30
Dependent Claim
66 words
The process of claim 18, wherein the process further comprises the steps of: shaping the dielectric material into a plurality of substrates, each of the plurality of substrates having at least one surface; forming a plurality of wiring patterns made of conductive material on at least one of the at least one surface; and stacking the plurality of substrates co-planarly to comprise a multi-layer circuit board.
References Cited (Backward Citations)
US4615987A
Cited
EP0198977A1
Cited
US4853349A
Cited
US5023207A
Cited
US5232765A
Cited
JPH0483737A
Cited
JPH0482297A
Cited
US5262595A
Cited
US5556585A
Cited
JPH04275975A
Cited
US5407871A
Cited
US5356841A
Cited
JPH04286181A
Cited
JPH04292460A
Cited
JPH05211006A
Cited
US5431955A
Cited
JPH06112657A
Cited
JPH06314916A
Cited
JPH06338686A
Cited
JPH0766563A
Cited
US5756408A
Cited
WO1997037948A1
Cited
US5821181A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-09-19 | 2004-03-20 | 2004-09-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-09-19 | 2008-03-20 | 2008-09-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-09-19 | 2012-03-20 | 2012-09-19 | $7700.00 | Window Closed / Lapsed |