Advanced etching method for VLSI fabrication
Assignee: Advanced Micro Devices Inc
•
Filing: 1997-12-19
•
Granted: 2000-02-29
•
Expires: 2017-12-19
Abstract
Abstract The present invention provides a method of etching microelectronic structures. The method utilizes an ion implantation device projecting ions into a silicon semiconductor or conducting substrate to selectively damage the surface causing damage differential. This process is highly controllable and directable, allowing fine manipulation of the substrate surface. After the ion implantation has destroyed selected portions of the surface, standard etching techniques known in the art can be used to selectively remove the damaged portions of the surface. The advantage of this technique is that it confers upon relatively imprecise prior art etching techniques a high degree of precision. Such techniques can be used to create isolation trenches by filling the surface with electrically isolating materials which isolate one semiconductor device from another.
Inventors
- 👤 Yowjuang W. Liu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 00:15
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/60; H10P50/64; H10P50/642; H10P50/69; H10P50/691; H10P50/693; H10P50/695; H10P30/00; H10P30/20; H10P30/22; H10P30/221; H10P30/222
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
112 words
A method for fabricating trenches in semiconductor substrates comprising the following steps: a) providing a semiconductor substrate, said substrate having a surface; b) forming a plurality of masking or protective layers on said surface to define a trench region; c) forming a conformal layer over said plurality of masking or protective layers and said semiconductor substrate in said trench region; d) bombarding said semiconductor substrate through said conformal layer with an ion implantation device to create specifically shaped selectively damaged areas in said semiconductor substrate; and e) etching away said selectively damaged areas of said semiconductor substrate to form trenches having a final profile determined by said specifically shaped selectively damaged areas.
Claim 2
Independent Claim
112 words
A method for fabricating trenches in semiconductor substrates comprising the following steps: a) providing a semiconductor substrate, said substrate having a surface; b) forming a plurality of masking or protective layers on said surface to define a trench region; c) forming a conformal layer over said plurality of masking or protective layers and said semiconductor substrate in said trench region; d) bombarding said semiconductor substrate through said conformal layer with an ion implantation device to create specifically shaped selectively damaged areas in said semiconductor substrate; and e) etching away said selectively damaged areas of said semiconductor substrate to form trenches having a final profile determined by said specifically shaped selectively damaged areas.
Claim 3
Independent Claim
189 words
A method for etching microelectronic integrated circuit structures comprising the following steps: a) providing a semiconductor substrate which may be doped or undoped; b) fabricating at least one of masking or protective layers on said semiconductor substrate according to a set pattern; c) a first etching to remove selected portions of said at least one of masking or protective layers exposing a portion of said semiconductor substrate creating a trench region; d) fabricating a conformal layer on said at least one of masking or protective layers including said exposed portion of said semiconductor substrate in said trench region; e) bombarding said semiconductor substrate through said conformal layer with an ion implantation device to create selectively damaged areas in said trench region of said semiconductor substrate, the selectively damaged areas having a shape being determined by the presence of said conformal layer; f) performing a second etching to remove said selectively damaged areas in said trench region of said semiconductor substrate to form an isolation trench; g) filling said isolation trench with electrically isolating material; and h) planarizing said electrically isolating material and said isolation trench using chemical mechanical polishing.
Claim 4
Independent Claim
189 words
A method for etching microelectronic integrated circuit structures comprising the following steps: a) providing a semiconductor substrate which may be doped or undoped; b) fabricating at least one of masking or protective layers on said semiconductor substrate according to a set pattern; c) a first etching to remove selected portions of said at least one of masking or protective layers exposing a portion of said semiconductor substrate creating a trench region; d) fabricating a conformal layer on said at least one of masking or protective layers including said exposed portion of said semiconductor substrate in said trench region; e) bombarding said semiconductor substrate through said conformal layer with an ion implantation device to create selectively damaged areas in said trench region of said semiconductor substrate, the selectively damaged areas having a shape being determined by the presence of said conformal layer; f) performing a second etching to remove said selectively damaged areas in said trench region of said semiconductor substrate to form an isolation trench; g) filling said isolation trench with electrically isolating material; and h) planarizing said electrically isolating material and said isolation trench using chemical mechanical polishing.
Claim 5
Dependent Claim
30 words
A process as in claim 2 wherein said at least one of masking or protective layers comprises a first layer of silicon dioxide and a second layer of silicon nitride.
Claim 6
Dependent Claim
30 words
A process as in claim 2 wherein said at least one of masking or protective layers comprises a first layer of silicon dioxide and a second layer of silicon oxynitride.
Claim 7
Dependent Claim
23 words
A process as in claim 2 wherein said at least one of masking or protective layers comprise a single layer of silicon dioxide.
Claim 8
Dependent Claim
14 words
A process as in claim 2 wherein said conformal layer is comprised of polysilicon.
Claim 9
Dependent Claim
42 words
A process as in claim 2, wherein said step, e), of bombarding said semiconductor substrate through said conformal layer with an ion implantation device to selectively damage said trench region further includes shaping said selectively damaged areas by controlling ion implantation parameters.
Claim 10
Independent Claim
191 words
A method for etching microelectronic integrated circuit structures comprising the following steps: a) providing a semiconductor substrate which may be doped or undoped; b) fabricating at least one of masking or protective layers over said semiconductor substrate according to a set pattern; c) etching away portions of said at least one of masking or protective layers in a first etch step, exposing a portion of said semiconductor substrate creating a trench region; d) fabricating a silicon dioxide conformal layer on said at least one of masking or protective layers and on said exposed portions of semiconductor substrate including said trench region; e) etching away portions of silicon dioxide conformal layer in a second etch step, forming spacers which cover portions of said trench region; f) after steps d) and e), bombarding said semiconductor substrate and said spacers with an ion implantation device to selectively damage portions of said trench region; g) removing said selectively damaged portions of semiconductor substrate and said spacers creating an isolation trench region; h) filling said isolation trench region with electrically isolating material to create isolation trenches; and i) planarizing said isolation trenches with chemical mechanical polishing.
Claim 11
Independent Claim
191 words
A method for etching microelectronic integrated circuit structures comprising the following steps: a) providing a semiconductor substrate which may be doped or undoped; b) fabricating at least one of masking or protective layers over said semiconductor substrate according to a set pattern; c) etching away portions of said at least one of masking or protective layers in a first etch step, exposing a portion of said semiconductor substrate creating a trench region; d) fabricating a silicon dioxide conformal layer on said at least one of masking or protective layers and on said exposed portions of semiconductor substrate including said trench region; e) etching away portions of silicon dioxide conformal layer in a second etch step, forming spacers which cover portions of said trench region; f) after steps d) and e), bombarding said semiconductor substrate and said spacers with an ion implantation device to selectively damage portions of said trench region; g) removing said selectively damaged portions of semiconductor substrate and said spacers creating an isolation trench region; h) filling said isolation trench region with electrically isolating material to create isolation trenches; and i) planarizing said isolation trenches with chemical mechanical polishing.
Claim 12
Dependent Claim
30 words
A process as in claim 8 wherein said at least one of masking or protective layers comprise a first layer of silicon dioxide and a second layer of silicon nitride.
Claim 13
Dependent Claim
29 words
A process as in claim 8 wherein said at least one of masking or protective layers comprise a first layer of silicon dioxide and a second layer of oxynitride.
Claim 14
Dependent Claim
23 words
A process as in claim 8 wherein said at least one of masking or protective layers comprise a single layer of silicon dioxide.
Claim 15
Dependent Claim
28 words
A process as in claim 8 wherein said second etch step is performed using a technique selected from the group consisting of reactive ion etching and plasma etching.
Claim 16
Dependent Claim
181 words
A process for fabricating isolation trenches with doped walls comprising the following steps: a) providing an N- or P-doped semiconductor substrate; b) fabricating a plurality of masking or protective layers over said semiconductor substrate according to a set pattern; c) a first etching to remove selected portions of said plurality of masking or protective layers to expose portions of said semiconductor substrate defining a trench region; d) fabricating a conformal layer on said plurality of masking or protective layers including said exposed portions of said semiconductor substrate in said trench region; e) bombarding said semiconductor substrate through said conformal layer with ions having a same charge as said semiconductor substrate to simultaneously create a doped region in said semiconductor substrate and selectively damage portions of said semiconductor substrate in said trench region; f) performing a second etch to remove portions of said selectively damaged semiconductor substrate while leaving said doped region in place forming an isolation trench; g) filling said isolation trench with electrically isolating material; and h) planarizing said electrically isolating material, including said isolation trench, using chemical mechanical polishing.
Claim 17
Dependent Claim
181 words
A process for fabricating isolation trenches with doped walls comprising the following steps: a) providing an N- or P-doped semiconductor substrate; b) fabricating a plurality of masking or protective layers over said semiconductor substrate according to a set pattern; c) a first etching to remove selected portions of said plurality of masking or protective layers to expose portions of said semiconductor substrate defining a trench region; d) fabricating a conformal layer on said plurality of masking or protective layers including said exposed portions of said semiconductor substrate in said trench region; e) bombarding said semiconductor substrate through said conformal layer with ions having a same charge as said semiconductor substrate to simultaneously create a doped region in said semiconductor substrate and selectively damage portions of said semiconductor substrate in said trench region; f) performing a second etch to remove portions of said selectively damaged semiconductor substrate while leaving said doped region in place forming an isolation trench; g) filling said isolation trench with electrically isolating material; and h) planarizing said electrically isolating material, including said isolation trench, using chemical mechanical polishing.
Claim 18
Dependent Claim
207 words
A process for fabricating isolation trenches with doped walls comprising the following steps: a) providing an N- or P-doped semiconductor substrate; b) fabricating a plurality of masking or protective layers over said semiconductor substrate according to a set pattern; c) etching away portions of said plurality of masking or protective layers in a first etch step, exposing portions of said semiconductor substrate creating a trench region; d) fabricating a silicon dioxide conformal layer on said plurality of masking or protective layers and said exposed portions of said semiconductor substrate in said trench region; e) etching away portions of said silicon dioxide conformal layer in a second etch step, leaving spacers; f) after steps d) and e), bombarding said semiconductor substrate with ions having a same charge as said semiconductor substrate to simultaneously create a doped region in said semiconductor substrate and to selectively damage portions of said semiconductor substrate in said trench region; g) performing a second etch to remove portions of said selectively damaged semiconductor substrate while leaving said doped region in place forming an isolation trench; h) filling said isolation trench region with electrically isolating material to create isolation trenches; and i) planarizing said electrically isolating material and said isolation trenches with chemical mechanical polishing.
Claim 19
Dependent Claim
207 words
A process for fabricating isolation trenches with doped walls comprising the following steps: a) providing an N- or P-doped semiconductor substrate; b) fabricating a plurality of masking or protective layers over said semiconductor substrate according to a set pattern; c) etching away portions of said plurality of masking or protective layers in a first etch step, exposing portions of said semiconductor substrate creating a trench region; d) fabricating a silicon dioxide conformal layer on said plurality of masking or protective layers and said exposed portions of said semiconductor substrate in said trench region; e) etching away portions of said silicon dioxide conformal layer in a second etch step, leaving spacers; f) after steps d) and e), bombarding said semiconductor substrate with ions having a same charge as said semiconductor substrate to simultaneously create a doped region in said semiconductor substrate and to selectively damage portions of said semiconductor substrate in said trench region; g) performing a second etch to remove portions of said selectively damaged semiconductor substrate while leaving said doped region in place forming an isolation trench; h) filling said isolation trench region with electrically isolating material to create isolation trenches; and i) planarizing said electrically isolating material and said isolation trenches with chemical mechanical polishing.
Claim 20
Independent Claim
147 words
A method for etching microelectronic integrated circuit structures comprising the following steps: a) providing a semiconductor substrate; b) fabricating a plurality of masking or protective layers over said semiconductor substrate according to a set pattern; c) removing portions of said plurality of masking or protective layers in a first removing step, revealing a surface of said semiconductor substrate creating a trench region; d) fabricating a polysilicon conformal layer on said plurality of masking or protective layers and on said exposed portions of semiconductor substrate including said trench region; e) bombarding said semiconductor substrate through said polysilicon conformal layer with an ion implantation device to selectively damage said trench region, said selective damage having a shape being determined by said polysilicon conformal layer; and f) performing a single etch to remove both said selectively damaged trench region and said polysilicon conformal layer to create a shaped trench region.
Claim 21
Independent Claim
147 words
A method for etching microelectronic integrated circuit structures comprising the following steps: a) providing a semiconductor substrate; b) fabricating a plurality of masking or protective layers over said semiconductor substrate according to a set pattern; c) removing portions of said plurality of masking or protective layers in a first removing step, revealing a surface of said semiconductor substrate creating a trench region; d) fabricating a polysilicon conformal layer on said plurality of masking or protective layers and on said exposed portions of semiconductor substrate including said trench region; e) bombarding said semiconductor substrate through said polysilicon conformal layer with an ion implantation device to selectively damage said trench region, said selective damage having a shape being determined by said polysilicon conformal layer; and f) performing a single etch to remove both said selectively damaged trench region and said polysilicon conformal layer to create a shaped trench region.
Claim 22
Dependent Claim
44 words
A method as in claim 15, wherein an isolation trench may be formed by including the further steps of: g) filling said shaped trench region with electrically isolating material; and h) planarizing said electrically isolating material in said trench region with chemical mechanical polishing.
Claim 23
Dependent Claim
28 words
A process as in claim 15 wherein said plurality of masking or protective layers comprise a first layer of silicon dioxide and a second layer of silicon nitride.
Claim 24
Dependent Claim
49 words
A process as in claim 15 wherein said step, e), of bombarding said semiconductor substrate through said conformal layer with an ion implantation device to create said selectively damaged areas in said trench region further includes determining the shape of said selectively damaged areas by controlling ion implantation parameters.
References Cited (Backward Citations)
US3767492A
Cited
US4925805A
Cited
US5358908A
Cited
US5350484A
Cited
US5436174A
Cited
US5449630A
Cited
US5641380A
Cited
US5662768A
Cited
US5872045A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-02-28 | 2003-08-30 | 2004-02-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-02-28 | 2007-08-30 | 2008-02-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-02-28 | 2011-08-30 | 2012-02-29 | $7700.00 | Window Closed / Lapsed |