Method for forming suspended micromechanical structures
Assignee: National Technology and Engineering Solutions of Sandia LLC
•
Filing: 1998-10-08
•
Granted: 2000-02-01
•
Expires: 2018-10-08
Abstract
Abstract A micromachining method is disclosed for forming a suspended micromechanical structure from {111} crystalline silicon. The micromachining method is based on the use of anisotropic dry etching to define lateral features of the structure which are etched down into a {111}-silicon substrate to a first etch depth, thereby forming sidewalls of the structure. The sidewalls are then coated with a protection layer, and the substrate is dry etched to a second etch depth to define a spacing of the structure from the substrate. A selective anisotropic wet etchant (e.g. KOH, EDP, TMAH, NaOH or CsOH) is used to laterally undercut the structure between the first and second etch depths, thereby forming a substantially planar lower surface of the structure along a {111} crystal plane that is parallel to an upper surface of the structure. The lateral extent of undercutting by the wet etchant is controlled and effectively terminated by either timing the etching, by the location of angled {111}-silicon planes or by the locations of preformed etch-stops. This present method allows the formation of suspended micromechanical structures having large vertical dimensions and large masses while allowing for detailed lateral features which can be provided by dry etch definition. Additionally, the method of the present invention is compatible with the formation of electronic circuitry on the substrate.
Inventors
- 👤 James G. Fleming
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 17:35
CPC Classifications
B; B81; B81C; B81C1/00; B81C1/00436; B81C1/00555; B81C1/00626; B81C2201/00; B81C2201/01; B81C2201/0101; B81C2201/0128; B81C2201/013; B81C2201/0132; B81C2201/0133; B81C2201/0135; B81C2201/014; B81C2201/05; B81C2201/053
Claims Analysis
Total Claims: 72
Claim 1
Independent Claim
114 words
A micromachining method for forming a suspended micromechanical structure in a silicon substrate having a top surface oriented along a {111} crystal plane, comprising steps for: (a) dry etching portions of the substrate down to a first etch depth below the top surface of the substrate and thereby forming a plurality of sidewalls of the suspended micromechanical structure; (b) coating the sidewalls with a protection layer; (c) dry etching the substrate down beyond the first etch depth to a second etch depth; and (d) wet etching the substrate with a selective anisotropic wet etchant and laterally undercutting the substrate below the first etch depth to define a lower surface of the suspended micromechanical structure.
Claim 2
Dependent Claim
114 words
A micromachining method for forming a suspended micromechanical structure in a silicon substrate having a top surface oriented along a {111} crystal plane, comprising steps for: (a) dry etching portions of the substrate down to a first etch depth below the top surface of the substrate and thereby forming a plurality of sidewalls of the suspended micromechanical structure; (b) coating the sidewalls with a protection layer; (c) dry etching the substrate down beyond the first etch depth to a second etch depth; and (d) wet etching the substrate with a selective anisotropic wet etchant and laterally undercutting the substrate below the first etch depth to define a lower surface of the suspended micromechanical structure.
Claim 3
Dependent Claim
19 words
The method of claim 1 wherein the protection layer is resistant to attack by the selective anisotropic wet etchant.
Claim 4
Dependent Claim
28 words
The method of claim 2 wherein the selective anisotropic wet etchant is selected from the group consisting of potassium hydroxide, tetramethyl ammonium hydroxide (TMAH) and ethylenediamine pyrocatechol (EDP).
Claim 5
Dependent Claim
21 words
The method of claim 3 wherein the undercutting etch step is performed at a temperature in the range of 10-100° C.
Claim 6
Dependent Claim
25 words
The method of claim 4 further including a step for forming at least one etch-stop to limit a lateral extent of the undercutting etch step.
Claim 7
Dependent Claim
27 words
The method of claim 5 further including steps for forming electronic circuitry comprising a plurality of interconnected transistors on the substrate proximate to the suspended micromechanical structure.
Claim 8
Dependent Claim
21 words
The method of claim 6 wherein the steps for forming the electronic circuitry are performed prior to the undercutting etch step.
Claim 9
Dependent Claim
26 words
The method of claim 7 wherein the steps for forming the electronic circuitry further include a step for forming electrical interconnections to the suspended micromechanical structure.
Claim 10
Dependent Claim
9 words
A product formed by the method of claim 1.
Claim 11
Dependent Claim
9 words
A product formed by the method of claim 8.
Claim 12
Dependent Claim
130 words
A micromachining method for forming a suspended micromechanical structure in a {111} crystalline silicon substrate, comprising steps for: (a) masking a top surface of the substrate to define an outline of the suspended structure to be formed in the substrate; (b) etching the substrate outside the outline of the suspended structure down to a first etch depth and thereby forming a plurality of exposed sidewalls of the suspended structure; (c) forming a protection layer over the exposed sidewalls of the suspended structure; (d) etching the substrate outside the outline of the suspended structure down to a second etch depth which is greater than the first etch depth; and (e) laterally undercutting the substrate below the suspended structure between the first and second etch depths using a selective anisotropic wet etchant.
Claim 13
Dependent Claim
130 words
A micromachining method for forming a suspended micromechanical structure in a {111} crystalline silicon substrate, comprising steps for: (a) masking a top surface of the substrate to define an outline of the suspended structure to be formed in the substrate; (b) etching the substrate outside the outline of the suspended structure down to a first etch depth and thereby forming a plurality of exposed sidewalls of the suspended structure; (c) forming a protection layer over the exposed sidewalls of the suspended structure; (d) etching the substrate outside the outline of the suspended structure down to a second etch depth which is greater than the first etch depth; and (e) laterally undercutting the substrate below the suspended structure between the first and second etch depths using a selective anisotropic wet etchant.
Claim 14
Dependent Claim
24 words
The method of claim 11 wherein the steps for etching the substrate down to the first and second etch depths comprises anisotropic dry etching.
Claim 15
Dependent Claim
14 words
The method of claim 12 wherein the anisotropic dry etching comprises reactive ion etching.
Claim 16
Dependent Claim
26 words
The method of claim 11 wherein the protection layer is selected from the group consisting of silicon dioxide, silicon nitride, silicate glass, metals and metal alloys.
Claim 17
Dependent Claim
22 words
The method of claim 14 wherein the step for forming the protection layer comprises depositing the protection layer by chemical vapor deposition.
Claim 18
Dependent Claim
23 words
The method of claim 14 wherein the step for forming the protection layer comprises depositing the protection layer by plasma-enhanced chemical vapor deposition.
Claim 19
Dependent Claim
18 words
The method of claim 11 wherein the step for forming the protection layer comprises forming a thermal oxide.
Claim 20
Dependent Claim
16 words
The method of claim 11 wherein the selective anisotropic wet etchant comprises an alkali hydroxide etchant.
Claim 21
Dependent Claim
24 words
The method of claim 18 wherein the alkali hydroxide etchant is selected from the group consisting of potassium hydroxide, sodium hydroxide and cesium hydroxide.
Claim 22
Dependent Claim
16 words
The method of claim 11 wherein the selective anisotropic wet etchant comprises tetramethyl ammonium hydroxide (TMAH).
Claim 23
Dependent Claim
15 words
The method of claim 11 wherein the selective anisotropic wet etchant comprises ethylenediamine pyrocatechol (EDP).
Claim 24
Dependent Claim
24 words
The method of claim 11 further including a step for forming at least one etch-stop for limiting a lateral extent of undercutting etch step.
Claim 25
Dependent Claim
20 words
The method of claim 11 further including steps for forming electronic circuitry on the substrate proximate to the suspended structure.
Claim 26
Dependent Claim
35 words
The method of claim 23 wherein the electronic circuitry comprises a plurality of interconnected transistors selected from the group consisting of bipolar transistors, complementary metal-oxide semiconductor (CMOS) transistors and bipolar complementary metal-oxide semiconductor (BiCMOS) transistors.
Claim 27
Dependent Claim
21 words
The method of claim 23 wherein the steps for forming the electronic circuitry are performed prior to the undercutting etch step.
Claim 28
Dependent Claim
9 words
A product formed by the method of claim 11.
Claim 29
Dependent Claim
9 words
A product formed by the method of claim 23.
Claim 30
Dependent Claim
212 words
A micromachining method for forming a suspended micromechanical structure from crystalline silicon with substantially planar and parallel upper and lower surfaces, comprising steps for: (a) providing a silicon substrate having a top surface aligned substantially along a {111} crystal plane; (b) forming a patterned mask layer over the top surface of the silicon substrate to define a substantially planar upper surface of the suspended structure being formed in the substrate; (c) etching portions of the substrate not covered by the patterned mask layer down to a first etch depth, thereby forming a plurality of exposed sidewalls of the suspended structure being formed; (d) forming a protection layer over the exposed sidewalls of the suspended structure being formed; (e) etching the portions of the substrate not covered by the patterned mask layer down to a second etch depth greater than the first etch depth; and (f) laterally undercutting the substrate below the suspended structure being formed by removing substrate material at depths between the first and second etch depths using a selective anisotropic wet etchant that substantially terminates etching upon reaching a plurality of {111} crystal planes of the silicon substrate, thereby forming a substantially planar lower surface of the suspended structure, with the lower surface being substantially parallel to the upper surface.
Claim 31
Dependent Claim
212 words
A micromachining method for forming a suspended micromechanical structure from crystalline silicon with substantially planar and parallel upper and lower surfaces, comprising steps for: (a) providing a silicon substrate having a top surface aligned substantially along a {111} crystal plane; (b) forming a patterned mask layer over the top surface of the silicon substrate to define a substantially planar upper surface of the suspended structure being formed in the substrate; (c) etching portions of the substrate not covered by the patterned mask layer down to a first etch depth, thereby forming a plurality of exposed sidewalls of the suspended structure being formed; (d) forming a protection layer over the exposed sidewalls of the suspended structure being formed; (e) etching the portions of the substrate not covered by the patterned mask layer down to a second etch depth greater than the first etch depth; and (f) laterally undercutting the substrate below the suspended structure being formed by removing substrate material at depths between the first and second etch depths using a selective anisotropic wet etchant that substantially terminates etching upon reaching a plurality of {111} crystal planes of the silicon substrate, thereby forming a substantially planar lower surface of the suspended structure, with the lower surface being substantially parallel to the upper surface.
Claim 32
Dependent Claim
38 words
The method of claim 28 wherein the step for forming the patterned mask layer comprises depositing and patterning a masking material selected from the group consisting of photoresist, silicon dioxide, silicate glass, silicon nitride, metals and metal alloys.
Claim 33
Dependent Claim
34 words
The method of claim 29 wherein the step for patterning the masking material comprises providing a patterned photoresist over the masking material and dry etching the masking material through openings in the patterned photoresist.
Claim 34
Dependent Claim
24 words
The method of claim 28 wherein the step for etching portions of the substrate down to the first etch depth comprises anisotropic dry etching.
Claim 35
Dependent Claim
25 words
The method of claim 31 wherein the step for etching the portions of the substrate down to the second etch depth comprises anisotropic dry etching.
Claim 36
Dependent Claim
15 words
The method of claim 32 wherein each anisotropic dry etching step comprises reactive ion etching.
Claim 37
Dependent Claim
24 words
The method of claim 28 wherein the sidewalls of the suspended structure are oriented at substantially 90 degrees to the surface of the substrate.
Claim 38
Dependent Claim
29 words
The method of claim 28 wherein the step for forming the protection layer comprises depositing the protection layer by chemical vapor deposition (CVD) or plasma-enhanced chemical vapor deposition (PECVD).
Claim 39
Dependent Claim
26 words
The method of claim 28 wherein the protection layer is selected from the group consisting of silicon dioxide, silicon nitride, silicate glass, metals and metal alloys.
Claim 40
Dependent Claim
18 words
The method of claim 28 wherein the step for forming the protection layer comprises forming a thermal oxide.
Claim 41
Dependent Claim
30 words
The method of claim 28 wherein the step for forming the protection layer comprises forming a silicon dioxide layer by chemical vapor deposition (CVD) or plasma-enhanced chemical vapor deposition (PECVD).
Claim 42
Dependent Claim
30 words
The method of claim 28 wherein the step for forming the protection layer comprises forming a silicate glass layer by chemical vapor deposition (CVD) or plasma-enhanced chemical vapor deposition (PECVD).
Claim 43
Dependent Claim
29 words
The method of claim 28 wherein the step for forming the protection layer comprises forming a nitride layer by chemical vapor deposition (CVD) or plasma-enhanced chemical vapor deposition (PECVD).
Claim 44
Dependent Claim
22 words
The method of claim 28 wherein the step for forming the protection layer comprises forming a metal layer by evaporation or sputtering.
Claim 45
Dependent Claim
11 words
The method of claim 41 wherein the metal layer comprises tungsten.
Claim 46
Dependent Claim
23 words
The method of claim 28 wherein the step for forming the protection layer comprises forming a metal alloy layer by evaporation or sputtering.
Claim 47
Dependent Claim
22 words
The method of claim 43 wherein the metal alloy layer comprises a titanium nitride (TiN) alloy or a titanium tungsten (TiW) alloy.
Claim 48
Dependent Claim
15 words
The method of claim 28 wherein the selective anisotropic wet etchant comprises potassium hydroxide (KOH).
Claim 49
Dependent Claim
16 words
The method of claim 28 wherein the selective anisotropic wet etchant comprises tetramethyl ammonium hydroxide (TMAH).
Claim 50
Dependent Claim
15 words
The method of claim 28 wherein the selective anisotropic wet etchant comprises ethylenediamine pyrocatechol (EDP).
Claim 51
Dependent Claim
15 words
The method of claim 28 wherein the selective anisotropic wet etchant comprises sodium hydroxide (NaOH).
Claim 52
Dependent Claim
15 words
The method of claim 28 wherein the selective anisotropic wet etchant comprises cesium hydroxide (CsOH).
Claim 53
Dependent Claim
21 words
The method of claim 28 wherein the undercutting etch step is performed at a temperature within the range of 10-100° C.
Claim 54
Dependent Claim
23 words
The method of claim 28 further comprising a step for removing the patterned mask layer and protection layer after the undercutting etch step.
Claim 55
Dependent Claim
20 words
The method of claim 28 wherein the undercutting etch step forms a pedestal connecting the suspended structure to the substrate.
Claim 56
Dependent Claim
17 words
The method of claim 52 wherein the pedestal is formed at one edge of the suspended structure.
Claim 57
Dependent Claim
17 words
The method of claim 52 wherein the pedestal is formed near the center of the suspended structure.
Claim 58
Dependent Claim
19 words
The method of claim 28 wherein undercutting etch step forms the suspended structure as a cantilevered plate or beam.
Claim 59
Dependent Claim
44 words
The method of claim 28 further comprising steps for etching a shaped opening into the substrate to a third etch depth greater than the second etch depth and forming an etch-stop in the opening to terminate the undercutting etch step upon reaching the etch-stop.
Claim 60
Dependent Claim
29 words
The method of claim 56 wherein the etch-stop is formed from at least one material selected from the group consisting of polysilicon, silicon dioxide, silicon nitride and silicate glass.
Claim 61
Dependent Claim
16 words
The method of claim 57 wherein the etch-stop electrically insulates the suspended structure from the substrate.
Claim 62
Dependent Claim
18 words
The method of claim 56 wherein the shaped opening is located within an outline of the suspended structure.
Claim 63
Dependent Claim
19 words
The method of claim 56 wherein the shaped opening is located adjacent to an outline of the suspended structure.
Claim 64
Dependent Claim
20 words
The method of claim 28 further comprising steps for forming electronic circuitry on the substrate proximate to the suspended structure.
Claim 65
Dependent Claim
12 words
The method of claim 61 wherein the electronic circuitry comprises bipolar circuitry.
Claim 66
Dependent Claim
15 words
The method of claim 61 wherein the electronic circuitry comprises complementary metal-oxide semiconductor (CMOS) circuitry.
Claim 67
Dependent Claim
16 words
The method of claim 61 wherein the electronic circuitry comprises bipolar complementary metal-oxide semiconductor (BiCMOS) circuitry.
Claim 68
Dependent Claim
21 words
The method of claim 61 wherein the steps for forming the electronic circuitry are performed prior to the undercutting etch step.
Claim 69
Dependent Claim
26 words
The method of claim 61 wherein the steps for forming the electronic circuitry further include a step for forming electrical interconnections to the suspended micromechanical structure.
Claim 70
Dependent Claim
38 words
The method of claim 61 wherein the steps for forming the electronic circuitry further include a step for forming a passivation layer over the electronic circuitry to protect the electronic circuitry from exposure to the anisotropic wet etchant.
Claim 71
Dependent Claim
9 words
A product formed by the method of claim 28.
Claim 72
Dependent Claim
10 words
A product formed according to the method of claim 61.
References Cited (Backward Citations)
US4470875A
Cited
US4783237A
Cited
US4812199A
Cited
US4922756A
Cited
US5087124A
Cited
US5554304A
Cited
US5719073A
Cited
US5426070A
Cited
US5633552A
Cited
US5441600A
Cited
US5709773A
Cited
US5804314A
Cited
US5770465A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-01-31 | 2003-08-02 | 2004-02-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-01-31 | 2007-08-02 | 2008-02-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-01-31 | 2011-08-02 | 2012-02-01 | $7700.00 | Window Closed / Lapsed |