Method for improving the yield on dynamic random access memory (DRAM) with cylindrical capacitor structures
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1998-09-04
•
Granted: 2000-01-18
•
Expires: 2018-09-04
Abstract
Abstract A new method for forming stacked capacitors for DRAMs having improved yields when the bottom electrode is misaligned to the node contact is achieved. A planar silicon oxide (SiO 2 ) first insulating layer, a Si 3 N 4 etch-stop layer, and a disposable second insulating layer are deposited. First openings for node contacts are etched in the insulating layers. A polysilicon layer is deposited and etched back to form node contacts in the first openings. The node contacts are recessed in the second insulating layer, but above the etch-stop layer to form node contacts abutting the etch-stop layer. A disposable third SiO 2 layer is deposited. Second openings for bottom electrodes are etched over and to the node contacts. A conformal second polysilicon layer is deposited and chem/mech polished back to form the bottom electrodes in the second openings. The third and second insulating layers are removed by wet etching to the etch-stop layer. When the second openings are misaligned over the node contact openings, the polysilicon plugs abutting the Si 3 N 4 etch-stop layer protect the SiO 2 first insulating layer from being eroded over the devices on the substrate. The capacitors are completed by forming a thin dielectric layer on the bottom electrodes, and forming top electrodes from a patterned third polysilicon layer.
Inventors
- 👤 Kuo Ching Huang
- 👤 Yu Hua Lee
- 👤 Cheng-Ming Wu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 21:55
CPC Classifications
H; H10; H10B; H10B12/00; H10B12/01; H10B12/02; H10B12/03; H10B12/033; H10B12/30; H10B12/31; H10B12/318
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
265 words
A method for fabricating stacked capacitors for memory devices comprising the steps of: providing a semiconductor substrate having device areas with semiconductor devices; forming a planar first insulating layer over said device areas on said substrate; depositing a blanket etch-stop layer on said first insulating layer; depositing a second insulating layer on said etch-stop layer; selectively etching first openings for capacitor node contacts in said second insulating layer, said etch-stop layer, and said first insulating layer to said device areas; depositing a conductively doped first polysilicon layer to fill said first openings, and etching back said first polysilicon layer to form polysilicon plugs that are recessed below the surface of said second insulating layer and above said etch-stop layer; depositing a third insulating layer; selectively etching second openings, over and wider than said first openings, in said third and said second insulating layers to the top surface of said etch-stop layer and to said polysilicon plugs; depositing a conformal second polysilicon layer over and in said second openings and contacting said polysilicon plugs; polishing back said second polysilicon layer to said third insulating layer to form bottom electrodes in said second openings; isotropically etching said third and said second insulating layers selectively to said etch-stop layer to leave free-standing said bottom electrodes, while said polysilicon plugs that abut said etch-stop layer prevent said etching from eroding said first insulating layer when said second openings are misaligned to said first openings; depositing an interelectrode dielectric layer on said bottom electrodes; depositing and patterning a third polysilicon layer to form top electrodes and completing said stacked capacitors.
Claim 2
Independent Claim
265 words
A method for fabricating stacked capacitors for memory devices comprising the steps of: providing a semiconductor substrate having device areas with semiconductor devices; forming a planar first insulating layer over said device areas on said substrate; depositing a blanket etch-stop layer on said first insulating layer; depositing a second insulating layer on said etch-stop layer; selectively etching first openings for capacitor node contacts in said second insulating layer, said etch-stop layer, and said first insulating layer to said device areas; depositing a conductively doped first polysilicon layer to fill said first openings, and etching back said first polysilicon layer to form polysilicon plugs that are recessed below the surface of said second insulating layer and above said etch-stop layer; depositing a third insulating layer; selectively etching second openings, over and wider than said first openings, in said third and said second insulating layers to the top surface of said etch-stop layer and to said polysilicon plugs; depositing a conformal second polysilicon layer over and in said second openings and contacting said polysilicon plugs; polishing back said second polysilicon layer to said third insulating layer to form bottom electrodes in said second openings; isotropically etching said third and said second insulating layers selectively to said etch-stop layer to leave free-standing said bottom electrodes, while said polysilicon plugs that abut said etch-stop layer prevent said etching from eroding said first insulating layer when said second openings are misaligned to said first openings; depositing an interelectrode dielectric layer on said bottom electrodes; depositing and patterning a third polysilicon layer to form top electrodes and completing said stacked capacitors.
Claim 3
Dependent Claim
26 words
The method of claim 1, wherein said first insulating layer is silicon oxide, and has a thickness of between about 3000 and 6000 Angstroms after planarizing.
Claim 4
Dependent Claim
31 words
The method of claim 1, wherein said first polysilicon layer is doped with conductive impurities to a concentration of between about 1.0 E 17 and 1.0 E 21 atoms/cm 3 .
Claim 5
Dependent Claim
23 words
The method of claim 1, wherein said etch-stop layer is silicon nitride and has a thickness of between about 100 and 300 Angstroms.
Claim 6
Dependent Claim
26 words
The method of claim 1, wherein said second insulating layer is silicon oxide and is deposited to a thickness of between about 2000 and 5000 Angstroms.
Claim 7
Dependent Claim
26 words
The method of claim 1, wherein said third insulating layer is silicon oxide and is deposited to a thickness of between about 1000 and 4000 Angstroms.
Claim 8
Dependent Claim
43 words
The method of claim 1, wherein said second polysilicon layer is conductively doped in-situ to a concentration of between about 1.0 E 19 and 1.0 E 21 atoms/cm 3 , and is deposited to a thickness of between about 500 and 2000 Angstroms.
Claim 9
Dependent Claim
25 words
The method of claim 1, wherein said isotropic etching of said third and said second insulating layers is carried out in a hydrofluoric acid solution.
Claim 10
Dependent Claim
27 words
The method of claim 1, wherein said interelectrode dielectric layer is silicon oxide/silicon nitride/silicon oxide (ONO), and has a thickness of between about 40 and 100 Angstroms.
Claim 11
Dependent Claim
42 words
The method of claim 1, wherein said third polysilicon layer is doped with conductive impurities to a concentration of between about 1.0 E 19 and 1.0 E 21 atoms/cm 3 , and has a thickness of between about 500 and 2000 Angstroms.
Claim 12
Independent Claim
271 words
A method for fabricating dynamic random access memory (DRAM) devices having stacked capacitors comprising the steps of: providing a semiconductor substrate having device areas with semiconductor devices; forming a planar first insulating layer over said device areas on said substrate; depositing a blanket silicon nitride etch-stop layer on said first insulating layer; depositing a second insulating layer on said etch-stop layer; selectively etching first openings for capacitor node contacts in said second insulating layer, said etch-stop layer, and said first insulating layer to said device areas; depositing a conductively doped first polysilicon layer to fill said first openings, and etching back said first polysilicon layer to form polysilicon plugs that are recessed below the surface of said second insulating layer and above said etch-stop layer; depositing a third insulating layer; selectively etching second openings, over and wider than said first openings, in said third and said second insulating layers to the top surface of said etch-stop layer and to said polysilicon plugs; depositing a conformal second polysilicon layer over and in said second openings and contacting said polysilicon plugs; polishing back said second polysilicon layer to said third insulating layer to form bottom electrodes in said second openings; isotropically etching said third and said second insulating layers selectively to said etch-stop layer to leave free-standing said bottom electrodes, while said polysilicon plugs that abut said etch-stop layer prevent said etching from eroding said first insulating layer when said second openings are misaligned to said first openings; depositing an interelectrode dielectric layer on said bottom electrodes; depositing and patterning a third polysilicon layer to form top electrodes and completing said stacked capacitors.
Claim 13
Independent Claim
271 words
A method for fabricating dynamic random access memory (DRAM) devices having stacked capacitors comprising the steps of: providing a semiconductor substrate having device areas with semiconductor devices; forming a planar first insulating layer over said device areas on said substrate; depositing a blanket silicon nitride etch-stop layer on said first insulating layer; depositing a second insulating layer on said etch-stop layer; selectively etching first openings for capacitor node contacts in said second insulating layer, said etch-stop layer, and said first insulating layer to said device areas; depositing a conductively doped first polysilicon layer to fill said first openings, and etching back said first polysilicon layer to form polysilicon plugs that are recessed below the surface of said second insulating layer and above said etch-stop layer; depositing a third insulating layer; selectively etching second openings, over and wider than said first openings, in said third and said second insulating layers to the top surface of said etch-stop layer and to said polysilicon plugs; depositing a conformal second polysilicon layer over and in said second openings and contacting said polysilicon plugs; polishing back said second polysilicon layer to said third insulating layer to form bottom electrodes in said second openings; isotropically etching said third and said second insulating layers selectively to said etch-stop layer to leave free-standing said bottom electrodes, while said polysilicon plugs that abut said etch-stop layer prevent said etching from eroding said first insulating layer when said second openings are misaligned to said first openings; depositing an interelectrode dielectric layer on said bottom electrodes; depositing and patterning a third polysilicon layer to form top electrodes and completing said stacked capacitors.
Claim 14
Dependent Claim
26 words
The method of claim 11, wherein said first insulating layer is silicon oxide, and has a thickness of between about 3000 and 6000 Angstroms after planarizing.
Claim 15
Dependent Claim
31 words
The method of claim 11, wherein said first polysilicon layer is doped with conductive impurities to a concentration of between about 1.0 E 17 and 1.0 E 21 atoms/cm 3 .
Claim 16
Dependent Claim
23 words
The method of claim 11, wherein said etch-stop layer is silicon nitride and has a thickness of between about 100 and 300 Angstroms.
Claim 17
Dependent Claim
26 words
The method of claim 11, wherein said second insulating layer is silicon oxide and is deposited to a thickness of between about 2000 and 5000 Angstroms.
Claim 18
Dependent Claim
26 words
The method of claim 11, wherein said third insulating layer is silicon oxide and is deposited to a thickness of between about 1000 and 4000 Angstroms.
Claim 19
Dependent Claim
43 words
The method of claim 11, wherein said second polysilicon layer is conductively doped in-situ to a concentration of between about 1.0 E 19 and 1.0 E 21 atoms/cm 3 , and is deposited to a thickness of between about 500 and 2000 Angstroms.
Claim 20
Dependent Claim
25 words
The method of claim 11, wherein said isotropic etching of said third and said second insulating layers is carried out in a hydrofluoric acid solution.
Claim 21
Dependent Claim
27 words
The method of claim 11, wherein said interelectrode dielectric layer is silicon oxide/silicon nitride/silicon oxide (ONO), and has a thickness of between about 40 and 100 Angstroms.
Claim 22
Dependent Claim
42 words
The method of claim 11, wherein said third polysilicon layer is doped with conductive impurities to a concentration of between about 1.0 E 19 and 1.0 E 21 atoms/cm 3 , and has a thickness of between about 500 and 2000 Angstroms.
References Cited (Backward Citations)
US5430614A
Cited
US5332685A
Cited
US5550078A
Cited
US5688713A
Cited
US5759892A
Cited
US5681773A
Cited
US5710075A
Cited
US5716883A
Cited
US5753547A
Cited
US5728618A
Cited
US5736450A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-01-17 | 2003-07-19 | 2004-01-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-01-17 | 2007-07-19 | 2008-01-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-01-17 | 2011-07-19 | 2012-01-18 | $7700.00 | Window Closed / Lapsed |