Substrate having uniform tungsten silicide film and method of manufacture
Assignee: Applied Materials Inc
•
Filing: 1997-05-27
•
Granted: 1999-12-07
•
Expires: 2017-05-27
Abstract
Abstract A tungsten silicide film is deposited on a substrate from a premixed deposition gas mixture comprising: (i) silicon source gas, such as SiCl2H2 and (ii) tungsten source gas, such as WF6. A seeding gas, such as silane, is used during the initial deposition stages to deposit a substantially uniform interfacial WSix layer on the substrate, so that the tungsten to silicon ratio of the WSix layer is substantially uniform through the thickness of the WSix film. An apparatus for performing the process is also described.
Inventors
- 👤 Susan G. Telford
- 👤 Meng Chu Tseng
- 👤 Michio Aruga
- 👤 Klaus-Dieter Rinnen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 15:02
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/44; C23C16/455; C23C16/45561; C23C16/22; C23C16/30; C23C16/42
Claims Analysis
Total Claims: 52
Claim 1
Independent Claim
162 words
A chemical vapor deposition process for depositing WSi x on a substrate, the process comprising the steps of: (a) placing a substrate in a deposition chamber having first and second gas inlets; (b) forming a mixed deposition gas by combining silicon source gas and tungsten source gas sufficiently upstream of the deposition chamber that the mixed deposition gas is substantially uniformly mixed prior to introduction into the deposition chamber; (c) during an initial deposition stage, introducing the mixed deposition gas into the deposition chamber through the first gas inlet, separately introducing a seeding gas into the deposition chamber through the second gas inlet, and maintaining the deposition chamber at process conditions suitable for depositing an interfacial layer on the substrate; and (d) during a second deposition stage, stopping flow of seeding gas while continuing to introduce the mixed deposition gas into the deposition chamber, and maintaining the deposition chamber at process conditions suitable for depositing a WSi x layer on the substrate.
Claim 2
Dependent Claim
162 words
A chemical vapor deposition process for depositing WSi x on a substrate, the process comprising the steps of: (a) placing a substrate in a deposition chamber having first and second gas inlets; (b) forming a mixed deposition gas by combining silicon source gas and tungsten source gas sufficiently upstream of the deposition chamber that the mixed deposition gas is substantially uniformly mixed prior to introduction into the deposition chamber; (c) during an initial deposition stage, introducing the mixed deposition gas into the deposition chamber through the first gas inlet, separately introducing a seeding gas into the deposition chamber through the second gas inlet, and maintaining the deposition chamber at process conditions suitable for depositing an interfacial layer on the substrate; and (d) during a second deposition stage, stopping flow of seeding gas while continuing to introduce the mixed deposition gas into the deposition chamber, and maintaining the deposition chamber at process conditions suitable for depositing a WSi x layer on the substrate.
Claim 3
Dependent Claim
29 words
The process of claim 1, wherein in step (b) the silicon source gas and the tungsten source gas are combined at least 2.5 inches upstream of the deposition chamber.
Claim 4
Dependent Claim
36 words
The process of claim 1, wherein in step (b) the silicon source gas and the tungsten source gas are selected so that substantially no gas phase nucleation of the gases occurs when the gases are mixed.
Claim 5
Dependent Claim
34 words
The process of claim 1, wherein step (b) further comprises the step of maintaining the mixed deposition gases at a temperature at which substantially no gas phase nucleation occurs in the mixed deposition gas.
Claim 6
Dependent Claim
21 words
The process of claim 1, wherein the silicon source gas comprises dichlorosilane and the tungsten source gas comprises WF 6 .
Claim 7
Dependent Claim
28 words
The process of claim 5, wherein during both stages of the process, the volumetric flow ratio of dichlorosilane to WF 6 is from about 5:1 to about 400:1.
Claim 8
Dependent Claim
23 words
The process of claim 1 wherein the seeding gas is selected from the group consisting of monosilane, disilane, trisilane and H 2 .
Claim 9
Dependent Claim
33 words
The process of claim 1 wherein the initial deposition stage is performed for only a sufficient period to initiate deposition of an interfacial layer comprising WSi x having a substantially uniform Si:W ratio.
Claim 10
Dependent Claim
24 words
The process of claim 1 wherein in step (c), the seeding gas is introduced in the deposition chamber for less than about 20 seconds.
Claim 11
Dependent Claim
24 words
The process of claim 9 wherein in step (c), the seeding gas is introduced in the deposition chamber for less than about 10 seconds.
Claim 12
Dependent Claim
25 words
The process of claim 1 wherein during both stages of the process, the substrate is heated to a temperature of at least about 450° C.
Claim 13
Dependent Claim
25 words
The process of claim 1 wherein in step (c) the volumetric flow rate of the seeding gas ranges from about 10 to about 500 sccm.
Claim 14
Dependent Claim
33 words
The process of claim 1 wherein in step (c) the total volume of seeding gas introduced into the deposition chamber during the initial deposition stage ranges from about 1 to about 125 scc.
Claim 15
Dependent Claim
113 words
A process for depositing a WSi x layer on a substrate, the process comprising the steps: (a) placing a substrate within a deposition zone; (b) during an initial stage, introducing a first process gas consisting of seeding gas into the deposition zone, and maintaining the deposition zone at process conditions suitable for depositing an interfacial layer on the substrate, the interfacial layer capable of serving as a seeding layer; and (c) during at least one subsequent stage, flowing a second process gas comprising silicon source gas and tungsten source gas into the deposition zone, and maintaining the deposition zone at process conditions suitable for depositing a WSi x layer on the interfacial layer.
Claim 16
Dependent Claim
113 words
A process for depositing a WSi x layer on a substrate, the process comprising the steps: (a) placing a substrate within a deposition zone; (b) during an initial stage, introducing a first process gas consisting of seeding gas into the deposition zone, and maintaining the deposition zone at process conditions suitable for depositing an interfacial layer on the substrate, the interfacial layer capable of serving as a seeding layer; and (c) during at least one subsequent stage, flowing a second process gas comprising silicon source gas and tungsten source gas into the deposition zone, and maintaining the deposition zone at process conditions suitable for depositing a WSi x layer on the interfacial layer.
Claim 17
Dependent Claim
18 words
The process of claim 14, wherein in step (b), the seeding gas consists of a silicon source gas.
Claim 18
Dependent Claim
27 words
The process of claim 14, wherein in step (b), the seeding gas is selected from the group consisting of monosilane, disilane, trisilane, dichlorosilane, and H 2 .
Claim 19
Dependent Claim
80 words
The process of claim 14, wherein the substantially uniform WSi x layer on the substrate is characterized by: (i) is at least 300 Å thick, (ii) contains less than 10 18 fluorine atoms/cc, (iii) comprises an average value of x within each strata of the WSi x layer that is between ±10% of the average bulk value of x through the thickness of the WSi x layer, and (iv) comprises a value of x of from about 2.0 to 2.8.
Claim 20
Dependent Claim
29 words
The process of claim 14, wherein in step (c) the silicon source gas and the tungsten source gas are combined at least 2.5 inches upstream of the deposition chamber.
Claim 21
Dependent Claim
24 words
The process of claim 14, wherein in step (c) the silicon source gas comprises dichlorosilane and the tungsten source gas comprises WF 6 .
Claim 22
Dependent Claim
25 words
The process of claim 19, wherein in step (c) the volumetric flow ratio of dichlorosilane to WF 6 is from about 5:1 to about 400:1.
Claim 23
Dependent Claim
12 words
The process of claim 14 wherein the seeding gas consists of monosilane.
Claim 24
Dependent Claim
43 words
The process of claim 14 wherein in step (b) the seeding gas is introduced into the deposition zone only at the onset of the process and for a sufficient period to deposit an interfacial WSi x layer having a substantially uniform Si:W ratio.
Claim 25
Dependent Claim
21 words
The process of claim 22 wherein the seeding gas is introduced in the deposition zone for less than about 20 seconds.
Claim 26
Dependent Claim
21 words
The process of claim 23 wherein the seeding gas is introduced in the deposition zone for less than about 10 seconds.
Claim 27
Dependent Claim
25 words
The process of claim 14 wherein in step (b) the volumetric flow rate of the seeding gas ranges from about 10 to about 500 sccm.
Claim 28
Dependent Claim
33 words
The process of claim 14 wherein in step (b) the total volume of seeding gas introduced into the deposition zone during the initial deposition stage ranges from about 1 to about 125 sccm.
Claim 29
Dependent Claim
177 words
A process for depositing a WSi x layer on a substrate, the process comprising the steps: (a) placing a substrate within a deposition zone; (b) during an initial stage, introducing a first process gas consisting of seeding gas into the deposition zone, and maintaining the deposition zone at process conditions suitable for depositing an interfacial layer on the substrate, the interfacial layer capable of serving as a seeding layer; and (c) during at least one subsequent stage, flowing a second process gas comprising silicon source gas and tungsten source gas into the deposition zone, and maintaining the deposition zone at process conditions suitable for depositing a WSi x layer on the interfacial layer, whereby the WSi x layer is at least 300 Å thick, contains less than 10 18 fluorine atoms/cc, comprises an average value of x within each strata of the WSi x layer that is between ±10% of the average bulk value of x through the thickness of the WSi x layer, and comprises a value of x of from about 2.0 to about 2.8.
Claim 30
Dependent Claim
177 words
A process for depositing a WSi x layer on a substrate, the process comprising the steps: (a) placing a substrate within a deposition zone; (b) during an initial stage, introducing a first process gas consisting of seeding gas into the deposition zone, and maintaining the deposition zone at process conditions suitable for depositing an interfacial layer on the substrate, the interfacial layer capable of serving as a seeding layer; and (c) during at least one subsequent stage, flowing a second process gas comprising silicon source gas and tungsten source gas into the deposition zone, and maintaining the deposition zone at process conditions suitable for depositing a WSi x layer on the interfacial layer, whereby the WSi x layer is at least 300 Å thick, contains less than 10 18 fluorine atoms/cc, comprises an average value of x within each strata of the WSi x layer that is between ±10% of the average bulk value of x through the thickness of the WSi x layer, and comprises a value of x of from about 2.0 to about 2.8.
Claim 31
Dependent Claim
22 words
The process of claim 27 wherein the seeding gas comprises one or more of monosilane, disilane, trisilane, dichlorosilane, or H 2 .
Claim 32
Dependent Claim
15 words
The process of claim 27 wherein the seeding gas consists of a silicon source gas.
Claim 33
Dependent Claim
12 words
The process of claim 27 wherein the seeding gas consists of monosilane.
Claim 34
Dependent Claim
26 words
The process of claim 27 wherein the silicon source gas and the tungsten source gas are combined at least 2.5 inches upstream of the deposition chamber.
Claim 35
Dependent Claim
21 words
The process of claim 27 wherein the silicon source gas comprises dichlorosilane and the tungsten source gas comprises WF 6 .
Claim 36
Dependent Claim
22 words
The process of claim 32 wherein the volumetric flow ratio of dichlorosilane to WF 6 is from about 5:1 to about 400:1.
Claim 37
Dependent Claim
41 words
The process of claim 27 wherein the seeding gas is introduced into the deposition zone only at the onset of the process and for a sufficient period to deposit an interfacial layer comprising WSi x having a substantially uniform Si:W ratio.
Claim 38
Dependent Claim
21 words
The process of claim 27 wherein the seeding gas is introduced in the deposition zone for less than about 20 seconds.
Claim 39
Dependent Claim
130 words
A process for depositing a WSi x layer on a substrate, the process comprising the steps: (a) placing a substrate within a deposition zone; (b) during an initial stage, introducing a first process gas consisting of seeding gas into the deposition zone, and maintaining the deposition zone at process conditions suitable for depositing an interfacial layer on the substrate, the interfacial layer capable of serving as a seeding layer; and (c) during at least one subsequent stage, forming a second process gas by combining a silicon source gas and a tungsten source gas at least 2.5 inches upstream of the deposition chamber, flowing the second process gas into the deposition zone, and maintaining the deposition zone at process conditions suitable for depositing a WSi x layer on the interfacial layer.
Claim 40
Dependent Claim
130 words
A process for depositing a WSi x layer on a substrate, the process comprising the steps: (a) placing a substrate within a deposition zone; (b) during an initial stage, introducing a first process gas consisting of seeding gas into the deposition zone, and maintaining the deposition zone at process conditions suitable for depositing an interfacial layer on the substrate, the interfacial layer capable of serving as a seeding layer; and (c) during at least one subsequent stage, forming a second process gas by combining a silicon source gas and a tungsten source gas at least 2.5 inches upstream of the deposition chamber, flowing the second process gas into the deposition zone, and maintaining the deposition zone at process conditions suitable for depositing a WSi x layer on the interfacial layer.
Claim 41
Dependent Claim
15 words
The process of claim 36 wherein the seeding gas consists of a silicon source gas.
Claim 42
Dependent Claim
22 words
The process of claim 36 wherein the seeding gas comprises one or more of monosilane, disilane, trisilane, dichlorosilane, or H 2 .
Claim 43
Dependent Claim
21 words
The process of claim 36 wherein the silicon source gas comprises dichlorosilane and the tungsten source gas comprises WF 6 .
Claim 44
Dependent Claim
22 words
The process of claim 39 wherein the volumetric flow ratio of dichlorosilane to WF 6 is from about 5:1 to about 400:1.
Claim 45
Dependent Claim
12 words
The process of claim 36 wherein the seeding gas consists of monosilane.
Claim 46
Dependent Claim
41 words
The process of claim 36 wherein the seeding gas is introduced into the deposition zone only at the onset of the process and for a sufficient period to deposit an interfacial layer comprising WSi x having a substantially uniform Si:W ratio.
Claim 47
Dependent Claim
21 words
The process of claim 36 wherein the seeding gas is introduced in the deposition zone for less than about 20 seconds.
Claim 48
Dependent Claim
178 words
A chemical vapor deposition process for depositing WSi x on a substrate, the process comprising the steps of: (a) placing a substrate within a deposition zone; (b) forming a process gas by combining dicholorosilane and WF 6 in a feedline at least about 2.5 inches upstream from the deposition zone; (c) introducing the process gas into the deposition zone; (d) maintaining the pressure in the deposition zone sufficiently low and heating the substrate to a temperature sufficiently high to deposit WSi x on the substrate, wherein the process gas is combined sufficiently upstream of the deposition zone so that the process gas is substantially uniform when introduced into the deposition zone, and whereby the uniform process gas deposits a substantially uniform, substantially fluorine-free layer of WSi x on the substrate, the WSi x layer having an average value of x within each strata of the WSi x layer that is between ±10% of the average bulk value of x through the thickness of the WSi x layer, the value of x being from about 2.0 to about 2.8.
Claim 49
Dependent Claim
178 words
A chemical vapor deposition process for depositing WSi x on a substrate, the process comprising the steps of: (a) placing a substrate within a deposition zone; (b) forming a process gas by combining dicholorosilane and WF 6 in a feedline at least about 2.5 inches upstream from the deposition zone; (c) introducing the process gas into the deposition zone; (d) maintaining the pressure in the deposition zone sufficiently low and heating the substrate to a temperature sufficiently high to deposit WSi x on the substrate, wherein the process gas is combined sufficiently upstream of the deposition zone so that the process gas is substantially uniform when introduced into the deposition zone, and whereby the uniform process gas deposits a substantially uniform, substantially fluorine-free layer of WSi x on the substrate, the WSi x layer having an average value of x within each strata of the WSi x layer that is between ±10% of the average bulk value of x through the thickness of the WSi x layer, the value of x being from about 2.0 to about 2.8.
Claim 50
Dependent Claim
23 words
The process of claim 44 wherein the process gas comprises a seeding gas for initiating the deposition of WSi x onto the substrate.
Claim 51
Dependent Claim
19 words
The process of claim 44 wherein the substrate is heated to a temperature of at least about 500° C.
Claim 52
Dependent Claim
22 words
The process of claim 44, wherein the volumetric flow ratio of DCS to WF 6 is from about 5:1 to about 400:1.
References Cited (Backward Citations)
US4180596A
Cited
US4391846A
Cited
US4629635A
Cited
US5183782A
Cited
US5231056A
Cited
US5326723A
Cited
US5500249A
Cited
JPH07100860A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-12-06 | 2003-06-07 | 2003-12-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-12-06 | 2007-06-07 | 2007-12-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-12-06 | 2011-06-07 | 2011-12-07 | $7700.00 | Window Closed / Lapsed |