Uniform tungsten silicide films produced by chemical vapor deposition
Assignee: Applied Materials Inc
•
Filing: 1993-05-18
•
Granted: 1996-03-19
•
Expires: 2013-05-18
Abstract
Abstract A tungsten silicide film is deposited from WF 6 and SiCl 2 H 2 onto a substrate so that the tungsten to silicon ratio is substantially uniform through the thickness of the WSi x film, and the WSi x film is substantially free of fluorine. The film can be deposited by a multi-stage process where the pressure in the chamber is varied, or by a high temperature, high pressure deposition process in a plasma cleaned deposition chamber. Preferably the SiCl 2 H 2 and the WF 6 are mixed upstream of the deposition chamber. A seeding gas can be added to the process gases.
Inventors
- 👤 Susan G. Telford
- 👤 Meng C. Tseng
- 👤 Michio Aruga
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 00:05
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/44; C23C16/455; C23C16/45512; C23C16/22; C23C16/30; C23C16/42; C23C16/4401; C23C16/4405; C23C16/45561; Y; Y10; Y10S; Y10S148/00; Y10S148/019; Y10S148/027
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
130 words
A chemical vapor deposition process for depositing a substantially uniform, substantially fluorine free layer of WSi x on a substrate, the process comprising the steps of: (a) placing a substrate within a deposition zone; (b) during an initial deposition stage, (i) introducing seeding gas, dichlorosilane and tungsten hexa-fluoride into the deposition zone; and (ii) maintaining the deposition zone at process conditions suitable for depositing an interfacial layer of WSi x having a substantially uniform Si:W ratio directly on the substrate; and (c) during a second deposition stage, (i) stopping flow of the seeding gas, while continuing to flow dichlorosilane and tungsten hexa-fluoride into the deposition zone; and (ii) maintaining the deposition zone at process conditions suitable for depositing a substantially uniform WSi x layer on the interfacial WSi x layer.
Claim 2
Dependent Claim
130 words
A chemical vapor deposition process for depositing a substantially uniform, substantially fluorine free layer of WSi x on a substrate, the process comprising the steps of: (a) placing a substrate within a deposition zone; (b) during an initial deposition stage, (i) introducing seeding gas, dichlorosilane and tungsten hexa-fluoride into the deposition zone; and (ii) maintaining the deposition zone at process conditions suitable for depositing an interfacial layer of WSi x having a substantially uniform Si:W ratio directly on the substrate; and (c) during a second deposition stage, (i) stopping flow of the seeding gas, while continuing to flow dichlorosilane and tungsten hexa-fluoride into the deposition zone; and (ii) maintaining the deposition zone at process conditions suitable for depositing a substantially uniform WSi x layer on the interfacial WSi x layer.
Claim 3
Dependent Claim
25 words
The process of claim 1 wherein in step (b) the seeding gas is selected from the group consisting of SiH 4 and H 2 .
Claim 4
Dependent Claim
25 words
The process of claim 1 wherein in step (b) the volumetric flow rate of the seeding gas ranges from about 10 to about 500 sccm.
Claim 5
Dependent Claim
33 words
The process of claim 1 wherein in step (b) the total volume of seeding gas introduced into the deposition zone during the initial deposition stages ranges from about 1 to about 125 scc.
Claim 6
Dependent Claim
21 words
The process of claim 1, wherein in both stages the substrate is heated to a temperature of at least 500° C.
Claim 7
Dependent Claim
24 words
The process of claim 5, wherein in both stages the substrate is heated to a temperature from about 550° C. to about 700° C.
Claim 8
Dependent Claim
24 words
The process of claim 1, wherein in both stages the pressure in the deposition zone is from about 1 Torr to about 20 Torr.
Claim 9
Dependent Claim
35 words
The process of claim 1, wherein in both stages the DCS and WF 6 is combined sufficiently upstream of the deposition zone that the process gas is substantially uniform when introduced into the deposition zone.
Claim 10
Dependent Claim
25 words
The process of claim 1, wherein in both stages the volumetric flow ratio of DCS to WF 6 is from about 5:1 to about 400:1.
Claim 11
Dependent Claim
20 words
The process of claim 1 wherein the substrate is selected from the group consisting of silicon, silicon oxide, and polysilicon.
Claim 12
Dependent Claim
32 words
The process of claim 1 further comprising the step of annealing the WSi x layer on the substrate, and wherein the WSi x layer does not separate from the substrate during annealing.
References Cited (Backward Citations)
US4391846A
Cited
US4692343A
Cited
US4737474A
Cited
US5183510A
Cited
US5203956A
Cited
US4966869A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-03-19 | 1999-09-18 | 2000-03-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-03-19 | 2003-09-18 | 2004-03-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-03-19 | 2007-09-18 | 2008-03-19 | $7700.00 | Window Closed / Lapsed |