Elevated source/drain salicide CMOS technology
Assignee: Advanced Micro Devices Inc
•
Filing: 1998-07-09
•
Granted: 1999-11-30
•
Expires: 2018-07-09
Abstract
Abstract Low resistivity metal silicide layers are formed on a gate electrode and source/drain regions at an optimum thickness for reducing parasitic series resistances with an attendant consumption of silicon from the gate electrode and source/drain regions. Consumed silicon from the gate electrode and source/drain regions is then replaced employing metal induced crystallization, thereby avoiding a high leakage current. Embodiments include depositing a layer of amorphous silicon on the metal silicide layers and heating at a temperature of about 400° C. to about 600° C. initiating metal induced crystallization, thereby causing the metal silicide layers grow upwardly as silicon in the underlying gate electrode and source/drain regions is replaced.
Inventors
- 👤 Qi Xiang
- 👤 Shekhar Pramanick
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 21:30
CPC Classifications
H; H10; H10D; H10D62/00; H10D62/10; H10D62/13; H10D62/149; H10D62/151; H10D30/00; H10D30/01; H10D30/021; H10D30/0223; H10D30/0227; H10D30/027; H10D30/0275; H10D30/60; H10D30/601; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112; H10D64/0113; H10D64/013; H10D64/01302; H10D64/01304; H10D64/01306; H10D64/01308; H10D64/0131; H10D64/01324; H10D64/20; H10D64/23; H10D64/251; H10D64/258; H10D64/259; H10D64/60; H10D64/66; H10D64/661; H10D64/662; H10D64/663; H10D30/0212; Y; Y10; Y10S; Y10S148/00; Y10S148/147
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
244 words
A method of manufacturing a semiconductor device, the method comprising: forming a structure comprising: a crystalline silicon substrate having a main surface; source/drain regions extending from the main surface into the substrate with a channel region therebetween; a gate dielectric layer on the substrate over the channel region; a polycrystalline silicon gate electrode, having side surfaces and a first height defined between a first upper surface and a lower surface, on the gate dielectric layer; and a dielectric sidewall spacer on each side surface of the gate electrode, leaving a portion of each source/drain region exposed; forming a metal silicide layer: on the first upper surface of the gate electrode, thereby reducing the first height of the gate electrode to a second height defined between a second upper surface and the lower surface; and on each exposed source/drain region extending below the main surface into each source/drain region; depositing a layer of amorphous silicon on the metal silicide layers and on the sidewall spacers; and heating to cause metal induced crystallization, thereby: crystallizing the amorphous silicon layers on the source/drain regions while the metal silicide layers on the source/drain regions move upwardly such that the metal silicide layers do not extend below the main surface; and crystallizing the amorphous silicon layer on the second upper surface gate electrode while the metal silicide layer on the gate electrode moves upwardly such that it does not extend below the first upper surface of the gate electrode.
Claim 2
Independent Claim
244 words
A method of manufacturing a semiconductor device, the method comprising: forming a structure comprising: a crystalline silicon substrate having a main surface; source/drain regions extending from the main surface into the substrate with a channel region therebetween; a gate dielectric layer on the substrate over the channel region; a polycrystalline silicon gate electrode, having side surfaces and a first height defined between a first upper surface and a lower surface, on the gate dielectric layer; and a dielectric sidewall spacer on each side surface of the gate electrode, leaving a portion of each source/drain region exposed; forming a metal silicide layer: on the first upper surface of the gate electrode, thereby reducing the first height of the gate electrode to a second height defined between a second upper surface and the lower surface; and on each exposed source/drain region extending below the main surface into each source/drain region; depositing a layer of amorphous silicon on the metal silicide layers and on the sidewall spacers; and heating to cause metal induced crystallization, thereby: crystallizing the amorphous silicon layers on the source/drain regions while the metal silicide layers on the source/drain regions move upwardly such that the metal silicide layers do not extend below the main surface; and crystallizing the amorphous silicon layer on the second upper surface gate electrode while the metal silicide layer on the gate electrode moves upwardly such that it does not extend below the first upper surface of the gate electrode.
Claim 3
Dependent Claim
41 words
The method according to claim 1, wherein; silicon in each source/drain region and gate electrode is consumed during formation of the metal silicide layers; and the consumed silicon in the source/drain region gate electrode is substantially restored during metal induced crystallization.
Claim 4
Dependent Claim
39 words
The method according to claim 2, comprising heating to cause the metal induced crystallization to crystallize: the amorphous silicon layer on the source/drain regions into monocrystalline silicon; and the amorphous silicon layer on the gate electrode into polycrystalline silicon.
Claim 5
Dependent Claim
161 words
The method according to claim 3, comprising replacing the consumed silicon by: depositing a layer of amorphous silicon on the metal silicide layers and on the sidewall spacers; heating at a temperature of about 400° C. to about 600° C. to cause metal induced crystallization, thereby: crystallizing the amorphous silicon layers on the source/drain regions into monocrystalline silicon while the metal silicide layers on the source/drain regions move upwardly such that the metal silicide layers do not extend below the main surface; and crystallizing the amorphous silicon layer on the gate electrode into polycrystalline silicon while the metal silicide layer on the gate electrode moves upwardly such that the metal silicide layer does not extend below the first upper surface of the gate electrode; and removing remaining amorphous silicon on the sidewall spacers by wet etching employing the metal silicide on the gate electrode and source/drain regions as a mask to protect the gate electrode and source/drain regions, respectively, from etching.
Claim 6
Dependent Claim
24 words
The method according to claim 4, comprising depositing the amorphous silicon at a temperature of about 180° C. to less than about 280° C.
Claim 7
Dependent Claim
28 words
The method according to claim 4, wherein each source/drain region comprises a shallow extension region under the sidewall spacer and a heavily doped region constituting the exposed portion.
Claim 8
Dependent Claim
16 words
The method according to claim 1, further comprising removing remaining amorphous silicon on the sidewall spacers.
Claim 9
Dependent Claim
46 words
The method according to claim 7, comprising removing the amorphous silicon by wet etching employing the metal silicide layer on a gate electrode and the metal silicide layer on the source/drain regions as a mask to protect the gate electrode and source/drain regions, respectively, from etching.
Claim 10
Dependent Claim
25 words
The method according to claim 1, comprising heating at a temperature of about 400° C. to about 600° C. to cause the metal induced crystallization.
Claim 11
Dependent Claim
34 words
The method according to claim 1, comprising depositing the layer of amorphous silicon at a temperature of about 180° C. to less than about 280° C. by physical vapor deposition or chemical vapor deposition.
Claim 12
Dependent Claim
21 words
The method according to claim 1, comprising depositing the amorphous silicon layer at a thickness of about 200Å to about 1000Å.
Claim 13
Dependent Claim
18 words
The method according to claim 1, wherein the metal silicide comprises titanium silicide, nickel silicide or cobalt silicide.
Claim 14
Dependent Claim
16 words
The method according to claim 12, wherein the metal silicide comprises nickel silicide or cobalt silicide.
Claim 15
Dependent Claim
24 words
the method according to claim 1, wherein each sidewall spacer comprises silicon dioxide, silicon nitride, or a composite of silicon dioxide and silicon nitride.
Claim 16
Dependent Claim
28 words
The method according to claim 1, wherein each source/drain region comprises a shallow extension region under the sidewall spacer and a heavily doped region constituting the exposed portion.
Claim 17
Dependent Claim
18 words
The method according to claim 1, wherein each source/drain region has a junction depth less than about 800Å.
Claim 18
Independent Claim
195 words
A method of manufacturing a semiconductor device, the method comprising: forming a structure comprising: a crystalline silicon substrate having a main surface; source/drain regions extending from the main surface into the substrate with a channel region therebetween; a gate dielectric layer on the substrate over the channel region; a polycrystalline silicon gate electrode, having side surfaces and a first height defined between a first upper surface and a lower surface, on the gate dielectric layer; and a dielectric sidewall spacer on each side surface of the gate electrode leaving a portion of each source/drain region exposed; forming a metal silicide layer, comprising titanium silicide, nickel silicide or cobalt silicide: on and extending below the first upper surface of the gate electrode thereby reducing the first height of the gate electrode to a second height defined between a second upper surface and the lower surface; and on each exposed source/drain region extending below the main surface into each source/drain region, wherein silicon in the gate electrode and in each source/drain region is consumed during metal silicide formation; and replacing the consumed silicon in the gate electrode and source/drain regions while moving the metal silicide layers upwardly.
Claim 19
Independent Claim
195 words
A method of manufacturing a semiconductor device, the method comprising: forming a structure comprising: a crystalline silicon substrate having a main surface; source/drain regions extending from the main surface into the substrate with a channel region therebetween; a gate dielectric layer on the substrate over the channel region; a polycrystalline silicon gate electrode, having side surfaces and a first height defined between a first upper surface and a lower surface, on the gate dielectric layer; and a dielectric sidewall spacer on each side surface of the gate electrode leaving a portion of each source/drain region exposed; forming a metal silicide layer, comprising titanium silicide, nickel silicide or cobalt silicide: on and extending below the first upper surface of the gate electrode thereby reducing the first height of the gate electrode to a second height defined between a second upper surface and the lower surface; and on each exposed source/drain region extending below the main surface into each source/drain region, wherein silicon in the gate electrode and in each source/drain region is consumed during metal silicide formation; and replacing the consumed silicon in the gate electrode and source/drain regions while moving the metal silicide layers upwardly.
Claim 20
Dependent Claim
25 words
The method according to claim 17, wherein each sidewall spacer comprises a silicon, dioxide, silicon nitride, or a composite of silicon dioxide and silicon nitride.
Claim 21
Dependent Claim
19 words
The method according to claim 17, wherein each source/drain region has a junction depth less than about 800 Å.
Claim 22
Dependent Claim
19 words
The method according to claim 17, wherein each source/drain region has a junction depth of about 500Å or less.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-11-29 | 2003-05-31 | 2003-11-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-11-29 | 2007-05-31 | 2007-11-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-11-29 | 2011-05-31 | 2011-11-30 | $7700.00 | Window Closed / Lapsed |