US4835112A
Expired / Lapsed
US
⏱️ 0.0 years remaining
CMOS salicide process using germanium implantation
Assignee: NXP USA Inc
•
Filing: 1988-03-08
•
Granted: 1989-05-30
•
Expires: 2008-03-08
Abstract
Abstract A salicided twin-tub CMOS process using germanium implantation to retard the diffusion of the dopants, such as phosphorus and boron. Implantation of n+ and p+ dopants after titanium salicidation is employed to fabricate devices with low junction leakage and good short-channel effects. Also, the germanium dopant may be introduced before or after the formation of the refractory metal silicide formation, and may be implanted independently or together with the dopant whose diffusion in the silicon it will modify. The employment of germanium permits the use of a phosphorus implant through a relatively thick refractory metal silicide contact layer. If arsenic is implanted through the silicide layer to solve the deep junction problem, the silicide layer must be thin to permit the passage of the larger arsenic atoms typically stopped by the silicide. Thinner silicide layers have the disadvantage of higher sheet resistances.
Inventors
- 👤 James R. Pfiester
- 👤 John R. Yeargain
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 19:39
CPC Classifications
H; H10; H10P; H10P30/00; H10P30/20; H10P30/202; H10P30/204; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0223; H10D30/0227; H10D30/60; H10D62/00; H10D62/10; H10D62/13; H10D62/149; H10D62/151; H10D84/00; H10D84/01; H10D84/0123; H10D84/0126; H10D84/0165; H10D84/0172; H10D84/0174; H10D84/02; H10D84/03; H10D84/038; H10P30/208; H10P30/21; H10P30/212; H10P30/28; H10P32/00; Y; Y10; Y10S; Y10S257/00; Y10S257/90
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
141 words
A process for fabricating a field effect transistor (FET) on a semiconductor substrate, comprising the steps of: providing a semiconductor substrate having a surface; providing a dielectric layer over the surface of the semiconductor substrate; providing a conductive gate on the dielectric layer; and thereafter performing the following steps in the following order: introducing germanium into future source/drain regions of the semiconductor substrate on either side of the conductive gate; removing at least a portion of the dielectric layer over the future source/drain regions to form openings; forming refractory metal silicide layers in the openings in the dielectric layer over the future source/drain regions; introducing a conductivity altering dopant into the future source/drain regions in the substrate; and annealing the conductivity altering dopant to form source/drain regions whereby the diffusion of the dopant is retarded by the presence of the germanium.
Claim 2
Dependent Claim
141 words
A process for fabricating a field effect transistor (FET) on a semiconductor substrate, comprising the steps of: providing a semiconductor substrate having a surface; providing a dielectric layer over the surface of the semiconductor substrate; providing a conductive gate on the dielectric layer; and thereafter performing the following steps in the following order: introducing germanium into future source/drain regions of the semiconductor substrate on either side of the conductive gate; removing at least a portion of the dielectric layer over the future source/drain regions to form openings; forming refractory metal silicide layers in the openings in the dielectric layer over the future source/drain regions; introducing a conductivity altering dopant into the future source/drain regions in the substrate; and annealing the conductivity altering dopant to form source/drain regions whereby the diffusion of the dopant is retarded by the presence of the germanium.
Claim 3
Dependent Claim
36 words
The process of claim 1 wherein the semiconductor substrate is selected from the group consisting of polycrystalline, monocrystalline and amorphous silicon, and the conductivity altering dopant is selected from the group consisting of phosphorus and boron.
Claim 4
Dependent Claim
11 words
The process of claim 1 wherein the refractory metal is titanium.
Claim 5
Dependent Claim
38 words
The process of claim 1 wherein after the provision of the conductive gate, a sidewall spacer is formed around the gate, and further wherein the future source/drain regions are spaced apart from the gate by the sidewall spacer.
Claim 6
Dependent Claim
17 words
The process of claim 1 wherein the conductivity altering dopant is implanted through the refractory metal silicide.
Claim 7
Dependent Claim
163 words
A process for fabricating a field effect transistor (FET) on a semiconductor substrate, comprising the steps of: providing a semiconductor substrate having a surface; providing a dielectric layer over the surface of the semiconductor substrate; providing a gate electrode on the dielectric layer; and thereafter performing the following steps in the following order: introducing germanium into future source/drain regions of the semiconductor substrate on either side of the conductive gate; introducing a first conductivity altering dopant into future source/drain regions of the semiconductor substrate on either side of the gate electrode; removing at least a portion of the dielectric layer over the future source/drain regions to form openings; forming refractory metal silicide layers in the openings in the dielectric layer over the future source/drain regions; introducing a second conductivity altering dopant into the future source/drain regions in the substrate; and annealing the conductivity altering dopants to form source/drain regions whereby the diffusion of the dopant is retarded by the presence of the germanium.
Claim 8
Dependent Claim
163 words
A process for fabricating a field effect transistor (FET) on a semiconductor substrate, comprising the steps of: providing a semiconductor substrate having a surface; providing a dielectric layer over the surface of the semiconductor substrate; providing a gate electrode on the dielectric layer; and thereafter performing the following steps in the following order: introducing germanium into future source/drain regions of the semiconductor substrate on either side of the conductive gate; introducing a first conductivity altering dopant into future source/drain regions of the semiconductor substrate on either side of the gate electrode; removing at least a portion of the dielectric layer over the future source/drain regions to form openings; forming refractory metal silicide layers in the openings in the dielectric layer over the future source/drain regions; introducing a second conductivity altering dopant into the future source/drain regions in the substrate; and annealing the conductivity altering dopants to form source/drain regions whereby the diffusion of the dopant is retarded by the presence of the germanium.
Claim 9
Dependent Claim
36 words
The process of claim 6 wherein the semiconductor substrate is selected from the group consisting of polycrystalline, monocrystalline and amorphous silicon, and the conductivity altering dopant is selected from the group consisting of phosphorus and boron.
Claim 10
Dependent Claim
11 words
The process of claim 6 wherein the refractory metal is titanium.
Claim 11
Dependent Claim
38 words
The process of claim 6 wherein after the provision of the conductive gate, a sidewall spacer is formed around the gate, and further wherein the future source/drain regions are spaced apart from the gate by the sidewall spacer.
Claim 12
Dependent Claim
173 words
A process for fabricating a field effect transistor (FET) on a semiconductor substrate, comprising the steps of: providing a semiconductor substrate having a surface; providing a dielectric layer over the surface of the semiconductor substrate; providing a conductive gate on the dielectric layer; and performing the following steps in the following order: introducing a first conductivity altering dopant into future source/drain regions of the semiconductor substrate on either side of the conductive gate; forming sidewall spacers around the conductive gate; introducing germanium into future source/drain regions in the semiconductor substrate on either side of the sidewall spacers of the conductive gate; removing at least a portion of the dielectric layer over the future source/drain regions to form openings; forming refractory metal silicide layers in the openings in the dielectric layer over the future source/drain regions; introducing a second conductivity altering dopant into the future source/drain regions in the substrate; and annealing the conductivity altering dopants to form source/drain regions whereby the diffusion of the dopant is retarded by the presence of the germanium.
Claim 13
Dependent Claim
173 words
A process for fabricating a field effect transistor (FET) on a semiconductor substrate, comprising the steps of: providing a semiconductor substrate having a surface; providing a dielectric layer over the surface of the semiconductor substrate; providing a conductive gate on the dielectric layer; and performing the following steps in the following order: introducing a first conductivity altering dopant into future source/drain regions of the semiconductor substrate on either side of the conductive gate; forming sidewall spacers around the conductive gate; introducing germanium into future source/drain regions in the semiconductor substrate on either side of the sidewall spacers of the conductive gate; removing at least a portion of the dielectric layer over the future source/drain regions to form openings; forming refractory metal silicide layers in the openings in the dielectric layer over the future source/drain regions; introducing a second conductivity altering dopant into the future source/drain regions in the substrate; and annealing the conductivity altering dopants to form source/drain regions whereby the diffusion of the dopant is retarded by the presence of the germanium.
Claim 14
Dependent Claim
36 words
The process of claim 10 wherein the semiconductor substrate is selected from the group consisting of polycrystalline, monocrystalline and amorphous silicon, and the conductivity altering dopant is selected from the group consisting of phosphorus and boron.
Claim 15
Dependent Claim
11 words
The process of claim 10 wherein the refractory metal is titanium.
Claim 16
Dependent Claim
63 words
The process of claim 10 wherein the first conductivity altering dopant and the second conductivity altering dopant are selected from the group consisting of phosphorus, arsenic and boron, and the first conductivity altering dopant has a first impurity level and the second conductivity altering dopant has a second impurity level and the second impurity level is relatively greater than the first impurity level.
Claim 17
Dependent Claim
179 words
A process for fabricating a field effect transistor (FET) on a semiconductor substrate, comprising the steps of: providing a silicon substrate having a surface; providing a silicon dioxide layer over the surface of the silicon substrate; providing a conductive gate on the silicon dioxide layer; introducing phosphorus at a low impurity level into the silicon substrate on either side of the gate; providing a sidewall spacer around the gate; and performing the following steps in the following order; introducing germanium into future source/drain regions of the silicon substrate on either side of the sidewall spacer around the conductive gate; removing at least a portion of the dielectric layer over the future source/drain regions to form openings on either side of the sidewall spacer; forming a titanium silicide layer in the openings in the dielectric layer over the future source/drain regions; introducing phosphorus at a high impurity level into the future source/drain regions in the substrate; and annealing the conductivity altering dopant to form source/drain regions whereby the diffusion of the phosphorus is retarded by the presence of the germanium.
Claim 18
Dependent Claim
179 words
A process for fabricating a field effect transistor (FET) on a semiconductor substrate, comprising the steps of: providing a silicon substrate having a surface; providing a silicon dioxide layer over the surface of the silicon substrate; providing a conductive gate on the silicon dioxide layer; introducing phosphorus at a low impurity level into the silicon substrate on either side of the gate; providing a sidewall spacer around the gate; and performing the following steps in the following order; introducing germanium into future source/drain regions of the silicon substrate on either side of the sidewall spacer around the conductive gate; removing at least a portion of the dielectric layer over the future source/drain regions to form openings on either side of the sidewall spacer; forming a titanium silicide layer in the openings in the dielectric layer over the future source/drain regions; introducing phosphorus at a high impurity level into the future source/drain regions in the substrate; and annealing the conductivity altering dopant to form source/drain regions whereby the diffusion of the phosphorus is retarded by the presence of the germanium.
References Cited (Backward Citations)
US4111719A
Cited
US4622735A
Cited
US4385938A
Cited
US4558507A
Cited
US4616399A
Cited
US4617066A
Cited
US4683645A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-29 | 1992-11-28 | 1993-05-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-29 | 1996-11-28 | 1997-05-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-29 | 2000-11-28 | 2001-05-30 | $7700.00 | Window Closed / Lapsed |