Abstract
Abstract p- and n- layers in GaAs by dual implants with either Ge and Ga or Ge and As into GaAs have been produced. The amphoteric behavior of Ge implants is modified in a predictable manner through control of ion dose and annealing temperature by dual implantation. The (Ge+Ga) dual implants have produced p-type conductivity for all doses up to an anneal temperature of 900 DEG C. The (Ge+As) dual implants have yielded a significant enhancement of the n-type activity for ion doses >/=1x1015/cm2, a conductivity type conversion for intermediate doses and little effect upon p-type activity for ion doses </=3x1013/cm2. By selecting appropriate ion energy, ion dose, and annealing temperature, formation of p-n junction is envisioned.
Inventors
- 👤 Yoon S. Park
- 👤 Yung K. Yeo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 23:03
CPC Classifications
H; H10; H10P; H10P30/00; H10P30/20; H10P30/202; H10P30/206; H10P30/218; Y; Y10; Y10S; Y10S148/00; Y10S148/084
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
78 words
A method of forming a p-n junction in semiconducting GaAs device comprising: a. dual ion implantation of Ge and Ga to provide a layer having p-type conductivity activity; b. forming an n-layer by dual ion implantation of Ge and As at a dose in the range from about 1×10 14 /cm 2 extending to at least 3×10 15 /cm 2 at an energy level substantially less than that used to form the p-layer; and c. annealing said device.
Claim 2
Independent Claim
78 words
A method of forming a p-n junction in semiconducting GaAs device comprising: a. dual ion implantation of Ge and Ga to provide a layer having p-type conductivity activity; b. forming an n-layer by dual ion implantation of Ge and As at a dose in the range from about 1×10 14 /cm 2 extending to at least 3×10 15 /cm 2 at an energy level substantially less than that used to form the p-layer; and c. annealing said device.
Claim 3
Dependent Claim
15 words
The method of claim 1, wherein the annealing temperature is approximately 900° C. or less.
Claim 4
Dependent Claim
72 words
The method of claim 1, wherein said GaAs is Cr doped; wherein preceding step (a) the surface is prepared by a lap and polish followed by a chemical etch; wherein step (a) comprises an ion dose at approximately 3×10 13 /cm 2 at an energy level of approximately 400 keV; and wherein step (b) comprises an ion dose of approximately 1×10 15 /cm 2 at an energy level of approximately 100 keV.
Claim 5
Dependent Claim
150 words
The method of claim 3, wherein between steps (b) and (c) the device is cleaned and then encapsulated with approximately 1000 angstroms of oxygen-free Si 3 N 4 in a pyrolytic reactor which provides rapid heating and fast deposition, the Si 3 N 4 deposition time being approximately 35 seconds at 700° C. with the device brought to 700° C. within 9 seconds; wherein the annealing step (c) is done in flowing hydrogen at a temperature of 700° C. to 1,000° C., and during the annealing step the device rests cap-side down on a bare GaAs substrate; wherein after the annealing step the encapsulant is stripped in 48% hydrofluoric acid; and wherein after the annealing step an indium electrical contact is formed on the device using an ultrasonic soldering iron, following which the contact is heated at 300° C. for three minutes in flowing argon gas to produce ohmic behavior.
Claim 6
Independent Claim
60 words
A method of forming a layer in a semi-insulating GaAs device comprising: a. dual ion implantation of Ge and Ga with any dose from at least as low as 1×10 13 /cm 2 up to at least 3×10 15 /cm 2 ; and b. annealing, wherein an annealing temperature up to 900° C. produces p-type conductivity activity in said layer.
Claim 7
Independent Claim
60 words
A method of forming a layer in a semi-insulating GaAs device comprising: a. dual ion implantation of Ge and Ga with any dose from at least as low as 1×10 13 /cm 2 up to at least 3×10 15 /cm 2 ; and b. annealing, wherein an annealing temperature up to 900° C. produces p-type conductivity activity in said layer.
Claim 8
Dependent Claim
63 words
The method of claim 5, wherein a conductivity type conversion occurs for ion doses equal or greater than 1×10 15 /cm 2 followed by annealing at a temperature of 900° C. to 950° C.; and wherein n-type activity is produced for ion doses of approximately 1×10 15 /cm 2 or above followed by annealing at a temperature of approximately 950° C. or above.
Claim 9
Independent Claim
97 words
A method of forming a layer in a semi-insulating GaAs device comprising: a. dual ion implantation of Ge and As at a dose in the range of approximately 1×10 14 /cm 2 up to at least 3×10 15 /cm 2 to produce n-type conductivity in said layer; and b. annealing at a temperature in the range of at least 700° to 1,000° C.; wherein a conductivity type conversion occurs for ion doses of approximately 1×10 14 /cm 2 ; and wherein p-type conductivity activity results from an ion dose of approximately 3×10 13 /cm 2 or below.
Claim 10
Independent Claim
97 words
A method of forming a layer in a semi-insulating GaAs device comprising: a. dual ion implantation of Ge and As at a dose in the range of approximately 1×10 14 /cm 2 up to at least 3×10 15 /cm 2 to produce n-type conductivity in said layer; and b. annealing at a temperature in the range of at least 700° to 1,000° C.; wherein a conductivity type conversion occurs for ion doses of approximately 1×10 14 /cm 2 ; and wherein p-type conductivity activity results from an ion dose of approximately 3×10 13 /cm 2 or below.
Claim 11
Independent Claim
52 words
A method of forming a layer in a semi-insulating GaAs device comprising: a. dual ion implantation of Ge and As with a dose up to 3×10 13 /cm 2 , and b. annealing, wherein any annealing temperature in the range of 700° to 1,000° C. produces p-type conductivity activity in said layer.
Claim 12
Independent Claim
52 words
A method of forming a layer in a semi-insulating GaAs device comprising: a. dual ion implantation of Ge and As with a dose up to 3×10 13 /cm 2 , and b. annealing, wherein any annealing temperature in the range of 700° to 1,000° C. produces p-type conductivity activity in said layer.
Claim 13
Dependent Claim
105 words
The method of claim 5, 6, 7 or 8, wherein between the ion implanting and annealing steps the device is cleaned and then encapsulated with approximately 1000 angstroms of oxygen-free Si 3 N 4 in a pyrolytic reactor which provides rapid heating and fast deposition, the Si 3 N 4 deposition time being approximately 35 seconds at 700° C. with the device brought to 700° C. within 9 seconds; wherein the annealing step is done in flowing hydrogen at said temperature with the device resting cap-side down on a bare GaAs substrate; wherein after the annealing step the encapsulant is stripped in 48% hydrofluoric acid.
Claim 14
Dependent Claim
44 words
The method of claim 9, wherein after the annealing step an indium electrical contact is formed on the device using an ultrasonic soldering iron, following which the contact is heated at 300° C. for three minutes in flowing argon gas to produce ohmic behavior.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-05-30 | 1986-11-29 | 1987-05-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-05-30 | 1990-11-29 | 1991-05-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-05-30 | 1994-11-29 | 1995-05-31 | $7700.00 | Window Closed / Lapsed |