US5926728A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for fabricating tungsten polycide contacts
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1997-04-08
•
Granted: 1999-07-20
•
Expires: 2017-04-08
Abstract
Abstract A method for fabricating polycide contacts to semiconductor substrates, and more specifically for self-aligned contacts on substrates having field effect transistors (FETs) is achieved. After forming conventional FETs from a patterned first polysilicon layer provided with contact areas, an insulating layer is deposited. Self-aligned contact openings are etched in the insulating layer to the contact areas on the substrate, and a patterned polycide (second polysilicon/silicide) layer is used to form the electrical contacts and interconnections. However, in prior art when a photoresist mask and plasma etching are used to pattern a polycide layer, misalignment of the mask can result in notching in the sidewalls of the patterned second polysilicon layer resulting in contact damage and high leakage currents. The method of the present invention utilizes a critical pre-etch rapid thermal anneal (RTA) that essentially eliminates the notching during etching of these marginally misaligned contacts. This allows tighter design ground rules to be used without high leakage currents, thereby providing higher density integrated circuits with improved product yield.
Inventors
- 👤 Hsiang-Fan Lee
- 👤 Jhon-Jhy Liaw
- 👤 Yi-Miaw Lin
- 👤 Liang Szuma
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:32
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/069; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0113; H10W20/0698
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
207 words
A method for fabricating tungsten polycide contacts over and in contact openings to a semiconductor substrate for integrated circuits, comprising the steps of: providing said semiconductor substrate having device areas; depositing a first polysilicon layer on said substrate; patterning said first polysilicon layer and forming portions of semiconductor devices on said device areas; depositing an insulating layer over said patterned first polysilicon layer, and elsewhere on said device areas; photoresist masking and anisotropically plasma etching said contact openings in said insulating layer to said device areas adjacent to said semiconductor devices; depositing a second polysilicon layer in and over said contact openings and elsewhere on said insulating layer; depositing a tungsten silicide layer, by low-pressure chemical vapor deposition using a reactant gas of tungsten hexafluoride and dichlorosilane, on said second polysilicon layer, and forming a polycide layer; annealing said polycide layer on said substrate by rapid thermal anneal at a temperature of between 720 and 880° C. for 25 to 35 seconds; patterning said polycide layer by photoresist masking and anisotropic plasma etching leaving portions of said polycide layer over said contact openings, and furthermore said annealing preventing notching in sidewalls of said second polysilicon layer where said sidewalls are aligned over edges of said contact openings.
Claim 2
Independent Claim
207 words
A method for fabricating tungsten polycide contacts over and in contact openings to a semiconductor substrate for integrated circuits, comprising the steps of: providing said semiconductor substrate having device areas; depositing a first polysilicon layer on said substrate; patterning said first polysilicon layer and forming portions of semiconductor devices on said device areas; depositing an insulating layer over said patterned first polysilicon layer, and elsewhere on said device areas; photoresist masking and anisotropically plasma etching said contact openings in said insulating layer to said device areas adjacent to said semiconductor devices; depositing a second polysilicon layer in and over said contact openings and elsewhere on said insulating layer; depositing a tungsten silicide layer, by low-pressure chemical vapor deposition using a reactant gas of tungsten hexafluoride and dichlorosilane, on said second polysilicon layer, and forming a polycide layer; annealing said polycide layer on said substrate by rapid thermal anneal at a temperature of between 720 and 880° C. for 25 to 35 seconds; patterning said polycide layer by photoresist masking and anisotropic plasma etching leaving portions of said polycide layer over said contact openings, and furthermore said annealing preventing notching in sidewalls of said second polysilicon layer where said sidewalls are aligned over edges of said contact openings.
Claim 3
Dependent Claim
31 words
The method of claim 1, wherein said first polysilicon layer is heavily doped with a conductive dopant having a concentration of between about 1.0×10 19 and 1.0×10 21 atoms/cm 3 .
Claim 4
Dependent Claim
19 words
The method of claim 1, wherein first polysilicon layer has a thickness of between about 1500 and 2000 Angstroms.
Claim 5
Dependent Claim
31 words
The method of claim 1, wherein said patterned first polysilicon layer forms gate electrodes for field effect transistors, and further, sidewalls of said patterned first polysilicon layer have insulating sidewall spacers.
Claim 6
Dependent Claim
31 words
The method of claim 1, wherein said insulating layer is a silicon oxide deposited by plasma enhanced chemical vapor deposition and has a thickness of between about 2000 and 4000 Angstroms.
Claim 7
Dependent Claim
21 words
The method of claim 1, wherein said contact openings extend over said patterned first polysilicon layer, thereby forming self-aligned contact openings.
Claim 8
Dependent Claim
24 words
The method of claim 1, wherein said second polysilicon layer is deposited by low pressure chemical vapor deposition using a reactant gas of silane.
Claim 9
Dependent Claim
20 words
The method of claim 1, wherein said second poly-silicon layer has a thickness of between about 900 and 1100 Angstroms.
Claim 10
Dependent Claim
31 words
The method of claim 1, wherein said second polysilicon layer is heavily doped with a conductive dopant having a concentration of between about 1.0×10 20 and 1.0×10 21 atoms/cm 3 .
Claim 11
Dependent Claim
28 words
The method of claim 1, wherein said patterning of said polycide layer is carried out in a reactive ion etcher using an etch gas mixture containing chlorine ions.
Claim 12
Dependent Claim
235 words
A novel method for fabricating tungsten polycide contacts over and in self-aligned contact openings of field effect transistors for integrated circuits, comprising the steps of: providing a semiconductor substrate having device areas; depositing a first polysilicon layer on said substrate; patterning said first polysilicon layer and thereby forming gate electrodes for said field effect transistors on said device areas; depositing a conformal sidewall spacer insulating layer, and anisotropically etching back to form sidewall spacers on said gate electrodes; depositing an insulating layer over said patterned first polysilicon layer, and elsewhere on said device areas; photoresist masking and anisotropically plasma etching contact openings in said insulating layer to said device areas adjacent to and extending over said gate electrodes, thereby forming said self-aligned contact openings; depositing a second polysilicon layer in and over said self-aligned contact openings and elsewhere on said insulating layer; depositing a tungsten silicide layer on said second polysilicon layer, and forming a polycide layer; annealing said polycide layer on said substrate by rapid thermal anneal at a temperature of between about 720 and 880° C. for a time of between about 25 and 35 seconds; patterning said polycide layer by photoresist masking and anisotropic plasma etching leaving portions of said polycide layer over said self-aligned contact openings, and furthermore said annealing preventing notching in sidewalls of said second polysilicon layer where said sidewalls are aligned over edges of said self-aligned contact openings.
Claim 13
Dependent Claim
235 words
A novel method for fabricating tungsten polycide contacts over and in self-aligned contact openings of field effect transistors for integrated circuits, comprising the steps of: providing a semiconductor substrate having device areas; depositing a first polysilicon layer on said substrate; patterning said first polysilicon layer and thereby forming gate electrodes for said field effect transistors on said device areas; depositing a conformal sidewall spacer insulating layer, and anisotropically etching back to form sidewall spacers on said gate electrodes; depositing an insulating layer over said patterned first polysilicon layer, and elsewhere on said device areas; photoresist masking and anisotropically plasma etching contact openings in said insulating layer to said device areas adjacent to and extending over said gate electrodes, thereby forming said self-aligned contact openings; depositing a second polysilicon layer in and over said self-aligned contact openings and elsewhere on said insulating layer; depositing a tungsten silicide layer on said second polysilicon layer, and forming a polycide layer; annealing said polycide layer on said substrate by rapid thermal anneal at a temperature of between about 720 and 880° C. for a time of between about 25 and 35 seconds; patterning said polycide layer by photoresist masking and anisotropic plasma etching leaving portions of said polycide layer over said self-aligned contact openings, and furthermore said annealing preventing notching in sidewalls of said second polysilicon layer where said sidewalls are aligned over edges of said self-aligned contact openings.
Claim 14
Dependent Claim
31 words
The method of claim 11, wherein said first polysilicon layer is heavily doped with a conductive dopant having a concentration of between about 1.0×10 19 and 1.0×10 21 atoms/cm 3 .
Claim 15
Dependent Claim
20 words
The method of claim 11 wherein said first polysilicon layer has a thickness of between about 1500 and 2000 Angstroms.
Claim 16
Dependent Claim
33 words
The method of claim 11, wherein said insulating layer is composed of silicon oxide and is deposited by plasma enhanced chemical vapor deposition to a thickness of between about 2000 and 4000 Angstroms.
Claim 17
Dependent Claim
22 words
The method of claim 11, wherein said second polysilicon layer is deposited by chemical vapor deposition using a reactant gas of silane.
Claim 18
Dependent Claim
20 words
The method of claim 11, wherein said second poly-silicon layer has a thickness of between about 900 and 1100 Angstroms.
Claim 19
Dependent Claim
31 words
The method of claim 11, wherein said second polysilicon layer is heavily doped with a conductive dopant having a concentration of between about 1.0×10 20 and 1.0×10 21 atoms/cm 3 .
Claim 20
Dependent Claim
27 words
The method of claim 11, wherein said tungsten silicide layer is deposited by low pressure chemical vapor deposition using a reactant gas of tungsten hexafluoride and dichlorosilane.
Claim 21
Dependent Claim
28 words
The method of claim 11, wherein said patterning of said polycide layer is carried out in a reactive ion etcher using an etch gas mixture containing chlorine ions.
References Cited (Backward Citations)
US4774201A
Cited
US5483104A
Cited
US5306951A
Cited
US5422311A
Cited
US5510296A
Cited
US5547892A
Cited
US5763303A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-07-19 | 2003-01-18 | 2003-07-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-07-19 | 2007-01-18 | 2007-07-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-07-19 | 2011-01-18 | 2011-07-20 | $7700.00 | Window Closed / Lapsed |