Method of manufacturing low resistance and low junction leakage contact
Assignee: TSMC China Co Ltd
•
Filing: 1998-03-18
•
Granted: 1999-05-04
•
Expires: 2018-03-18
Abstract
Abstract A new method of forming an amorphous silicon glue layer in the formation of a contact is described. Semiconductor device structures are provided in and on a semiconductor substrate. An insulating layer is deposited overlying the semiconductor device structures. An opening is etched through the insulating layer to contact one of the semiconductor device structures. An amorphous silicon layer is deposited overlying the insulating layer and within the opening. Ions are implanted into the amorphous silicon layer whereby grain sizes within the amorphous silicon layer are reduced. Native oxide on the surface of the amorphous silicon layer is removed. A titanium/titanium nitride layer is deposited overlying the amorphous silicon layer. A metal layer is deposited overlying the titanium/titanium nitride layer and filling the opening. The substrate is annealed whereby the titanium layer reacts with the amorphous silicon layer and the silicon semiconductor substrate to form titanium silicide. The metal layer is etched back or patterned to complete metallization in the fabrication of an integrated circuit device.
Inventors
- 👤 Fouriers Tseng
- 👤 Peng-Cheng Chou
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 04:36
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/032; H10W20/052; H10W20/0523; H10W20/033; H10W20/047; H10W20/056
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
162 words
A method of metallization in a fabrication of an integrated circuit device comprising: providing semiconductor device structures in and on a silicon semiconductor substrate; depositing an insulating layer overlying said semiconductor device structures; etching an opening through said insulating layer to contact one of said semiconductor device structures; depositing an amorphous silicon layer overlying said insulating layer and within said opening; implanting ions into said amorphous silicon layer whereby grain sizes within said amorphous silicon layer are reduced; thereafter removing native oxide on the surface of said amorphous silicon layer; thereafter depositing a titanium layer overlying said amorphous silicon layer; depositing a metal layer overlying said titanium layer and filling said opening; thereafter annealing said substrate whereby said titanium layer reacts with said amorphous silicon layer and said silicon semiconductor substrate to form titanium silicide; and etching back said metal layer to leave said metal layer only within said opening to complete said metallization in the fabrication of said integrated circuit device.
Claim 2
Independent Claim
162 words
A method of metallization in a fabrication of an integrated circuit device comprising: providing semiconductor device structures in and on a silicon semiconductor substrate; depositing an insulating layer overlying said semiconductor device structures; etching an opening through said insulating layer to contact one of said semiconductor device structures; depositing an amorphous silicon layer overlying said insulating layer and within said opening; implanting ions into said amorphous silicon layer whereby grain sizes within said amorphous silicon layer are reduced; thereafter removing native oxide on the surface of said amorphous silicon layer; thereafter depositing a titanium layer overlying said amorphous silicon layer; depositing a metal layer overlying said titanium layer and filling said opening; thereafter annealing said substrate whereby said titanium layer reacts with said amorphous silicon layer and said silicon semiconductor substrate to form titanium silicide; and etching back said metal layer to leave said metal layer only within said opening to complete said metallization in the fabrication of said integrated circuit device.
Claim 3
Dependent Claim
31 words
The method according to claim 1 wherein said semiconductor device structures include gate electrodes and source/drain regions and wherein said one of said semiconductor device structures contacted is a source/drain region.
Claim 4
Dependent Claim
28 words
The method according to claim 1 wherein said amorphous silicon layer is deposited by chemical vapor deposition and has a thickness of between about 200 and 400 Angstroms.
Claim 5
Dependent Claim
41 words
The method according to claim 1 wherein said step of implanting ions into said amorphous silicon layer is performed at an energy of between about 20 and 40 KeV with a dosage of between about 1E12 and 1E13 atoms/cm 2 .
Claim 6
Dependent Claim
12 words
The method according to claim 1 wherein said ions are arsenic ions.
Claim 7
Dependent Claim
12 words
The method according to claim 1 wherein said ions are argon ions.
Claim 8
Dependent Claim
13 words
The method according to claim 1 wherein said ions are SiF 2 ions.
Claim 9
Dependent Claim
23 words
The method according to claim 1 wherein said step of removing said native oxide is performed by a hydrofluoric acid (HF) vapor clean.
Claim 10
Dependent Claim
20 words
The method according to claim 1 wherein said titanium layer has a thickness of between about 300 and 450 Angstroms.
Claim 11
Dependent Claim
27 words
The method according to claim 1 further comprising depositing a titanium nitride layer having a thickness of between about 200 and 400 Angstroms overlying said titanium layer.
Claim 12
Dependent Claim
39 words
The method according to claim 1 wherein said annealing is a rapid thermal annealing performed by flowing nitrogen gas at a temperature of between about 650 and 850° C. for a duration of between about 20 to 120 seconds.
Claim 13
Dependent Claim
12 words
The method according to claim 1 wherein said metal layer comprises tungsten.
Claim 14
Independent Claim
184 words
A method of metallization in a fabrication of an integrated circuit device comprising: providing semiconductor device structures in and on a silicon semiconductor substrate; depositing an insulating layer overlying said semiconductor device structures; etching an opening through said insulating layer to contact one of said semiconductor device structures; depositing an amorphous silicon layer overlying said insulating layer and within said opening; implanting ions into said amorphous silicon layer whereby grain sizes within said amorphous silicon layer are reduced; thereafter removing native oxide on a surface of said amorphous silicon layer; thereafter depositing a titanium layer overlying said amorphous silicon layer; depositing a titanium nitride barrier layer overlying said titanium layer; depositing a tungsten layer overlying said barrier layer and filling said opening; annealing said substrate whereby said titanium layer reacts with said amorphous silicon layer and said silicon semiconductor substrate to form titanium silicide; etching back said tungsten layer to leave said tungsten layer only within said opening; and depositing a metal layer overlying said tungsten layer and patterning said metal layer to complete said metallization in the fabrication of said integrated circuit device.
Claim 15
Independent Claim
184 words
A method of metallization in a fabrication of an integrated circuit device comprising: providing semiconductor device structures in and on a silicon semiconductor substrate; depositing an insulating layer overlying said semiconductor device structures; etching an opening through said insulating layer to contact one of said semiconductor device structures; depositing an amorphous silicon layer overlying said insulating layer and within said opening; implanting ions into said amorphous silicon layer whereby grain sizes within said amorphous silicon layer are reduced; thereafter removing native oxide on a surface of said amorphous silicon layer; thereafter depositing a titanium layer overlying said amorphous silicon layer; depositing a titanium nitride barrier layer overlying said titanium layer; depositing a tungsten layer overlying said barrier layer and filling said opening; annealing said substrate whereby said titanium layer reacts with said amorphous silicon layer and said silicon semiconductor substrate to form titanium silicide; etching back said tungsten layer to leave said tungsten layer only within said opening; and depositing a metal layer overlying said tungsten layer and patterning said metal layer to complete said metallization in the fabrication of said integrated circuit device.
Claim 16
Dependent Claim
31 words
The method according to claim 13 wherein said semiconductor device structures include gate electrodes and source/drain regions and wherein said one of said semiconductor device structures contacted is a source/drain region.
Claim 17
Dependent Claim
28 words
The method according to claim 13 wherein said amorphous silicon layer is deposited by chemical vapor deposition and has a thickness of between about 200 and 400 Angstroms.
Claim 18
Dependent Claim
41 words
The method according to claim 13 wherein said step of implanting ions into said amorphous silicon layer is performed at an energy of between about 20 and 40 KeV with a dosage of between about 1E12 and 1E13 atoms/cm 2 .
Claim 19
Dependent Claim
21 words
The method according to claim 13 wherein said ions are chosen from the group containing arsenic, argon, and SiF 2 ions.
Claim 20
Dependent Claim
23 words
The method according to claim 13 wherein said step of removing said native oxide is performed by a hydrofluoric acid (HF) vapor clean.
Claim 21
Dependent Claim
20 words
The method according to claim 13 wherein said titanium layer has a thickness of between about 300 and 450 Angstroms.
Claim 22
Dependent Claim
25 words
The method according to claim 13 wherein said titanium nitride layer has a thickness of between about 200 and 400 Angstroms overlying said titanium layer.
Claim 23
Dependent Claim
39 words
The method according to claim 13 wherein said annealing is a rapid thermal annealing performed by flowing nitrogen gas at a temperature of between about 650 and 850° C. for a duration of between about 20 to 120 seconds.
Claim 24
Independent Claim
226 words
A method of forming a contact having reduced resistance and reduced junction leakage in a fabrication of an integrated circuit device comprising: providing semiconductor device structures including gate electrodes and source/drain regions in and on a silicon semiconductor substrate; depositing an insulating layer overlying said semiconductor device structures; etching an opening through said insulating layer to contact one of said source/drain regions; depositing an amorphous silicon layer overlying said insulating layer and within said opening; implanting ions into said amorphous silicon layer whereby grain sizes within said amorphous silicon layer are reduced and whereby contact resistance is reduced; thereafter cleaning said amorphous silicon layer with hydrofluoric acid vapor to remove native oxide on a surface of said amorphous silicon layer; thereafter depositing a titanium layer overlying said amorphous silicon layer; depositing a titanium nitride barrier layer overlying said titanium layer; depositing a tungsten layer overlying said barrier layer and filling said opening; annealing said substrate whereby said titanium layer reacts with said amorphous silicon layer and said silicon semiconductor substrate to form titanium silicide and wherein said amorphous silicon layer prevents penetration of said one of said source/drain regions by said titanium silicide and thereby reduces junction leakage; and patterning said tungsten layer to complete said formation of said contact having reduced resistance and reduced junction leakage metallization in the fabrication of said integrated circuit device.
Claim 25
Independent Claim
226 words
A method of forming a contact having reduced resistance and reduced junction leakage in a fabrication of an integrated circuit device comprising: providing semiconductor device structures including gate electrodes and source/drain regions in and on a silicon semiconductor substrate; depositing an insulating layer overlying said semiconductor device structures; etching an opening through said insulating layer to contact one of said source/drain regions; depositing an amorphous silicon layer overlying said insulating layer and within said opening; implanting ions into said amorphous silicon layer whereby grain sizes within said amorphous silicon layer are reduced and whereby contact resistance is reduced; thereafter cleaning said amorphous silicon layer with hydrofluoric acid vapor to remove native oxide on a surface of said amorphous silicon layer; thereafter depositing a titanium layer overlying said amorphous silicon layer; depositing a titanium nitride barrier layer overlying said titanium layer; depositing a tungsten layer overlying said barrier layer and filling said opening; annealing said substrate whereby said titanium layer reacts with said amorphous silicon layer and said silicon semiconductor substrate to form titanium silicide and wherein said amorphous silicon layer prevents penetration of said one of said source/drain regions by said titanium silicide and thereby reduces junction leakage; and patterning said tungsten layer to complete said formation of said contact having reduced resistance and reduced junction leakage metallization in the fabrication of said integrated circuit device.
Claim 26
Dependent Claim
28 words
The method according to claim 22 wherein said amorphous silicon layer is deposited by chemical vapor deposition and has a thickness of between about 200 and 400 Angstroms.
Claim 27
Dependent Claim
41 words
The method according to claim 22 wherein said step of implanting ions into said amorphous silicon layer is performed at an energy of between about 20 and 40 KeV with a dosage of between about 1E12 and 1E13 atoms/cm 2 .
Claim 28
Dependent Claim
21 words
The method according to claim 22 wherein said ions are chosen from the group containing arsenic, argon, and SiF 2 ions.
Claim 29
Dependent Claim
20 words
The method according to claim 22 wherein said titanium layer has a thickness of between about 300 and 450 Angstroms.
Claim 30
Dependent Claim
25 words
The method according to claim 22 wherein said titanium nitride layer has a thickness of between about 200 and 400 Angstroms overlying said titanium layer.
Claim 31
Dependent Claim
39 words
The method according to claim 22 wherein said annealing is a rapid thermal annealing performed by flowing nitrogen gas at a temperature of between about 650 and 850° C. for a duration of between about 20 to 120 seconds.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-05-03 | 2002-11-02 | 2003-05-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-05-03 | 2006-11-02 | 2007-05-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-05-03 | 2010-11-02 | 2011-05-04 | $7700.00 | Window Closed / Lapsed |