Process for the production of shaped bodies from biodegradable material and shaped body
Assignee: Fardis Nv
•
Filing: 1995-01-26
•
Granted: 1998-12-15
•
Expires: 2015-01-26
Abstract
Abstract The invention relates to a process for the production of shaped bodies, in particular packaging shaped bodies, from biologically decomposable material using a viscous mass containing biologically decomposable fiber material, water and starch, which is baked with the formation of a composite of fiber material and starch in a baking mould, and a shaped body produced according to this process. The use of native and pre-gelatinated or modified starch in connection with a fiber material feed stock from fibers or fiber bundles of differing lengths is especially advantageous.
Inventors
- 👤 Gerd Arnold
- 👤 Hans Jurgen Steiger
- 👤 Christian Gass
- 👤 Friedrich Wissmueller
- 👤 Erhard Buettner
- 👤 Wolfgang Melzer
- 👤 Brunhilde Schoenberg
- 👤 Frank Dubbert
- 👤 Thomas Koeblitz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 07:59
CPC Classifications
B; B65; B65D; B65D65/00; B65D65/38; B65D65/46; B65D65/466; B65D1/00; C; C08; C08J; C08J5/00; C08J5/04; C08J5/045; C08J7/00; C08J7/04; C08J7/0427; C08L; C08L1/00; C08L1/02; C08L3/00; C08L3/02; D; D21; D21J; D21J3/00; D21J3/10; B65D2565/00; B65D2565/38; B65D2565/381; B65D2565/382; B65D2565/383; C08J2303/00; C08J2303/02; C08J2467/00; C08L2201/00; C08L2201/06; C08L2205/00; C08L2205/14; C08L2205/16; Y; Y02; Y02A; Y02A40/00; Y02A40/90; Y02W; Y02W30/00; Y02W30/50; Y02W30/80; Y02W90/00; Y02W90/10; Y10; Y10S; Y10S264/00; Y10S264/911; Y10S264/913; Y10S264/914
Claims Analysis
Total Claims: 46
Claim 1
Independent Claim
102 words
A process for the production of a shaped body of a biodegradable material comprising: providing a viscous mass containing a biodegradable fiber material, water and 15 wt % to 200 wt % starch based on the dry weight of said fiber material; placing the viscous mass in a baking mold and then closing the baking mold; and heating the viscous mass within the baking mold at a baking temperature between 105° C. and 300° C. for a period of between 0.5 and 15 minutes, under increasing pressure due to evaporation of the water within the baking mold, to produce the shaped body.
Claim 2
Dependent Claim
102 words
A process for the production of a shaped body of a biodegradable material comprising: providing a viscous mass containing a biodegradable fiber material, water and 15 wt % to 200 wt % starch based on the dry weight of said fiber material; placing the viscous mass in a baking mold and then closing the baking mold; and heating the viscous mass within the baking mold at a baking temperature between 105° C. and 300° C. for a period of between 0.5 and 15 minutes, under increasing pressure due to evaporation of the water within the baking mold, to produce the shaped body.
Claim 3
Dependent Claim
33 words
The process of claim 1 further comprising comminuting a fibrous raw material to defibrate the fibrous raw material, and to thereby form the biodegradable fiber material, prior to incorporation into the viscous mass.
Claim 4
Dependent Claim
26 words
The process of claim 2 wherein said fibrous raw material is selected from the group consisting of waste paper, wood dust, paper dust, and beet slices.
Claim 5
Dependent Claim
24 words
The process of claim 2 wherein said comminuting is carried out only to the extent of reducing the fibrous raw materials to fiber bundles.
Claim 6
Dependent Claim
30 words
The process of claim 1 wherein said biodegradable fiber material is a mixture of fibers or fiber bundles having different lengths within the range of 0.5 mm to 50 mm.
Claim 7
Dependent Claim
11 words
The process of claim 1 wherein said starch is native starch.
Claim 8
Dependent Claim
16 words
The process of claim 1 wherein said starch is 30-50 wt % of said viscous mass.
Claim 9
Dependent Claim
24 words
The process of claim 1 wherein the ratio of water to said fiber material, on a dry weight basis, is up to about 8:1.
Claim 10
Dependent Claim
27 words
The process of claim 1 wherein said starch is a pre-gelatinated or modified starch in an amount up to about 30% by weight of said viscous mass.
Claim 11
Dependent Claim
63 words
The process of claim 1 wherein said starch is present in said viscous mass in an amount providing a ratio of said starch to said water in a range of about 1:10 to 1:1 and further comprising: adding said water in the form of a modified starch or a pre-gelatinated starch, with excess water, to said fiber material, to provide the viscous mass.
Claim 12
Dependent Claim
50 words
The process of claim 1 wherein said fiber material is 15 wt % to 30 wt % of the viscous mass, said starch is 5 wt % to 40 wt % of the viscous mass and said water is 70 wt % to 40 wt % of the viscous mass.
Claim 13
Dependent Claim
28 words
The process of claim 1 wherein said starch is a pre-gelatinated or modified starch and is present in the amount of 1-10% by weight of said viscous mass.
Claim 14
Dependent Claim
45 words
The process of claim 1 further comprising: comminuting a fibrous raw material; and then reducing the fiber structure of the comminuted fibrous raw material in the presence of said water and said starch to produce said biodegradable fiber material and to provide said viscous mass.
Claim 15
Dependent Claim
38 words
The process of claim 1 further comprising: comminuting a fibrous raw material in the presence of water; and subsequently reducing the comminuted fibrous raw material to its fiber structure and adding native starch to provide said viscous mass.
Claim 16
Dependent Claim
32 words
The process of claim 13 wherein said reducing is by mixing and kneading to generate internal shearing forces and to thereby produce fibers or loosened fiber bundles from said fibrous raw material.
Claim 17
Dependent Claim
31 words
The process of claim 1 wherein said biodegradable fiber material is a mixture of short and long fibers or fiber bundles of a length ranging from 0.5 mm to 5 mm.
Claim 18
Dependent Claim
33 words
The process of claim 1 further comprising classifying a fibrous raw material to provide plural fractions of different fiber length and utilizing one or more of said fractions as said biodegradable fiber material.
Claim 19
Dependent Claim
26 words
The process of claim 13 wherein said starch is native starch and is added at least in part during said comminuting, as a pre-mix with fillers.
Claim 20
Dependent Claim
26 words
The process of claim 13 wherein said starch is pre-gelatinated starch and is added at least in part during said comminuting, as a pre-mix with fillers.
Claim 21
Dependent Claim
35 words
The process of claim 15 wherein said starch is native starch in admixture with a filler and is added prior to said comminuting or subsequent to said comminuting and prior to said mixing and kneading.
Claim 22
Dependent Claim
24 words
The process of claim 15 wherein said starch is pre-gelatinated starch and is added during the mixing and kneading to form the viscous mass.
Claim 23
Dependent Claim
26 words
The process of claim 14 wherein said starch is native starch and is added at least in part during said comminuting, as a pre-mix with fillers.
Claim 24
Dependent Claim
14 words
The process of claim 13 wherein said comminuting is by means of beater mills.
Claim 25
Dependent Claim
14 words
The process of claim 14 wherein said comminuting is by means of beater mills.
Claim 26
Dependent Claim
26 words
The process of claim 14 wherein said starch is pre-gelatinated starch and is added at least in part during said comminuting, as a pre-mix with fillers.
Claim 27
Dependent Claim
19 words
The process of claim 1 further comprising adding an alkaline substance to said viscous material as a fluxing agent.
Claim 28
Dependent Claim
54 words
The process of claim 1 further comprising: converting said viscous mass into a doughy state; rolling said viscous mass in said doughy state to form a sheet of a thickness approximating wall thickness of the shaped body; punching blanks out of the rolled sheet; and placing one of said blanks in the baking mold.
Claim 29
Dependent Claim
37 words
The process of claim 1 wherein the baking mold includes upper and lower baking plates and further comprising: pre-shaping said viscous mass with the upper baking plate or with a die prior to closing said baking mold.
Claim 30
Dependent Claim
18 words
The process of claim 1 further comprising preheating said baking mold prior to placing the viscous mass therein.
Claim 31
Dependent Claim
52 words
The process of claim 1 wherein the baking mold includes upper and lower baking plates and further comprising placing the upper baking plate loosely on the viscous mass for a period of time sufficient to reduce water content of the viscous mass by means of evaporation, prior to closing the baking mold.
Claim 32
Dependent Claim
48 words
The process of claim 1 wherein the baking mold includes upper and lower baking plates and further comprising locking the upper and lower plates in position relative to each other to ensure a constant distance therebetween during said heating, thereby defining a wall thickness for the shaped body.
Claim 33
Dependent Claim
23 words
The process of claim 1 further comprising controlling a discharge of steam from the baking mold produced by said evaporation of the water.
Claim 34
Dependent Claim
17 words
The process of claim 32 wherein said control of discharge of steam is responsive to heating time.
Claim 35
Dependent Claim
21 words
The process of claim 1 further comprising: pressing the viscous mass within the heating mold at the beginning of said heating.
Claim 36
Dependent Claim
21 words
The process of claim 1 further comprising mechanically reducing the amount of water in said viscous mass prior to said heating.
Claim 37
Dependent Claim
39 words
The process of claim 1 further comprising pre-shaping viscous mass in a sieve-type mold to produce a pre-shaped blank and placing said pre-shaped blank, in the baking mold, said sieve-type mold substantially corresponding to geometry of the baking mold.
Claim 38
Dependent Claim
33 words
The process of claim 36 further comprising: contacting the pre-shaped blank with a heated baking tong to cause water to evaporate from the viscous mass prior to the closing of the baking mold.
Claim 39
Dependent Claim
33 words
The process of claim 1 wherein the baking mold includes upper and lower baking plates and wherein said heating is accompanied by a reduction in distance between the upper and lower baking plates.
Claim 40
Dependent Claim
93 words
The process of claim 1 further comprising: comminuting the fibrous raw material; mixing and kneading the comminuted fibrous raw material to disintegrate the fibrous raw material into fiber bundles; and mixing said fiber bundles, as said biodegradable fiber material, with 30% by wt to 50% by wt of the starch, based on the dry weight of the biodegradable fiber material; and wherein the baking mold is in the form of cooperating baking plates and wherein the viscous mass is heated in the baking mold at a temperature of 150° C. to 200° C.
Claim 41
Dependent Claim
93 words
The process of claim 1 further comprising: comminuting the fibrous raw material; mixing and kneading the comminuting fibrous raw material to disintegrate the fibrous raw material into fiber bundles; and mixing said fiber bundles, as said biodegradable fiber material, with 15% by wt to 30% by wt of the starch, based on the dry weight of the biodegradable fiber material; and wherein the baking mold is in the form of cooperating baking plates and wherein the viscous mass is heated in the baking mold at a temperature of 150° C. to 200° C.
Claim 42
Dependent Claim
48 words
The process of claim 1 wherein said biodegradable fiber material is in the form of an admixture of long fibers or fiber bundles having a length ranging from 10 mm to 50 mm and short fibers or fiber bundles having a length of 0.5 mm to 20 mm.
Claim 43
Dependent Claim
29 words
The shaped body produced by the process of claim 1 wherein the ratio of said biodegradable fiber material to said starch is within the range of 4:1 to 1:2.
Claim 44
Dependent Claim
27 words
A shaped body according to claim 41 wherein said biodegradable fiber material consists of fibers or fiber bundles of a length of 0.5 mm to 5 mm.
Claim 45
Dependent Claim
11 words
The shaped body of claim 43 wherein said starch is pre-gelatinated.
Claim 46
Dependent Claim
21 words
The shaped body of claim 42 in the form of a matrix of said starch reinforced by said biodegradable fiber material.
References Cited (Backward Citations)
GB632911A
Cited
US4377440A
Cited
US4508595A
Cited
DE3813984A1
Cited
US5582682A
Cited
DE4009408A1
Cited
JPH0656172A
Cited
WO1994018384A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-12-14 | 2002-06-15 | 2002-12-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-12-14 | 2006-06-15 | 2006-12-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-12-14 | 2010-06-15 | 2010-12-15 | $7700.00 | Window Closed / Lapsed |