Process and a composition for making cellulosic composites
Assignee: Revocable Trust Louise C Wilt
•
Filing: 1994-05-31
•
Granted: 1996-12-10
•
Expires: 2014-05-31
Abstract
Abstract The specification discloses an unorthodox system for manufacturing strong, light-weight and weather-resistant cellulosic composite materials from discarded paper and newsprint, and papermill sludge--and from an unlimited variety of particulated fibrous lignocellulosics--without the use of an extrinsic adhesive. Both the matrix-forming resin and the fiber-substrate, which comprise the entire composite, are spontaneously created in situ at ambient conditions by the ammoniation of a mixture of a protein-containing material and a particulated cellulosic. Heating an article shaped from such a mixture to above 175° C. polymerizes the resin and bonds the fiber-substrate into a cellulosic composite product. Also disclosed is a process for manufacturing reinforced and laminated composites as well as a composition which simplifies the production of both cellulosic composites and all-biomass thermosetting resins.
Inventors
- 👤 Arthur Ferretti
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 18:22
CPC Classifications
C; C08; C08H; C08H1/00; C10; C10L; C10L5/00; C10L5/02; C10L5/06; C10L5/10; C10L5/14; Y; Y10; Y10S; Y10S162/00; Y10S162/09
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
120 words
A process for manufacturing a cellulosic composite with a essentially of a thermoset Maillard resin wherein both a carbohydrate reactant of said resin and a substrate-forming solids-residue are derived from a particulated cellulosic feedstock, which process comprises: a) ammoniating to alkalinity a mixture of amounts of said cellulosic feedstock and a protein-containing material effective to create said resin and obtain a cellulosic composite-forming mixture; b) unifying said composite-forming mixture with a consolidating and shaping means that applies pressure at least sufficient to express virtually, all entrapped gases from the resulting unified mixture; and c) heating said unified mixture at a temperature between about 175° C. and about 260° C. for an interval of time sufficient to produce said cellulosic composite.
Claim 2
Dependent Claim
120 words
A process for manufacturing a cellulosic composite with a essentially of a thermoset Maillard resin wherein both a carbohydrate reactant of said resin and a substrate-forming solids-residue are derived from a particulated cellulosic feedstock, which process comprises: a) ammoniating to alkalinity a mixture of amounts of said cellulosic feedstock and a protein-containing material effective to create said resin and obtain a cellulosic composite-forming mixture; b) unifying said composite-forming mixture with a consolidating and shaping means that applies pressure at least sufficient to express virtually, all entrapped gases from the resulting unified mixture; and c) heating said unified mixture at a temperature between about 175° C. and about 260° C. for an interval of time sufficient to produce said cellulosic composite.
Claim 3
Dependent Claim
88 words
The process of claim 1 for manufacturing a cellulosic composite wherein: (a) said particulated cellulosic feedstock is a fibrous lignocellulosic, a refined cellulosic, or delignified cellulose powder, or any mixture of said particulated cellulosic feedstocks; (b) said protein-containing material is whey, a protein-containing whey-derivative, or a flour made from pulse or a protein-rich wheat, or a mixture of said protein-containing materials; and (c) said composite-forming mixture is created by employing ammonia in the form of a gas, an aqueous solution, anhydrous liquid ammonia, or a dry ammonia-evolving compound.
Claim 4
Dependent Claim
46 words
The process of claim 1, which process includes the additional step of post-forming said unified composite-forming mixture during an interruption of said heating, which interruption is made to occur after said unified mixture is essentially dry but before said resin of said composite-forming mixture is thermoset.
Claim 5
Dependent Claim
64 words
A cellulosic composite manufactured by the process of claim 1 wherein said particulated cellulosic feedstock is a mixture of fiberized wood and a sludge evolved during a cellulosic-processing operation, said protein-containing material is a flour made from pulse or a protein-rich wheat, and said means for consolidation and shaping is hot-roll or vacuum forming, pressing, molding, or extrusion, or a combination of said means.
Claim 6
Dependent Claim
38 words
A process for manufacturing a reinforced cellulosic composite wherein a functional amount of random-length fiber is mixed with said particulated cellulosic feedstock of claim 1 prior to the preparation of said mixture of said feedstock and said protein-containing-material.
Claim 7
Dependent Claim
76 words
The process of claim 5 wherein said particulated cellulosic feedstock is a sludge evolved during an operation selected from the group of cellulosic processing operations consisting of paper or fibre-board making, paper recycling, and vacuum molding, or a combination of said operations, and said random-length fiber is made from a material selected from the group consisting of glass, metal, lignocellulosics, process-inert synthetic polymers, ceramics and carbon, or a mixture of random-length fiber made from said materials.
Claim 8
Dependent Claim
49 words
A reinforced cellulosic composite manufactured by the process of claim 6 wherein said particulated cellulosic feedstock is a paper-recycling sludge, which sludge contains the impurities and minerals found in a sludge evolved during a paper-recycling operation, and the material from which said random-length fiber is made is a lignocellulosic.
Claim 9
Dependent Claim
104 words
The process of claim 1 wherein said process incorporates an essentially-dry cellulosic-composite-forming mixture, which process comprises: a) ammoniating to alkalinity a mixture of amounts of a nominally-dry particulated cellulosic feedstock and a nominally-dry protein-containing material effective to create said resin and obtain said essentially-dry cellulosic composite-forming mixture; b) unifying said essentially-dry composite-forming mixture with a consolidating and shaping means that applies pressure at least sufficient to express virtually all entrapped gases from the resulting unified mixture; and c) heating said unified mixture at a temperature between about 175° C. and about 260° C. for an interval of time sufficient to produce said cellulosic composite.
Claim 10
Dependent Claim
62 words
The essentially-dry cellulosic composite-forming mixture obtained during the process of claim 8 wherein the form of ammonia employed to ammoniate said mixture of a cellulosic feedstock and a protein-containing material is anhydrous liquid ammonia, a dry ammonia-evolving compound, or a gas, said nominally-dry cellulosic feedstock is a sludge evolved during a paper-recycling operation, and said nominally-dry protein-containing material is a soy flour.
Claim 11
Dependent Claim
12 words
A cellulosic composite manufactured in accordance with the process of claim 8.
Claim 12
Dependent Claim
45 words
A cellulosic composite comprised of a matrix, which matrix consists essentially of a thermoset Maillard resin formed by a protein-carbohydrate reaction, and a cellulosic fiber substrate wherein both a carbohydrate reactant of said resin and a substrate-forming solids-residue are derived from a particulated cellulosic feedstock.
Claim 13
Dependent Claim
45 words
A cellulosic composite comprised of a matrix, which matrix consists essentially of a thermoset Maillard resin formed by a protein-carbohydrate reaction, and a cellulosic fiber substrate wherein both a carbohydrate reactant of said resin and a substrate-forming solids-residue are derived from a particulated cellulosic feedstock.
Claim 14
Dependent Claim
13 words
The cellulosic composite of claim 11 wherein said matrix is created in situ.
Claim 15
Dependent Claim
67 words
The cellulosic composite of claim 12, wherein said particulated cellulosic feedstock is: (a) a fibrous lignocellulosic, or a mixture of fibrous lignocellulosics; (b) a refined cellulosic selected from the group consisting of repulped paper, paper-making furnish, or a sludge, which sludge is evolved during a cellulosic-processing operation, or a mixture of said refined cellulosics; (c) delignified cellulose powder; or (d) any mixture of said particulated cellulosic feedstocks.
Claim 16
Dependent Claim
40 words
The cellulosic composite of claim 13, wherein said cellulosic feedstock is a mixture of a fibrous cellulosic and a sludge evolved during a paper-recycling operation, which sludge contains the impurities and clay, ash, and minerals found in a paper-recycling sludge.
Claim 17
Dependent Claim
109 words
A single-step process for manufacturing a cellulosic composite with a matrix consisting essentially of a thermoset Maillard resin wherein both a carbohydrate reactant of said resin and a substrate-forming solids-residue are derived from a particulated cellulosic feedstock, and wherein a mixture of amounts of said cellulosic feedstock and a protein-containing material effective to create said resin will produce said cellulosic composite when said mixture is ammoniated to alkalinity, unified and subjected to said single process step, which step is comprised of heating said ammoniated and unified mixture at a temperature between about 175° C. and about 260° C. for an interval of time sufficient to produce said cellulosic composite.
Claim 18
Dependent Claim
109 words
A single-step process for manufacturing a cellulosic composite with a matrix consisting essentially of a thermoset Maillard resin wherein both a carbohydrate reactant of said resin and a substrate-forming solids-residue are derived from a particulated cellulosic feedstock, and wherein a mixture of amounts of said cellulosic feedstock and a protein-containing material effective to create said resin will produce said cellulosic composite when said mixture is ammoniated to alkalinity, unified and subjected to said single process step, which step is comprised of heating said ammoniated and unified mixture at a temperature between about 175° C. and about 260° C. for an interval of time sufficient to produce said cellulosic composite.
Claim 19
Dependent Claim
34 words
The process of claim 15 wherein said heating is effected in a consolidating and shaping means that applies pressure at least sufficient to express virtually all entrapped gases from said ammoniated and unified mixture.
Claim 20
Dependent Claim
126 words
A process for manufacturing a cellulosic composite with a matrix consisting essentially of a thermoset Maillard resin with the optimum strength realizable from a particulated cellulosic feedstock, wherein both a carbohydrate reactant of said resin and a substrate-forming solids-residue are derived from said cellulosic feedstock, which process comprises: a) admixing with said cellulosic feedstock a mixture of the minimum amounts of ammonia and a protein-containing material that will yield, after the resulting admixture has been sufficiently compressed and heated, a cellulosic composite with the optimum strength realizable from said cellulosic feedstock; b) compressing said admixture with force sufficient to express therefrom virtually all entrapped gasses; and c) heating said compressed admixture at a temperature of at least about 175° C. until said matrix-forming resin is thermoset.
Claim 21
Dependent Claim
126 words
A process for manufacturing a cellulosic composite with a matrix consisting essentially of a thermoset Maillard resin with the optimum strength realizable from a particulated cellulosic feedstock, wherein both a carbohydrate reactant of said resin and a substrate-forming solids-residue are derived from said cellulosic feedstock, which process comprises: a) admixing with said cellulosic feedstock a mixture of the minimum amounts of ammonia and a protein-containing material that will yield, after the resulting admixture has been sufficiently compressed and heated, a cellulosic composite with the optimum strength realizable from said cellulosic feedstock; b) compressing said admixture with force sufficient to express therefrom virtually all entrapped gasses; and c) heating said compressed admixture at a temperature of at least about 175° C. until said matrix-forming resin is thermoset.
Claim 22
Dependent Claim
65 words
The process of claim 17 wherein said particulated cellulosic feedstock is a fibrous lignocellulosic, a refined cellulosic, or a mixture of said particulated cellulosics, said protein-containing material is a soy flour, whey, or a protein-containing whey derivative, said ammonia is an aqueous solution, or a dry ammonia-evolving compound, and the means for compressing said admixture is hot roll or vacuum forming, molding, pressing, or extrusion.
References Cited (Backward Citations)
GB191008325A
Cited
US1542539A
Cited
US2116544A
Cited
GB600628A
Cited
US2534908A
Cited
US2654296A
Cited
GB892744A
Cited
US3113065A
Cited
US3166466A
Cited
US3895997A
Cited
JPS5016442A
Cited
US4221751A
Cited
US4524164A
Cited
US5017319A
Cited
US4828643A
Cited
US4692478A
Cited
US5008329A
Cited
US5008359A
Cited
US4992519A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-12-10 | 2000-06-10 | 2000-12-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-12-10 | 2004-06-10 | 2004-12-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-12-10 | 2008-06-10 | 2008-12-10 | $7700.00 | Window Closed / Lapsed |