Liquified cellulosic fiber, resin binders and articles manufactured therewith, and method of manufacturing same
Assignee: Masonite Corp
•
Filing: 1987-01-12
•
Granted: 1989-05-09
•
Expires: 2007-01-12
Abstract
Abstract A method of manufacturing a liquified fiber-phenol-formaldehyde resin includes heating a mixture of phenol, formaldehyde, liquified cellulosic fiber and alkali at a temperature of 60 DEG C. to 100 DEG C. and a pH of 8-13. The liquified cellulosic fiber comprises about 5 to about 80 percent of the total weight of phenol, formaldehyde and liquified fiber. Also disclosed are fibrous articles manufactured using this resin as a binder, such as fiberboards, particle board, plywood, oriented strand board, and waferboard.
Inventors
- 👤 William Newman
- 👤 Michael E. Rakauskas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 02:36
CPC Classifications
C; C08; C08G; C08G16/00; C08L; C08L97/00; C08L97/02; Y; Y10; Y10T; Y10T428/00; Y10T428/25; Y10T428/253; Y10T428/31504; Y10T428/31942; Y10T428/31949; Y10T428/31957; Y10T428/3196
Claims Analysis
Total Claims: 65
Claim 1
Independent Claim
66 words
A method of liquifying cellulosic fibers comprising heating a mixture of cellulosic fibers in an alkali solution having an alkali concentration of at least 2% by weight at a temperature of at least 140° C. and a pressure of at least 150 psi, wherein the weight ratio of alkali solution to cellulosic fibers is at least 4:1, for a time sufficient to liquify the cellulosic fibers.
Claim 2
Independent Claim
66 words
A method of liquifying cellulosic fibers comprising heating a mixture of cellulosic fibers in an alkali solution having an alkali concentration of at least 2% by weight at a temperature of at least 140° C. and a pressure of at least 150 psi, wherein the weight ratio of alkali solution to cellulosic fibers is at least 4:1, for a time sufficient to liquify the cellulosic fibers.
Claim 3
Dependent Claim
60 words
The method of claim 1 wherein the mixture is heated at a temperature of at least 180° C.; wherein the alkali concentration of the alkali solution is at least 8% by weight; wherein the weight ratio of alkali solution to cellulosic fibers is at least 5:1, and wherein the mixture is heated under said conditions for at least 5 minutes.
Claim 4
Dependent Claim
60 words
The method of claim 2 wherein the mixture is heated at a temperature of 180° C. to 220° C.; wherein the alkali concentration of the alkali solution is 8% to 15% by weight; wherein the weight ratio alkali solution to cellulosic fibers is 5:1 to 15:1, and wherein the mixture is heated under said conditions for 5 to 90 minutes.
Claim 5
Dependent Claim
67 words
The method of claim 2 wherein the mixture is heated at a temperature of at least 190° C.; wherein the alkali concentration of the alkali solution is at least 10% by weight; wherein the weight ratio of alkali solution to cellulosic fibers is at least 6:1, and wherein the mixture is heated for a time sufficient to liquify at least 80% by weight of the cellulosic fibers.
Claim 6
Dependent Claim
82 words
The method of claim 2 wherein the mixture is heated at a temperature of at least 190° C.; wherein the alkali concentration of the alkali solution is about 10% to 15% by weight; wherein the mixture is heated at a pressure of 150 psi to 350 psi; wherein the weight ratio of alkali solution to cellulosic fibers is at least 7:1; and wherein the mixture is heated for a time sufficient to liquify at least 90% by weight of the cellulosic fibers.
Claim 7
Dependent Claim
33 words
The method of claim 5 wherein the mixture is heated at a temperature of at least 195° C. for a time sufficient to liquify at least 95% by weight of the cellulosic fibers.
Claim 8
Dependent Claim
25 words
The method of claim 6 wherein the mixture is heated for a time sufficient to liquify at least 98% by weight of the cellulosic fibers.
Claim 9
Dependent Claim
38 words
The method of claim 1 wherein the mixture is heated at a temperature of 140° C. to 200° C. and wherein the weight ratio of alkali solution to cellulosic fibers is in the range of 5:1 to 9:1.
Claim 10
Dependent Claim
14 words
The method of claim 2 wherein the alkali solution is an aqueous alkali solution.
Claim 11
Dependent Claim
50 words
The method of claim 9 wherein the mixture is heated at a temperature of at least 180° C.; wherein the alkali concentration of the aqueous alkali solution is at least 8% by weight; and wherein the weight ratio of the aqueous alkali solution to cellulosic fibers is at least 6:1.
Claim 12
Independent Claim
94 words
A method of manufacturing a liquified cellulosic fiber-phenol-formaldehyde resin comprising liquifying cellulosic fibers by heating a mixture of cellulosic fibers in an alkali solution at a temperature of at least 100° C. and at above atmospheric pressure and an alkali concentration sufficient to liquify said cellulosic fibers to form liquified cellulosic fiber;, and heating said liquified cellulosic fibers with phenol, formaldehyde, and caustic solution to form said liquified cellulosic fiber-phenol-formaldehyde resin wherein said liquified cellulosic fibers comprises about 5 to about 80 percent of the total weight of phenol, formaldehyde and liquified cellulosic fiber.
Claim 13
Independent Claim
94 words
A method of manufacturing a liquified cellulosic fiber-phenol-formaldehyde resin comprising liquifying cellulosic fibers by heating a mixture of cellulosic fibers in an alkali solution at a temperature of at least 100° C. and at above atmospheric pressure and an alkali concentration sufficient to liquify said cellulosic fibers to form liquified cellulosic fiber;, and heating said liquified cellulosic fibers with phenol, formaldehyde, and caustic solution to form said liquified cellulosic fiber-phenol-formaldehyde resin wherein said liquified cellulosic fibers comprises about 5 to about 80 percent of the total weight of phenol, formaldehyde and liquified cellulosic fiber.
Claim 14
Dependent Claim
32 words
The method of claim 11 wherein said liquified cellulosic fiber-phenol-formaldehyde mixture is heated at a temperature of 60° C. to 100° C. and at a pH of 8-13 to form said polymer.
Claim 15
Dependent Claim
18 words
The method of claim 11 wherein said phenol, formaldehyde and liquified cellulosic fiber are mixed prior to heating.
Claim 16
Dependent Claim
29 words
The method of claim 11 wherein said liquified cellulosic fiber comprises about 30% to about 60% by total weight of the mixture of liquified cellulosic fber, phenol and formaldehyde.
Claim 17
Dependent Claim
29 words
The method of claim 11 wherein the caustic solution is an aqueous caustic solution and wherein the caustic solution to cellulosic fiber ratio is at least 4 to 1.
Claim 18
Independent Claim
96 words
A method of manufacturing a man-made board comprising contacting a plurality of fibers with a liquified cellulosic fiber-phenol-formaldehyde resin and hot pressing said resin contacted fibers together to cause said fibers to adhere to each other in a desired configuration, wherein said resin is formed by heating cellulosic fibers in caustic solution at a temperature of at least 100° C. and a pressure of at least 150 psi and at a caustic concentration sufficient to liquify said cellulosic fibers, and heating a mixture of said liquified cellulosic fiber with phenol and formaldehyde to form said resin.
Claim 19
Independent Claim
96 words
A method of manufacturing a man-made board comprising contacting a plurality of fibers with a liquified cellulosic fiber-phenol-formaldehyde resin and hot pressing said resin contacted fibers together to cause said fibers to adhere to each other in a desired configuration, wherein said resin is formed by heating cellulosic fibers in caustic solution at a temperature of at least 100° C. and a pressure of at least 150 psi and at a caustic concentration sufficient to liquify said cellulosic fibers, and heating a mixture of said liquified cellulosic fiber with phenol and formaldehyde to form said resin.
Claim 20
Dependent Claim
43 words
The method of claim 16 wherein said liquified cellulosic fiber-phenol-formaldehyde mixture is heated at a pH of 8-13 for a period of time sufficient that said resin has a viscosity in the range of 10 to 5000 centipoises and then retarding further polymerization.
Claim 21
Independent Claim
107 words
A method of molding a fibrous object having a predetermined configuration comprising disposing a fiber-resin composition in a mold cavity, closing said mold cavity and applying heat and pressure to said composition to adhere said composition together into said predetermined configuration, wherein said fiber-resin composition comprises a plurality of fibers and a liquified cellulosic fiber-phenol-formaldehyde resin formaldehyde resin formed by reacting a resin mixture of liquified cellulosic fiber, phenol, formaldehyde and caustic, wherein said liquidfied cellulosic fibers are formed by heating a mixture of cellulosic fibers in an alkali solution at a sufficiently elevated temperature, above atomspheric pressure and sufficient alkali concentration to liquify the cellulosic fibers.
Claim 22
Independent Claim
107 words
A method of molding a fibrous object having a predetermined configuration comprising disposing a fiber-resin composition in a mold cavity, closing said mold cavity and applying heat and pressure to said composition to adhere said composition together into said predetermined configuration, wherein said fiber-resin composition comprises a plurality of fibers and a liquified cellulosic fiber-phenol-formaldehyde resin formaldehyde resin formed by reacting a resin mixture of liquified cellulosic fiber, phenol, formaldehyde and caustic, wherein said liquidfied cellulosic fibers are formed by heating a mixture of cellulosic fibers in an alkali solution at a sufficiently elevated temperature, above atomspheric pressure and sufficient alkali concentration to liquify the cellulosic fibers.
Claim 23
Dependent Claim
30 words
The method of claim 18 wherein said liquified cellulosic fiber comprises about 50% to about 80% by total weight of liquified cellulosic fiber, phenol and formaldehyde in said resin mixture.
Claim 24
Dependent Claim
30 words
The method of claim 19 wherein said liquified cellulosic fiber comprises about 40% to about 60% by total weight of liquified cellulosic fiber, phenol and formaldehyde in said resin mixture.
Claim 25
Dependent Claim
20 words
The method of claim 18 including heating said resin mixture at a temperature of about 85° to about 95° C.
Claim 26
Dependent Claim
87 words
An article of manufacture comprising a plurality of fibers adhered together under heat and pressure with a liquified cellulosic fiber modified phenol-formaldehyde resin wherein said resin is formed by mixing a resin mixture of liquified cellulosic fiber with phenol, formaldehyde and an alkali to form a reaction mixture and polymerizing said mixture, wherein said liquified cellulosic fibers are formed by heating a mixture of cellulosic fibers in an alkali solution at a sufficiently elevated temperature, above atmospheric pressure and sufficient alkali concentration to liquify the cellulosic fibers.
Claim 27
Dependent Claim
87 words
An article of manufacture comprising a plurality of fibers adhered together under heat and pressure with a liquified cellulosic fiber modified phenol-formaldehyde resin wherein said resin is formed by mixing a resin mixture of liquified cellulosic fiber with phenol, formaldehyde and an alkali to form a reaction mixture and polymerizing said mixture, wherein said liquified cellulosic fibers are formed by heating a mixture of cellulosic fibers in an alkali solution at a sufficiently elevated temperature, above atmospheric pressure and sufficient alkali concentration to liquify the cellulosic fibers.
Claim 28
Dependent Claim
30 words
The article of claim 22 wherein said liquified cellulosic fiber comprises about 30% to about 60% by total weight of liquified cellulosic fiber, phenol and formaldehyde in said resin mixture.
Claim 29
Dependent Claim
30 words
The article of claim 22 wherein said liquified cellulosic fiber comprises about 40% to about 50% by total weight of liquified cellulosic fiber, phenol and formaldehyde in said resin mixture.
Claim 30
Dependent Claim
12 words
The article of claim 22 wherein said cellulosic fibers are wood fibers.
Claim 31
Dependent Claim
116 words
A liquified cellulosic fiber modified phenol-formaldehyde resin formed by heating a mixture of phenol, formaldehyde, a liquified cellulosic fiber and alkali wherien said liquified cellulosic fiber comprises about 5 to about 80 percent of the total weight of phenol, formaldehyde and liquified cellulosic fiber; and wherein said liquified cellulosic fibers are formed by heating a mixture of cellulosic fibers in an alkali solution at a sufficiently elevated temperature, above atmospheric pressure and sufficient alkali concentration to liquify the cellulosic fibers; polymerizing said mixture at a temperature of 60° C. to 100° C. to form a liquified cellulosic fiber modified phenol-formaldehyde resin; and retarding polymerization of said reaction mixture when the viscosity reaches 10 to 4000 centipoises.
Claim 32
Dependent Claim
116 words
A liquified cellulosic fiber modified phenol-formaldehyde resin formed by heating a mixture of phenol, formaldehyde, a liquified cellulosic fiber and alkali wherien said liquified cellulosic fiber comprises about 5 to about 80 percent of the total weight of phenol, formaldehyde and liquified cellulosic fiber; and wherein said liquified cellulosic fibers are formed by heating a mixture of cellulosic fibers in an alkali solution at a sufficiently elevated temperature, above atmospheric pressure and sufficient alkali concentration to liquify the cellulosic fibers; polymerizing said mixture at a temperature of 60° C. to 100° C. to form a liquified cellulosic fiber modified phenol-formaldehyde resin; and retarding polymerization of said reaction mixture when the viscosity reaches 10 to 4000 centipoises.
Claim 33
Dependent Claim
32 words
The resin of claim 26 wherein the reaction mixture is diluted to 10 to 30% solids after the viscosity of the reaction mixture reaches 10 to 150 centipoises to prevent further polymerization.
Claim 34
Dependent Claim
13 words
The resin of claim 27 wherein the reaction mixture is diluted with water.
Claim 35
Independent Claim
132 words
A method of manufacturing a sheet material formed from a plurality of discrete members adhered together, including contacting a plurality of discrete sheet material members with a binding resin; disposing each of said sheet material members in contact with at least one other of said sheet material members and pressing said sheet material members together with sufficient heat and pressure to form a consolidated sheet material, the improvement comprising said binding resin, wherein said resin is formed by mixing a liquified cellulosic fiber, formed by heating cellulosic fibers in caustic solution at a temperature of at least 100° C. and a pressure of at least 150 psi and at a caustic concentration sufficient to liquify said cellulosic phenol fibers; formaldehyde; and an alkali to form a reaction mixture and polymerizing said mixture.
Claim 36
Independent Claim
132 words
A method of manufacturing a sheet material formed from a plurality of discrete members adhered together, including contacting a plurality of discrete sheet material members with a binding resin; disposing each of said sheet material members in contact with at least one other of said sheet material members and pressing said sheet material members together with sufficient heat and pressure to form a consolidated sheet material, the improvement comprising said binding resin, wherein said resin is formed by mixing a liquified cellulosic fiber, formed by heating cellulosic fibers in caustic solution at a temperature of at least 100° C. and a pressure of at least 150 psi and at a caustic concentration sufficient to liquify said cellulosic phenol fibers; formaldehyde; and an alkali to form a reaction mixture and polymerizing said mixture.
Claim 37
Dependent Claim
30 words
The method of claim 29 wherein said liquified cellulosic fibers comprises about 30% to about 60% by total weight of liquified cellulosic fibers, phenol and formaldehyde in said reaction mixture.
Claim 38
Dependent Claim
30 words
The method of claim 29 wherein said liquified cellulosic fibers comprises about 40% to about 50% by total weight of liquified cellulosic fiber, phenol and formaldehyde in said resin mixture.
Claim 39
Dependent Claim
12 words
The method of claim 29 wherein said discrete members include cellulosic fibers.
Claim 40
Dependent Claim
13 words
The method of claim 29 wherein said discrete members comprise discrete wood pieces.
Claim 41
Dependent Claim
14 words
The method of claim 29 wherein said discrete members comprise resin bound fiberglass pieces.
Claim 42
Independent Claim
162 words
A method of manufacturing a sheet material formed from a plurality of discrete members adhered together, including contacting a plurality of discrete sheet material members with a binding resin; disposing each of said sheet material members in contact with at least one other of said sheet material members and pressing said sheet material members together with sufficient heat and pressure to form a sheet material, the improvement comprising said binding resin, wherein said resin is formed by polymerizing a mixture of phenol, formaldehyde, and liquified cellulosic fiber wherein said liquified cellulosic fiber is formed by heating cellulosic fibers in caustic solution at a temperature of at least 100° C. and a pressure of at least 150 psi and at a caustic concentration sufficient to liquify said cellulosic fibers, and comprises about 5 to about 80 percent of the total weight of phenol, formaldehyde and liquified cellulosic fiber and wherein said liquified cellulosic fiber is mixed withsaid phenol and formaldehyde under alkaline conditions.
Claim 43
Independent Claim
162 words
A method of manufacturing a sheet material formed from a plurality of discrete members adhered together, including contacting a plurality of discrete sheet material members with a binding resin; disposing each of said sheet material members in contact with at least one other of said sheet material members and pressing said sheet material members together with sufficient heat and pressure to form a sheet material, the improvement comprising said binding resin, wherein said resin is formed by polymerizing a mixture of phenol, formaldehyde, and liquified cellulosic fiber wherein said liquified cellulosic fiber is formed by heating cellulosic fibers in caustic solution at a temperature of at least 100° C. and a pressure of at least 150 psi and at a caustic concentration sufficient to liquify said cellulosic fibers, and comprises about 5 to about 80 percent of the total weight of phenol, formaldehyde and liquified cellulosic fiber and wherein said liquified cellulosic fiber is mixed withsaid phenol and formaldehyde under alkaline conditions.
Claim 44
Dependent Claim
32 words
The method of claim 35 wherein the reaction mixture is diluted to 10 to 30% solids after the viscosity of the reaction mixture reaches 10 to 4000 centipoises to prevent further polymerization.
Claim 45
Independent Claim
92 words
A method of manufacturing a cohesive article of a desired configuration comprising contacting a plurality of fibers with a liquified cellulosic fiber modified phenol-formaldehyde resin and hot pressing said resin contacted fibers together to cause said fibers to adhere to each other, wherein said resin is formed by heating cellulosic fibers at a temperature of at least 100° C. and a pressure of at least 150 psi with an alkali solution to substantially liquify said cellulosic fibers, and polymerizing a mixture of said liquified cellulosic fibers, phenol and formaldehyde, under alkaline conditions.
Claim 46
Independent Claim
92 words
A method of manufacturing a cohesive article of a desired configuration comprising contacting a plurality of fibers with a liquified cellulosic fiber modified phenol-formaldehyde resin and hot pressing said resin contacted fibers together to cause said fibers to adhere to each other, wherein said resin is formed by heating cellulosic fibers at a temperature of at least 100° C. and a pressure of at least 150 psi with an alkali solution to substantially liquify said cellulosic fibers, and polymerizing a mixture of said liquified cellulosic fibers, phenol and formaldehyde, under alkaline conditions.
Claim 47
Dependent Claim
35 words
The method of claim 37 wherein said mixture is polymerized at a pH of 8-13 for a period of time sufficient that said polymer has a viscosity in the range of 10 to 4000 centipoises.
Claim 48
Independent Claim
133 words
A method of molding an object having a predetermined configuration from a plurality of smaller objects comprising disposing an object-resin composition in a mold cavity, closing said mold cavity and pressing said composition to adhere said composition together into said predetermined configuration, wherein said object-resin composition comprises a plurality of said smaller objects and a liquified cellulosic fiber modified phenol-formaldehyde resin formed by mixing a liquified cellulosic fiber, phenol and formaldehyde to form a reaction mixture, while adding said liquified cellulosic fiber incrementally to control the temperature rise of the mixture during reaction to thereby polymerizing said mixture, wherein said liquified cellulosic fibers are formed by heating a mixture of cellulosic fibers in an alkali solution at a sufficiently elevated temperature, above atmospheric pressure and sufficient alkali concentration to liquify the cellulosic fibers.
Claim 49
Independent Claim
133 words
A method of molding an object having a predetermined configuration from a plurality of smaller objects comprising disposing an object-resin composition in a mold cavity, closing said mold cavity and pressing said composition to adhere said composition together into said predetermined configuration, wherein said object-resin composition comprises a plurality of said smaller objects and a liquified cellulosic fiber modified phenol-formaldehyde resin formed by mixing a liquified cellulosic fiber, phenol and formaldehyde to form a reaction mixture, while adding said liquified cellulosic fiber incrementally to control the temperature rise of the mixture during reaction to thereby polymerizing said mixture, wherein said liquified cellulosic fibers are formed by heating a mixture of cellulosic fibers in an alkali solution at a sufficiently elevated temperature, above atmospheric pressure and sufficient alkali concentration to liquify the cellulosic fibers.
Claim 50
Independent Claim
166 words
A method of manufacturing a solid article comprising a plurality of solid members bound with a liquified cellulosic fiber modified phenolformaldehyde polymer comprising: polymerizing a mixture of phenol, formaldehyde, liquified cellulosic fiber and alkali wherein said liquified cellulosic fiber is formed by heating cellulosic fibers in caustic solution at a temperature of at least 100° C. and a pressure of at least 150 psi and at a caustic concentration sufficient to liquify said cellulosic fibers, and comprises about 5 to about 80 percent of the total weight of phenol, formaldehyde and liquified cellulosic fiber and wherein said liquified cellulosic fiber is mixed with said phenol and formaldehyde under alkaline conditions before substantial reaction between said phenol and said formaldehyde; reacting said mixture to form a liquified cellulosic fiber modified phenol-formaldehyde polymer; coating at least a portion of said solid members with said polymer; and pressing said solid members together under conditions to adhere said solid members together with said polymer and thereby manufacture said solid article.
Claim 51
Independent Claim
166 words
A method of manufacturing a solid article comprising a plurality of solid members bound with a liquified cellulosic fiber modified phenolformaldehyde polymer comprising: polymerizing a mixture of phenol, formaldehyde, liquified cellulosic fiber and alkali wherein said liquified cellulosic fiber is formed by heating cellulosic fibers in caustic solution at a temperature of at least 100° C. and a pressure of at least 150 psi and at a caustic concentration sufficient to liquify said cellulosic fibers, and comprises about 5 to about 80 percent of the total weight of phenol, formaldehyde and liquified cellulosic fiber and wherein said liquified cellulosic fiber is mixed with said phenol and formaldehyde under alkaline conditions before substantial reaction between said phenol and said formaldehyde; reacting said mixture to form a liquified cellulosic fiber modified phenol-formaldehyde polymer; coating at least a portion of said solid members with said polymer; and pressing said solid members together under conditions to adhere said solid members together with said polymer and thereby manufacture said solid article.
Claim 52
Dependent Claim
29 words
The method of claim 40 wherein said mixture is polymerized at a temperature of 60° C. to 100° C. and at a pH of 8-13 to form said polymer.
Claim 53
Independent Claim
92 words
A method of manufacturing a plywood article including applying a binder comprising a polymer between two layers of wood and pressing said wood layers together under conditions sufficient to adhere said layers together, the improvement comprising said polymer wherein said polymer is formed by polymerizing a mixture of liquified cellulosic fiber, formed by heating cellulosic fibers in caustic solution at a temperature of at least 100° C. and a pressure of at least 150 psi and at a caustic concentration sufficient to liquify said cellulosic fibers; phenol; and formaldehyde, under alkaline conditions.
Claim 54
Independent Claim
92 words
A method of manufacturing a plywood article including applying a binder comprising a polymer between two layers of wood and pressing said wood layers together under conditions sufficient to adhere said layers together, the improvement comprising said polymer wherein said polymer is formed by polymerizing a mixture of liquified cellulosic fiber, formed by heating cellulosic fibers in caustic solution at a temperature of at least 100° C. and a pressure of at least 150 psi and at a caustic concentration sufficient to liquify said cellulosic fibers; phenol; and formaldehyde, under alkaline conditions.
Claim 55
Dependent Claim
89 words
A plywood article manufactured by applying a binder comprising a polymer between two layers of wood and pressing said wood layers together under conditions sufficient to adhere said layers together, the improvement comprising said polymer wherein said polymer is formed by heating a mixture of liquified cellulosic fiber, phenol and formaldehyde, under alkaline conditions, wherein said liquified cellulosic fibers are formed by heating a mixture of cellulosic fibers in an alkali solution at a sufficiently elevated temperature, above atomospheric pressure and sufficient alkali concentration to liquify the cellulosic fibers.
Claim 56
Dependent Claim
89 words
A plywood article manufactured by applying a binder comprising a polymer between two layers of wood and pressing said wood layers together under conditions sufficient to adhere said layers together, the improvement comprising said polymer wherein said polymer is formed by heating a mixture of liquified cellulosic fiber, phenol and formaldehyde, under alkaline conditions, wherein said liquified cellulosic fibers are formed by heating a mixture of cellulosic fibers in an alkali solution at a sufficiently elevated temperature, above atomospheric pressure and sufficient alkali concentration to liquify the cellulosic fibers.
Claim 57
Independent Claim
113 words
A method of manufacturing an oriented strand board including at least partially coating a plurality of wood fiber strand members with a polymeric binder; disposing said coated strand members in contact with at least one other of said strand members; and pressing said wood fiber strand members to adhere said strand members together; the improvement comprising said polymeric binder wherein said polymer is formed by polymerizing a mixture of liquified cellulosic fiber, formed by heating cellulosic fibers in caustic solution at a temperature of at least 100° C. and a pressure of at least 150 psi and at a caustic concentration sufficient to liquify said cellulosic fibers, phenol, and formaldehyde, under alkaline conditions.
Claim 58
Independent Claim
113 words
A method of manufacturing an oriented strand board including at least partially coating a plurality of wood fiber strand members with a polymeric binder; disposing said coated strand members in contact with at least one other of said strand members; and pressing said wood fiber strand members to adhere said strand members together; the improvement comprising said polymeric binder wherein said polymer is formed by polymerizing a mixture of liquified cellulosic fiber, formed by heating cellulosic fibers in caustic solution at a temperature of at least 100° C. and a pressure of at least 150 psi and at a caustic concentration sufficient to liquify said cellulosic fibers, phenol, and formaldehyde, under alkaline conditions.
Claim 59
Dependent Claim
110 words
An oriented strand board manufactured by at least partially coating a plurality of wood fiber strand members with a polymeric binder; disposing said coated strand members in contact with at least one other of said strand members; and pressing said wood fiber strand members to adhere said strand members together; the improvement comprising said polymeric binder wherein said polymer is formed by polymerizing a mixture of liquified cellulosic fiber, phenol and formaldehyde, under alkaline conditions, wherein said liquified cellulosic fibers are formed by heating a mixture of cellulosic fibers in an alkali solution at a sufficiently elevated temperature, above atomospheric pressure and sufficient alkali concentration to liquify the cellulosic fibers.
Claim 60
Dependent Claim
110 words
An oriented strand board manufactured by at least partially coating a plurality of wood fiber strand members with a polymeric binder; disposing said coated strand members in contact with at least one other of said strand members; and pressing said wood fiber strand members to adhere said strand members together; the improvement comprising said polymeric binder wherein said polymer is formed by polymerizing a mixture of liquified cellulosic fiber, phenol and formaldehyde, under alkaline conditions, wherein said liquified cellulosic fibers are formed by heating a mixture of cellulosic fibers in an alkali solution at a sufficiently elevated temperature, above atomospheric pressure and sufficient alkali concentration to liquify the cellulosic fibers.
Claim 61
Independent Claim
122 words
A method of manufacturing a waferboard including binding togeter a plurality of discrete, relatively thin wood pieces with a polymer binder under pressure sufficient to adhere said wood pieces together into sheet form, the improvement comprising the polymer binder wherein said polymer is formed by polymerizing a mixture of liquified cellulosic fiber, formed by heating cellulosic fibers in caustic solution at a temperature of at least 100° C. and a pressure of at least 150 psi and at a caustic concentration sufficient to liquify said cellulosic fibers; phenol; and formaldehyde, under alkaline conditions. together into sheet form, the improvement comprising the polymer binder wherein said polymer is formed by polymerizing a mixture of liquified cellulosic fiber, phenol and formaldehyde, under alkaline conditions.
Claim 62
Independent Claim
122 words
A method of manufacturing a waferboard including binding togeter a plurality of discrete, relatively thin wood pieces with a polymer binder under pressure sufficient to adhere said wood pieces together into sheet form, the improvement comprising the polymer binder wherein said polymer is formed by polymerizing a mixture of liquified cellulosic fiber, formed by heating cellulosic fibers in caustic solution at a temperature of at least 100° C. and a pressure of at least 150 psi and at a caustic concentration sufficient to liquify said cellulosic fibers; phenol; and formaldehyde, under alkaline conditions. together into sheet form, the improvement comprising the polymer binder wherein said polymer is formed by polymerizing a mixture of liquified cellulosic fiber, phenol and formaldehyde, under alkaline conditions.
Claim 63
Dependent Claim
28 words
The method of claim 46 including applying said polymer binder to said wood pieces as a powder having a moisture content of less than about 15% by weight.
Claim 64
Dependent Claim
94 words
A waferboard manufactured by binding together a plurality of discrete, relatively thin wood pieces with a polymer binder under pressure sufficient to adhere said wood pieces together into sheet form, the improvement comprising the polymer binder wherein said polymer is formed by reacting a mixture of liquified cellulosic fibers, phenol and formaldehyde, under alkaline conditions, said liquified cellulosic fibers formed by heating cellulosic fibers in caustic solution at a temperature of at least 100° C. and a pressure of at least 150 psi and at a caustic concentration sufficient to liquify said cellulosic fibers.
Claim 65
Dependent Claim
94 words
A waferboard manufactured by binding together a plurality of discrete, relatively thin wood pieces with a polymer binder under pressure sufficient to adhere said wood pieces together into sheet form, the improvement comprising the polymer binder wherein said polymer is formed by reacting a mixture of liquified cellulosic fibers, phenol and formaldehyde, under alkaline conditions, said liquified cellulosic fibers formed by heating cellulosic fibers in caustic solution at a temperature of at least 100° C. and a pressure of at least 150 psi and at a caustic concentration sufficient to liquify said cellulosic fibers.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-08 | 1992-11-07 | 1993-05-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-08 | 1996-11-07 | 1997-05-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-08 | 2000-11-07 | 2001-05-09 | $7700.00 | Window Closed / Lapsed |