US4508595A Expired / Lapsed US ⏱️ 0.0 years remaining

Process for manufacturing of formed products

Assignee: Individual
•
Filing: 1983-03-21
•
Granted: 1985-04-02
•
Expires: 2003-03-21
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract A method of making a shaped cellulosic paper or paperboard, comprising the steps of: (a) diluting cellulosic fibers with water to form an aqueous suspension of less than 10 percent by weight cellulosic fibers; (b) agitating the aqueous suspension of cellulosic fibers until the fibers become separated from each other and swollen; (c) dewatering the aqueous suspension to at least 20 percent weight cellulosic fibers; (d) preparing a homogeneous, plastically formable material by adding to the suspension sufficient hydrocolloid to bind substantially all of the water in the material to prevent the water from bleeding out during subsequent shaping and to prevent the fibers from flocculating, and by kneading the material, said material containing water in the range of from about 50 to about 90 percent, fibers in the range of from about 8 to 49 percent, and hydrocolloid in the range of from about 1 to about 20 percent, by weight; (e) shaping the material by extrusion, injection molding, rolling, pressing or drawing, and (f) bonding the solids of the material by drying the shaped material.

Inventors

  • 👤 Stein Gasland

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-10-27 21:24
CPC Classifications
D; D21; D21H; D21H17/00; D21H17/20; C; C04; C04B; C04B26/00; C04B26/02; C04B28/00; C04B28/02; C04B30/00; C04B30/02; D21H23/00; D21H23/02; D21H23/22; D21H23/24; D21H23/26

Claims Analysis

Total Claims: 3
Claim 1
Independent Claim 200 words
A method of making a shaped cellulosic paper or paperboard article from a dilute aqueous suspension of cellulosic fibers, comprising the steps of: (a) diluting cellulosic fibers with water to form a dilute aqueous suspension of less than 10 percent by weight cellulosic fibers; (b) then agitating the dilute aqueous suspension of cellulosic fibers until the fibers become separated from each other and swollen; (c) then dewatering the aqueous suspension to obtain an aqueous suspension of at least 20 percent weight cellulosic fibers; (d) then preparing a homogenous, plastically formable material by adding to the suspension sufficient hydrocolloid to bind substantially all of the water in the material to prevent the water from bleeding out during subsequent shaping and to prevent the fibers from flocculating, and by kneading the material, said material containing water in the range of from about 50 to about 90 percent, fibers in the range of from about 8 to 49 percent, and hydrocolloid in the range of from about 1 to about 20 percent, by weight; (e) shaping the material into the desired shape by extrusion, injection molding, rolling, pressing or drawing, and (f) bonding the solids of the material by drying the shaped material.
Claim 2
Independent Claim 200 words
A method of making a shaped cellulosic paper or paperboard article from a dilute aqueous suspension of cellulosic fibers, comprising the steps of: (a) diluting cellulosic fibers with water to form a dilute aqueous suspension of less than 10 percent by weight cellulosic fibers; (b) then agitating the dilute aqueous suspension of cellulosic fibers until the fibers become separated from each other and swollen; (c) then dewatering the aqueous suspension to obtain an aqueous suspension of at least 20 percent weight cellulosic fibers; (d) then preparing a homogenous, plastically formable material by adding to the suspension sufficient hydrocolloid to bind substantially all of the water in the material to prevent the water from bleeding out during subsequent shaping and to prevent the fibers from flocculating, and by kneading the material, said material containing water in the range of from about 50 to about 90 percent, fibers in the range of from about 8 to 49 percent, and hydrocolloid in the range of from about 1 to about 20 percent, by weight; (e) shaping the material into the desired shape by extrusion, injection molding, rolling, pressing or drawing, and (f) bonding the solids of the material by drying the shaped material.
Claim 3
Dependent Claim 39 words
A homogeneous, plastically formable material capable of being shaped into cellulosic paper or paperboard articles by extrusion, injection molding, coating, rolling, pressing or drawing without the water in the material bleeding out prepared by the method of claim 12.

References Cited (Backward Citations)

US570361A Cited
GB1371096A Cited
US3895998A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1988-04-01 1988-10-01 1989-04-02 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1992-04-01 1992-10-01 1993-04-02 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1996-04-01 1996-10-01 1997-04-02 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag