Composite optical and electro-optical devices
Assignee: Onyx Optics
•
Filing: 1995-12-29
•
Granted: 1998-12-08
•
Expires: 2015-12-29
Abstract
Abstract A method of forming defect-free permanent bonds without the use of adhesives as well as devices formed by this method is disclosed. In general, the disclosed process allows similar or dissimilar crystalline, vitreous or dense polycrystalline ceramic, metallic or organic polymeric components to be first joined by optical contacting and then heat treated to stabilize the bond. The heat treatment can be performed at a low enough temperature to prevent interdiffusion between species, thus insuring that the bond is not subjected to excessive mechanical stresses and that the materials do not undergo phase changes. Therefore stable bonds can be formed using the disclosed process between materials of widely differing physical, mechanical, thermal, optical and electro-optical properties such as different hardness, chemical durability, mechanical strength, coefficients of thermal expansion, thermal conductivity, crystal structure, refractive indices, optical birefringence, nonlinear optical coefficients, electrical conductivity, or semiconducting properties.
Inventors
- 👤 Helmuth E. Meissner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 20:05
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/10; G02B6/12; G02B6/13; G02B6/134; G02B6/1342; B; B32; B32B; B32B17/00; B32B37/00; C; C03; C03C; C03C27/00; C30; C30B; C30B29/00; C30B29/10; C30B29/16; C30B29/22; C30B29/28; C30B33/00; G02B6/122; G02F; G02F1/00; G02F1/35; G02F1/355; G02F1/3551; B32B2307/00; B32B2307/40; B32B2309/00; B32B2309/60; B32B2309/68; G02F1/353; G02F1/3544; G02F1/3548; H; H01; H01S; H01S3/00; H01S3/05; H01S3/06; H01S3/0602; H01S3/0612; H01S3/0617; H01S3/0627; Y; Y10; Y10S; Y10S148/00; Y10S148/012; Y10S148/135; Y10T; Y10T428/00; Y10T428/30; Y10T428/31504
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
151 words
An optical element with an optical interface exhibiting negligible scatter prepared by a process comprising the steps of: (a) optically contacting surfaces of first and second single crystal materials to form an assembly comprising said optical interface, wherein said first and second single crystal materials have different melting temperatures, and wherein said optically contacted surfaces are indicated by a complete disappearance of interference fringes at said optical interface; (b) bonding said optically contacted surfaces of step (a), by gradually heating said surfaces to a temperature below the fusion temperature of said surfaces, but at a temperature and for a time sufficient to diffusion bond said surfaces of said first and second materials; and (c) cooling the bonded structure of step (b) at a rate which allows the removal of stress by annealing, wherein a bonding agent or bonding film is not present between said bonded first and second single crystal materials.
Claim 2
Dependent Claim
151 words
An optical element with an optical interface exhibiting negligible scatter prepared by a process comprising the steps of: (a) optically contacting surfaces of first and second single crystal materials to form an assembly comprising said optical interface, wherein said first and second single crystal materials have different melting temperatures, and wherein said optically contacted surfaces are indicated by a complete disappearance of interference fringes at said optical interface; (b) bonding said optically contacted surfaces of step (a), by gradually heating said surfaces to a temperature below the fusion temperature of said surfaces, but at a temperature and for a time sufficient to diffusion bond said surfaces of said first and second materials; and (c) cooling the bonded structure of step (b) at a rate which allows the removal of stress by annealing, wherein a bonding agent or bonding film is not present between said bonded first and second single crystal materials.
Claim 3
Dependent Claim
35 words
The optical element of claim 1, wherein said bonding temperature of step (b) is a temperature corresponding from about 0.4 to about 0.9 times the value of the lower of the respective material's melting temperature.
Claim 4
Dependent Claim
26 words
The optical element of claim 1, wherein said first single crystal material is a Nd crystal and said second single crystal material is a YAG crystal.
Claim 5
Dependent Claim
133 words
An optical element comprising at least one optical interface, wherein said interface is defect free and exhibits negligible optical scatter, and wherein said interface permanently bonds a first material to a second material without the use of a bonding agent, wherein said first and second materials are dissimilar, and wherein said interface is formed by a process comprising the steps of: precision polishing a surface of said first material and a surface of said second material; optically contacting said surfaces of said first and second materials to form said interface, wherein a complete disappearance of interference fringes at said interface indicates optically contacted surfaces; heating said optically contacted surfaces to stabilize said bonded interface, said heating step at a temperature above 80° C. and below a fusion temperature; and cooling said bonded surfaces.
Claim 6
Dependent Claim
133 words
An optical element comprising at least one optical interface, wherein said interface is defect free and exhibits negligible optical scatter, and wherein said interface permanently bonds a first material to a second material without the use of a bonding agent, wherein said first and second materials are dissimilar, and wherein said interface is formed by a process comprising the steps of: precision polishing a surface of said first material and a surface of said second material; optically contacting said surfaces of said first and second materials to form said interface, wherein a complete disappearance of interference fringes at said interface indicates optically contacted surfaces; heating said optically contacted surfaces to stabilize said bonded interface, said heating step at a temperature above 80° C. and below a fusion temperature; and cooling said bonded surfaces.
Claim 7
Dependent Claim
16 words
The optical element of claim 4, wherein said interface is free of trapped gas or fluid.
Claim 8
Dependent Claim
16 words
The optical element of claim 4, wherein at least one of said materials is a glass.
Claim 9
Dependent Claim
15 words
The optical element of claim 4, wherein at least one of said materials is crystalline.
Claim 10
Dependent Claim
24 words
The optical element of claim 4, wherein at least one of said surfaces is coated with an optical coating prior to forming said interface.
Claim 11
Dependent Claim
29 words
The optical element of claim 4, wherein said optical element is a waveguide and said first material is a guiding layer and said second material is a cladding material.
Claim 12
Dependent Claim
15 words
The optical element of claim 4, wherein at least one of said materials is doped.
Claim 13
Dependent Claim
26 words
The optical element of claim 4, wherein the main function of one of said materials is to conduct heat away from the other of said materials.
Claim 14
Dependent Claim
28 words
The optical element of claim 4, wherein said first and second materials are nonlinear optical crystals and said optical element is a quasi-phase-matched stack used for frequency conversion.
Claim 15
Dependent Claim
20 words
The optical element of claim 12, wherein said nonlinear optical crystals have defined crystallographic orientations of the zinc blende structure.
Claim 16
Dependent Claim
27 words
The optical element of claim 4, wherein said optical element is a multi-element optical component and said first and second materials are first and second optical members.
Claim 17
Dependent Claim
22 words
The optical element of claim 4, wherein said first material is a first fiber and said second material is a second fiber.
References Cited (Backward Citations)
US3123953A
Cited
US3565508A
Cited
US3880632A
Cited
US4149902A
Cited
US4509175A
Cited
US4671846A
Cited
EP0136050A1
Cited
US4531809A
Cited
US4810318A
Cited
US4638552A
Cited
US4983251A
Cited
EP0232935A1
Cited
US5013380A
Cited
US5441803A
Cited
US5201977A
Cited
EP0456060A1
Cited
JPH05255000A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-12-07 | 2002-06-08 | 2002-12-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-12-07 | 2006-06-08 | 2006-12-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-12-07 | 2010-06-08 | 2010-12-08 | $7700.00 | Window Closed / Lapsed |