Silicon chemical mechanical polish etch (CMP) stop for reduced trench fill erosion and method for formation
Assignee: NXP USA Inc
•
Filing: 1997-08-01
•
Granted: 1998-11-17
•
Expires: 2017-08-01
Abstract
Abstract A method for forming shallow trench isolation (STI) (100) begins by forming an oxidizable layer (106) preferably made of polysilicon. An opening is patterned and etched through this layer (106) to define and form the trench isolation region (108). Silicon sidewalls of the trench (108) and the polysilicon layer (106) are then exposed to an oxidizing ambient to form a thermal oxide trench liner (107a) and an erosion-protection polysilicon-oxide layer (107b). A trench fill material (110a) is then deposited and chemically mechanically polished (CMP) utilizing the polysilicon layer (106) as a polish stop. The final polished trench fill plug comprises an ozone TEOS bulk material (110c) and an annular peripheral upper erosion-protection portion formed of the polysilicon-oxide (107d). The annular polysilicon-oxide protection regions (107d) either reduce or entirely eliminate adverse sidewall parasitic erosion which occurs in conventional trench technology when processing active areas (124).
Inventors
- 👤 Sergio Ajuria
- 👤 Soolin Kao
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 00:49
CPC Classifications
H; H10; H10P; H10P95/00; H10P95/06; H10P95/062; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/014; H10W10/10; H10W10/17; Y; Y10; Y10S; Y10S148/00; Y10S148/05
Claims Analysis
Total Claims: 36
Claim 1
Independent Claim
122 words
A method for forming a semiconductor structure, the method comprising the steps of: providing a semiconductor substrate; depositing an oxidizable layer over the semiconductor substrate; patterning the oxidizable layer to form an opening in the oxidizable layer, wherein the oxidizable layer has a sidewall portion and a top portion; oxidizing an exposed portion of the oxidizable layer to form an oxidized top portion and an oxidized sidewall portion of the oxidizable layer; filling the opening with a fill material; removing the oxidized top portion of the oxidizable layer and the oxidizable layer, wherein the fill material and at least a portion of the oxidized sidewall portion remain to form a trench plug region; and exposing the semiconductor structure to a removal environment.
Claim 2
Independent Claim
122 words
A method for forming a semiconductor structure, the method comprising the steps of: providing a semiconductor substrate; depositing an oxidizable layer over the semiconductor substrate; patterning the oxidizable layer to form an opening in the oxidizable layer, wherein the oxidizable layer has a sidewall portion and a top portion; oxidizing an exposed portion of the oxidizable layer to form an oxidized top portion and an oxidized sidewall portion of the oxidizable layer; filling the opening with a fill material; removing the oxidized top portion of the oxidizable layer and the oxidizable layer, wherein the fill material and at least a portion of the oxidized sidewall portion remain to form a trench plug region; and exposing the semiconductor structure to a removal environment.
Claim 3
Dependent Claim
24 words
The method of claim 1, where in the step of depositing an oxidizable layer further comprises: depositing a silicon-containing material as the oxidizable layer.
Claim 4
Dependent Claim
22 words
The method of claim 2, where in the step of depositing an oxidizable layer further comprises: depositing polysilicon as the oxidizable layer.
Claim 5
Dependent Claim
23 words
The method of claim 2, where in the step of depositing an oxidizable layer further comprises: depositing amorphous silicon as the oxidizable layer.
Claim 6
Dependent Claim
24 words
The method of claim 1, wherein the step of filling further comprises: filling the opening with a oxide dielectric material as the fill material.
Claim 7
Dependent Claim
23 words
The method of claim 5, wherein the step of filling further comprises: filling the opening with an ozone TEOS as the dielectric material.
Claim 8
Dependent Claim
23 words
The method of claim 5, wherein the step of filling further comprises: filling the opening with a composite dielectric as the dielectric material.
Claim 9
Dependent Claim
39 words
The method of claim 1, wherein the step of removing comprises the substeps of: polishing away at least some portions of the oxidized top portion; and etching away the oxidizable layer to expose active areas for subsequent processing steps.
Claim 10
Dependent Claim
33 words
The method of claim 1, further comprising the step of: exposing the trench plug region to an etch environment wherein the oxidizable sidewall portion etches at a slower rate than the fill material.
Claim 11
Dependent Claim
46 words
The method of claim 1, wherein the step of oxidizing further comprises the substep of: introducing nitrogen during at least a portion of the oxidizing step to form an oxynitride layer as both the oxidized top portion and the oxidized sidewall portion of the oxidizable layer.
Claim 12
Dependent Claim
22 words
The method of claim 1, further comprising a step of: forming an oxide layer between the oxidizable layer and the semiconductor substrate.
Claim 13
Dependent Claim
31 words
The method of claim 1, wherein the step of oxidizing further comprises the substep of: forming the oxidized top portion and the oxidized sidewall portion as a thermally-grown polysilicon dioxide region.
Claim 14
Dependent Claim
54 words
The method of claim 1, wherein the step of oxidizing further comprises the substep of: forming a thermal silicon dioxide layer on a trenched portion of the semiconductor substrate which underlies the opening in the oxidizable layer wherein the thermal silicon dioxide layer is thinner than the oxidized sidewall portion of the oxidizable layer.
Claim 15
Independent Claim
170 words
A method for forming a semiconductor structure, the method comprising the steps of: providing a semiconductor substrate; forming a dielectric layer over the semiconductor substrate; forming an oxidizable layer over the dielectric layer; forming an opening through the oxidizable layer, through the dielectric layer, and into the semiconductor substrate, the opening defining a oxidizable sidewall portion of the oxidizable layer, a dielectric sidewall portion of the dielectric layer, and a semiconductor substrate sidewall portion of the semiconductor substrate; forming an oxide on the oxidizable sidewall portion of the oxidizable layer to form a first oxidized sidewall on the oxidizable layer and forming an oxide on the semiconductor substrate sidewall portion of the semiconductor substrate to form a second oxidized sidewall; forming a fill layer over the opening; planarizing to expose a top portion of the oxidizable layer; removing the oxidizable layer, wherein the first oxidized sidewall remains along with a portion of the fill layer to create a trench plug region; and exposing the semiconductor structure to a removal environment.
Claim 16
Independent Claim
170 words
A method for forming a semiconductor structure, the method comprising the steps of: providing a semiconductor substrate; forming a dielectric layer over the semiconductor substrate; forming an oxidizable layer over the dielectric layer; forming an opening through the oxidizable layer, through the dielectric layer, and into the semiconductor substrate, the opening defining a oxidizable sidewall portion of the oxidizable layer, a dielectric sidewall portion of the dielectric layer, and a semiconductor substrate sidewall portion of the semiconductor substrate; forming an oxide on the oxidizable sidewall portion of the oxidizable layer to form a first oxidized sidewall on the oxidizable layer and forming an oxide on the semiconductor substrate sidewall portion of the semiconductor substrate to form a second oxidized sidewall; forming a fill layer over the opening; planarizing to expose a top portion of the oxidizable layer; removing the oxidizable layer, wherein the first oxidized sidewall remains along with a portion of the fill layer to create a trench plug region; and exposing the semiconductor structure to a removal environment.
Claim 17
Dependent Claim
30 words
The method of claim 14, wherein the step of forming the opening further comprises: forming, as the opening, an isolation trench which separates two active regions of the semiconductor substrate.
Claim 18
Dependent Claim
44 words
The method of claim 14, wherein the step of forming the oxide further comprises: forming the first oxidized sidewall to have a first thickness and the second oxidized sidewall to have a second thickness, wherein the first thickness is greater than the second thickness.
Claim 19
Dependent Claim
32 words
The method of claim 14, wherein the step of forming the oxide further comprises forming the first oxidized sidewall and the second oxidized sidewall simultaneously in time from a same growth ambient.
Claim 20
Dependent Claim
44 words
The method of claim 14, wherein the step of forming the oxide further comprises: forming the first oxidized sidewall to have a first thickness and the second oxidized sidewall to have a second thickness, wherein the first thickness is approximately double the second thickness.
Claim 21
Dependent Claim
23 words
The method of claim 14, wherein the step of forming the oxide further comprises: forming substantially no oxide on the dielectric sidewall portion.
Claim 22
Dependent Claim
22 words
The method of claim 14, wherein the step of forming a fill layer further comprises: forming the fill layer with deposited TEOS.
Claim 23
Dependent Claim
24 words
The method of claim 14, wherein the step of forming a fill layer further comprises: forming the fill layer with ozone-TEOS as the TEOS.
Claim 24
Dependent Claim
87 words
The method of claim 14, wherein: the step of forming an oxide further comprises forming the first oxide where the first oxide has an inner sidewall edge adjacent to the opening and an outer sidewall edge adjacent to the oxidizable layer; and the step of removing the oxidizable layer comprises removing the oxidizable layer wherein the outer sidewall edge is exposed to an ambient and the inner sidewall edge is adjacent to a portion of the fill layer which remains as part of the trench plug region.
Claim 25
Dependent Claim
41 words
The method of claim 14, wherein the step of forming an oxide further comprises the substeps of: introducing nitrogen during at least a portion of the oxidizing step to form an oxynitride layer as both the first and second oxidized sidewall.
Claim 26
Dependent Claim
36 words
The method of claim 14, wherein the step of forming an oxide further comprises the substeps of: introducing nitrogen in a nitrous oxide or nitric oxide form during growth of the first and second oxidized sidewall.
Claim 27
Dependent Claim
64 words
The method of claim 14, further comprising the steps of: exposing active areas, adjacent to the trench plug region, to etch environments which erode the trench plug region, the first oxidized sidewall eroding at a slower rate than the portion of the fill layer whereby trench erosion adjacent a sidewall of the active areas is reduced via the presence of the first oxidized sidewall.
Claim 28
Dependent Claim
36 words
The method of claim 14, wherein the step of planarizing further comprises: planarizing by chemical mechanical polishing down to the top portion of the oxidizable layer by using the oxidizable material as a polish stop material.
Claim 29
Dependent Claim
32 words
The method of claim 14, wherein the step of forming an oxidizable layer comprises: forming the oxidizable layer as a layer of polysilicon wherein the first oxidized sidewall is a polysilicon-oxide region.
Claim 30
Independent Claim
243 words
A method for forming a semiconductor structure, the method comprising the steps of: providing a semiconductor substrate; forming a dielectric layer over the semiconductor substrate; depositing a silicon-containing layer over the dielectric layer, the silicon-containing layer being semiconductive; forming an isolation trench through the silicon-containing layer, the dielectric layer, and the semiconductor substrate, wherein the isolation trench includes a silicon-containing sidewall portion, a dielectric sidewall portion, and a semiconductor substrate sidewall portion; forming an oxide on the silicon-containing sidewall portion to form a first oxidized sidewall and forming an oxide on the semiconductor substrate sidewall portion to form a second oxidized sidewall; depositing a dielectric fill layer over the isolation trench; densifying the dielectric fill layer; patterning a reverse masked region above the isolation trench to form exposed portions of the dielectric fill layer; etching the exposed portions of the dielectric fill layer using the silicon-containing layer as an etch stop; removing the reverse masked region; chemical mechanical polishing to form a planarized surface using the silicon-containing layer as a polish stop; etching the silicon-containing layer whereby a portion of the dielectric fill layer and a portion of the first oxidized sidewall remain behind to form a trench isolation plug; and processing an active area of the semiconductor substrate to erode the first oxidized sidewall at a slower rate than the dielectric fill layer in the isolation trench wherein the first oxidized sidewall prevents substantial exposure of a sidewall of the active area.
Claim 31
Independent Claim
243 words
A method for forming a semiconductor structure, the method comprising the steps of: providing a semiconductor substrate; forming a dielectric layer over the semiconductor substrate; depositing a silicon-containing layer over the dielectric layer, the silicon-containing layer being semiconductive; forming an isolation trench through the silicon-containing layer, the dielectric layer, and the semiconductor substrate, wherein the isolation trench includes a silicon-containing sidewall portion, a dielectric sidewall portion, and a semiconductor substrate sidewall portion; forming an oxide on the silicon-containing sidewall portion to form a first oxidized sidewall and forming an oxide on the semiconductor substrate sidewall portion to form a second oxidized sidewall; depositing a dielectric fill layer over the isolation trench; densifying the dielectric fill layer; patterning a reverse masked region above the isolation trench to form exposed portions of the dielectric fill layer; etching the exposed portions of the dielectric fill layer using the silicon-containing layer as an etch stop; removing the reverse masked region; chemical mechanical polishing to form a planarized surface using the silicon-containing layer as a polish stop; etching the silicon-containing layer whereby a portion of the dielectric fill layer and a portion of the first oxidized sidewall remain behind to form a trench isolation plug; and processing an active area of the semiconductor substrate to erode the first oxidized sidewall at a slower rate than the dielectric fill layer in the isolation trench wherein the first oxidized sidewall prevents substantial exposure of a sidewall of the active area.
Claim 32
Dependent Claim
29 words
The method of claim 28, wherein the step of forming the oxide further comprises: forming an oxide layer; and introducing a nitrogen containing species to form an oxynitride layer.
Claim 33
Dependent Claim
25 words
The method of claim 28, wherein the step of introducing the nitrogen further comprises: introducing nitric oxide or nitrous oxide as the nitrogen containing species.
Claim 34
Dependent Claim
20 words
The method of claim 28, wherein the step of depositing the silicon-containing layer further comprises: depositing a doped silicon-containing layer.
Claim 35
Dependent Claim
20 words
The method of claim 28, wherein the step of depositing the silicon-containing layer further comprises: depositing an undoped silicon-containing layer.
Claim 36
Dependent Claim
44 words
The method of claim 28, wherein the step of etching the silicon-containing layer further comprises: performing an oxide break-up etch to remove any remaining oxide overlying the silicon-containing layer; and switching etch chemistry to a silicon etching environment to substantially etch the silicon-containing layer.
References Cited (Backward Citations)
US5190889A
Cited
US5229316A
Cited
US5506168A
Cited
US5677229A
Cited
US5340769A
Cited
US5387540A
Cited
US5578518A
Cited
US5766823A
Cited
US5604159A
Cited
US5455194A
Cited
US5712185A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-11-16 | 2002-05-18 | 2002-11-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-11-16 | 2006-05-18 | 2006-11-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-11-16 | 2010-05-18 | 2010-11-17 | $7700.00 | Window Closed / Lapsed |