Protected encapsulation of catalytic layer for electroless copper interconnect
Assignee: Cornell Research Foundation Inc
•
Filing: 1996-01-16
•
Granted: 1998-10-20
•
Expires: 2016-01-16
Abstract
Abstract A method for utilizing electroless copper deposition to form interconnects on a semiconductor. Once a via or a trench is formed in a dielectric layer, a titanium nitride (TiN) or tantalum (Ta) barrier layer is deposited. Then, a catalytic copper seed layer is conformally blanket deposited in vacuum over the barrier layer. Next, without breaking the vacuum, an aluminum protective layer is deposited onto the catalytic layer to encapsulate and protect the catalytic layer from oxidizing. An electroless deposition technique is then used to auto-catalytically deposit copper on the catalytic layer. The electroless deposition solution dissolves the overlying protective layer to expose the surface of the underlying catalytic layer. The electroless copper deposition occurs on this catalytic surface, and continues until the via/trench is filled. Subsequently, the copper and barrier material are polished by an application of chemical-mechanical polishing (CMP) to remove excess copper and barrier material from the surface, so that the only copper and barrier material remaining are in the via/trench openings. Then an overlying silicon nitride (SiN) layer is formed above the exposed copper in order to form a dielectric barrier layer. The copper interconnect is fully encapsulated from the adjacent material by the TiN (or Ta) barrier layer and the overlying SiN layer.
Inventors
- 👤 Yosef Schacham-Diamand
- 👤 Valery M. Dubin
- 👤 Chiu H. Ting
- 👤 Bin Zhao
- 👤 Prahalad K. Vasudev
- 👤 Melvin Desilva
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 07:07
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/074; H10W20/077; H10W20/031; H10W20/032; H10W20/033; H10W20/042; H10W20/044; H10W20/047; H10W20/049; Y; Y10; Y10S; Y10S977/00; Y10S977/70; Y10S977/701; Y10S977/712; Y10S977/81; Y10S977/84; Y10S977/888; Y10S977/89
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
105 words
A method of forming a protected catalytic seed surface in order to deposit metal by electroless deposition to form an interconnect structure on a semiconductor wafer, comprising the steps of: depositing a barrier layer; depositing a catalytic seed layer on said barrier layer under vacuum; depositing a protective layer over said catalytic seed layer without breaking vacuum seal from the previous step in order to prevent oxidation of said catalytic seed layer; subjecting said wafer to an electroless deposition solution, wherein said electroless deposition solution dissolves said protective layer to expose said underlying catalytic seed layer, which then allows copper to be electrolessly deposited thereon.
Claim 2
Independent Claim
105 words
A method of forming a protected catalytic seed surface in order to deposit metal by electroless deposition to form an interconnect structure on a semiconductor wafer, comprising the steps of: depositing a barrier layer; depositing a catalytic seed layer on said barrier layer under vacuum; depositing a protective layer over said catalytic seed layer without breaking vacuum seal from the previous step in order to prevent oxidation of said catalytic seed layer; subjecting said wafer to an electroless deposition solution, wherein said electroless deposition solution dissolves said protective layer to expose said underlying catalytic seed layer, which then allows copper to be electrolessly deposited thereon.
Claim 3
Dependent Claim
22 words
The method of claim 1 wherein said barrier layer is formed by depositing TiN, Ta, Ti, W, WN, TiSiN, TaSiN or TaN.
Claim 4
Dependent Claim
23 words
The method of claim 2 wherein said catalytic seed layer is formed by depositing Ni, Co, Ag, Au, Pd, Pt, Rh or Cu.
Claim 5
Dependent Claim
14 words
The method of claim 3 wherein said protective layer is formed by depositing Al.
Claim 6
Dependent Claim
139 words
In a fabrication of a semiconductor device, a method of forming a protected catalytic seed surface on a barrier metal in order to deposit metal by electroless deposition to form an interconnect structure on a semiconductor wafer, comprising the steps of: depositing a metal barrier layer; depositing a catalytic metal on said metal barrier layer under vacuum in order to form a catalytic seed surface for electroless deposition of copper; depositing a protective layer to coat said catalytic seed surface without breaking vacuum seal from the previous step, in order to prevent oxidation of said catalytic seed surface when said wafer is removed from said vacuum; subjecting said wafer to an electroless deposition solution, wherein said electroless deposition solution dissolves said protective layer to expose said underlying catalytic seed surface, which then allows copper to be electrolessly deposited thereon.
Claim 7
Dependent Claim
139 words
In a fabrication of a semiconductor device, a method of forming a protected catalytic seed surface on a barrier metal in order to deposit metal by electroless deposition to form an interconnect structure on a semiconductor wafer, comprising the steps of: depositing a metal barrier layer; depositing a catalytic metal on said metal barrier layer under vacuum in order to form a catalytic seed surface for electroless deposition of copper; depositing a protective layer to coat said catalytic seed surface without breaking vacuum seal from the previous step, in order to prevent oxidation of said catalytic seed surface when said wafer is removed from said vacuum; subjecting said wafer to an electroless deposition solution, wherein said electroless deposition solution dissolves said protective layer to expose said underlying catalytic seed surface, which then allows copper to be electrolessly deposited thereon.
Claim 8
Dependent Claim
22 words
The method of claim 5 wherein said barrier layer is formed by depositing TiN, Ta, Ti, W, WN, TiSiN, TaSiN or TaN.
Claim 9
Dependent Claim
22 words
The method of claim 6 wherein said catalytic surface is formed by depositing Ni, Co, Ag, Au, Pd, Pt, Rh or Cu.
Claim 10
Dependent Claim
13 words
The method of claim 7 said protective layer is formed by depositing Al.
Claim 11
Dependent Claim
165 words
In a formation of a semiconductor interconnect structure in which two conductive regions are separated by a dielectric layer and connected by said interconnect structure, a method of forming a protected catalytic seed surface on a barrier metal in order to deposit metal by electroless deposition to form an interconnect structure on a semiconductor wafer, comprising the steps of: forming an opening in said dielectric layer; depositing a barrier layer in said opening; depositing a catalytic metal on said barrier layer under vacuum in order to form a catalytic seed layer for electroless deposition of copper; depositing a protective layer to coat said catalytic seed layer without breaking vacuum seal from the previous step in order to prevent oxidation of said catalytic seed layer when said wafer is removed from said vacuum; subjecting said wafer to an electroless deposition solution, wherein said electroless deposition solution dissolves said protective layer to expose said underlying catalytic seed layer, which then allows copper to be electrolessly deposited thereon.
Claim 12
Dependent Claim
165 words
In a formation of a semiconductor interconnect structure in which two conductive regions are separated by a dielectric layer and connected by said interconnect structure, a method of forming a protected catalytic seed surface on a barrier metal in order to deposit metal by electroless deposition to form an interconnect structure on a semiconductor wafer, comprising the steps of: forming an opening in said dielectric layer; depositing a barrier layer in said opening; depositing a catalytic metal on said barrier layer under vacuum in order to form a catalytic seed layer for electroless deposition of copper; depositing a protective layer to coat said catalytic seed layer without breaking vacuum seal from the previous step in order to prevent oxidation of said catalytic seed layer when said wafer is removed from said vacuum; subjecting said wafer to an electroless deposition solution, wherein said electroless deposition solution dissolves said protective layer to expose said underlying catalytic seed layer, which then allows copper to be electrolessly deposited thereon.
Claim 13
Dependent Claim
17 words
The method of claim 9 wherein said barrier layer is formed by depositing titanium nitride or tantalum.
Claim 14
Dependent Claim
14 words
The method of claim 10 wherein said catalytic layer is formed by depositing copper.
Claim 15
Dependent Claim
11 words
The method of claim 11 wherein said protective layer is aluminum.
Claim 16
Dependent Claim
17 words
The method of claim 12 wherein said interconnect structure is a plug formed in a via opening.
Claim 17
Dependent Claim
18 words
The method of claim 13 wherein said interconnect structure is a metal line formed in a trench opening.
Claim 18
Dependent Claim
27 words
The method of claim 14 wherein said opening is for both via and trench fill and said interconnect structure forms both a plug and a metal line.
Claim 19
Dependent Claim
172 words
In a formation of a semiconductor interconnect structure in which two conductive regions are separated by a dielectric layer and connected by said interconnect structure, a method of forming a protected catalytic seed surface on a barrier metal in order to deposit metal by electroless deposition to form an interconnect structure on a semiconductor wafer, comprising the steps of: forming an opening in said dielectric layer; depositing a metal barrier layer in said opening; depositing at least several mono-layers of copper atoms on said barrier layer under vacuum in order to form a copper seed layer for electroless deposition of copper; depositing a protective layer to coat said copper seed layer without breaking vacuum seal from the previous step in order to prevent oxidation of copper when said wafer is removed from said vacuum; subjecting said wafer to an electroless deposition solution, wherein said electroless deposition solution dissolves said protective layer to expose said underlying copper seed layer, which then allows copper for forming said interconnect structure to be electrolessly deposited thereon.
Claim 20
Dependent Claim
172 words
In a formation of a semiconductor interconnect structure in which two conductive regions are separated by a dielectric layer and connected by said interconnect structure, a method of forming a protected catalytic seed surface on a barrier metal in order to deposit metal by electroless deposition to form an interconnect structure on a semiconductor wafer, comprising the steps of: forming an opening in said dielectric layer; depositing a metal barrier layer in said opening; depositing at least several mono-layers of copper atoms on said barrier layer under vacuum in order to form a copper seed layer for electroless deposition of copper; depositing a protective layer to coat said copper seed layer without breaking vacuum seal from the previous step in order to prevent oxidation of copper when said wafer is removed from said vacuum; subjecting said wafer to an electroless deposition solution, wherein said electroless deposition solution dissolves said protective layer to expose said underlying copper seed layer, which then allows copper for forming said interconnect structure to be electrolessly deposited thereon.
Claim 21
Dependent Claim
17 words
The method of claim 16 wherein said barrier layer is formed by depositing titanium nitride or tantalum.
Claim 22
Dependent Claim
11 words
The method of claim 17 wherein said protective layer is aluminum.
Claim 23
Dependent Claim
17 words
The method of claim 18 wherein said interconnect structure is a plug formed in a via opening.
Claim 24
Dependent Claim
18 words
The method of claim 18 wherein said interconnect structure is a metal line formed in a trench opening.
Claim 25
Dependent Claim
27 words
The method of claim 18 wherein said opening is for both via and trench fill and said interconnect structure forms both a plug and a metal line.
Claim 26
Dependent Claim
39 words
The method of claim 18 further including the step of depositing an adhesion promoter layer prior to the step of depositing said barrier layer in order to improve bonding of said barrier layer when said barrier layer is deposited.
References Cited (Backward Citations)
US4574095A
Cited
US4789648A
Cited
US4985750A
Cited
US4894260A
Cited
US5192581A
Cited
US5183795A
Cited
US5151168A
Cited
US5240497A
Cited
US5580668A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-10-19 | 2002-04-20 | 2002-10-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-10-19 | 2006-04-20 | 2006-10-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-10-19 | 2010-04-20 | 2010-10-20 | $7700.00 | Window Closed / Lapsed |