US5795627A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for annealing damaged semiconductor regions allowing for enhanced oxide growth
Assignee: Monterey Research LLC
•
Filing: 1997-02-14
•
Granted: 1998-08-18
•
Expires: 2017-02-14
Abstract
Abstract A method of forming an oxide enhancing region, such as phosphorus, in a semiconductor substrate with minimal damage is provided. The method includes the steps of forming an oxide enhancing region in the semiconductor substrate to a depth below the semiconductor substrate. A 308 nm excimer laser is then applied to the oxide enhancing region in order to reduce the damage caused by forming the oxide enhancing region. A uniform and reliable oxide layer is then formed on the surface of the substrate over the damage reduced oxide enhancing region.
Inventors
- 👤 Sunil Mehta
- 👤 Emi Ishida
- 👤 Xiao-Yu Li
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 05:46
CPC Classifications
H; H10; H10W; H10W10/00; H10W10/10; H10W10/13; H10B; H10B69/00; H10D; H10D84/00; H10D84/01; H10D84/0123; H10D84/0126; H10D84/0144; H10P; H10P14/00; H10P14/60; H10W10/01; H10W10/011; H10W10/012; H10W10/0125; H10P14/63; H10P14/6302; H10P14/6304; H10P14/6306; H10P14/6308; H10P14/6309; H10P14/6322
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
86 words
A method of forming a region of impurity in a semiconductor substrate, comprising: (a) forming a mask layer on the surface of the semiconductor substrate; (b) patterning the mask layer to expose a portion of the semiconductor substrate; (c) forming an oxide growth enhancing impurity region in the semiconductor substrate; (d) applying laser energy to the semiconductor substrate at a sufficient magnitude to liquify the oxide growth enhancing impurity region; and (e) growing an oxide layer having a first thickness above the oxide growth enhancing region.
Claim 2
Independent Claim
86 words
A method of forming a region of impurity in a semiconductor substrate, comprising: (a) forming a mask layer on the surface of the semiconductor substrate; (b) patterning the mask layer to expose a portion of the semiconductor substrate; (c) forming an oxide growth enhancing impurity region in the semiconductor substrate; (d) applying laser energy to the semiconductor substrate at a sufficient magnitude to liquify the oxide growth enhancing impurity region; and (e) growing an oxide layer having a first thickness above the oxide growth enhancing region.
Claim 3
Dependent Claim
10 words
The method of claim 1, wherein the impurity is phosphorus.
Claim 4
Dependent Claim
10 words
The method of claim 1, wherein the impurity is arsenic.
Claim 5
Dependent Claim
10 words
The method of claim 1, wherein the impurity is boron.
Claim 6
Dependent Claim
37 words
The method of claim 1, wherein the step of forming an oxide growth enhancing impurity region comprises: (a) applying laser energy to the semiconductor substrate to incorporate the oxide growth enhancing impurity region in the semiconductor substrate.
Claim 7
Dependent Claim
28 words
The method of claim 1, wherein the step of forming an oxide growth enhancing impurity region comprises ion implanting the oxide growth enhancing impurity into the semiconductor substrate.
Claim 8
Dependent Claim
39 words
The method of claim 1, wherein the applying step comprises applying energy from an XeCl laser having a wavelength of 308 nm at an energy in a range of approximately 750 mJ/cm 2 to approximately 1.3 J/cm 2 .
Claim 9
Dependent Claim
16 words
The method of claim 1, wherein the applying step comprises applying energy from an excimer laser.
Claim 10
Independent Claim
134 words
A method of forming a region of oxide growth enhancing impurity in a semiconductor substrate, comprising: (a) forming a mask layer on a surface of the semiconductor substrate; (b) patterning the mask layer to expose a portion of the semiconductor substrate surface into which the oxide growth enhancing impurity is to be implanted; (c) implanting the oxide growth enhancing impurity into the exposed portion of the semiconductor substrate; (d) applying laser energy to the exposed portion of the semiconductor substrate surface at a sufficient magnitude to liquify the oxide growth enhancing impurity region; and (e) growing an oxide layer having a first thickness above the exposed portion of the semiconductor substrate and having a second thickness above a non-exposed portion of the semiconductor substrate, wherein the first thickness is greater than the second thickness.
Claim 11
Independent Claim
134 words
A method of forming a region of oxide growth enhancing impurity in a semiconductor substrate, comprising: (a) forming a mask layer on a surface of the semiconductor substrate; (b) patterning the mask layer to expose a portion of the semiconductor substrate surface into which the oxide growth enhancing impurity is to be implanted; (c) implanting the oxide growth enhancing impurity into the exposed portion of the semiconductor substrate; (d) applying laser energy to the exposed portion of the semiconductor substrate surface at a sufficient magnitude to liquify the oxide growth enhancing impurity region; and (e) growing an oxide layer having a first thickness above the exposed portion of the semiconductor substrate and having a second thickness above a non-exposed portion of the semiconductor substrate, wherein the first thickness is greater than the second thickness.
Claim 12
Dependent Claim
39 words
The method of claim 9, wherein the applying step comprises applying energy from an XeCl laser having a wavelength of 308 nm at an energy in a range of approximately 750 mJ/cm 2 to approximately 1.3 J/cm 2 .
Claim 13
Dependent Claim
16 words
The method of claim 9, wherein the applying step comprises applying energy from an excimer laser.
Claim 14
Dependent Claim
13 words
The method of claim 9, wherein the oxide growth enhancing impurity is phosphorus.
Claim 15
Dependent Claim
13 words
The method of claim 9, wherein the oxide growth enhancing impurity is arsenic.
Claim 16
Dependent Claim
13 words
The method of claim 9, wherein the oxide growth enhancing impurity is boron.
Claim 17
Independent Claim
96 words
A method for forming a phosphorus region in a silicon substrate, comprising the steps of: (a) forming the phosphorus region in the silicon substrate to a depth below a surface of the silicon substrate; (b) applying laser energy to the surface of the silicon substrate at a sufficient energy and for a sufficient time to melt the phosphorus region to at least said depth; and (c) growing an oxide layer having a first thickness above the phosphorus region and a second thickness above the non-phosphorus region, wherein the first thickness is greater than the second thickness.
Claim 18
Independent Claim
96 words
A method for forming a phosphorus region in a silicon substrate, comprising the steps of: (a) forming the phosphorus region in the silicon substrate to a depth below a surface of the silicon substrate; (b) applying laser energy to the surface of the silicon substrate at a sufficient energy and for a sufficient time to melt the phosphorus region to at least said depth; and (c) growing an oxide layer having a first thickness above the phosphorus region and a second thickness above the non-phosphorus region, wherein the first thickness is greater than the second thickness.
Claim 19
Dependent Claim
43 words
The method of claim 15, wherein the step of forming comprises: (i) placing the silicon substrate in an atmosphere of a compound having phosphorus; (ii) applying laser energy to the surface of the silicon substrate to incorporate the phosphorus into the phosphorus region.
Claim 20
Dependent Claim
19 words
The method of claim 15, wherein the step of forming comprises ion implanting the phosphorus into the silicon substrate.
Claim 21
Dependent Claim
44 words
The method of claim 15, further including the steps, prior to the forming step, of forming a mask layer on the surface of the silicon substrate, and patterning the mask layer to expose a portion of the substrate into which the phosphorus is formed.
Claim 22
Independent Claim
134 words
A method for forming an oxide on a surface of a silicon substrate, comprising the steps of: (a) forming a mask layer on the surface of the silicon substrate; (b) patterning the mask layer to expose a portion of the silicon substrate; (c) implanting phosphorus into the exposed portion of the silicon substrate to a depth below a surface of the substrate in order to form a program junction; (d) applying laser energy to the surface of the exposed portion of the silicon substrate at a sufficient energy and for time to melt the substrate to approximately the depth of the phosphorus in the program junction; and (e) forming an oxide on the surface of the silicon substrate, at least a portion of the oxide being formed over the exposed portion of the substrate.
Claim 23
Independent Claim
134 words
A method for forming an oxide on a surface of a silicon substrate, comprising the steps of: (a) forming a mask layer on the surface of the silicon substrate; (b) patterning the mask layer to expose a portion of the silicon substrate; (c) implanting phosphorus into the exposed portion of the silicon substrate to a depth below a surface of the substrate in order to form a program junction; (d) applying laser energy to the surface of the exposed portion of the silicon substrate at a sufficient energy and for time to melt the substrate to approximately the depth of the phosphorus in the program junction; and (e) forming an oxide on the surface of the silicon substrate, at least a portion of the oxide being formed over the exposed portion of the substrate.
Claim 24
Dependent Claim
20 words
The method of claim 19, wherein the depth of the phosphorus is between approximately 20 nanometers and approximately 150 nanometers.
Claim 25
Dependent Claim
39 words
The method of claim 19, wherein the step (d) comprises applying energy from an XeCl laser having a wavelength of 308 nm at an energy in a range of approximately 750 mJ/cm 2 to approximately 1.3 J/cm 2 .
Claim 26
Dependent Claim
16 words
The method of claim 19, wherein the step (d) comprises applying energy from an excimer laser.
Claim 27
Dependent Claim
19 words
The method of claim 19, wherein the step of implanting comprises ion implanting the phosphorus into the silicon substrate.
Claim 28
Dependent Claim
46 words
The method of claim 19 wherein the step of implanting comprises: (i) placing the substrate in an atmosphere of a compound having phosphorus; (ii) applying laser energy to the surface of the silicon substrate to incorporate the phosphorus into the exposed portion of the silicon substrate.
References Cited (Backward Citations)
US4500365A
Cited
US4482393A
Cited
US4924278A
Cited
US5620931A
Cited
US5227329A
Cited
US5514880A
Cited
US5316969A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-08-17 | 2002-02-16 | 2002-08-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-08-17 | 2006-02-16 | 2006-08-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-08-17 | 2010-02-16 | 2010-08-18 | $7700.00 | Window Closed / Lapsed |