Method for forming silicon-germanium/Si/silicon dioxide heterostructure using germanium implant
Assignee: Sharp Corp
•
Filing: 1993-08-30
•
Granted: 1998-08-11
•
Expires: 2013-08-30
Abstract
Abstract A method for fabricating a GeSi/Si/SiO 2 heterostructure comprises the steps of: (a) providing a monocrystalline Si substrate; (b) defining a GeSi region within the Si substrate while leaving a Si cap overlying the GeSi region, the Si cap being an integral part of the monocrystalline substrate; and (c) oxidizing part of the Si cap to thereby produce the GeSi/Si/SiO 2 heterostructure.
Inventors
- 👤 Tatsuo Nakato
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 10:08
CPC Classifications
B; B82; B82Y; B82Y10/00; H; H10; H10P; H10P30/00; H10P30/20; H10P30/202; H10P30/204; H10D; H10D30/00; H10D30/01; H10D30/014; H10D30/021; H10D30/031; H10D30/0321; H10D30/0323; H10D30/60; H10D30/67; H10D30/674; H10D30/6741; H10D30/6748; H10D30/80; H10D30/801; H10D86/00; H10D86/01; H10D86/201; H10P30/208; H10P30/209
Claims Analysis
Total Claims: 39
Claim 1
Independent Claim
166 words
A method for fabricating a combination of a conductive region having a relatively high charge carrier mobility and an insulator in a substrate composed of a first semiconductive material having a comparatively lower first charge carrier mobility, said method comprising the steps of: (a) implanting a mobility enhancing species into a first region of the low-mobility first semiconductive material to thereby convert the first region into a second region composed of a second semiconductive material having a second charge carrier mobility that is substantially higher than the first charge carrier mobility of the first semiconductive material; and thereafter (b) oxidizing a portion of the low-mobility first semiconductive material that is spaced apart from the second region to thereby create a heterostructure having three layers formed in the recited order of: (1) the second region into which the mobility enhancing species are implanted; (2) a third region which remains substantially composed of the low-mobility first semiconductive material; and (3) the oxidized portion of the low-mobility semiconductive material.
Claim 2
Independent Claim
166 words
A method for fabricating a combination of a conductive region having a relatively high charge carrier mobility and an insulator in a substrate composed of a first semiconductive material having a comparatively lower first charge carrier mobility, said method comprising the steps of: (a) implanting a mobility enhancing species into a first region of the low-mobility first semiconductive material to thereby convert the first region into a second region composed of a second semiconductive material having a second charge carrier mobility that is substantially higher than the first charge carrier mobility of the first semiconductive material; and thereafter (b) oxidizing a portion of the low-mobility first semiconductive material that is spaced apart from the second region to thereby create a heterostructure having three layers formed in the recited order of: (1) the second region into which the mobility enhancing species are implanted; (2) a third region which remains substantially composed of the low-mobility first semiconductive material; and (3) the oxidized portion of the low-mobility semiconductive material.
Claim 3
Dependent Claim
55 words
The fabricating method of claim 1 wherein the low-mobility semiconductive material is a monocrystal, said method further comprising: annealing the low-mobility semiconductive material after said step of implanting the mobility enhancing species to thereby substantially repair damage caused to the crystal structure of the monocrystal due to said step of implanting the mobility enhancing species.
Claim 4
Dependent Claim
27 words
The fabricating method of claim 1 further comprising: doping the region into which the mobility enhancing species is implanted with a dopant having a pre-specified conductivity type.
Claim 5
Dependent Claim
63 words
The fabricating method of claim 1 further comprising: after said step of implanting the mobility enhancing species, chemically combining the mobility enhancing species with the low-mobility semiconductive material of said second region to thereby produce a compound of the mobility enhancing species and the low-mobility semiconductive material, where said compound has a comparatively higher charge carrier mobility than the low-mobility first semiconductive material.
Claim 6
Independent Claim
80 words
A method for fabricating a Ge x Si 1-x /Si/SiO 2 heterostructure comprising the steps of: providing a Si substrate; implanting Ge into the Si substrate to thereby define a Ge x Si 1-x region within the Si substrate while leaving a Si cap overlying the Ge x Si 1-x region, x being a value greater than zero but less than one; and oxidizing part of the Si cap to thereby produce said Ge x Si 1-x /Si/SiO 2 heterostructure.
Claim 7
Independent Claim
80 words
A method for fabricating a Ge x Si 1-x /Si/SiO 2 heterostructure comprising the steps of: providing a Si substrate; implanting Ge into the Si substrate to thereby define a Ge x Si 1-x region within the Si substrate while leaving a Si cap overlying the Ge x Si 1-x region, x being a value greater than zero but less than one; and oxidizing part of the Si cap to thereby produce said Ge x Si 1-x /Si/SiO 2 heterostructure.
Claim 8
Dependent Claim
52 words
The fabricating method of claim 5 wherein said step of implanting Ge includes: implanting a pre-specified concentration of Ge ions through a top surface of the substrate and into a first range of depths below the substrate top surface; and annealing the substrate to chemically combine the implanted Ge with neighboring Si.
Claim 9
Dependent Claim
36 words
The fabricating method of claim 6 wherein said step of implanting a pre-specified concentration of Ge ions includes: implanting the Ge ions using an implant energy in the range of approximately 40 KeV to 200 KeV.
Claim 10
Dependent Claim
38 words
The fabricating method of claim 6 wherein the pre-specified concentration of said step of implanting a pre-specified concentration of Ge ions is in the range of approximately 1×10 16 to 10×10 16 Ge atoms per centimeter 2 .
Claim 11
Dependent Claim
59 words
The fabricating method of claim 6 wherein said step of annealing includes maintaining an annealing temperature for sufficient time to chemically combine the implanted Ge with neighboring Si and substantially repair damage to the crystal structure of the Si cap due to said step of implanting the pre-specified concentration of Ge ions through the top surface of the substrate.
Claim 12
Dependent Claim
14 words
The fabricating method of claim 9 wherein said annealing temperature is approximately 1100° C.
Claim 13
Dependent Claim
14 words
The fabricating method of claim 9 wherein said sufficient time is approximately 30 minutes.
Claim 14
Dependent Claim
29 words
The fabricating method of claim 5 wherein said first range of depths is equal to or within 20 Å to 60 Å below the top surface of the substrate.
Claim 15
Dependent Claim
13 words
The fabricating method of claim 5 wherein said Si substrate is a monocrystal.
Claim 16
Dependent Claim
25 words
The fabricating method of claim 5 further comprising the step of: forming by implantation an insulation/dielectric layer located below the Ge x Si 1-x region.
Claim 17
Dependent Claim
66 words
The fabricating method of claim 14 wherein the step of forming an insulation/dielectric layer by implantation includes: a first implanting of a pre-specified concentration of oxygen and/or nitrogen ions through a top surface of the substrate and into a first range of depths below the substrate top surface; and a first annealing of the substrate to chemically combine the implanted oxygen and/or nitrogen with neighboring Si.
Claim 18
Dependent Claim
41 words
The fabricating method of claim 15 wherein said step of first implanting a pre-specified concentration of oxygen and/or nitrogen ions includes: implanting the oxygen and/or nitrogen ions using an implant energy in the range of approximately 20 KeV to 220 KeV.
Claim 19
Dependent Claim
43 words
The fabricating method of claim 15 wherein the pre-specified concentration of said step of first implanting a pre-specified concentration of oxygen and/or nitrogen ions is in the range of approximately 2×10 17 to 20×10 17 oxygen and/or nitrogen atoms per centimeter 2 .
Claim 20
Dependent Claim
66 words
The fabricating method of claim 15 wherein said step of first annealing includes maintaining a first annealing temperature for sufficient time to chemically combine the implanted oxygen and/or nitrogen with neighboring Si and substantially repair damage to the crystal structure of the Si cap due to said step of first implanting the pre-specified concentration of oxygen and/or nitrogen ions through the top surface of the substrate.
Claim 21
Dependent Claim
66 words
The fabricating method of claim 18 wherein said step of implanting Ge includes: a second implanting, after said first implanting, of a pre-specified concentration of Ge ions through a top surface of the substrate and into a second range of depths below the substrate top surface; and a second annealing, after said first annealing, of the substrate to chemically combine the implanted Ge with neighboring Si.
Claim 22
Dependent Claim
31 words
The fabricating method of claim 1 wherein said step of implanting the mobility enhancing species includes: (a.1) grading the concentration of the mobility enhancing species as a function of implant depth.
Claim 23
Dependent Claim
31 words
The fabricating method of claim 1 wherein said heterostructure defines a portion of a field effect transistor serving as a channel region of the transistor and gate insulation of the transistor.
Claim 24
Independent Claim
218 words
A method for fabricating an integrated circuit including a Ge x Si 1-x /Si/SiO 2 heterostructure, said method comprising the steps of: providing a Si substrate having a top surface; implanting oxygen and/or nitrogen ions through the top surface of the substrate to form an isolation layer below and spaced away from the substrate top surface; annealing the substrate a first time to chemically combine the implanted oxygen and/or nitrogen with neighboring Si to thereby further form the isolation layer below the top surface of the substrate, wherein the formed isolation layer divides the Si substrate into a lower bulk portion and into an upper active portion, said active portion being disposed between the top surface of the substrate and the formed isolation layer; implanting Ge into a region of the active portion where the Ge-implanted region is spaced away from the top surface of the substrates annealing the substrate a second time to chemically combine the implanted Ge with neighboring Si to form Ge x Si 1-x in the Ge-implanted region; selectively etching away areas of the active portion of the Si substrate essentially down to the isolation layer to thereby form one or more essentially isolated mesas, at least one of the formed mesas being for containing said Ge-implanted region; and oxidizing the Si surface area.
Claim 25
Independent Claim
218 words
A method for fabricating an integrated circuit including a Ge x Si 1-x /Si/SiO 2 heterostructure, said method comprising the steps of: providing a Si substrate having a top surface; implanting oxygen and/or nitrogen ions through the top surface of the substrate to form an isolation layer below and spaced away from the substrate top surface; annealing the substrate a first time to chemically combine the implanted oxygen and/or nitrogen with neighboring Si to thereby further form the isolation layer below the top surface of the substrate, wherein the formed isolation layer divides the Si substrate into a lower bulk portion and into an upper active portion, said active portion being disposed between the top surface of the substrate and the formed isolation layer; implanting Ge into a region of the active portion where the Ge-implanted region is spaced away from the top surface of the substrates annealing the substrate a second time to chemically combine the implanted Ge with neighboring Si to form Ge x Si 1-x in the Ge-implanted region; selectively etching away areas of the active portion of the Si substrate essentially down to the isolation layer to thereby form one or more essentially isolated mesas, at least one of the formed mesas being for containing said Ge-implanted region; and oxidizing the Si surface area.
Claim 26
Independent Claim
149 words
A method for fabricating an integrated circuit, said method comprising the steps of: (a) providing a monocrystalline Si substrate having a top surface; (b) implanting oxygen and/or nitrogen through the top surface of the substrate to form an isolation layer below and spaced away from the substrate top surface, said isolation layer dividing the Si substrate into a bulk lower portion and into an upper portion; (c) implanting Ge into one or more regions of the upper portion so as to form one or more the Ge-implanted regions that are spaced away from the top surface of the substrate, the spacing between the one or more Ge-implanted regions and the top surface defining capping Si; (d) annealing the substrate so as to further combine the implanted Ge with the Si in the one or more Ge-implanted regions; and (e) oxidizing a portion but not all of the capping Si.
Claim 27
Independent Claim
149 words
A method for fabricating an integrated circuit, said method comprising the steps of: (a) providing a monocrystalline Si substrate having a top surface; (b) implanting oxygen and/or nitrogen through the top surface of the substrate to form an isolation layer below and spaced away from the substrate top surface, said isolation layer dividing the Si substrate into a bulk lower portion and into an upper portion; (c) implanting Ge into one or more regions of the upper portion so as to form one or more the Ge-implanted regions that are spaced away from the top surface of the substrate, the spacing between the one or more Ge-implanted regions and the top surface defining capping Si; (d) annealing the substrate so as to further combine the implanted Ge with the Si in the one or more Ge-implanted regions; and (e) oxidizing a portion but not all of the capping Si.
Claim 28
Dependent Claim
53 words
A method for fabricating an integrated circuit according to claim 23 wherein: (c.1) said step (c) of implanting Ge further causes said one or more Ge-implanted regions to be spaced away from the isolation layer, the spacing between the one or more Ge-implanted regions and the isolation layer being occupied by monocrystalline Si.
Claim 29
Dependent Claim
54 words
A method for fabricating an integrated circuit according to claim 24 wherein: (c.2) said step (c) of implanting Ge further causes said one or more Ge-implanted regions to have other than Gaussian variations in concentrations of Ge relative to concentrations of Si therein, the variations being a function of depth below said top surface.
Claim 30
Dependent Claim
50 words
A method for fabricating an integrated circuit according to claim 25 wherein: (c.3) said step (c) of implanting Ge further causes said one or more Ge-implanted regions to have monotonicly decreasing concentrations of Ge relative to concentrations of Si therein as a function of increasing depth below said top surface.
Claim 31
Dependent Claim
46 words
A method for fabricating an integrated circuit according to claim 26 where in: (c.3) said step (c) of implanting Ge further causes said one or more Ge-implanted regions to have concentrations of Ge relative to concentrations of Si equal to or less than of 25% atomic.
Claim 32
Dependent Claim
41 words
A method for fabricating an integrated circuit according to claim 24 further comprising the step of: (f) implanting one or more dopants into said capping Si for defining one or more respectively doped regions of respective conductivities within the capping Si.
Claim 33
Dependent Claim
47 words
A method for fabricating an integrated circuit according to claim 28 further comprising the step of: (g) using the combination of an oxidized portion of the capping Si, a nonoxidized doped region of the capping Si, and a corresponding Ge-implanted region to define a field effect transistor.
Claim 34
Dependent Claim
33 words
A method for fabricating an integrated circuit according to claim 23 wherein: (c.1) said step (c) of implanting Ge includes implanting using at least two different Ge dosages and two different implant energies.
Claim 35
Dependent Claim
58 words
A method for fabricating an integrated circuit according to claim 23 further comprising the step of: (f) selectively etching away parts of the active portion of the Si substrate to thereby form one or more substantially isolated mesas, one or more of the formed mesas being situated for containing a respective one or more of the Ge-implanted regions.
Claim 36
Dependent Claim
80 words
A method for fabricating an integrated circuit according to claim 31 further comprising the step of: (g) using the combination of respective mesas and corresponding Ge-implanted regions to define a plurality of field effect transistors each having a channel portion, where each said channel portion is essentially isolated from said bulk lower portion of the substrate by the isolation layer, and where each said channel portion is further essentially isolated from neighboring transistors by isolation provided by the respective mesa.
Claim 37
Dependent Claim
34 words
A method for fabricating an integrated circuit according to claim 23 wherein: (c.1) said step (c) of implanting Ge causes said one or more Ge-implanted regions to be each completely surrounded by monocrystalline Si.
Claim 38
Independent Claim
115 words
A method for fabricating an integrated circuit, said method comprising the steps of: (a) providing a monocrystalline Si substrate having a top surface and a buried isolation layer formed below and spaced away from the substrate top surface, said isolation layer dividing the Si substrate into a lower portion and into an upper portion; (b) implanting Ge into one or more regions of the upper portion so as to form one or more the Ge-implanted regions that are spaced away from the top surface of the substrate, the spacing between the one or more Ge-implanted regions and the top surface defining capping Si; and (c) oxidizing a portion but not all of the capping Si.
Claim 39
Independent Claim
115 words
A method for fabricating an integrated circuit, said method comprising the steps of: (a) providing a monocrystalline Si substrate having a top surface and a buried isolation layer formed below and spaced away from the substrate top surface, said isolation layer dividing the Si substrate into a lower portion and into an upper portion; (b) implanting Ge into one or more regions of the upper portion so as to form one or more the Ge-implanted regions that are spaced away from the top surface of the substrate, the spacing between the one or more Ge-implanted regions and the top surface defining capping Si; and (c) oxidizing a portion but not all of the capping Si.
References Cited (Backward Citations)
US4816421A
Cited
US4837173A
Cited
US4920076A
Cited
US5215931A
Cited
US5223445A
Cited
US5215935A
Cited
US5312766A
Cited
US5137838A
Cited
US5356827A
Cited
US5360749A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-08-10 | 2002-02-09 | 2002-08-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-08-10 | 2006-02-09 | 2006-08-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-08-10 | 2010-02-09 | 2010-08-11 | $7700.00 | Window Closed / Lapsed |