Method for enhancing growth of SiO2 in Si by the implantation of germanium
Assignee: United States, AS REPRESENTED BY UNITED DEPARTMENT OF ENERGY
•
Filing: 1988-04-15
•
Granted: 1990-04-24
•
Expires: 2008-04-15
Abstract
Abstract A method for enhancing the conversion of Si to SiO 2 in a directional fashion wherein steam or wet oxidation of Si is enhanced by the prior implantation of Ge into the Si. The unique advantages of the Ge impurity include the directional enhancement of oxidation and the reduction in thermal budget, while at the same time, Ge is an electrically inactive impurity.
Inventors
- 👤 Orin W. Holland
- 👤 Dariush Fathy
- 👤 Clark W. White
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 08:11
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/65; H10P14/6502; H10P30/00; H10P30/20; H10P30/202; H10P30/204; H10P30/208; H10P14/63; H10P14/6302; H10P14/6304; H10P14/6306; H10P14/6308; H10P14/6309; H10P14/6322; Y; Y10; Y10S; Y10S438/00; Y10S438/933
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
185 words
A process for enhancing the thermal oxidation rate of a selected surface portion of a silicon substrate, comprising the steps of: providing a substrate consisting essentially of a single crystal of silicon and having a surface portion to be oxidized; forming a surface epitaxial layer consisting essentially of germanium for providing a concentration of germanium in a near surface region in said silicon substrate at said surface portion to be oxidized sufficient to form at least one uniform monolayer of germanium coextensive with said surface portion to be oxidized during a subsequent heating step; and heating said substrate in an oxidizing atmosphere containing H 2 O for effecting thermal oxidation of said surface portion and forming an essentially uniform epitaxial layer of germanium at least one monolayer in thickness at an interface between said substrate and a layer of silicon dioxide formed by said oxidation and with continuing heating of said substrate in said oxidizing atmosphere containing H 2 O for providing enhanced growth rate of said silicon dioxide layer at said surface portion due to the presence of the underlying uniform layer of germanium.
Claim 2
Dependent Claim
185 words
A process for enhancing the thermal oxidation rate of a selected surface portion of a silicon substrate, comprising the steps of: providing a substrate consisting essentially of a single crystal of silicon and having a surface portion to be oxidized; forming a surface epitaxial layer consisting essentially of germanium for providing a concentration of germanium in a near surface region in said silicon substrate at said surface portion to be oxidized sufficient to form at least one uniform monolayer of germanium coextensive with said surface portion to be oxidized during a subsequent heating step; and heating said substrate in an oxidizing atmosphere containing H 2 O for effecting thermal oxidation of said surface portion and forming an essentially uniform epitaxial layer of germanium at least one monolayer in thickness at an interface between said substrate and a layer of silicon dioxide formed by said oxidation and with continuing heating of said substrate in said oxidizing atmosphere containing H 2 O for providing enhanced growth rate of said silicon dioxide layer at said surface portion due to the presence of the underlying uniform layer of germanium.
Claim 3
Dependent Claim
34 words
The process as in claim 1 wherein said enhanced growth rate of said silicon dioxide layer is greater than that attainable on surface portions of said substrate devoid of said underlying layer of germanium.
Claim 4
Dependent Claim
29 words
The process as set forth in claim 2 wherein said heating step comprises heating said substrate at a temperature in the range of from about 700° to 1200° C.
Claim 5
Dependent Claim
20 words
The process as set forth in claim 3 wherein said forming step comprises implanting said surface region with germanium ions.
Claim 6
Dependent Claim
42 words
The process of claim 4 wherein said germanium ions are implanted with energies in the range of from about 50 to 160 keV at a fluence of at least 1×10 15 ions/cm 2 over the area of said surface to be oxidized.
Claim 7
Dependent Claim
30 words
The process as set forth in claim 5 wherein said heating step comprises heating said substrate in a steam atmosphere at a temperature of from about 900° to 1000° C.
Claim 8
Dependent Claim
142 words
A process for forming a uniform silicon dioxide layer on a silicon substrate, comprising the steps of: providing a substrate consisting essentially of a single crystal of silicon and having a surface portion to be oxidized; forming a surface epitaxial layer consisting essentially of germanium for providing a concentration of germanium in a near surface region in said silicon substrate at said surface portion to be oxidized sufficient to form at least one monolayer of germanium coextensive with said surface to be oxidized; and heating said substrate in an oxidizing atmosphere containing H 2 O for a period sufficient to form a uniform layer consisting essentially of silicon dioxide and having a desired thickness on said surface portion of said substrate and an epitaxial layer of germanium at least one monolayer in thickness intermediate said silicon substrate and said silicon dioxide layer.
Claim 9
Dependent Claim
142 words
A process for forming a uniform silicon dioxide layer on a silicon substrate, comprising the steps of: providing a substrate consisting essentially of a single crystal of silicon and having a surface portion to be oxidized; forming a surface epitaxial layer consisting essentially of germanium for providing a concentration of germanium in a near surface region in said silicon substrate at said surface portion to be oxidized sufficient to form at least one monolayer of germanium coextensive with said surface to be oxidized; and heating said substrate in an oxidizing atmosphere containing H 2 O for a period sufficient to form a uniform layer consisting essentially of silicon dioxide and having a desired thickness on said surface portion of said substrate and an epitaxial layer of germanium at least one monolayer in thickness intermediate said silicon substrate and said silicon dioxide layer.
Claim 10
Dependent Claim
29 words
The process as set forth in claim 7 wherein said heating step comprises heating said substrate at a temperature in the range of from about 700° to 1200° C.
Claim 11
Dependent Claim
19 words
The process as set forth in claim 8 wherein said forming step comprises implanting said region with germanium ions.
Claim 12
Dependent Claim
42 words
The process of claim 9 wherein said germanium ions are implanted with energies in the range of from about 50 to 160 keV at a fluence of at least 1×10 15 ions/cm 2 over the area of said surface to be oxidized.
Claim 13
Dependent Claim
23 words
A process as set forth in claim 10 wherein the interface between said germanium layer and said silicon dioxide layer is essentially planar.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-04-23 | 1993-10-23 | 1994-04-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-04-23 | 1997-10-23 | 1998-04-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-04-23 | 2001-10-23 | 2002-04-24 | $7700.00 | Window Closed / Lapsed |