Method of stripping a resist mask
Assignee: Fujitsu Ltd
•
Filing: 1994-02-09
•
Granted: 1998-06-30
•
Expires: 2014-02-09
Abstract
Abstract A method for removing a used organic resist in a downstream ashing apparatus on a silicon semiconductor wafer in which water vapor is added to an oxygen plasma gas generated by microwaves. The addition of the water vapor lowers an activation energy of the ashing reaction and increases the reactive species generated in the plasma. Accordingly, the ashing rate is increased even at a wafer processing temperature as low as 150° C. The addition of water vapor increases the ashing rate for a wide range of the percentage of water content, such as 5 to 80%, allowing easy control of the process. The lowered operating temperature prevents contamination of the semiconductor wafer. Since CF 4 is not used the SiO 2 layer is protected from being undesirably etched and the semiconductor characteristics do not deteriorate.
Inventors
- 👤 Shuzo Fujimura
- 👤 Keisuke Shinagawa
- 👤 Naomichi Abe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:15
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/28; H10P50/286; H10P50/287; G; G03; G03F; G03F7/00; G03F7/26; G03F7/42; G03F7/427
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
126 words
A downstream ashing method for removing an organic resist film from a semiconductor wafer, said method comprising: placing a semiconductor wafer having an organic resist film thereon in a reaction chamber; creating a gas plasma containing both electrically neutral species and charged particles by subjecting a gas containing oxygen to electromagnetic power; ashing the organic resist film on said semiconductor wafer by exposing the wafer with the film thereon to said neutral species while shielding the wafer from said charged particles; and reducing an activation energy of the ashing reaction between the organic resist film and said neutral species, thereby reducing the temperature necessary to drive the ashing reaction at a predetermined given rate, by causing said gas containing oxygen to also contain a water vapor.
Claim 2
Dependent Claim
126 words
A downstream ashing method for removing an organic resist film from a semiconductor wafer, said method comprising: placing a semiconductor wafer having an organic resist film thereon in a reaction chamber; creating a gas plasma containing both electrically neutral species and charged particles by subjecting a gas containing oxygen to electromagnetic power; ashing the organic resist film on said semiconductor wafer by exposing the wafer with the film thereon to said neutral species while shielding the wafer from said charged particles; and reducing an activation energy of the ashing reaction between the organic resist film and said neutral species, thereby reducing the temperature necessary to drive the ashing reaction at a predetermined given rate, by causing said gas containing oxygen to also contain a water vapor.
Claim 3
Dependent Claim
59 words
A downstream ashing method as set forth in claim 1, wherein said gas plasma is created in a plasma generating chamber adjacent said reaction chamber, and said electrically neutral species are caused to flow out of the plasma generating chamber and into said reaction chamber through holes in a wall between the plasma generating chamber and the reaction chamber.
Claim 4
Dependent Claim
31 words
A downstream ashing method as set forth in claim 2, wherein said gas containing oxygen and said water vapor are introduced separately into said plasma generating chamber from respective outside surfaces.
Claim 5
Dependent Claim
55 words
A downstream ashing method as set forth in claim 2, wherein said semiconductor wafer is placed within said reaction chamber such that it is protected against exposure to said electromagnetic power during said ashing operation and such that the organic resist reacts only with the electrically neutral species flowing through said holes during said ashing.
Claim 6
Dependent Claim
47 words
A downstream ashing method as set forth in claim 2, wherein said oxygen containing gas and said water vapor are each introduced into and exhausted from said plasma generating chamber so that the flow of said electrically neutral species through said holes is continuous during said ashing.
Claim 7
Dependent Claim
41 words
A downstream ashing method as set forth in claim 1, wherein the amount of water vapor in said gas containing oxygen is such that an activation energy of ashing the organic resist film is equal to or less than 0.42 eV.
Claim 8
Dependent Claim
27 words
A downstream ashing method as set forth in claim 6, wherein the amount of water vapor present in said gas containing oxygen is approximately 5 mol %.
Claim 9
Dependent Claim
50 words
A downstream ashing method as set forth in claim 1, wherein the amount of water vapor in said gas containing oxygen is such that the ashing rate of the organic resist is at least 0.3 μm per minute while the temperature of the semiconductor wafer is at least 150° C.
Claim 10
Dependent Claim
27 words
A downstream ashing method as set forth in claim 8, wherein the amount of water vapor present in said gas containing oxygen is approximately 40 mol %.
Claim 11
Dependent Claim
30 words
A downstream ashing method as set forth in claim 1, wherein said semiconductor wafer includes an insulating layer having a thickness of 20 nm or less underlying said resist film.
Claim 12
Dependent Claim
19 words
A downstream ashing method as set forth in claim 10, wherein said insulating layer is formed from silicon dioxide.
Claim 13
Dependent Claim
30 words
A downstream ashing method as set forth in claim 10, wherein said insulating layer is a gate insulating layer of a submicron device for a very large scale integrated circuit.
Claim 14
Dependent Claim
31 words
A downstream ashing method as set forth in claim 1, wherein said ashing is carried out by a purely chemical reaction in the absence of any substantial quantity of charged particles.
Claim 15
Dependent Claim
54 words
A downstream ashing method as set forth in claim 1, wherein said ashing of the organic resist layer is carried out at a rate no greater than 0.15 μm per minute and a temperature at which said ashing is carried out is sufficiently low to avoid substantial contamination of said semiconductor wafer by metal.
Claim 16
Dependent Claim
65 words
A downstream ashing method as set forth in claim 1, wherein the amount of water vapor present in said oxygen containing gas is such that said ashing of the organic resist layer is carried out at a rate no less than 0.3 μm per minute while the temperature at which said ashing is carried out is maintained at a level of at least 180° C.
Claim 17
Dependent Claim
35 words
A downstream ashing method as set forth in claim 15, wherein the amount of water vapor present in said gas containing oxygen is within the range of from about 14 to about 64 mol %.
Claim 18
Dependent Claim
29 words
A downstream ashing method as set forth in claim 1, wherein the amount of water vapor present in said gas containing oxygen is at least about 50 mol %.
Claim 19
Dependent Claim
28 words
A downstream ashing method as set forth in claim 1, wherein the ashing reaction is predominantly carried out by reaction between the organic resist layer and hydroxide radicals.
Claim 20
Dependent Claim
40 words
A downstream ashing method as set forth in claim 1, wherein the ashing reaction is predominantly carried out by reaction between the organic resist layer and a neutral radical species having a kinetic energy which is essentially a thermal energy.
References Cited (Backward Citations)
US3837856A
Cited
US4292384A
Cited
US4512868A
Cited
JPS6146751A
Cited
JPS6159338A
Cited
EP0216603A2
Cited
US4987284A
Cited
US5057187A
Cited
US4983254A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-06-29 | 2001-12-29 | 2002-06-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-06-29 | 2005-12-29 | 2006-06-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-06-29 | 2009-12-29 | 2010-06-30 | $7700.00 | Window Closed / Lapsed |