Bonded wafer processing
Assignee: Intersil Corp
•
Filing: 1995-12-15
•
Granted: 1998-03-17
•
Expires: 2015-12-15
Abstract
Abstract Low temperature wafer bonding using a silicon-oxidizing bonding liquid permits introduction of radiation hardening dopants and electrically active dopants as constituents of the bonding liquid. Oxidizers such as nitric acid may be used in the bonding liquid. Dielectric layers on the device wafer and the handle wafer may be used when additional silicon is provided for the oxidative bonding. Integrated circuits fabricated from such bonded wafers may have buried layers and radiation hardening with device silicon too thick for implantation.
Inventors
- 👤 Jack H. Linn
- 👤 Robert K. Lowry
- 👤 Geroge V. Rouse
- 👤 James F. Buller
- 👤 William Herman Speece
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 20:19
CPC Classifications
H; H10; H10D; H10D86/00; H10D86/80; H10D86/85; H10P; H10P30/00; H10P30/20; H10P90/00; H10P90/19; H10P90/1904; H10P90/1906; H10W; H10W10/00; H10W10/01; H10W10/061; H10W10/10; H10W10/181; H10P90/1914; H10W10/011; H10W10/014; H10W10/041; H10W10/17; H10W10/40; Y; Y10; Y10S; Y10S148/00; Y10S148/012; Y10S438/00; Y10S438/914; Y10S438/92
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
173 words
A method of wafer bonding, comprising the steps of: (a) providing a device wafer and a handle wafer; (b) placing an oxidant for oxidizing the surface of at least one of the wafers between opposite surfaces of the device wafer and the handle wafer, said oxidant containing a doping compound of a conductive impurity; (c) contacting the opposite surface of the wafers together with the oxidant therebetween; (d) in a single step simultaneously bonding the opposite surfaces of the handle wafer and the device wafer by creating a bonding layer between the device wafer to the handle wafer to bond the two wafers together, doping the bonding layer to radiation harden the device wafer with dopants selected from a first group consisting of fluorine, sulfur, phosphorus, and combinations thereof, and doping the device wafer to form a buried layer in the device wafer of the bonded wafer with dopants selected from the group consisting of boron, phosphorus, arsenic, antimony and combinations thereof, by heating the wafers in the range of about 800°-1000° C.
Claim 2
Independent Claim
173 words
A method of wafer bonding, comprising the steps of: (a) providing a device wafer and a handle wafer; (b) placing an oxidant for oxidizing the surface of at least one of the wafers between opposite surfaces of the device wafer and the handle wafer, said oxidant containing a doping compound of a conductive impurity; (c) contacting the opposite surface of the wafers together with the oxidant therebetween; (d) in a single step simultaneously bonding the opposite surfaces of the handle wafer and the device wafer by creating a bonding layer between the device wafer to the handle wafer to bond the two wafers together, doping the bonding layer to radiation harden the device wafer with dopants selected from a first group consisting of fluorine, sulfur, phosphorus, and combinations thereof, and doping the device wafer to form a buried layer in the device wafer of the bonded wafer with dopants selected from the group consisting of boron, phosphorus, arsenic, antimony and combinations thereof, by heating the wafers in the range of about 800°-1000° C.
Claim 3
Independent Claim
82 words
A method of wafer bonding, comprising the steps of: (a) providing a device wafer and a handle wafer; (b) coating opposite surfaces of the device and the handle wafer with polysilicon; (b) joining a surface of said device wafer to a surface of said handle wafer with a quantity therebetween of liquid oxidant for oxidizing the polysilicon of both wafers, said oxidant containing a doping compound; (c) heating said wafers in the range of about 800°-1000° C. wherein said wafers bond together.
Claim 4
Independent Claim
82 words
A method of wafer bonding, comprising the steps of: (a) providing a device wafer and a handle wafer; (b) coating opposite surfaces of the device and the handle wafer with polysilicon; (b) joining a surface of said device wafer to a surface of said handle wafer with a quantity therebetween of liquid oxidant for oxidizing the polysilicon of both wafers, said oxidant containing a doping compound; (c) heating said wafers in the range of about 800°-1000° C. wherein said wafers bond together.
Claim 5
Dependent Claim
35 words
The method of claim 2 wherein: (a) said device wafer comprises silicon; and (b) said heating causes reaction of the oxidant and the surface of the device wafer to yield a silicon oxynitride bonding layer.
Claim 6
Dependent Claim
36 words
The method of claim 3 wherein: (a) said quantity of oxidant is sufficient to result in formation of the silicon oxynitride bonding layer on said device wafer of thickness in the range of about 500-800 Å.
Claim 7
Dependent Claim
23 words
The method of claim 3 wherein: (a) said handle wafer is silicon with a dielectric layer at said surface of said handle wafer.
Claim 8
Dependent Claim
14 words
The method of claim 5 wherein: (a) said dielectric layer is a silicon oxide.
Claim 9
Dependent Claim
20 words
The method of claim 5 wherein: (a) said dielectric layer is a silicon oxynitride sublayer on a silicon oxide sublayer.
Claim 10
Dependent Claim
13 words
The method of claim 5 wherein: (a) said dielectric layer includes aluminum oxide.
Claim 11
Dependent Claim
11 words
The method of claim 2 wherein: (a) said oxidant includes nitrate.
Claim 12
Dependent Claim
22 words
The method of claim 2 wherein: (a) said dopants are taken from the group consisting of fluorine, sulfur, phosphorus, and combinations thereof.
Claim 13
Dependent Claim
23 words
The method of claim 2 wherein: (a) said dopants are taken from the group consisting of boron, phosphorus, arsenic, antimony and combinations thereof.
References Cited (Backward Citations)
JPS5658269A
Cited
US5236546A
Cited
US4878957A
Cited
JPH0218961A
Cited
US5322589A
Cited
US5241211A
Cited
US5294821A
Cited
US5187636A
Cited
US5362667A
Cited
US5387555A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-03-16 | 2001-09-15 | 2002-03-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-03-16 | 2005-09-15 | 2006-03-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-03-16 | 2009-09-15 | 2010-03-17 | $7700.00 | Window Closed / Lapsed |