Process for fabricating thin-film semiconductor device without plasma induced damage
Assignee: Semiconductor Energy Laboratory Co Ltd
•
Filing: 1995-10-19
•
Granted: 1998-03-17
•
Expires: 2015-10-19
Abstract
Abstract Disclosed herein is a process for fabricating a thin-film semiconductor device which includes (1) a step of etching a silicon film by wet etching or gas etching, the former employing a liquid containing hydrazine or ethylene diamine, the latter employing chlorine fluoride, thereby forming an island-like silicon semiconductor region having inclined edges, and (2) a step of forming thereon a gate insulating film by plasma-free process such as heated CVD. The process yields the island-like silicon region and gate insulating film completely free from plasma-induced damage. This reduces the leakage current between the source and drain (which is due to plasma-induced damage) and prevents the degradation of characteristic properties.
Inventors
- 👤 Hideomi Suzawa
- 👤 Shunpei Yamazaki
- 👤 Toshiji Hamatani
- 👤 Yasuhiko Takemura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 06:30
CPC Classifications
H; H10; H10P; H10P70/00; H10P70/20; H10P50/00; H10P50/20; H10P50/24; H10P50/242; H10P50/60; H10P50/64; H10P50/642; H10P50/644; Y; Y10; Y10S; Y10S438/00; Y10S438/978; Y10S438/98
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
88 words
A process for fabricating a thin-film semiconductor device comprising the steps of: selectively forming a mask on a silicon film formed on an insulating surface, said silicon film having a thickness of approximately 100-1000 Å; and etching the silicon film using the mask by the aid of a liquid or unionized gas capable of etching silicon to form an island-like thin-film silicon semiconductor region that has no plasma induced damage, wherein said thin-film silicon semiconductor region includes at least source, drain and channel regions of said semiconductor device.
Claim 2
Dependent Claim
88 words
A process for fabricating a thin-film semiconductor device comprising the steps of: selectively forming a mask on a silicon film formed on an insulating surface, said silicon film having a thickness of approximately 100-1000 Å; and etching the silicon film using the mask by the aid of a liquid or unionized gas capable of etching silicon to form an island-like thin-film silicon semiconductor region that has no plasma induced damage, wherein said thin-film silicon semiconductor region includes at least source, drain and channel regions of said semiconductor device.
Claim 3
Dependent Claim
13 words
The process of claim 1 wherein the island-like silicon region has tapered edges.
Claim 4
Dependent Claim
12 words
The process of claim 1 wherein the mask is a photoresist film.
Claim 5
Dependent Claim
28 words
The process of claim 1 wherein the mask comprises a material selected from the group consisting of silicon oxide film, silicon nitride film, and silicon oxide nitrogen film.
Claim 6
Dependent Claim
20 words
The process of claim 1 wherein the liquid capable of etching silicon is one which has the NH 2 group.
Claim 7
Dependent Claim
17 words
The process of claim 1 wherein the liquid capable of etching silicon is one which contains hydrazine.
Claim 8
Dependent Claim
17 words
The process of claim 1 wherein the liquid capable of etching silicon is one which contains ethylenediamine.
Claim 9
Dependent Claim
18 words
The process of claim 1 wherein the gas capable of etching silicon is one which contains chlorine fluoride.
Claim 10
Dependent Claim
34 words
The process of claim 1 further comprising the step of forming a gate insulating film on the etched silicon film to a thickness two to ten times larger than that of the silicon film.
Claim 11
Dependent Claim
77 words
A process for fabricating a thin-film semiconductor device comprising the steps of: etching a silicon film formed on an insulating surface by the aid of a liquid or unionized gas to form an island-like thin-film silicon semiconductor region that has no plasma induced damage; and forming a gate insulating film covering said silicon semiconductor region by plasma-free chemical vapor deposition wherein said silicon semiconductor region includes at least source, drain and channel regions of said semiconductor device.
Claim 12
Dependent Claim
77 words
A process for fabricating a thin-film semiconductor device comprising the steps of: etching a silicon film formed on an insulating surface by the aid of a liquid or unionized gas to form an island-like thin-film silicon semiconductor region that has no plasma induced damage; and forming a gate insulating film covering said silicon semiconductor region by plasma-free chemical vapor deposition wherein said silicon semiconductor region includes at least source, drain and channel regions of said semiconductor device.
Claim 13
Dependent Claim
13 words
The process of claim 10 wherein the island-like silicon region has tapered edges.
Claim 14
Dependent Claim
20 words
The process of claim 10 wherein the liquid capable of etching silicon is one which has the NH 2 group.
Claim 15
Dependent Claim
17 words
The process of claim 10 wherein the liquid capable of etching silicon is one which contains hydrazine.
Claim 16
Dependent Claim
17 words
The process of claim 10 wherein the liquid capable of etching silicon is one which contains ethylenediamine.
Claim 17
Dependent Claim
18 words
The process of claim 10 wherein the gas capable of etching silicon is one which contains chlorine fluoride.
Claim 18
Dependent Claim
26 words
The process of claim 10 wherein the gate insulating film is formed by heated CVD which employs silane and oxygen or nitrogen oxide as feed gases.
Claim 19
Dependent Claim
32 words
The process of claim 10 further comprising a step of annealing the gate insulating film at 450°-600° C. in an atmosphere of dinitrogen monoxide after the formation of the gate insulating film.
Claim 20
Dependent Claim
21 words
The process of claim 10 wherein the gate insulating film is two to ten times as thick as the silicon film.
Claim 21
Dependent Claim
15 words
The process of claim 10 wherein the silicon film has a thickness of 100-1000 Å.
Claim 22
Dependent Claim
85 words
A process for fabricating a thin-film semiconductor device comprising the steps of: forming a semiconductor film having crystalline silicon on an insulating surface; disposing a mask pattern on said semiconductor film; patterning said semiconductor film by etching in accordance with said mask pattern to form at least one semiconductor island that has no plasma induced damage; forming source and drain regions within said semiconductor island with a channel region defined therebetween, wherein said etching is performed with a liquid etchant having an NH 2 group.
Claim 23
Dependent Claim
85 words
A process for fabricating a thin-film semiconductor device comprising the steps of: forming a semiconductor film having crystalline silicon on an insulating surface; disposing a mask pattern on said semiconductor film; patterning said semiconductor film by etching in accordance with said mask pattern to form at least one semiconductor island that has no plasma induced damage; forming source and drain regions within said semiconductor island with a channel region defined therebetween, wherein said etching is performed with a liquid etchant having an NH 2 group.
Claim 24
Dependent Claim
10 words
The process of claim 20 wherein said etchant is hydrazine.
Claim 25
Dependent Claim
10 words
The process of claim 20 wherein said etchant is ethylenediamine.
Claim 26
Dependent Claim
29 words
The process of claim 20 wherein said mask pattern comprises a material selected from the group consisting of silicon oxide film, silicon nitride film, and silicon oxide nitrogen film.
Claim 27
Dependent Claim
87 words
A process for fabricating a thin-film semiconductor device comprising the steps of: forming a semiconductor film having crystalline silicon on an insulating surface; disposing a mask pattern on said semiconductor film; patterning said semiconductor film by etching in accordance with said mask pattern to form at least one semiconductor island that has no plasma induced damage; forming source and drain regions within said semiconductor island with a channel region defined therebetween, wherein said etching is performed with a gaseous etchant having chlorine fluoride in a non-plasma state.
Claim 28
Dependent Claim
87 words
A process for fabricating a thin-film semiconductor device comprising the steps of: forming a semiconductor film having crystalline silicon on an insulating surface; disposing a mask pattern on said semiconductor film; patterning said semiconductor film by etching in accordance with said mask pattern to form at least one semiconductor island that has no plasma induced damage; forming source and drain regions within said semiconductor island with a channel region defined therebetween, wherein said etching is performed with a gaseous etchant having chlorine fluoride in a non-plasma state.
Claim 29
Dependent Claim
12 words
The process of claim 24 wherein said mask pattern comprises a photoresist.
Claim 30
Dependent Claim
24 words
The process of claim 24 wherein said chlorine fluoride is selected from the group consisting of ClF, ClF 3 , and ClF 5 .
Claim 31
Dependent Claim
13 words
The process of claim 24 wherein said chlorine fluoride is ClF 3 .
References Cited (Backward Citations)
US3936331A
Cited
US4056414A
Cited
US4937808A
Cited
JPH0432556A
Cited
JPH04186784A
Cited
US5489542A
Cited
US5326406A
Cited
US5545571A
Cited
US5406109A
Cited
US5393682A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-03-16 | 2001-09-15 | 2002-03-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-03-16 | 2005-09-15 | 2006-03-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-03-16 | 2009-09-15 | 2010-03-17 | $7700.00 | Window Closed / Lapsed |