Inorganic particles coated with organic polymeric binders composite sheets including same and methods of making said coated particles
Assignee: 3M Co
•
Filing: 1996-11-22
•
Granted: 1998-03-03
•
Expires: 2016-11-22
Abstract
Abstract A granular material is presented comprising inorganic particles coated with an organometallic polymeric binder, the organometallic polymeric binder comprising the reaction product of water with at least one component of a binder precursor composition. The binder precursor composition is selected from the group consisting of 1) a first composition comprising an inert organic polymer and a hydrolyzable liquid organometallic solvent; 2) a second composition comprising a water reactive organic polymer dissolved in an inert organic solvent; and 3) a third composition comprising the water reactive organic polymer dissolved in the hydrolyzable liquid organometallic solvent.
Inventors
- 👤 W. Stuart Bigham
- 👤 Dean M. Moren
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 12:18
CPC Classifications
C; C08; C08G; C08G83/00; C08G83/001; C04; C04B; C04B20/00; C04B20/10; C04B20/1051; E; E04; E04D; E04D7/00; E04D7/005; C04B2111/00; C04B2111/00474; C04B2111/00586
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
107 words
Coated granules suitable for use as roofing granule material comprising inorganic particles coated directly with an organometallic polymeric binder, wherein said inorganic particles comprise raw rock material, and said organometallic polymeric binder comprising the reaction product of water with at least one component of a binder precursor composition, said binder precursor composition comprising an uncured mixture, said uncured mixture comprising a water reactive organic polymer dissolved in a hydrolyzable liquid organometallic solvent, wherein said water reactive organic polymer of said uncured mixture has a weight average molecular weight of at least 100 wherein at least two in any sequence of three consecutive polymeric backbone atoms is carbon.
Claim 2
Dependent Claim
107 words
Coated granules suitable for use as roofing granule material comprising inorganic particles coated directly with an organometallic polymeric binder, wherein said inorganic particles comprise raw rock material, and said organometallic polymeric binder comprising the reaction product of water with at least one component of a binder precursor composition, said binder precursor composition comprising an uncured mixture, said uncured mixture comprising a water reactive organic polymer dissolved in a hydrolyzable liquid organometallic solvent, wherein said water reactive organic polymer of said uncured mixture has a weight average molecular weight of at least 100 wherein at least two in any sequence of three consecutive polymeric backbone atoms is carbon.
Claim 3
Dependent Claim
16 words
Granular material in accordance with claim 1 wherein said organometallic polymeric binder includes an organic pigment.
Claim 4
Dependent Claim
95 words
Granular material in accordance with claim 1, wherein said hydrolyzable organometallic compound is selected from the group consisting of compounds within the general formula: (R.sup.1 O).sub.x MR.sup.2.sub.(y--x) wherein R 1 is selected from the group consisting of alkyl, cycloalkyl, aryl, or acyl; R 2 is selected from the group consisting of hydrogen, alkyl, cycloalkyl, or aryl; x is selected from the group consisting of an integer ranging from 1 to y, inclusive; y is an integer equaling the valence of M; and M is selected from the group consisting of B, Al, Si, or Ti.
Claim 5
Dependent Claim
18 words
Granular material in accordance with claim 1 wherein said water reactive organic polymer comprises a silane-functional addition polymer.
Claim 6
Dependent Claim
18 words
Granular material in accordance with claim 1 wherein the water reactive organic polymer comprises addition polymerized monomer units.
Claim 7
Dependent Claim
29 words
Granular material in accordance with claim 5 wherein said monomers are selected from the group consisting of acrylates, methacrylates, acrylamides, vinyl esters, vinyl aromatics, vinyl ethers, and vinyl heterocycles.
Claim 8
Dependent Claim
18 words
Granular material in accordance with claim 1 wherein said water reactive organic polymer comprises pendant hydrolyzable siloxane functionalities.
Claim 9
Dependent Claim
23 words
Granular material in accordance with claim 1 wherein said water reactive organic polymer comprises a hydrolyzable copolymer of an alkyl methacrylate and methacryloxypropyltrimethoxysilane.
Claim 10
Dependent Claim
27 words
Granular material in accordance with claim 1 wherein said water reactive organic polymer comprises a polymer blend formed from a combination of 2 or more dissimilar polymers.
Claim 11
Dependent Claim
31 words
Granular material in accordance with claim 1 wherein said water reactive organic polymer comprises polymers derived from hydrolyzable siloxane-functional monomers selected from the group consisting of vinyltriethoxysilane, vinyltris(2-methoxyethoxy) silane, and 3-methacryloxypropyltrimethoxysilane.
Claim 12
Dependent Claim
53 words
Granular materials in accordance with claim 1 wherein said hydrolyzable liquid organometallic solvent is selected from the group consisting of trimethyl borate, triethyl borate, triisopropyl borate, tri-n-butyl borate, aluminum tri-sec-butoxide, diethylaluminum ethoxide, tetramethoxysilane, tetraethoxysilane, tetraphenoxysilane, tetra(2-(2-methoxyethoxy)ethoxy)silane, tetraacetoxysilane, triethoxysilane, ethyl triethoxysilane, dimethyldiethoxysilane, trimethylsilylphenoxide, diphenyldimethoxysilane, titanium (IV) isopropoxide, titanium (IV) propoxide, and titanium (IV) 2-ethylhexoxide.
Claim 13
Dependent Claim
15 words
Granular material in accordance with claim 11 wherein the hydrolyzable liquid organometallic solvent is tetraethoxysilane.
Claim 14
Dependent Claim
115 words
Granular material in accordance with claim 1 wherein said hydrolyzable liquid organometallic solvent is tetraethoxysilane and the water reactive organic polymer is a hydrolyzable copolymer derived from the reaction of an alkyl methacrylate and an alkoxysilylalkylmethacrylate, said alkoxysilylalkylmethacrylate being selected from the group consisting of compounds within the general formula ##STR2## wherein: n=an integer ranging from 1 to 3 inclusive; z=an integer ranging from 1 to 10 inclusive; R 1 is selected from the group consisting of alkyl, cycloalkyl, aryl, or acyl; and R 4 is selected from the group consisting of hydrogen, alkyl, cycloalkyl, or aryl, said binder further including a compound selected from the group consisting of hindered amine sebacates and substituted benzotriazoles.
Claim 15
Dependent Claim
22 words
Granular material in accordance with claim 13 wherein said hindered amine sebacate is bis-(1-octyloxy-2,2,6,6-tetramethyl-4-piperidinyl) sebacate and said substituted benzotriazole is 3-(2H-benzotriazol-2-yl)-5-(1,1-dimethylethyl)-4-hydroxybenzenepropanoic acid.
Claim 16
Dependent Claim
94 words
A method of making coated granules suitable for use as roofing granules, the method comprising the steps of: (a) forming a binder precursor composition as described in claim 1; (b) exposing a plurality of inorganic granules to moisture thereby yielding moisturized inorganic granules; (c) optionally combining an organic pigment with the moisturized inorganic granules to form pigmented moisturized inorganic granules; (d) combining the moisturized inorganic granules with the binder precursor composition to yield binder precursor composition-coated granules; and (e) exposing the binder precursor composition-coated granules to conditions sufficient to polymerize the binder precursor composition.
Claim 17
Dependent Claim
61 words
A method of making coated granules suitable for use as roofing granules, the method comprising the steps of: (a) combining a binder precursor composition as described in claim 1 with moisture, inorganic granules, and optionally an organic pigment, to yield binder precursor composition-coated granules; and (e) exposing the binder precursor composition-coated granules to conditions sufficient to polymerize the binder precursor composition.
Claim 18
Dependent Claim
86 words
A method of making coated granules suitable for use as roofing granules, the method comprising the steps of: (a) combining a binder precursor composition as described in claim 1 with an organic pigment to form an intermediate composition; (b) exposing a plurality of inorganic granules to moisture thereby yielding moisturized inorganic granules; (c) combining the moisturized inorganic granules with the intermediate composition to form pigmented binder precursor composition-coated granules; and (d) exposing the binder precursor composition-coated granules to conditions sufficient to polymerize the binder precursor composition.
Claim 19
Dependent Claim
55 words
Method in accordance with claim 15 wherein the exposing step (e) comprises heating the binder precursor coated granules to a temperature and for a duration sufficient to cure the binder precursor composition, the temperature ranging from about 100° C. to about 150° C., and the duration preferably ranging from about 10 to about 60 minutes.
Claim 20
Dependent Claim
20 words
Granular material in accordance with claim 1 wherein said inorganic particles have a particle size of greater than 425 micrometers.
Claim 21
Dependent Claim
24 words
Granular material in accordance with claim 1 wherein said water reactive organic polymer comprises a hydrolyzable copolymer of an alkyl methacrylate and an alkoxysilylalkylmethacrylate.
References Cited (Backward Citations)
US2491487A
Cited
US3249464A
Cited
US3228907A
Cited
US3498809A
Cited
US4080190A
Cited
US4313979A
Cited
US4426476A
Cited
US4582425A
Cited
EP0314584A1
Cited
US4999249A
Cited
US5218014A
Cited
US5162390A
Cited
US5214085A
Cited
US5328683A
Cited
US5230962A
Cited
US5346939A
Cited
US5364693A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-03-02 | 2001-09-01 | 2002-03-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-03-02 | 2005-09-01 | 2006-03-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-03-02 | 2009-09-01 | 2010-03-03 | $7700.00 | Window Closed / Lapsed |