Processes for forming thin, durable coatings of cation-containing polymers on selected substrates
Assignee: Dow Chemical Co
•
Filing: 1995-09-20
•
Granted: 1998-02-17
•
Expires: 2015-09-20
Abstract
Abstract Non-evaporative processes for coating ion-containing polymers onto selected substrates and the articles made thereby, which processes fundamentally comprise contacting a substrate with a dispersion or solution of an ion-containing polymer and especially a solventless dispersion of a perfluorosulfonic acid ionomer, and thereafter contacting the dispersion- or solution-wetted substrate with a solution of a salt or of a strongly ionizing acid of a sufficient concentration to cause an adherent coating of the ion-containing polymer to be formed on the substrate.
Inventors
- 👤 Charles W. Martin
- 👤 Stan H. Baker
- 👤 Terry D. Gordon
- 👤 Melisa Davila
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 05:40
CPC Classifications
B; B05; B05D; B05D3/00; B05D3/10; B05D3/107; B05D5/00; B05D5/08; B05D5/083
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
77 words
A process for coating a cation-containing polymer onto a substrate, which comprises: contacting the substrate with a colloidal dispersion or solution of the cation-containing polymer; and then contacting the dispersion- or solution-wetted substrate, while still wetted with the colloidal dispersion or solution and without an intervening drying step, with a solution of a salt or of a strongly ionizing acid of a concentration to cause an adherent coating of the cation-containing polymer to form on the substrate.
Claim 2
Dependent Claim
77 words
A process for coating a cation-containing polymer onto a substrate, which comprises: contacting the substrate with a colloidal dispersion or solution of the cation-containing polymer; and then contacting the dispersion- or solution-wetted substrate, while still wetted with the colloidal dispersion or solution and without an intervening drying step, with a solution of a salt or of a strongly ionizing acid of a concentration to cause an adherent coating of the cation-containing polymer to form on the substrate.
Claim 3
Dependent Claim
64 words
A process as defined in claim 1, wherein a perfluorosulfonic acid ionomer is employed as the cation-containing polymer represented by ##STR3## wherein n is 1 or more and the ratio of a:b is about 7 to 1, or by ##STR4## wherein the ratio of a:b is about 7 to 1, or which is an alkali metal-exchanged salt of one of these perfluorosulfonic acid ionomers.
Claim 4
Dependent Claim
42 words
A process as defined in claim 2, wherein the substrate is in the form of a fiber, powder, fabric or article of polytetrafluoroethylene, polyvinylidene fluoride, a fluorinated ethylene-propylene copolymer, poly(vinyl chloride), glass, polypropylene, carbon, steel, platinum, chlorotrifluoroethylene or a perfluoroalkoxyvinyl ether-tetrafluoroethylene copolymer.
Claim 5
Dependent Claim
32 words
A process as defined in claim 1, further comprising contacting the coated substrate with a solution containing a different cation, so that a different cation-exchanged form of the coated cation-containing polymer results.
Claim 6
Dependent Claim
101 words
A process as defined in claim 1 or as defined in claim 4, further comprising heat treating the coated substrate at an elevated temperature after a first coating of the cation-containing polymer has been applied to the substrate and has been contacted with the salt solution or the strongly ionizing acid, then contacting the heat-treated, coated substrate a second time with a colloidal dispersion or solution of a cation-containing polymer and then with a solution of a salt or strongly ionizing acid of a concentration to cause a second coating of cation-containing polymer to form on the first coating the substrate.
Claim 7
Dependent Claim
24 words
A process as defined in claim 5, which further comprises annealing the coated substrate at a glass transition temperature of the ionomer or greater.
Claim 8
Dependent Claim
33 words
A process as defined in claim 6, wherein the substrate is polymeric in nature and further, wherein the annealing of the coated substrate occurs at a crystalline melting point of the polymeric substrate.
Claim 9
Dependent Claim
44 words
A process as defined in claim 1, wherein a sulfonated polystyrene, a copolymer of a non-acid, ethylenically unsaturated monomer with an ethylenically unsaturated carboxylic monomer, or a perfluorocarbon ionomer is employed in the colloidal dispersion or solution for forming the coating on the substrate.
Claim 10
Dependent Claim
64 words
A process as defined in claim 8, wherein a perfluorosulfonic acid ionomer is employed as the cation-containing polymer represented by ##STR5## wherein n is 1 or more and the ratio of a:b is about 7 to 1, or by ##STR6## wherein the ratio of a:b is about 7 to 1, or which is an alkali metal-exchanged salt of one of these perfluorosulfonic acid ionomers.
Claim 11
Dependent Claim
48 words
A process as defined in claim 1 or as defined in claim 9, wherein the colloidal dispersion or solution is employed for forming the coating on the substrate which when brought into contact with the substrate does not contain any solvent or any liquid medium other than water.
Claim 12
Dependent Claim
42 words
A process as defined in claim 10, wherein the substrate is in the form of a fiber, powder, fabric or article of polytetrafluoroethylene, polyvinylidene fluoride, a fluorinated ethylene-propylene copolymer, poly(vinyl chloride), glass, polypropylene, carbon, steel, platinum, chlorotrifluoroethylene or a perfluoroalkoxyvinyl ether-tetrafluoroethylene copolymer.
Claim 13
Dependent Claim
68 words
A process as defined in claim 10, wherein: the substrate is polytetrafluoroethylene, polyvinylidene fluoride, poly(vinyl chloride), polypropylene, a fluorinated ethylene-propylene copolymer, chlorotrifluoroethylene or a perfluoroalkoxyvinyl ether-tetrafluoroethylene copolymer and is in the form of a powder, fibers or a mixture of powder and fibers; and contacting the substrate with the colloidal dispersion or solution involves adding the dispersion to the substrate and subjecting the mixture to high shear conditions.
Claim 14
Dependent Claim
97 words
A process as defined in claim 12, wherein the solventless dispersion or solution is formed of a perfluorosulfonic acid ionomer of the cation-containing polymer having the formula ##STR7## wherein the ratio of a:b is about 7 to 1 and the ionomer has an equivalent weight of from about 550 to about 1000, the ionomer solids are combined with the substrate in a ratio by weight of 0.015 to 1 or greater, and the shearing of the mixture is accomplished with a blade on a blending device at a tip speed of 240 meters per minute or greater.
Claim 15
Dependent Claim
23 words
A process as defined in claim 13, wherein the perfluorosulfonic acid ionomer has an equivalent weight of from about 550 to about 800.
Claim 16
Dependent Claim
12 words
A process as defined in claim 14, wherein the substrate is polytetrafluoroethylene.
Claim 17
Dependent Claim
12 words
A process as defined in claim 13, wherein the substrate is polytetrafluoroethylene.
Claim 18
Dependent Claim
12 words
A process as defined in claim 12, wherein the substrate is polytetrafluoroethylene.
References Cited (Backward Citations)
US3072618A
Cited
US3772059A
Cited
US3799901A
Cited
US4169024A
Cited
US4262041A
Cited
US4243504A
Cited
US4348310A
Cited
US4453991A
Cited
US4433082A
Cited
US4454176A
Cited
US4666573A
Cited
US4661411A
Cited
US4731263A
Cited
US4680101A
Cited
US4720334A
Cited
US4990252A
Cited
US5082697A
Cited
US5136474A
Cited
US5206279A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-02-16 | 2001-08-18 | 2002-02-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-02-16 | 2005-08-18 | 2006-02-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-02-16 | 2009-08-18 | 2010-02-17 | $7700.00 | Window Closed / Lapsed |