Diaphragm for electrolytic cell
Assignee: PPG Industries Ohio Inc
•
Filing: 1986-11-04
•
Granted: 1988-01-19
•
Expires: 2006-11-04
Abstract
Abstract A liquid permeable diaphragm formed of a major amount polyfluorocarbon fibrils and a minor amount perfluorinated ion exchange material is disclosed. Optionally, the diaphragm may also include inorganic materials such as zirconium oxide, titanium dioxide, aluminum oxide, talc, barium sulfate or potassium titanate, or hydrous inorganic gels such as magnesium oxide gel, zirconium oxide gel, titanium oxide gel or zirconyl phosphate gel. The diaphragm can be prepared by depositing the polyfluorocarbon fibrils and the perfluorinated ion exchange material from a slurry, preferably an aqueous slurry. Optionally, a pore former such as, e.g., polypropylene can be codeposited from the slurry and subsequently removed by heat or dissolution to provide the desired permeability.
Inventors
- 👤 Donald W. DuBois
- 👤 William W. Carlin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 20:26
CPC Classifications
C; C25; C25B; C25B13/00; C25B13/04; C25B13/08; Y; Y10; Y10S; Y10S516/00; Y10S516/01; Y10S516/02
Claims Analysis
Total Claims: 45
Claim 1
Independent Claim
104 words
A liquid permeable, diaphragm for an electrolytic cell, said diaphragm comprised of from about 65 to 99 percent by weight fibrillated polyfluorocarbon and from 1 to about 35 percent by weight perfluorinated ion exchange material, basis total weight of polyfluorocarbon and ion exchange material, said diaphragm prepared by depositing polyfluorocarbon fibrils and perfluorinated ion exchange material from a slurry onto a foraminous cathode whereby to form an entangled mat and heating the deposited mat at temperatures below the sintering or decomposition temperatures of both the polyfluorocarbon fibrils and the perfluorinated ion exchange material for a sufficient time to secure the mat upon the cathode.
Claim 2
Dependent Claim
104 words
A liquid permeable, diaphragm for an electrolytic cell, said diaphragm comprised of from about 65 to 99 percent by weight fibrillated polyfluorocarbon and from 1 to about 35 percent by weight perfluorinated ion exchange material, basis total weight of polyfluorocarbon and ion exchange material, said diaphragm prepared by depositing polyfluorocarbon fibrils and perfluorinated ion exchange material from a slurry onto a foraminous cathode whereby to form an entangled mat and heating the deposited mat at temperatures below the sintering or decomposition temperatures of both the polyfluorocarbon fibrils and the perfluorinated ion exchange material for a sufficient time to secure the mat upon the cathode.
Claim 3
Dependent Claim
41 words
The diaphragm of claim 1 wherein the perfluorinated ion exchange material is a perfluorinated organic polymer having ion exchange functional groups selected from the group consisting of --COOM and --SO 3 M where M is hydrogen or an alkali metal ion.
Claim 4
Dependent Claim
10 words
The diaphragm of claim 1 wherein the polyfluorocarbon comprises polytetrafluoroethylene.
Claim 5
Dependent Claim
10 words
The diaphragm of claim 2 wherein the polyfluorocarbon comprises polytetrafluoroethylene.
Claim 6
Dependent Claim
40 words
The diaphragm of claim 3 wherein fibrillated polytetrafluoroethylene is coated with a perfluorinated organic polymer containing ion exchange functional groups selected from the group consisting of --COOM and --SO 3 M where M is hydrogen or an alkali metal ion.
Claim 7
Dependent Claim
16 words
The diaphragm of claim 4 wherein perfluorinated ion exchange material is in the form of particulates.
Claim 8
Dependent Claim
32 words
The diaphragm of claim 4 wherein a pore forming material selected from the group consisting of cellulose, rayon, polypropylene, polyethylene, nylon or starch is codeposited from the slurry onto the foraminous cathode.
Claim 9
Dependent Claim
32 words
The diaphragm of claim 5 wherein a pore forming material selected from the group consisting of cellulose, rayon, polypropylene, polyethylene, nylon or starch is codeposited from the slurry onto the foraminous cathode.
Claim 10
Dependent Claim
34 words
The diaphragm of claim 4 further including a minor amount of inorganic particulates selected from the group consisting of titanium dioxide, zirconium oxide, potassium titanate, aluminum oxide, barium sulfate, silicon carbide, asbestos or talc.
Claim 11
Dependent Claim
42 words
The diaphragm of claim 4 further including a minor amount of inorganic particluates selected from the group consisting of titanium dioxide, zirconium oxide, potassium titanate, aluminum oxide, barium sulfate, silicon carbide, asbestos or talc codeposited from the slurry onto the foraminous cathode.
Claim 12
Dependent Claim
40 words
The diaphragm of claim 10 wherein inorganic particulates are coated with the perfluorinated organic polymer having ion exchange functional groups selected from the group consisting of --COOM and --SO 3 M where M is hydrogen or an alkali metal ion.
Claim 13
Dependent Claim
40 words
The diaphragm of claim 11 wherein fibrillated polytetrafluoroethylene is coated with a perfluorinated organic polymer containing ion exchange functional groups selected from the group consisting of --COOM and --SO 3 M where M is hydrogen or an alkali metal ion.
Claim 14
Dependent Claim
32 words
The diaphragm of claim 10 wherein a pore forming material selected from the group consisting of cellulose, rayon, polypropylene, polyethylene, nylon or starch is codeposited from the slurry onto the foraminous cathode.
Claim 15
Dependent Claim
10 words
The diaphram of claim 4 wherein the diaphragm is asbestos-free.
Claim 16
Dependent Claim
35 words
The diaphragm of claim 7 further including an inorganic gel selected from the group consisting of hydrous magnesium oxide gel, hydrous zirconium oxide gel, hydrous titanium oxide gel, zirconyl phosphate gel, or ferric hydroxide gel.
Claim 17
Dependent Claim
82 words
A process of preparing a liquid permeable diaphragm comprising: (a) providing a slurry including a liquid medium, polyfluorocarbon fibrils and perfluorinated ion exchange material; (b) depositing the polyfluorocarbon fibrils and perfluorinated ion exchange material from said slurry onto a foraminous cathode whereby to form a diaphragm; and (c) heating the deposited diaphragm at temperatures below the sintering or decomposition temperatures of both the polyfluorocarbon fibrils and the perfluorinated ion exchange material for a sufficient time to secure the diaphragm upon the cathode.
Claim 18
Dependent Claim
82 words
A process of preparing a liquid permeable diaphragm comprising: (a) providing a slurry including a liquid medium, polyfluorocarbon fibrils and perfluorinated ion exchange material; (b) depositing the polyfluorocarbon fibrils and perfluorinated ion exchange material from said slurry onto a foraminous cathode whereby to form a diaphragm; and (c) heating the deposited diaphragm at temperatures below the sintering or decomposition temperatures of both the polyfluorocarbon fibrils and the perfluorinated ion exchange material for a sufficient time to secure the diaphragm upon the cathode.
Claim 19
Dependent Claim
48 words
The process of claim 16 wherein the polyfluorocarbon fibrils are polytetrafluoroethylene fibrils and the perfluorinated ion exchange material is a perfluorinated organic polymer having ion exchange functional groups selected from the group consisting of --COOM, and --SO 3 M where M is hydrogen or an alkali metal ion.
Claim 20
Dependent Claim
50 words
The process of claim 17 wherein the slurry further includes a pore forming material selected from the group consisting of cellulose, rayon, polypropylene, polyethylene, nylon or starch and the pore forming material is codeposited from the slurry upon the cathode with the polyfluorocarbon fibrils and the perfluorinated ion exchange material.
Claim 21
Dependent Claim
37 words
The process of claim 17 wherein the liquid medium is selected from the group of water, isopropanol, ethanol, dimethyl sulfoxide, propylene carbonate, ethylene glycol, an aqueous sodium chloride solution, an aqueous sodium hydroxide solution or mixtures thereof.
Claim 22
Dependent Claim
28 words
The process of claim 17 wherein the liquid medium is water and the slurry further includes a viscosity modifier and a surfactant capable of dispersing the polyfluorocarbon fibrils.
Claim 23
Dependent Claim
28 words
The process of claim 18 wherein the liquid medium is water and the slurry further includes a viscosity modifier and a surfactant capable of dispersing the polyfluorocarbon fibrils.
Claim 24
Dependent Claim
33 words
The process of claim 17 wherein the slurry further includes inorganic particulates selected from the group consisting of titanium dioxide, zirconium oxide, potassium titanate, silicon carbide, aluminum oxide, barium sulfate, asbestos or talc.
Claim 25
Dependent Claim
16 words
The process of claim 22 wherein inorganic particulates are precoated with the perfluorinated ion exchange material.
Claim 26
Dependent Claim
33 words
The process of claim 18 wherein the slurry further includes inorganic particulates selected from the group consisting of titanium dioxide, zirconium oxide, potassium titanate, silicon carbide, aluminum oxide, barium sulfate, asbestos or talc.
Claim 27
Dependent Claim
16 words
The process of claim 24 wherein inorganic particulates are precoated with the perfluorinated ion exchange material.
Claim 28
Dependent Claim
40 words
The process of claim 17 wherein an inorganic gel selected from the group consisting of hydrous magnesium oxide gel, hydrous zirconium oxide gel, zirconyl phosphate gel, hydrous titanium oxide gel, or ferric hydroxide gel is precipitated within the deposited diaphragm.
Claim 29
Dependent Claim
20 words
The process of claim 26 wherein the inorganic gel is precipitated in situ within the deposited diaphragm during cell operation.
Claim 30
Dependent Claim
40 words
The process of claim 18 wherein an inorganic gel selected from the group consisting of hydrous magnesium oxide gel, hydrous zirconium oxide gel, zirconyl phosphate gel, hydrous titanium oxide gel, or ferric hydroxide gel is precipitated within the deposited diaphragm.
Claim 31
Dependent Claim
20 words
The process of claim 28 wherein the inorganic gel is precipitated in situ within the deposited diaphragm during cell operation.
Claim 32
Dependent Claim
59 words
The process of claim 20 wherein the surfactant is a non-ionic surfactant represented by the formula R(OR') x Cl wherein R is a C 8 -C 15 linear or branched alkyl, R' is an ethylene group represented by --CH 2 --CH(R")-- wherein R" is hydrogen, methyl, ethyl or mixtures thereof and x is a number from 8 to 12.
Claim 33
Dependent Claim
59 words
The process of claim 21 wherein the surfactant is a non-ionic surfactant represented by the formula R(OR') x Cl wherein R is a C 8 -C 15 linear or branched alkyl, R' is an ethylene group represented by --CH 2 --CH(R")-- wherein R" is hydrogen, methyl, ethyl or mixtures thereof and x is a number from 8 to 12.
Claim 34
Dependent Claim
79 words
In a process of electrolyzing alkali metal chloride in an electrolytic cell including a liquid permeable diaphragm, the improvement which comprises utilizing a diaphragm comprising from about 65 to 99 weight percent fibrillated polytetrafluoroethylene and from about 1 to about 35 weight percent perfluorinated organic polymer having ion exchange groups selected from the group consisting of --COOM or --SO 3 M where M is hydrogen or an alkali metal ion, basis total weight of polytetrafluoroethylene and perfluorinated organic polymer.
Claim 35
Dependent Claim
79 words
In a process of electrolyzing alkali metal chloride in an electrolytic cell including a liquid permeable diaphragm, the improvement which comprises utilizing a diaphragm comprising from about 65 to 99 weight percent fibrillated polytetrafluoroethylene and from about 1 to about 35 weight percent perfluorinated organic polymer having ion exchange groups selected from the group consisting of --COOM or --SO 3 M where M is hydrogen or an alkali metal ion, basis total weight of polytetrafluoroethylene and perfluorinated organic polymer.
Claim 36
Dependent Claim
48 words
The process of claim 32 wherein the diaphragm includes a pore forming material selected from the group consisting of cellulose, rayon, polypropylene, polyethylene, nylon or starch and the liquid permeability of the diaphragm is increased by the in situ removal of the pore forming material during cell operation.
Claim 37
Dependent Claim
53 words
The process of claim 32 wherein the liquid permeability of the diaphragm is reduced by the formation of an inorganic gel in situ within the diaphragm, the gel selected from the group consisting of hydrous magnesium oxide gel, hydrous zirconia oxide gel, hydrous titanium oxide gel, zirconyl phosphate gel or ferric hydroxide gel.
Claim 38
Dependent Claim
33 words
The process of claim 32 wherein the slurry further includes inorganic particulates selected from the group consisting of titanium dioxide, zirconium oxide, potassium titanate, silicon carbide, aluminum oxide, barium sulfate, asbestos or talc.
Claim 39
Dependent Claim
40 words
The process of claim 35 wherein inorganic particulates are coated with the perfluorinated organic polymer having ion exchange functional groups selected from the group consisting of --COOM and --SO 3 M where M is hydrogen or an alkali metal ion.
Claim 40
Dependent Claim
40 words
The process of claim 36 wherein fibrillated polytetrafluoroethylene is coated with a perfluorinated organic polymer containing ion exchange functional groups selected from the group consisting of --COOM and --SO 3 M where M is hydrogen or an alkali metal ion.
Claim 41
Dependent Claim
40 words
The process of claim 32 wherein fibrillated polytetrafluoroethylene is coated with a perfluorinated organic polymer containing ion exchange functional groups selected from the group consisting of --COOM and --SO 3 M where M is hydrogen or an alkali metal ion.
Claim 42
Dependent Claim
66 words
In a process of dispersing polyfluorocarbon particulates in an aqueous medium, the improvement which comprises utilizing a non-ionic surfactant represented by the formula R(OR') x Cl wherein R is a C 8 -C 15 linear or branched alkyl, R' is an ethylene group represented by --CH 2 --CH(R")-- wherein R" is hydrogen, methyl, ethyl or mixtures thereof and x is a number from 8 to 12.
Claim 43
Dependent Claim
66 words
In a process of dispersing polyfluorocarbon particulates in an aqueous medium, the improvement which comprises utilizing a non-ionic surfactant represented by the formula R(OR') x Cl wherein R is a C 8 -C 15 linear or branched alkyl, R' is an ethylene group represented by --CH 2 --CH(R")-- wherein R" is hydrogen, methyl, ethyl or mixtures thereof and x is a number from 8 to 12.
Claim 44
Dependent Claim
11 words
The process of claim 39 wherein the polyfluorocarbon particulates are polytetrafluoroethylene.
Claim 45
Dependent Claim
24 words
The process of claim 40 wherein R is a mixture of C 12 -C 15 linear alkyls, R" is hydrogen, and x is 9.
References Cited (Backward Citations)
US4003818A
Cited
US4210515A
Cited
US4036729A
Cited
US4125451A
Cited
US4138314A
Cited
US4154666A
Cited
US4238303A
Cited
US4170539A
Cited
US4432860A
Cited
US4539085A
Cited
US4421579A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-01-18 | 1991-07-20 | 1992-01-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-01-18 | 1995-07-20 | 1996-01-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-01-18 | 1999-07-20 | 2000-01-19 | $7700.00 | Window Closed / Lapsed |