Method for preventing titanium lifting during and after metal etching
Assignee: GlobalFoundries Singapore Pte Ltd
•
Filing: 1995-08-03
•
Granted: 1998-01-06
•
Expires: 2015-08-03
Abstract
Abstract A process for forming metal composites, using a titanium underlay as part of the composite, with reduced risk of titanium adhesion loss or lifting, has been developed. Several solutions, resulting in protective layers being formed on the exposed titanium sidewall, have been shown. One solution features the addition of nitrogen, as part of reactive ion etching chemistry, during the patterning of the underlying titanium layer. The resulting titanium nitride formation, on the exposed titanium sidewall, protects against subsequent processing steps that may degrade the adhesion of titanium to an underlying material. A second solution describes the formation of a titanium oxide film on the exposed titanium sidewall. This formation occurs during a photoresist plasma strip, using an oxygen-stream ambient. The titanium oxide film again results in protection of the titanium interface, during subsequent processing steps.
Inventors
- 👤 Lianjun Liu
- 👤 Chiu-Kwan Man
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 15:32
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/28; H10P50/286; H10P50/287; H10P50/26; H10P50/264; H10P50/266; H10P50/267
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
144 words
A method for forming metal patterns on a semiconductor substrate comprising the steps of: depositing a titanium layer on said semiconductor substrate; depositing a layer of titanium-tungsten on said titanium layer; depositing a layer of an aluminum based layer on said titanium-tungsten layer; forming a photoresist image on said aluminum based layer; anisotropically etching the exposed part of said aluminum based layer; anisotropically etching the exposed part of said titanium-tungsten layer; anisotropically etching the exposed part of said titanium layer using a reaction ambient, containing between about 5 to 80 sccm of N 2 , as one of the reactants, at a temperature between about 45° to 70° C. forming a titanium nitride film, between about 10 to 100 Angstroms in thickness, on the exposed sides of said titanium layer, during the anisotropic etching of said titanium layer; and removal of said photoresist image.
Claim 2
Independent Claim
144 words
A method for forming metal patterns on a semiconductor substrate comprising the steps of: depositing a titanium layer on said semiconductor substrate; depositing a layer of titanium-tungsten on said titanium layer; depositing a layer of an aluminum based layer on said titanium-tungsten layer; forming a photoresist image on said aluminum based layer; anisotropically etching the exposed part of said aluminum based layer; anisotropically etching the exposed part of said titanium-tungsten layer; anisotropically etching the exposed part of said titanium layer using a reaction ambient, containing between about 5 to 80 sccm of N 2 , as one of the reactants, at a temperature between about 45° to 70° C. forming a titanium nitride film, between about 10 to 100 Angstroms in thickness, on the exposed sides of said titanium layer, during the anisotropic etching of said titanium layer; and removal of said photoresist image.
Claim 3
Dependent Claim
16 words
The method of claim 1, wherein said titanium layer is between about 200 to 2000 Angstroms.
Claim 4
Dependent Claim
35 words
The method of claim 1, wherein said titanium-tungsten layer is composed of between about 8 to 12% titanium, and between about 88 to 92% tungsten, deposited to a thickness between about 0 to 3000 Angstroms.
Claim 5
Dependent Claim
23 words
The method of claim 1, wherein said aluminum based layer is 100% aluminum, deposited to a thickness between about 4000 to 10000 Angstroms.
Claim 6
Dependent Claim
31 words
The method of claim 1, wherein said aluminum based layer contains between about 0 to 2% copper, by weight, and is deposited to a thickness between about 4000 to 10000 Angstroms.
Claim 7
Dependent Claim
41 words
The method of claim 1, wherein said anisotropic etching of the said aluminum based layer occurs in a mixture of between about 20 to 100 sccm of BCl 3 , and between about 20 to 80 sccm of Cl 2 .
Claim 8
Dependent Claim
25 words
The method of claim 1, wherein said anisotropic etching of said titanium-tungsten layer occurs in between about 10 to 80 sccm of SF 6 .
Claim 9
Dependent Claim
48 words
The method of claim 1, wherein said anisotropic etching of titanium layer occurs in an ambient comprised of between about 10 to 80 sccm of SF 6 , and between about 5 to 80 sccm of N 2 , at a temperature between about 45° to 70° C.
Claim 10
Dependent Claim
43 words
The method of claim 1, wherein said titanium nitride film, formed on the exposed sides of said titanium layer, is between about 10 to 100 Angstroms in thickness, formed during the etching of between about 200 to 2000 Angstroms of said titanium layer.
Claim 11
Dependent Claim
25 words
The method of claim 1, wherein said photoresist is removed via plasma ashing in 100% oxygen, at a temperature between about 100° to 300° C.
Claim 12
Independent Claim
135 words
A method for forming metal patterns on a semiconductor substrate, comprising the steps of: depositing a titanium layer on said semiconductor substrate; depositing a titanium-tungsten layer on said titanium layer; depositing an aluminum based layer on said titanium-tungsten layer; forming a photoresist shape on said aluminum based layer; anisotropically etching the exposed part of said aluminum based layer; anisotropically etching the exposed part of said titanium-tungsten layer; anisotropically etching the exposed part of said titanium layer; removal of said photoresist shape, in a plasma comprised of between about 500 to 4000 sccm of H 2 O, and between about 20 to 100% O 2 ; and formation of a titanium oxide film, between about 10 to 100 Angstroms in thickness, on the exposed sides of said titanium layer, formed during said photoresist shape removal process.
Claim 13
Independent Claim
135 words
A method for forming metal patterns on a semiconductor substrate, comprising the steps of: depositing a titanium layer on said semiconductor substrate; depositing a titanium-tungsten layer on said titanium layer; depositing an aluminum based layer on said titanium-tungsten layer; forming a photoresist shape on said aluminum based layer; anisotropically etching the exposed part of said aluminum based layer; anisotropically etching the exposed part of said titanium-tungsten layer; anisotropically etching the exposed part of said titanium layer; removal of said photoresist shape, in a plasma comprised of between about 500 to 4000 sccm of H 2 O, and between about 20 to 100% O 2 ; and formation of a titanium oxide film, between about 10 to 100 Angstroms in thickness, on the exposed sides of said titanium layer, formed during said photoresist shape removal process.
Claim 14
Dependent Claim
16 words
The method of claim 11, wherein said titanium layer is between about 200 to 2000 Angstroms.
Claim 15
Dependent Claim
16 words
The method of claim 11, wherein said titanium-tungsten layer is between about 0 to 3000 Angstroms.
Claim 16
Dependent Claim
24 words
The method of claim 11, wherein said aluminum based layer is 100% aluminum, and deposited to a thickness between about 4000 to 10000 Angstroms.
Claim 17
Dependent Claim
31 words
The method of claim 11, wherein said aluminum based layer contains between about 0 to 2% copper, by weight and is deposited to a thickness between about 4000 to 10000 Angstroms.
Claim 18
Dependent Claim
39 words
The method of claim 11, wherein said anisotropic etching of said aluminum based layer occurs in a mixture between about 20 to 100 sccm of BCl 3 , and between about 20 to 80 sccm of Cl 2 .
Claim 19
Dependent Claim
25 words
The method of claim 11, wherein said anisotropic etching of said titanium-tungsten layer occurs in between about 10 to 80 sccm of SF 6 .
Claim 20
Dependent Claim
25 words
The method of claim 11, wherein said anisotropic etching of said titanium layer occurs in between about 10 to 80 sccm of SF 6 .
Claim 21
Dependent Claim
43 words
The method of claim 11, wherein said photoresist is removed in a plasma, containing between about 500 to 4000 sccm of H 2 O, and between about 20 to 100% of O 2 , at a temperature between about 100° to 300° C.
Claim 22
Dependent Claim
36 words
The method of claim 11, wherein said titanium oxide film, is formed to a thickness between about 10 to 100 Angstroms, on the exposed sides of said titanium layer, during the removal of said photoresist shape.
Claim 23
Independent Claim
151 words
A method for forming metal patterns on a semiconductor substrate, comprising the steps of: depositing a titanium layer on said semiconductor substrate; depositing a titanium-tungsten layer on said titanium layer; depositing an aluminum based layer on said titanium-tungsten layer; forming a photoresist shape on said aluminum based layer; anisotropically etching exposed part of said aluminum based layer; anisotropically etching exposed part of said titanium-tungsten layer; anisotropically etching exposed part of said titanium layer, in an ambient containing between about 5 to 80 sccm of N 2 as one of the reactants, using N2 as one of the reactants; forming a titanium nitride layer, between about 10 to 100 Angstroms in thickness, on the exposed sides of said titanium layer, during the anisotropic etching of said titanium layer; and removal of said photoresist shape in an oxygen-steam plasma, forming an aluminum oxide film, on the exposed sides of said aluminum based layer.
Claim 24
Independent Claim
151 words
A method for forming metal patterns on a semiconductor substrate, comprising the steps of: depositing a titanium layer on said semiconductor substrate; depositing a titanium-tungsten layer on said titanium layer; depositing an aluminum based layer on said titanium-tungsten layer; forming a photoresist shape on said aluminum based layer; anisotropically etching exposed part of said aluminum based layer; anisotropically etching exposed part of said titanium-tungsten layer; anisotropically etching exposed part of said titanium layer, in an ambient containing between about 5 to 80 sccm of N 2 as one of the reactants, using N2 as one of the reactants; forming a titanium nitride layer, between about 10 to 100 Angstroms in thickness, on the exposed sides of said titanium layer, during the anisotropic etching of said titanium layer; and removal of said photoresist shape in an oxygen-steam plasma, forming an aluminum oxide film, on the exposed sides of said aluminum based layer.
Claim 25
Dependent Claim
36 words
The method of claim 21, wherein said anisotropic etching of said titanium layer occurs in between about 10 to 80 sccm of SF 6 , and between about 5 to 80 sccm of N 2 .
Claim 26
Dependent Claim
44 words
The method of claim 21, wherein said titanium nitride film, formed on exposed sides of said titanium layer to a thickness between about 10 to 100 Angstroms, and formed during the anisotropic etching of between about 200 to 2000 Angstroms of said titanium layer.
Claim 27
Dependent Claim
31 words
The method of claim 21, wherein said photoresist is removed in a plasma containing between about 500 to 4000 sccm of H 2 O, and between about 20 to 100% oxygen.
References Cited (Backward Citations)
JPS5376937A
Cited
US4412885A
Cited
US4567058A
Cited
US4654120A
Cited
US5057187A
Cited
US4948462A
Cited
US5397432A
Cited
US5310456A
Cited
US5561084A
Cited
US5314576A
Cited
US5407862A
Cited
US5412250A
Cited
US5545289A
Cited
US5522520A
Cited
US5430328A
Cited
US5449639A
Cited
US5527736A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-01-05 | 2001-07-07 | 2002-01-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-01-05 | 2005-07-07 | 2006-01-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-01-05 | 2009-07-07 | 2010-01-06 | $7700.00 | Window Closed / Lapsed |