Method for producing a semiconductor device having semiconductor layers of SiC by the use of an ion-implantation technique
Assignee: Wolfspeed Inc
•
Filing: 1996-04-24
•
Granted: 1998-01-06
•
Expires: 2016-04-24
Abstract
Abstract A method for producing a semiconductor device having semiconductor layers of SiC with at least three doped layers on top of each other, comprises the steps of growing a first semiconductor layer of SiC; implanting an impurity dopant into the first layer to form a second doped surface layer as a sub-layer therein, the second doped surface layer being surrounded, except for the top surface thereof, by the first semiconductor layer; and epitaxially growing a third semiconductor layer of SiC on top of the second layer of SiC and regions of the first layer adjacent thereto to totally bury the second semiconductor layer. The impurity dopant implanted into the first semiconductor layer is of a first conductivity n or p type, and the first semiconductor layer being doped with a second, opposite conductivity type, so as to form a pn-junction at the interface between the first and second layers.
Inventors
- 👤 Kurt Rottner
- 👤 Adolf Schoner
- 👤 Nils Nordell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 14:00
CPC Classifications
H; H10; H10D; H10D12/00; H10D12/01; H10D12/031; H10D30/00; H10D30/01; H10D30/051; H10D30/80; H10D30/83; H10D30/831; H10D62/00; H10D62/80; H10D62/83; H10D62/832; H10D62/8325; H10P; H10P30/00; H10P30/20; H10P30/202; H10P30/204; H10P30/2042; H10P30/21; H10W; H10W15/00; H10W15/01; Y; Y10; Y10S; Y10S438/00; Y10S438/931
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
153 words
A method for producing a semiconductor device having semiconductor layers of SiC with at least three doped layers on top of each other, comprising the steps of: a) growing a first semiconductor layer of SiC; b) implanting an impurity dopant into said first layer to form a second doped surface layer as a sub-layer therein, said second doped surface layer being surrounded, except for the top surface thereof, by said first semiconductor layer; and c) epitaxially growing a third semiconductor layer of SiC on top of said second layer of SiC and regions of said first layer adjacent thereto to totally bury said second semiconductor layer; and wherein said impurity dopant implanted into said first semiconductor layer is of a first conductivity n or p type, said first semiconductor layer being doped with a second, opposite conductivity type, so as to form a pn-junction at the interface between said first and second layers.
Claim 2
Independent Claim
153 words
A method for producing a semiconductor device having semiconductor layers of SiC with at least three doped layers on top of each other, comprising the steps of: a) growing a first semiconductor layer of SiC; b) implanting an impurity dopant into said first layer to form a second doped surface layer as a sub-layer therein, said second doped surface layer being surrounded, except for the top surface thereof, by said first semiconductor layer; and c) epitaxially growing a third semiconductor layer of SiC on top of said second layer of SiC and regions of said first layer adjacent thereto to totally bury said second semiconductor layer; and wherein said impurity dopant implanted into said first semiconductor layer is of a first conductivity n or p type, said first semiconductor layer being doped with a second, opposite conductivity type, so as to form a pn-junction at the interface between said first and second layers.
Claim 3
Dependent Claim
35 words
A method according to claim 1 wherein said growing in step c) is carried out at such a temperature that the dopants implanted in step b) are made electrically active and implantation damage is reduced.
Claim 4
Dependent Claim
14 words
A method according to claim 1 wherein said temperature is higher than 1,500° C.
Claim 5
Dependent Claim
21 words
A method according to claim 1 wherein in step c) said third semiconductor layer is grown by Chemical Vapor Deposition (CVD).
Claim 6
Dependent Claim
17 words
A method according to claim 1 wherein said impurity dopant implanted in step b) is of p-type.
Claim 7
Dependent Claim
15 words
A method according to claim 5, wherein boron is said impurity dopant in step b).
Claim 8
Dependent Claim
15 words
A method according to claim 5, wherein aluminum is said impurity dopant in step b).
Claim 9
Dependent Claim
28 words
A method according to claim 6 wherein the implantation step b) is carried out while keeping the first semiconductor layer of SiC at a temperature of 400°-600° C.
Claim 10
Dependent Claim
24 words
A method according to claim 1 wherein adjacent layers of said three layers are doped with dopants of different n or p conductivity types.
Claim 11
Dependent Claim
34 words
A method according to claim 9 wherein in step c) said third semiconductor layer is grown with a lower doping concentration than the doping concentration of the second semiconductor layer obtained by said implantation.
Claim 12
Dependent Claim
28 words
A method according to claim 1 wherein said first and third layers are epitaxially grown in step a) and step c) while doping said layers with n-type dopants.
Claim 13
Dependent Claim
30 words
A method according to claim 11 wherein said third semiconductor layer is grown in step c) at a lower doping concentration than the dopant concentration of the second semiconductor layer.
Claim 14
Dependent Claim
22 words
A method according to claim 1 further comprising several alternating successive steps of implantation and regrowth according to steps b) and c).
Claim 15
Dependent Claim
57 words
A method according to claim 13 wherein the regrowth of layer is coordinated with the conditions of the implantation step following thereupon to make the layer obtained by that implantation step extending through the entire layer previously regrown and connecting to the layer previously obtained by the previous implantation step for forming a continuous thick implanted layer.
Claim 16
Dependent Claim
35 words
A method according to claim 1 wherein a regrowth step is carried out after the last implantation step to form said thick continuous implanted layer thereby forming a semiconductor device having a thick buried layer.
References Cited (Backward Citations)
US4775882A
Cited
JPH01109738A
Cited
US5135885A
Cited
US5030580A
Cited
US5270554A
Cited
US5322802A
Cited
US5378642A
Cited
US5510281A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-01-05 | 2001-07-07 | 2002-01-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-01-05 | 2005-07-07 | 2006-01-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-01-05 | 2009-07-07 | 2010-01-06 | $7700.00 | Window Closed / Lapsed |