US5665203A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Silicon etching method
Assignee: International Business Machines Corp
•
Filing: 1995-04-28
•
Granted: 1997-09-09
•
Expires: 2015-04-28
Abstract
Abstract A method for etching silicon is described incorporating first and second steps of reactive ion etching through a patterned oxide layer in respective atmospheres of HBr, Cl 2 and O 2 and then HBr and O 2 in situ by terminating the first etching step and removing substantially all Cl 2 before continuing with the second step of etching. The invention overcomes the problem of uneven etching of n+ and p+ silicon gates for CMOS transistor logic during the step of simultaneously etching silicon to form sub 0.25 micron gate lengths and vertical sidewalls while stopping on the gate oxide.
Inventors
- 👤 Young Hoon Lee
- 👤 Keith Raymond Milkove
- 👤 John William Stiebritz, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 10:54
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/26; H10P50/264; H10P50/266; H10P50/267; H10P50/268
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
154 words
A method for forming vertical sidewalls from a silicon layer situated on top of a dielectric layer, comprising the steps of: providing a patterned oxide layer on top of said silicon layer protecting the areas which are not to be etched during a subsequent etch step, and leaving other areas thereof exposed, first reactive ion etching the exposed areas of the silicon layer through the patterned oxide layer at a pressure of less than 50 mTorr in an atmosphere of HBr, Cl 2 , and O 2 whereby sidewalls of the patterned silicon layer are oxidized during said step, terminating said step of first reactive ion etching of said silicon layer a predetermined distance above said dielectric layer, removing substantially all Cl 2 from said atmosphere, and second reactive ion etching the exposed areas of the silicon layer through said patterned oxide layer down to said dielectric layer at a pressure below 50 mTorr.
Claim 2
Independent Claim
154 words
A method for forming vertical sidewalls from a silicon layer situated on top of a dielectric layer, comprising the steps of: providing a patterned oxide layer on top of said silicon layer protecting the areas which are not to be etched during a subsequent etch step, and leaving other areas thereof exposed, first reactive ion etching the exposed areas of the silicon layer through the patterned oxide layer at a pressure of less than 50 mTorr in an atmosphere of HBr, Cl 2 , and O 2 whereby sidewalls of the patterned silicon layer are oxidized during said step, terminating said step of first reactive ion etching of said silicon layer a predetermined distance above said dielectric layer, removing substantially all Cl 2 from said atmosphere, and second reactive ion etching the exposed areas of the silicon layer through said patterned oxide layer down to said dielectric layer at a pressure below 50 mTorr.
Claim 3
Dependent Claim
27 words
The method of claim 1, wherein said step of terminating includes the step of terminating first reactive ion etching 20 to 30 nm above said dielectric layer.
Claim 4
Dependent Claim
36 words
The method of claim 1, wherein said step of second reactive ion etching includes the step of providing a very low power density plasma in the range from 0.3 W/cm 2 to 10 W/cm 2 .
Claim 5
Dependent Claim
30 words
The method of claim 1, wherein said step of second reactive ion etching includes the step of providing an atmosphere of HBr and O 2 flowing through the plasma chamber.
Claim 6
Dependent Claim
39 words
The method of claim 1, wherein said step of second reactive ion etching includes the step of continuing to etch said silicon layer and the lower portions of said sidewalls to form vertical sidewalls down to said dielectric layer.
Claim 7
Dependent Claim
138 words
The method of claim 1, further including the steps of first forming a blanket polysilicon layer over said dielectric layer, implanting ions into said polysilicon layer, forming an oxide layer to function as a mask over said polysilicon layer, activating by partial thermal activation and redistribution of the implanted ions in said polysilicon layer, coating said oxide layer to function as a mask oxide layer with resist, lithographically patterning said oxide layer to function as a mask oxide layer, etching the oxide layer to function as a mask oxide layer to form the patterned oxide layer, removing said patterned resist, removing residual oxide from said polysilicon layer exposed by said patterned oxide and formed during said step of removing said resist, and controlling the ambient atmosphere after said step of removing to prevent oxidation of said polysilicon layer.
Claim 8
Dependent Claim
25 words
The method of claim 1 wherein said second reactive ion etching step includes the step of providing an atmosphere including HBr and O 2 .
Claim 9
Dependent Claim
26 words
The method of claim 1 wherein said second reactive ion etching step includes the step of providing an atmosphere including HBr, He and O 2 .
Claim 10
Dependent Claim
24 words
The method of claim 1 wherein said first reactive etching step includes providing a magnetic field in the range from 0 to 40 gauss.
Claim 11
Dependent Claim
27 words
The method of claim 1 wherein said first reactive ion etching step includes the step of providing a pressure in the range from 1 to 15 mTorr.
Claim 12
Dependent Claim
27 words
The method of claim 1 wherein said second reactive ion etching step includes the step of providing a pressure in the range from 1 to 15 mTorr.
Claim 13
Dependent Claim
21 words
The method of claim 1 wherein said first reactive ion etching step includes the step of supplying He to said atmosphere.
Claim 14
Dependent Claim
29 words
The method of claim 1 further including the step of selecting a silicon layer from a group consisting of single crystal silicon, polysilicon, amporphous silicon and silicon germanium alloy.
Claim 15
Dependent Claim
32 words
The method of claim 1 further including the step of removing any surface oxide that may have formed on an exposed silicon layer prior to said step of first reactive ion etching.
Claim 16
Dependent Claim
41 words
The method of claim 14 further including the steps of placing said silicon layer in a first chamber, reactive ion etching with a CF 4 plasma and transferring said silicon layer to a second chamber under a controlled atmosphere and pressure.
Claim 17
Dependent Claim
26 words
The method of claim 1, wherein said dielectric layer is a silicon dioxide layer intended to serve as gate oxide of a device to be formed.
References Cited (Backward Citations)
US5310456A
Cited
US5242536A
Cited
US5336365A
Cited
US5252502A
Cited
US5256245A
Cited
US5522966A
Cited
US5505816A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-09-08 | 2001-03-10 | 2001-09-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-09-08 | 2005-03-10 | 2005-09-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-09-08 | 2009-03-10 | 2009-09-09 | $7700.00 | Window Closed / Lapsed |