Biodegradable moldable surgical material
Assignee: United States Surgical Corp
•
Filing: 1995-06-07
•
Granted: 1997-06-24
•
Expires: 2015-06-07
Abstract
Abstract A moldable biodegradable surgical material is made of a bioabsorbable polymer derived from hydroxyacids, tactones, carbonates, etheresters, anhydrides, orthoesters and copolymers, terpolymers and/or blends thereof, the polymer blended with at least one surface active agent selected from the group consisting of fatty acid ester and poly(oxypropylene)/poly(oxyethylene) block copolymer. In one embodiment, a leaching agent is blended with the above-mentioned surgical material. Methods of making moldable biodegradable surgical material are provided. The surgical material may be used as a moldable bone wax in connection with repair of wounds and is an adaptable aid for any appropriate surgical use, e.g., hemostat, anchor, patch etc.
Inventors
- 👤 Walter Skalla
- 👤 Steven L. Bennett
- 👤 Ying Jiang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 17:04
CPC Classifications
A; A61; A61L; A61L31/00; A61L31/04; A61L31/041; A61L24/00; A61L24/001; A61L24/0036; A61L24/04; A61L24/043; A61L24/046; A61L27/00; A61L27/14; A61L27/18; A61L27/26; A61L27/50; A61L27/56; A61L31/06
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
73 words
A hand moldable biodegradable surgical material comprising a blend of a bioabsorbable polymer and a surface active agent selected from the group consisting of sorbitan fatty acid ester and poly(oxypropylene)/poly(oxyethylene) block copolymer and a leaching agent selected from the group consisting of calcium carbonate, calcium chloride, tricalcium phosphate and hydroxyapatite wherein the leaching agent is present in an amount ranging from about 1 percent to about 70 percent by weight of the material.
Claim 2
Dependent Claim
73 words
A hand moldable biodegradable surgical material comprising a blend of a bioabsorbable polymer and a surface active agent selected from the group consisting of sorbitan fatty acid ester and poly(oxypropylene)/poly(oxyethylene) block copolymer and a leaching agent selected from the group consisting of calcium carbonate, calcium chloride, tricalcium phosphate and hydroxyapatite wherein the leaching agent is present in an amount ranging from about 1 percent to about 70 percent by weight of the material.
Claim 3
Dependent Claim
38 words
A hand moldable biodegradable surgical material according to claim 1 wherein the bioabsorbable polymer is derived from a member selected from the group consisting of hydroxyacids, lactones, carbonates, etheresters, anhydrides, esteramides, orthoesters, and copolymers, terpolymers and blends thereof.
Claim 4
Dependent Claim
33 words
A hand moldable biodegradable surgical material according to claim 2 wherein the bioabsorbable polymer is selected from the group consisting of polylactide, polyglycolide, polydioxanone, polycaprolactone, polytrimethylene carbonate and copolymers, terpolymers and blends thereof.
Claim 5
Dependent Claim
22 words
A hand moldable biodegradable surgical material according to claim 3 wherein the bioabsorbable polymer is a star polymer of glycolide and caprolactone.
Claim 6
Dependent Claim
34 words
A hand moldable biodegradable surgical material according to claim 4 wherein glycolide is present in an amount of about 9.8 weight percent and caprolactone is present in an amount of about 90.2 weight percent.
Claim 7
Dependent Claim
32 words
A hand moldable biodegradable surgical material according to claim 1 wherein the sorbitan fatty acid ester is present in an amount ranging from about 10 weight percent to about 90 weight percent.
Claim 8
Dependent Claim
22 words
A hand moldable biodegradable surgical material according to claim 1 wherein the sorbitan fatty acid ester is polyoxyethylene sorbitan fatty acid ester.
Claim 9
Dependent Claim
21 words
A hand moldable biodegradable surgical material according to claim 7 wherein the polyoxyethylene sorbitan fatty acid ester is polyoxyethylene sorbitan monopalmitate.
Claim 10
Dependent Claim
32 words
A hand moldable biodegradable surgical material according to claim 1 wherein the bioabsorbable polymer is a star polymer of glycolide and caprolactone and the sorbitan fatty acid ester is polyoxyethylene sorbitan monopalmitate.
Claim 11
Dependent Claim
31 words
A hand moldable biodegradable surgical material according to claim 1 wherein the poly(oxypropylene)poly(oxyethylene) block copolymer is present in an amount ranging from about 2 weight percent to about 55 weight percent.
Claim 12
Dependent Claim
34 words
A hand moldable biodegradable surgical material according to claim 1 wherein the bioabsorbable material is a star polymer of glycolide and caprolactone and the poly(oxypropylene)poly(oxyethylene) block copolymer has a molecular weight of about 7500.
Claim 13
Dependent Claim
24 words
A method of effecting hemostasis comprising providing a moldable biodegradable surgical material according to claim 1 and applying the material to a suitable locus.
Claim 14
Independent Claim
80 words
A method of producing a hand moldable biodegradable surgical material comprising providing a bioabsorbable polymer and blending the bioabsorbable polymer with a surface active agent selected from the group consisting of sorbitan fatty acid ester and poly(oxypropylene)/poly(oxyethylene) block copolymer, and a leaching agent selected from the group consisting of calcium carbonate, calcium chloride, tricalcium phosphate and hydroxyapatite wherein the leaching agent is present in an amount ranging from about 1 percent to about 70 percent by weight of the material.
Claim 15
Independent Claim
80 words
A method of producing a hand moldable biodegradable surgical material comprising providing a bioabsorbable polymer and blending the bioabsorbable polymer with a surface active agent selected from the group consisting of sorbitan fatty acid ester and poly(oxypropylene)/poly(oxyethylene) block copolymer, and a leaching agent selected from the group consisting of calcium carbonate, calcium chloride, tricalcium phosphate and hydroxyapatite wherein the leaching agent is present in an amount ranging from about 1 percent to about 70 percent by weight of the material.
Claim 16
Dependent Claim
53 words
A hand moldable biodegradable surgical material comprising a blend of bioabsorbable polymer and a leaching agent selected from the group Consisting of calcium carbonate, calcium chloride, tricalcium phosphate and hydroxyapatite wherein the leaching agent is present in an amount ranging from about 1 percent to about 70 percent by weight of the material.
Claim 17
Dependent Claim
53 words
A hand moldable biodegradable surgical material comprising a blend of bioabsorbable polymer and a leaching agent selected from the group Consisting of calcium carbonate, calcium chloride, tricalcium phosphate and hydroxyapatite wherein the leaching agent is present in an amount ranging from about 1 percent to about 70 percent by weight of the material.
Claim 18
Dependent Claim
38 words
A hand moldable biodegradable surgical material according to claim 1 wherein the bioabsorbable polymer is derived from a member selected from the group consisting of hydroxyacids, lactones, carbonates, estheresters, anhydrides, esteramides, orthoesters, and copolymers, terpolymers and blends thereof.
Claim 19
Dependent Claim
29 words
A hand moldable biodegradable surgical material according to claim 14, wherein the bioabsorbable polymer is a star polymer of glycolide and caprolactone and the leaching agent is tricalcium phosphate.
References Cited (Backward Citations)
US3773919A
Cited
US3919163A
Cited
US4027676A
Cited
US4440789A
Cited
US4745160A
Cited
US4595713A
Cited
US4624256A
Cited
US4702917A
Cited
US4837381A
Cited
US4716203A
Cited
US5123912A
Cited
US5143730A
Cited
US5308623A
Cited
US5080665A
Cited
US5312437A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-06-23 | 2000-12-23 | 2001-06-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-06-23 | 2004-12-23 | 2005-06-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-06-23 | 2008-12-23 | 2009-06-24 | $7700.00 | Window Closed / Lapsed |