US5633187A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for fabricating read-only memory cells
Assignee: United Microelectronics Corp
•
Filing: 1995-09-22
•
Granted: 1997-05-27
•
Expires: 2015-09-22
Abstract
Abstract A process for fabricating memory cells of a read-only memory (ROM) device is disclosed. First, a gate oxide layer, a first polysilicon layer, and a first silicide layer are formed subsequently on the surface of a silicon substrate. The layers are patterned to form parallel strip-shaped configurations extending along a first direction on the surface of the silicon substrate. Next, impurities are implanted into the surface of the substrate in the areas between the strip-shaped configurations thereby constituting buried bit lines of the memory cells. Sidewall spacers are then formed on the sidewalls of the strip-shaped configurations. A second silicide layer is then formed over the exposed surface of the buried bit lines in a self-aligned process, thereby improving the electrical conductivity of the buried bit lines. After that, the portions of the second silicide layer and the first polysilicon layer covering the coding region of the memory cells are removed. A thick insulating layer is then formed to cover the entire substrate surface. The surface of the thick insulating layer is then polished to an extent revealing the surface of the first polysilicon. Finally, a second polysilicon layer is formed on the substrate covering the surface of the thick insulating layer and the exposed first polysilicon layer. An etching procedure is then performed to form parallel strip-shaped word lines in the second polysilicon layer that extend in a second direction on the plane of the substrate, with the second direction substantially orthogonal to the first direction. Portions of the first polysilicon not covered by the word lines are also removed in the etching procedure.
Inventors
- 👤 Chen-Chung Hsu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 21:47
CPC Classifications
H; H10; H10B; H10B20/00; H10B20/27; H10B20/30; H10B20/36
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
260 words
A process for fabricating memory cells of a read-only memory device comprising steps of: forming a gate oxide layer, a first polysilicon layer, and a first silicide layer on a surface of a silicon substrate, and patterning the gate oxide layer, the first polysilicon layer and the first silicide layer to form parallel strip-shaped configurations extending along a first direction on the surface of said silicon substrate; implanting impurities into said silicon substrate within areas between said parallel strip-shaped configurations, thereby constituting buried bit lines of said memory cells; forming sidewall spacers on sidewalls of said parallel strip-shaped configurations; forming a second silicide layer on a surface of said buried bit lines in a self-aligned process to improve electrical conductivity of said buried bit lines; removing portions of said first silicide layer and said first polysilicon layer to form a coding region of said read-only memory device; forming an insulating layer to fill said coding region and cover the surface of said silicon substrate; polishing a surface of said insulating layer to an extent revealing a surface of said first polysilicon layer; forming a second polysilicon layer on said silicon substrate covering the surface of said insulating layer and said first polysilicon layer; and etching said second polysilicon layer to form parallel strip-shaped word lines that extend in a second direction on a plane of said silicon substrate, said second direction being substantially orthogonal to said first direction, wherein portions of said first polysilicon layer not being covered by said word lines are also removed in said step of etching.
Claim 2
Dependent Claim
260 words
A process for fabricating memory cells of a read-only memory device comprising steps of: forming a gate oxide layer, a first polysilicon layer, and a first silicide layer on a surface of a silicon substrate, and patterning the gate oxide layer, the first polysilicon layer and the first silicide layer to form parallel strip-shaped configurations extending along a first direction on the surface of said silicon substrate; implanting impurities into said silicon substrate within areas between said parallel strip-shaped configurations, thereby constituting buried bit lines of said memory cells; forming sidewall spacers on sidewalls of said parallel strip-shaped configurations; forming a second silicide layer on a surface of said buried bit lines in a self-aligned process to improve electrical conductivity of said buried bit lines; removing portions of said first silicide layer and said first polysilicon layer to form a coding region of said read-only memory device; forming an insulating layer to fill said coding region and cover the surface of said silicon substrate; polishing a surface of said insulating layer to an extent revealing a surface of said first polysilicon layer; forming a second polysilicon layer on said silicon substrate covering the surface of said insulating layer and said first polysilicon layer; and etching said second polysilicon layer to form parallel strip-shaped word lines that extend in a second direction on a plane of said silicon substrate, said second direction being substantially orthogonal to said first direction, wherein portions of said first polysilicon layer not being covered by said word lines are also removed in said step of etching.
Claim 3
Dependent Claim
26 words
A process according to claim 1, wherein said first silicide layer is a tungsten silicide layer and said second silicide layer is a titanium silicide layer.
Claim 4
Dependent Claim
41 words
A process according to claim 2, wherein said buried bit lines are formed by implanting said impurities at an implantation energy level of about 50 to 100 KeV and a dosage of about 10 14 to 10 16 atoms/cm 2 .
Claim 5
Dependent Claim
15 words
A process according to claim 2, wherein said sidewall spacers are made of silicon dioxide.
Claim 6
Dependent Claim
107 words
A process according to claim 2, wherein said self-aligned process of said step of forming said second silicide layer comprises steps of: sputtering a titanium layer to a thickness of about 300 to 800 angstroms covering a surface of said tungsten silicide layer, said sidewall spacers and said buried bit lines; performing an annealing process at a temperature of about 600° to 900° C., thereby causing a portion of said titanium layer over said buried bit lines to react with said buried bit lines to form said titanium silicide layer; removing a remaining portion of said titanium layer which is not converted into said titanium silicide layer.
Claim 7
Dependent Claim
24 words
A process according to claim 2, wherein said insulating layer is a silicon dioxide layer having a thickness of greater than about 5,000 angstroms.
Claim 8
Dependent Claim
18 words
A process according to claim 2, wherein said step of polishing is a chemical mechanical polishing (CMP) procedure.
Claim 9
Dependent Claim
20 words
A process according to claim 2, wherein said second polysilicon layer has a thickness of about 2,000 to 5,000 angstroms.
Claim 10
Dependent Claim
20 words
A process according to claim 1, wherein said step of forming said gate oxide layer is a thermal oxidation procedure.
Claim 11
Dependent Claim
21 words
A process according to claim 1, wherein said step of forming said gate oxide layer is a chemical vapor deposition procedure.
Claim 12
Dependent Claim
20 words
A process according to claim 2, wherein said tungsten silicide layer has a thickness of about 500 to 1,000 angstroms.
Claim 13
Dependent Claim
34 words
A process according to claim 1, wherein said step of forming said sidewall spacers comprises: depositing a silicon dioxide layer; and performing a reactive ion etching procedure to etch back said silicon dioxide layer.
Claim 14
Dependent Claim
71 words
A process according to claim 1, wherein said step of removing said portions of said first silicide layer and said first polysilicon layer comprises: forming a photoresist layer on said surface of said silicon substrate, a coverage of a pattern of said photoresist layer revealing said coding region; and removing said first silicide layer and said first polysilicon layer by using said photoresist layer as a mask for an etching procedure.
Claim 15
Dependent Claim
41 words
A process according to claim 1, wherein said buried bit lines are formed by implanting said impurities at an implantation energy level of about 50 to 100 KeV and a dosage of about 10 14 to 10 16 atoms/cm 2 .
Claim 16
Dependent Claim
24 words
A process according to claim 1, wherein said insulating layer is a silicon dioxide layer having a thickness of greater than about 5,000 angstroms.
Claim 17
Dependent Claim
18 words
A process according to claim 1, wherein said step of polishing is a chemical mechanical polishing (CMP) procedure.
Claim 18
Dependent Claim
20 words
A process according to claim 1, wherein said second polysilicon layer has a thickness of about 2,000 to 5,000 angstroms.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-05-26 | 2000-11-25 | 2001-05-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-05-26 | 2004-11-25 | 2005-05-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-05-26 | 2008-11-25 | 2009-05-27 | $7700.00 | Window Closed / Lapsed |