Method for forming a contact with activation and silicide forming heat treatment
Assignee: NEC Electronics Corp
•
Filing: 1995-07-18
•
Granted: 1997-04-15
•
Expires: 2015-07-18
Abstract
Abstract A field oxide film 12, an n + -type dispersion layer 13, and an interlayer insulating film 14 are formed on a p-type semiconductor substrate, and a contact hole is formed therein. A titanium film 15 is deposited on the surface formed thus far, and arsenic is ion-implanted into a contact region through the titanium film, forming a phosphorus-dispersed layer. The substrate is heat-treated to activate the impurity in the phosphorus-dispersed layer 16 and to cause titanium and silicon to react with each other, thereby forming a titanium silicide film 17 in the contact region. A metal film is then deposited and patterned into a metal wiring 18 without removing a silicon nitride film 15a which has been produced from the titanium film.
Inventors
- 👤 Hiroshi Itoh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 17:23
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
137 words
A method for manufacturing a semiconductor device, comprising the steps of: (1) forming an insulating film on a surface of a silicon substrate; (2) forming an opening in said insulating film to partially expose the surface of said silicon substrate through said opening; (3) depositing a refractory metal on the surface of said silicon substrate, said insulating film and a sidewall of said opening; (4) implanting impurity ions selectively into the surface of said silicon substrate in said opening through said refractory metal; (5) heat-treating the silicon substrate to activate the implanted impurity ions and to selectively form a refractory metal silicide on the surface of said silicon substrate in said opening; and (6) growing a metal film on the refractory metal which has not been silicided and on the silicide generated in the heat-treating step (5).
Claim 2
Independent Claim
137 words
A method for manufacturing a semiconductor device, comprising the steps of: (1) forming an insulating film on a surface of a silicon substrate; (2) forming an opening in said insulating film to partially expose the surface of said silicon substrate through said opening; (3) depositing a refractory metal on the surface of said silicon substrate, said insulating film and a sidewall of said opening; (4) implanting impurity ions selectively into the surface of said silicon substrate in said opening through said refractory metal; (5) heat-treating the silicon substrate to activate the implanted impurity ions and to selectively form a refractory metal silicide on the surface of said silicon substrate in said opening; and (6) growing a metal film on the refractory metal which has not been silicided and on the silicide generated in the heat-treating step (5).
Claim 3
Dependent Claim
32 words
A method according to claim 1, wherein said refractory metal which is deposited in the depositing step (3) comprises titanium, said refractory metal having a thickness ranging from 10 to 100 nm.
Claim 4
Dependent Claim
30 words
A method according to claim 2, wherein said heat-treating step (5) is carried out in a nitrogen atmosphere in a temperature range from 650° C. to less than 850° C.
Claim 5
Dependent Claim
18 words
A method according to claim 1, wherein said heat-treating step (5) is carried out in a nitrogen atmosphere.
Claim 6
Dependent Claim
13 words
A method according to claim 1, wherein said impurity ions comprise phosphorus ions.
References Cited (Backward Citations)
US4558507A
Cited
JPS59181672A
Cited
JPS60138962A
Cited
US4788160A
Cited
JPH02114634A
Cited
US5102827A
Cited
JPH0329321A
Cited
EP0420748A1
Cited
US5314832A
Cited
US5330921A
Cited
EP0510374A1
Cited
US5286678A
Cited
US5444024A
Cited
JP3029321U
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-04-14 | 2000-10-14 | 2001-04-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-04-14 | 2004-10-14 | 2005-04-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-04-14 | 2008-10-14 | 2009-04-15 | $7700.00 | Window Closed / Lapsed |