Inducing tilted perpendicular alignment in liquid crystals

Claim 2

A substrate prepared by a method for preparing a treated substrate to produce a uniformly tilted perpendicular alignment of a liquid crystal on the substrate, the liquid crystal comprised of elongated molecules whose combined long molecular axes define a macroscopic director, comprising the steps of: supporting the substrate upon a pallet having a defined width; depositing a layer of silica on the substrate using a magnetron in-line sputtering device employing an RF power source and a sputtering target composed of silica with the sputtering target arranged in an elliptical racetrack configuration having a length greater than the width of said pallet so that the sputtering target overhangs the substrate from two opposite ends thereof thereby causing silica to be deposited on the substrate substantially from only the non-overhanging portion of the target; traversing the substrate at a rate of between 2 to 400 centimeters per minute at least once past the sputtering target so that deposition continues until the substrate is covered with a layer of liquid crystal having a thickness of between 250 to about 1500 Angstroms and, with said director at all points across the surface of the substrate having an azimuthal direction that is substantially uniform and with the projection of the director onto the substrate surface being everywhere approximately parallel.

Claim 3

A liquid crystal device prepared by a method for preparing a liquid crystal device having a uniformly tilted perpendicular alignment of liquid crystal on a substrate, the liquid crystal comprised of elongated modules whose combined long molecular axes define a macroscopic director, comprising the steps of: supporting the substrate upon a pallet having a defined width; moving a substrate past a sputtering target in an RF magnetron sputtering device with the sputtering target composed of silica and arranged to form an elliptical racetrack configuration having a length greater than the width of said pallet so that the sputtering target overhangs the substrate from two opposite ends thereof; depositing a layer of silica on the substrate by magnetron in-line sputtering from the non-overhanging portion of said sputtering target; traversing the substrate at least once past the target during the deposition until the substrate is covered with a layer of liquid crystal having a thickness of between 250 to about 1500 Angstroms; treating the silica-coated substrate with a long chain alcohol; and covering the alcohol-treated substrate with a layer of liquid crystal, so that the director at all points across the surface of the substrate has an azimuthal direction that is substantially uniform, and such that the projection of the director onto the substrate surface is everywhere approximately parallel.

Claim 4

A liquid crystal device prepared by a method for preparing a liquid crystal device having a uniformly tilted perpendicular alignment of liquid crystal on a substrate, the liquid crystal comprised of elongated modules whose combined long molecular axes define a macroscopic director, comprising the steps of: supporting the substrate upon a pallet having a defined width; moving a substrate past a sputtering target in an RF magnetron sputtering device with the sputtering target composed of silica and arranged to form an elliptical racetrack configuration having a length greater than the width of said pallet so that the sputtering target overhangs the substrate from two opposite ends thereof; depositing a layer of silica on the substrate by magnetron in-line sputtering from the non-overhanging portion of said sputtering target; traversing the substrate at least once past the target during the deposition until the substrate is covered with a layer of liquid crystal having a thickness of between 250 to about 1500 Angstroms; treating the silica-coated substrate with a long chain alcohol; and covering the alcohol-treated substrate with a layer of liquid crystal, so that the director at all points across the surface of the substrate has an azimuthal direction that is substantially uniform, and such that the projection of the director onto the substrate surface is everywhere approximately parallel.