Reduced notching of polycide gates using silicon anti reflection layer
Assignee: Industrial Technology Research Institute
•
Filing: 1995-05-25
•
Granted: 1997-02-18
•
Expires: 2015-05-25
Abstract
Abstract A method for fabricating MOSFET devices, with narrow gate structures, and narrow spaces between gate structures, has been developed. The addition of a rough surfaced silicon layer, as part of the gate structure, minimizes the amount of reflective and scattered light, resulting during the gate photolithographic processing. The reduction in reflective and scattered greatly enhances the ability to achieve sub-micron lines and spaces. The rough surfaced silicon can remain as a part of the gate structure, and is obtained by chemical vapor deposition of either an amorphous silicon, or a hemi-spherical grained silicon film.
Inventors
- 👤 Chang-Ming Dai
- 👤 Jau-Hwang Ho
- 👤 Lou G. Chine
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 20:26
CPC Classifications
H; H10; H10P; H10P76/00; H10P76/20; H10P76/204; H10P76/2041; H10P76/2043; H10D; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01304; H10D64/01326; Y; Y10; Y10S; Y10S438/00; Y10S438/942; Y10S438/948; Y10S438/952
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
164 words
A method of fabricating a MOSFET device on a semiconductor substrate, using an anti-reflective layer, as part of a photolithographic mask, to create a pattern of gate polycide lines and spaces, comprising the steps of: forming a field oxide region on specific portions of said substrate, while leaving bare silicon on remaining portions of said substrate; growing a gate oxide on said bare silicon; depositing a polysilicon layer on said gate oxide, and on said field oxide regions; forming a metal silicide layer on said polysilicon layer; depositing said anti-reflective layer, comprised of a hemi-spherical grain, silicon layer, on said metal silicide layer, at a temperature between about 550° and 580° C., to a thickness between about 300 and 1000 Angstroms; depositing an oxide layer on said hemi-spherical grain, silicon layer; patterning, to form polycide gate structure on said field oxide region and on said gate oxide; and ion implanting a first conductivity imparting dopant into regions not covered by said polycide gate structure.
Claim 2
Independent Claim
164 words
A method of fabricating a MOSFET device on a semiconductor substrate, using an anti-reflective layer, as part of a photolithographic mask, to create a pattern of gate polycide lines and spaces, comprising the steps of: forming a field oxide region on specific portions of said substrate, while leaving bare silicon on remaining portions of said substrate; growing a gate oxide on said bare silicon; depositing a polysilicon layer on said gate oxide, and on said field oxide regions; forming a metal silicide layer on said polysilicon layer; depositing said anti-reflective layer, comprised of a hemi-spherical grain, silicon layer, on said metal silicide layer, at a temperature between about 550° and 580° C., to a thickness between about 300 and 1000 Angstroms; depositing an oxide layer on said hemi-spherical grain, silicon layer; patterning, to form polycide gate structure on said field oxide region and on said gate oxide; and ion implanting a first conductivity imparting dopant into regions not covered by said polycide gate structure.
Claim 3
Dependent Claim
29 words
The method of claim 1, wherein said gate oxide is grown at a temperature between about 800° and 900° C., to a thickness between about 60 and 160 Angstroms.
Claim 4
Dependent Claim
42 words
The method of claim 1, wherein said polysilicon is grown at a temperature between about 600° and 640° C., to a thickness between about 1000 and 3000 Angstroms, and insitu doped with phosphine to a concentration between about 1E20 to 1E21 atoms/cm3.
Claim 5
Dependent Claim
33 words
The method of claim 1, wherein said metal silicide is tungsten silicide, deposited using LPCVD, at a temperature between about 500° and 650° C., to a thickness between about 1000 and 8000 Angstroms.
Claim 6
Dependent Claim
46 words
The method of claim 1, wherein said metal silicide is tungsten silicide formed by deposition of tungsten, and annealed at a temperature between about 800° and 900° C., for between about 30 and 60 min., to form between about 2000 and 4000 Angstroms of tungsten silicide.
Claim 7
Dependent Claim
31 words
The method of claim 1, wherein said oxide layer is deposited using LPCVD, at a temperature between about 700° and 750° C., to a thickness between about 1000 and 3000 Angstroms.
Claim 8
Dependent Claim
29 words
The method of claim 1, wherein said polycide gate structure is comprised of said oxide layer, said hemi-spherical grain silicon layer, said metal silicide layer, and said polysilicon layer.
Claim 9
Dependent Claim
33 words
The method of claim 1, wherein said first conductivity imparting dopant is arsenic, ion implanted at an energy between about 50 and 80 Kev., at a dose between about 8E15 to 5E15 atoms/cm2.
Claim 10
Independent Claim
170 words
A method of fabricating a MOSFET device, on a semiconductor substrate, using an anti-reflective layer, as part of a photolithographic mask, to create a pattern of gate polycide lines and spaces, comprising the steps of: forming a field oxide region on specific portions of said substrate, while leaving bare silicon on remaining portions of said substrate; growing a gate oxide on said bare silicon; depositing a polysilicon layer on said gate oxide, and on said field oxide regions; forming a metal silicide layer on said polysilicon layer; depositing an oxide layer on said metal silicide layer; depositing said anti-reflective layer, comprised of a hemi-spherical grain, silicon layer, on said oxide layer, at a temperature between about 550° C. and 580° C., to a thickness between about 300 and 1000 Angstroms; patterning to form polycide gate structure on said field oxide region and on said gate oxide; removal of said hemi-spherical grain, silicon layer, and ion implanting a first conductivity imparting dopant into regions not covered by said polycide gate structure.
Claim 11
Independent Claim
170 words
A method of fabricating a MOSFET device, on a semiconductor substrate, using an anti-reflective layer, as part of a photolithographic mask, to create a pattern of gate polycide lines and spaces, comprising the steps of: forming a field oxide region on specific portions of said substrate, while leaving bare silicon on remaining portions of said substrate; growing a gate oxide on said bare silicon; depositing a polysilicon layer on said gate oxide, and on said field oxide regions; forming a metal silicide layer on said polysilicon layer; depositing an oxide layer on said metal silicide layer; depositing said anti-reflective layer, comprised of a hemi-spherical grain, silicon layer, on said oxide layer, at a temperature between about 550° C. and 580° C., to a thickness between about 300 and 1000 Angstroms; patterning to form polycide gate structure on said field oxide region and on said gate oxide; removal of said hemi-spherical grain, silicon layer, and ion implanting a first conductivity imparting dopant into regions not covered by said polycide gate structure.
Claim 12
Dependent Claim
29 words
The method of claim 9, wherein said gate oxide is grown at a temperature between about 800° and 900° C., to a thickness between about 60 and 160 Angstrom.
Claim 13
Dependent Claim
44 words
The method of claim 9, wherein said polysilicon layer is grown at a temperature between about 600° and 640° C., to a thickness between about 1000 and 3000 Angstroms, and is insitu doped with phosphine, to a concentration between about 1E20 to 1E21 atoms/cm3.
Claim 14
Dependent Claim
34 words
The method of claim 9, wherein said metal silicide layer is tungsten silicide, deposited using LPCVD, at a temperature between about 50° and 650° C., to a thickness between about 1000 and 3000 Angstroms.
Claim 15
Dependent Claim
46 words
The method of claim 9, wherein said metal silicide is tungsten silicide, formed by deposition of tungsten, and annealed at a temperature between about 800° and 900° C., for between about 30 and 60 min., to form between about 2000 and 4000 Angstroms of tungsten silicide.
Claim 16
Dependent Claim
31 words
The method of claim 9, wherein said oxide layer is deposited using LPCVD, at a temperature between about 600° and 750° C., to a thickness between about 1000 and 3000 Angstroms.
Claim 17
Dependent Claim
24 words
The method of claim 9, wherein said polycide gate structure is comprised of said oxide layer, said metal silicide layer, and said polysilicon layer.
Claim 18
Dependent Claim
18 words
The method of claim 9, wherein said hemi-spherical grain silicon layer is removed via RIE processing using SF6.
Claim 19
Dependent Claim
33 words
The method of claim 9, wherein said first conductivity imparting dopant is arsenic, ion implanted at an energy between about 50 and 80 Kev., at a dose between about 2E15 and 5E15 atoms/cm2.
References Cited (Backward Citations)
US4740484A
Cited
US4782033A
Cited
US4935380A
Cited
JPS6441245A
Cited
US4933304A
Cited
EP0390509A2
Cited
US5068697A
Cited
JPH047822A
Cited
US5139974A
Cited
US5302538A
Cited
US5312780A
Cited
US5441914A
Cited
US5498558A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-02-18 | 2000-08-19 | 2001-02-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-02-18 | 2004-08-19 | 2005-02-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-02-18 | 2008-08-19 | 2009-02-18 | $7700.00 | Window Closed / Lapsed |