Method of forming salicided self-aligned contact for SRAM cells
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1996-04-22
•
Granted: 1996-11-12
•
Expires: 2016-04-22
Abstract
Abstract This invention provides a method of forming very low resistance self-aligned silicide contacts to devices formed in a silicon integrated circuit substrate while avoiding the formation of stringers or stray silicide conductor paths. The method uses a thin layer of polysilicon which is patterned so as to only cover the contact region of the device being contacted. A layer of metal such as titanium is then deposited and the silicide is formed using rapid thermal annealing. The unreacted metal is then etched away. The primary application is to form a low resistance V ss plate for adjacent pull down transistors in SRAM cells but can be used in any device requiring a low resistance contact to silicon.
Inventors
- 👤 Chue-San Yoo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 14:41
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
353 words
A method of forming self-aligned silicide contacts, comprising the steps of: providing a semiconductor substrate having devices and a first contact region formed therein; providing a number of gate oxide regions formed on said semiconductor substrate; providing a number of gate electrodes equal to the number of said gate oxide regions wherein each one of said gate electrodes is formed on one of said gate oxide regions; forming a first dielectric layer on said semiconductor substrate covering said gate electrodes; forming a first contact opening in said first dielectric layer directly over said first contact region thereby exposing said first contact region; forming a layer of polysilicon having a first polysilicon region and a second polysilicon region on said semiconductor substrate after said first contact opening has been formed, thereby covering said first dielectric layer and said first contact region, wherein said first polysilicon region is that part of said layer of polysilicon directly over said first contact region and said second polysilicon region is the remainder of said layer of polysilicon; etching away said second polysilicon region using photolithographic techniques; forming a metal layer having a first metal region and a second metal region on said semiconductor substrate after etching away said second polysilicon region, thereby covering said first polysilicon region and said first dielectric layer, wherein said first metal region is that part of said metal layer covering said first polysilicon region and said second metal region is the remainder of said metal layer; performing a first rapid thermal annealing of said first metal region, said first polysilicon region, and said first contact region thereby forming a metal silicide at the interface of said first polysilicon region and said first metal region; stripping said second metal region; and performing a second rapid thermal annealing of said first metal region, said first polysilicon region, and said first contact region after stripping said second metal region; forming a second dielectric layer on said semiconductor substrate after performing said second rapid thermal annealing; forming a number of second contact openings in said second dielectric layer; and filling said second contact openings with contact metal.
Claim 2
Independent Claim
353 words
A method of forming self-aligned silicide contacts, comprising the steps of: providing a semiconductor substrate having devices and a first contact region formed therein; providing a number of gate oxide regions formed on said semiconductor substrate; providing a number of gate electrodes equal to the number of said gate oxide regions wherein each one of said gate electrodes is formed on one of said gate oxide regions; forming a first dielectric layer on said semiconductor substrate covering said gate electrodes; forming a first contact opening in said first dielectric layer directly over said first contact region thereby exposing said first contact region; forming a layer of polysilicon having a first polysilicon region and a second polysilicon region on said semiconductor substrate after said first contact opening has been formed, thereby covering said first dielectric layer and said first contact region, wherein said first polysilicon region is that part of said layer of polysilicon directly over said first contact region and said second polysilicon region is the remainder of said layer of polysilicon; etching away said second polysilicon region using photolithographic techniques; forming a metal layer having a first metal region and a second metal region on said semiconductor substrate after etching away said second polysilicon region, thereby covering said first polysilicon region and said first dielectric layer, wherein said first metal region is that part of said metal layer covering said first polysilicon region and said second metal region is the remainder of said metal layer; performing a first rapid thermal annealing of said first metal region, said first polysilicon region, and said first contact region thereby forming a metal silicide at the interface of said first polysilicon region and said first metal region; stripping said second metal region; and performing a second rapid thermal annealing of said first metal region, said first polysilicon region, and said first contact region after stripping said second metal region; forming a second dielectric layer on said semiconductor substrate after performing said second rapid thermal annealing; forming a number of second contact openings in said second dielectric layer; and filling said second contact openings with contact metal.
Claim 3
Dependent Claim
13 words
The method of claim 1 wherein said first dielectric layer is silicon dioxide.
Claim 4
Dependent Claim
20 words
The method of claim 1 wherein said first dielectric layer has a thickness of between about 1000 and 1500 Angstroms.
Claim 5
Dependent Claim
20 words
The method of claim 1 wherein said layer of polysilicon has a thickness of between about 450 and 650 Angstroms.
Claim 6
Dependent Claim
11 words
The method of claim 1 wherein said metal layer is titanium.
Claim 7
Dependent Claim
19 words
The method of claim 1 wherein said metal layer has a thickness of between about 1200 and 1800 Angstroms.
Claim 8
Dependent Claim
12 words
The method of claim 1 wherein said metal silicide is titanium silicide.
Claim 9
Dependent Claim
32 words
The method of claim 1 wherein said first rapid thermal annealing is carried out at a temperature of between about 600° C. and 700° C. for between about 20 and 50 seconds.
Claim 10
Dependent Claim
32 words
The method of claim 1 wherein said second rapid thermal annealing is carried out at a temperature of between about 650° C. and 780° C. for between about 20 and 60 seconds.
Claim 11
Dependent Claim
13 words
The method of claim 1 wherein said gate electrodes are formed of polysilicon.
Claim 12
Independent Claim
306 words
A method of forming self-aligned silicide contacts, comprising the steps of: providing a semiconductor substrate having devices and a first contact region formed therein; forming a first dielectric layer on said semiconductor substrate; forming a first contact opening in said first dielectric layer directly over said first contact region thereby exposing said first contact region; forming a layer of polysilicon having a first polysilicon region and a second polysilicon region on said semiconductor substrate after said first contact opening has been formed, thereby covering said first dielectric layer and said first contact region, wherein said first polysilicon region is that part of said layer of polysilicon directly over said first contact region and said second polysilicon region is the remainder of said layer of polysilicon; etching away said second polysilicon region using photolithographic techniques; forming a metal layer having a first metal region and a second metal region on said semiconductor substrate after etching away said second polysilicon region, thereby covering said first polysilicon region and said first dielectric layer, wherein said first metal region is that part of said metal layer covering said first polysilicon region and said second metal region is the remainder of said metal layer; performing a first rapid thermal annealing of said first metal region, said first polysilicon region, and said first contact region thereby forming a metal silicide at the interface of said first polysilicon region and said first metal region; stripping said second metal region; and performing a second rapid thermal annealing of said first metal region, said first polysilicon region, and said first contact region after stripping said second metal region; forming a second dielectric layer on said semiconductor substrate after performing said second rapid thermal annealing; forming a number of second contact openings in said second dielectric layer; and filling said second contact openings with contact metal.
Claim 13
Independent Claim
306 words
A method of forming self-aligned silicide contacts, comprising the steps of: providing a semiconductor substrate having devices and a first contact region formed therein; forming a first dielectric layer on said semiconductor substrate; forming a first contact opening in said first dielectric layer directly over said first contact region thereby exposing said first contact region; forming a layer of polysilicon having a first polysilicon region and a second polysilicon region on said semiconductor substrate after said first contact opening has been formed, thereby covering said first dielectric layer and said first contact region, wherein said first polysilicon region is that part of said layer of polysilicon directly over said first contact region and said second polysilicon region is the remainder of said layer of polysilicon; etching away said second polysilicon region using photolithographic techniques; forming a metal layer having a first metal region and a second metal region on said semiconductor substrate after etching away said second polysilicon region, thereby covering said first polysilicon region and said first dielectric layer, wherein said first metal region is that part of said metal layer covering said first polysilicon region and said second metal region is the remainder of said metal layer; performing a first rapid thermal annealing of said first metal region, said first polysilicon region, and said first contact region thereby forming a metal silicide at the interface of said first polysilicon region and said first metal region; stripping said second metal region; and performing a second rapid thermal annealing of said first metal region, said first polysilicon region, and said first contact region after stripping said second metal region; forming a second dielectric layer on said semiconductor substrate after performing said second rapid thermal annealing; forming a number of second contact openings in said second dielectric layer; and filling said second contact openings with contact metal.
Claim 14
Dependent Claim
13 words
The method of claim 11 wherein said first dielectric layer is silicon dioxide.
Claim 15
Dependent Claim
20 words
The method of claim 11 wherein said first dielectric layer has a thickness of between about 1000 and 1500 Angstroms.
Claim 16
Dependent Claim
20 words
The method of claim 11 wherein said layer of polysilicon has a thickness of between about 450 and 650 Angstroms.
Claim 17
Dependent Claim
11 words
The method of claim 11 wherein said metal layer is titanium.
Claim 18
Dependent Claim
19 words
The method of claim 11 wherein said metal layer has a thickness of between about 1200 and 1800 Angstroms.
Claim 19
Dependent Claim
12 words
The method of claim 11 wherein said metal silicide is titanium silicide.
Claim 20
Dependent Claim
32 words
The method of claim 11 wherein said first rapid thermal annealing is carried out at a temperature of between about 600° C. and 700° C. for between about 20 and 60 seconds.
Claim 21
Dependent Claim
32 words
The method of claim 11 wherein said second rapid thermal annealing is carried out at a temperature of between about 650° C. and 780° C. for between about 20 and 60 seconds.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-11-12 | 2000-05-13 | 2000-11-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-11-12 | 2004-05-13 | 2004-11-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-11-12 | 2008-05-13 | 2008-11-12 | $7700.00 | Window Closed / Lapsed |