Intercalates and exfoliates formed with oligomers and polymers and composite materials containing same
Assignee: Amcol International Corp
•
Filing: 1995-06-07
•
Granted: 1996-09-03
•
Expires: 2015-06-07
Abstract
Abstract Exfoliated layered silicate material derived from intercalates formed by contacting the layer material, e.g., a phyllosilicate, with an intercalant polymer to sorb or intercalate the polymer between adjacent platelets of the layered material. Sufficient intercalant polymer is sorbed between adjacent platelets to expand the adjacent platelets to a spacing of at least about 10 Å (as measured after water removal), up to about 100 Å and preferably in the range of about 30-45 Å, so that the intercalate easily can be exfoliated, e.g., when mixed with a thermoplastic or thermosetting matrix polymer melt, to provide a matrix polymer/platelet nanocomposite material--the platelets being exfoliated from the intercalate.
Inventors
- 👤 Gary W. Beall
- 👤 Semeon Tsipsursky
- 👤 Anatoliy Sorokin
- 👤 Anatoliy Goldman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 16:08
CPC Classifications
C; C01; C01B; C01B33/00; C01B33/20; C01B33/36; C01B33/38; C01B33/44; C08; C08K; C08K3/00; C08K3/34; C08K9/00; C08K9/04; C11; C11C; C11C5/00; C11C5/002
Claims Analysis
Total Claims: 92
Claim 1
Independent Claim
132 words
An intercalate, capable of being exfoliated, formed by contacting a layered silicate material, having adjacent silicate platelets and having a moisture content of at least about 5% by weight, with a water-soluble intercalant polymer and water, without a coupling agent selected from the group consisting of onium ion and silane coupling agents, to form a mixture of said layered material in contact with an intercalate polymer composition, said intercalate polymer composition having a concentration of said polymer of at least about 2% by weight polymer, to achieve sorption of the water-soluble polymer between said adjacent silicate platelets of the layered silicate material to expand the spacing between a predominance of the adjacent platelets of said layered silicate material to at least about 10 Å, when measured after sorption of the water-soluble polymer.
Claim 2
Dependent Claim
132 words
An intercalate, capable of being exfoliated, formed by contacting a layered silicate material, having adjacent silicate platelets and having a moisture content of at least about 5% by weight, with a water-soluble intercalant polymer and water, without a coupling agent selected from the group consisting of onium ion and silane coupling agents, to form a mixture of said layered material in contact with an intercalate polymer composition, said intercalate polymer composition having a concentration of said polymer of at least about 2% by weight polymer, to achieve sorption of the water-soluble polymer between said adjacent silicate platelets of the layered silicate material to expand the spacing between a predominance of the adjacent platelets of said layered silicate material to at least about 10 Å, when measured after sorption of the water-soluble polymer.
Claim 3
Dependent Claim
25 words
An intercalate in accordance with claim 1, wherein the concentration of intercalant polymer in said intercalant polymer composition is at least about 5% by weight.
Claim 4
Dependent Claim
25 words
An intercalate in accordance with claim 2, wherein the concentration of intercalant polymer in said intercalant polymer composition is at least about 15% by weight.
Claim 5
Dependent Claim
56 words
An intercalate in accordance with claim 3, wherein the concentration of intercalant polymer in said intercalant polymer composition is at least about 20% by weight, and said intercalant polymer includes a functionality selected from the group consisting of an aromatic ring, a carboxyl, a hydroxyl, a carbonyl, an ether, an amine, an amide, and mixtures thereof.
Claim 6
Dependent Claim
25 words
An intercalate in accordance with claim 4, wherein the concentration of intercalant polymer in said intercalant polymer composition is at least about 30% by weight.
Claim 7
Dependent Claim
29 words
An intercalate in accordance with claim 5, wherein the concentration of intercalant polymer in said intercalant polymer composition in the range of about 50% to about 80% by weight.
Claim 8
Dependent Claim
29 words
An intercalate in accordance with claim 5, wherein the concentration of intercalant polymer in said intercalant polymer composition in the range of about 50% to about 100% by weight.
Claim 9
Dependent Claim
35 words
An intercalate in accordance with claim 1, wherein the concentration of intercalant polymer in the intercalant polymer composition is at least about 16% by weight, based on the dry weight of the layered material contacted.
Claim 10
Dependent Claim
40 words
An intercalate in accordance with claim 8, wherein the concentration of intercalant polymer in the intercalant polymer composition is in the range of about 16% to about 70% by weight, based on the dry weight of the layered material contacted.
Claim 11
Dependent Claim
42 words
An intercalate in accordance with claim 9, wherein the concentration of intercalant polymer in the intercalant polymer composition is in the range of about 16% to less than about 35% by weight, based on the dry weight of the layered material contacted.
Claim 12
Dependent Claim
42 words
An intercalate in accordance with claim 9, wherein the concentration of intercalant polymer in the intercalant polymer composition is in the range of about 35% to less than about 55% by weight, based on the dry weight of the layered material contacted.
Claim 13
Dependent Claim
43 words
An intercalate in accordance with claim 9, wherein the concentration of the intercalant polymer in the intercalant polymer composition is in the range of about 55% to less than about 70% by weight, based on the dry weight of the layered material contacted.
Claim 14
Dependent Claim
26 words
An intercalate in accordance with claim 1, wherein the intercalant polymer is selected from the group consisting of polyvinyl pyrrolidone; polyvinyl alcohol; polyvinylimine; and mixtures thereof.
Claim 15
Dependent Claim
26 words
An intercalate in accordance with claim 13, wherein the intercalant polymer is polyvinyl alcohol having less than about 5% by weight acetal substituents in the polymer.
Claim 16
Dependent Claim
26 words
An intercalate in accordance with claim 14, wherein the intercalant polymer is polyvinyl alcohol having less than about 1% by weight acetal substituents in the polymer.
Claim 17
Dependent Claim
26 words
An intercalate in accordance with claim 13, wherein the intercalant polymer has a weight average molecular weight in the range of about 100 to about 100,000.
Claim 18
Dependent Claim
26 words
An intercalate in accordance with claim 13, wherein the intercalant polymer has a weight average molecular weight in the range of about 200 to about 40,000.
Claim 19
Dependent Claim
14 words
An intercalate in accordance with claim 17, wherein the intercalant polymer is polyvinyl pyrrolidone.
Claim 20
Dependent Claim
14 words
An intercalate in accordance with claim 13, wherein the intercalant polymer is a polyvinylimine.
Claim 21
Dependent Claim
26 words
An intercalate in accordance with claim 19, wherein the intercalant polymer has a weight average molecular weight in the range of about 200 to about 40,000.
Claim 22
Dependent Claim
24 words
An intercalate in accordance with claim 1, wherein the intercalant polymer is selected from the group consisting of N-methylpyrrolidone, N-ethylpyrrolidone, N-vinylpyrrolidone, and mixtures thereof.
Claim 23
Independent Claim
95 words
A method of exfoliating a phyllosilicate comprising: contacting the phyllosilicate, having adjacent phyllosilicate platelets and having a moisture content of at least about 7% by weight, with an intercalant polymer-containing composition comprising at least about 2% by weight of a polymer, and without a coupling agent selected from the group consisting of onium ion and silane coupling agents, to achieve intercalation of said polymer between said adjacent phyllosilicate platelets in an amount sufficient to space said adjacent phyllosilicate platelets a distance of at least about 10 Å; and separating the platelets of the intercalated phyllosilicate.
Claim 24
Independent Claim
95 words
A method of exfoliating a phyllosilicate comprising: contacting the phyllosilicate, having adjacent phyllosilicate platelets and having a moisture content of at least about 7% by weight, with an intercalant polymer-containing composition comprising at least about 2% by weight of a polymer, and without a coupling agent selected from the group consisting of onium ion and silane coupling agents, to achieve intercalation of said polymer between said adjacent phyllosilicate platelets in an amount sufficient to space said adjacent phyllosilicate platelets a distance of at least about 10 Å; and separating the platelets of the intercalated phyllosilicate.
Claim 25
Dependent Claim
40 words
The method of claim 22, wherein said intercalant polymer-containing composition includes a water carrier comprising about 5% to about 95% by weight water, capable of dissolving said polymer, based on the total weight of said polymer-containing composition contacting said phyllosilicate.
Claim 26
Dependent Claim
17 words
The method of claim 23, wherein said carrier comprises about 30% to about 40% by weight water.
Claim 27
Dependent Claim
18 words
The method of claim 24, wherein said water carrier comprises about 35% to about 40% by weight water.
Claim 28
Dependent Claim
31 words
The method of claim 23, wherein said carrier comprises about 5% to about 50% by weight water, based on the total weight of the intercalant polymer in said polymer-containing phyllosilicate-contacting composition.
Claim 29
Dependent Claim
154 words
A composite material comprising a matrix polymer selected from the group consisting of a thermoplastic polymer, a thermosetting polymer, and mixtures thereof, in an amount of about 40% to about 99.95% by weight of the composite material, and about 0.05% to about 60% by weight exfoliated platelets of a phyllosilicate material, said platelets derived from an intercalate formed by contacting a phyllosilicate, having adjacent phyllosilicate platelets and having a water content of at least about 7% by weight, with an intercalant polymer, and without a coupling agent selected from the group consisting of onium ion and silane coupling agents, to form an intercalate composition, thereby achieving sorption of the intercalant polymer between the adjacent platelets of the phyllosilicate to expand the spacing between a predominance of the adjacent phyllosilicate platelets to at least about 10 Å, when measured after sorption of the polymer, and thereafter exfoliating the intercalate into a predominance of single platelets.
Claim 30
Dependent Claim
154 words
A composite material comprising a matrix polymer selected from the group consisting of a thermoplastic polymer, a thermosetting polymer, and mixtures thereof, in an amount of about 40% to about 99.95% by weight of the composite material, and about 0.05% to about 60% by weight exfoliated platelets of a phyllosilicate material, said platelets derived from an intercalate formed by contacting a phyllosilicate, having adjacent phyllosilicate platelets and having a water content of at least about 7% by weight, with an intercalant polymer, and without a coupling agent selected from the group consisting of onium ion and silane coupling agents, to form an intercalate composition, thereby achieving sorption of the intercalant polymer between the adjacent platelets of the phyllosilicate to expand the spacing between a predominance of the adjacent phyllosilicate platelets to at least about 10 Å, when measured after sorption of the polymer, and thereafter exfoliating the intercalate into a predominance of single platelets.
Claim 31
Dependent Claim
47 words
A composite material in accordance with claim 27, wherein the phyllosilicate is contacted with said intercalant polymer in the form of a composition comprising an intercalant polymer and water, and wherein the concentration of intercalant polymer in said phyllosilicate-contacting composition is at least about 5% by weight.
Claim 32
Dependent Claim
25 words
A composite material in accordance with claim 28, wherein the concentration of intercalant polymer in said phyllosilicate-contacting composition is at least about 15% by weight.
Claim 33
Dependent Claim
25 words
A composite material in accordance with claim 29, wherein the concentration of intercalant polymer in said phyllosilicate-contacting composition is at least about 20% by weight.
Claim 34
Dependent Claim
25 words
A composite material in accordance with claim 30, wherein the concentration of intercalant polymer in said phyllosilicate-contacting composition is at least about 30% by weight.
Claim 35
Dependent Claim
29 words
A composite material in accordance with claim 31, wherein the concentration of intercalant polymer in said phyllosilicate-contacting composition in the range of about 50% to about 80% by weight.
Claim 36
Dependent Claim
29 words
A composite material in accordance with claim 31, wherein the concentration of intercalant polymer in said phyllosilicate-contacting composition in the range of about 50% to about 100% by weight.
Claim 37
Dependent Claim
34 words
A composite material in accordance with claim 27, wherein the concentration of intercalant polymer in the phyllosilicate-contacting composition is at least about 16% by weight, based on the dry weight of the phyllosilicate contacted.
Claim 38
Dependent Claim
39 words
A composite material in accordance with claim 34, wherein the concentration of intercalant polymer in the phyllosilicate-contacting composition is in the range of about 16% to about 70% by weight, based on the dry weight of the phyllosilicate contacted.
Claim 39
Dependent Claim
41 words
A composite material in accordance with claim 35, wherein the concentration of intercalant polymer in the phyllosilicate-contacting composition is in the range of about 16% to less than about 35% by weight, based on the dry weight of the phyllosilicate contacted.
Claim 40
Dependent Claim
41 words
A composite material in accordance with claim 35, wherein the concentration of intercalant polymer in the phyllosilicate-contacting composition is in the range of about 35% to less than about 55% by weight, based on the dry weight of the phyllosilicate contacted.
Claim 41
Dependent Claim
42 words
A composite material in accordance with claim 35, wherein the concentration of the intercalant polymer in the phyllosilicate-contacting composition is in the range of about 55% to less than about 70% by weight, based on the dry weight of the phyllosilicate contacted.
Claim 42
Dependent Claim
25 words
A composite material in accordance with claim 27, wherein the intercalant polymer is selected from the group consisting of polyvinyl pyrrolidone; polyvinyl alcohol; and polyvinylimine.
Claim 43
Dependent Claim
27 words
A composite material in accordance with claim 39, wherein the intercalant polymer is polyvinyl alcohol having less than about 5% by weight acetal substituents in the polymer.
Claim 44
Dependent Claim
27 words
A composite material in accordance with claim 40, wherein the intercalant polymer is polyvinyl alcohol having less than about 1% by weight acetal substituents in the polymer.
Claim 45
Dependent Claim
27 words
A composite material in accordance with claim 39, wherein the intercalant polymer has a weight average molecular weight in the range of about 100 to about 100,000.
Claim 46
Dependent Claim
27 words
A composite material in accordance with claim 39, wherein the intercalant polymer has a weight average molecular weight in the range of about 200 to about 40,000.
Claim 47
Dependent Claim
15 words
A composite material in accordance with claim 43, wherein the intercalant polymer is polyvinyl pyrrolidone.
Claim 48
Dependent Claim
52 words
A composite material in accordance with claim 27, wherein the matrix polymer is selected from the group consisting of a polyamide; polyvinyl alcohol; polyethylene terephthalate; polybutylene terephthalate; a polymer polymerized from a monomer selected from the group consisting of dihydroxyethyl terephthalate; dihydroxybutyl terephthalate; hydroxyethylmethyl terephthalate; hydroxybutylmethyl terephthalate; polycarbonate; polyvinylimine; and mixtures thereof.
Claim 49
Dependent Claim
42 words
A composite material in accordance with claim 27, wherein the matrix polymer is a mixture of a polymer of hydroxyethyl terephthalate with a polymer polymerized from a monomer selected from the group consisting of dihydroxyethyl terephthalate and dihydroxybutyl terephthalate, and mixtures thereof.
Claim 50
Dependent Claim
15 words
A composite material in accordance with claim 46, wherein the matrix polymer is polyethylene terephthalate.
Claim 51
Independent Claim
183 words
A method of manufacturing a composite material containing about 10% to about 99.95% by weight of a matrix polymer selected from the group consisting of a thermoplastic polymer, a thermosetting polymer, and mixtures thereof, and about 0.05% to about 60% by weight of exfoliated platelets of a phyllosilicate material, said platelets derived from an intercalated phyllosilicate having adjacent phyllosilicate platelets and having a water-soluble polymer intercalated between and electrostatically bonded to a phyllosilicate platelet comprising: contacting the phyllosilicate, having a moisture contact of about 5% by weight to about 30% by weight, with a water-soluble intercalant polymer, and without a coupling agent selected from the group consisting of onium ion and silane coupling agents, to achieve intercalation of said polymer between said adjacent phyllosilicate platelets in an amount sufficient to space said adjacent phyllosilicate platelets a distance of at least about 10 Å; combining the intercalated phyllosilicate with said matrix polymer, and heating the matrix polymer sufficiently to provide for flow of said matrix polymer and exfoliation of said intercalated phyllosilicate into individual platelets; and dispersing said exfoliated platelets throughout said matrix polymer.
Claim 52
Independent Claim
183 words
A method of manufacturing a composite material containing about 10% to about 99.95% by weight of a matrix polymer selected from the group consisting of a thermoplastic polymer, a thermosetting polymer, and mixtures thereof, and about 0.05% to about 60% by weight of exfoliated platelets of a phyllosilicate material, said platelets derived from an intercalated phyllosilicate having adjacent phyllosilicate platelets and having a water-soluble polymer intercalated between and electrostatically bonded to a phyllosilicate platelet comprising: contacting the phyllosilicate, having a moisture contact of about 5% by weight to about 30% by weight, with a water-soluble intercalant polymer, and without a coupling agent selected from the group consisting of onium ion and silane coupling agents, to achieve intercalation of said polymer between said adjacent phyllosilicate platelets in an amount sufficient to space said adjacent phyllosilicate platelets a distance of at least about 10 Å; combining the intercalated phyllosilicate with said matrix polymer, and heating the matrix polymer sufficiently to provide for flow of said matrix polymer and exfoliation of said intercalated phyllosilicate into individual platelets; and dispersing said exfoliated platelets throughout said matrix polymer.
Claim 53
Dependent Claim
37 words
The method of claim 48, wherein said phyllosilicate is contacted with said intercalant polymer in an aqueous solution comprising about 5% to about 95% by weight water, based on the total weight of said intercalant polymer-containing solution.
Claim 54
Dependent Claim
15 words
The method of claim 49, wherein said solution comprises about 10% to about 90% water.
Claim 55
Dependent Claim
15 words
The method of claim 50, wherein said solution comprises about 30% to about 40% water.
Claim 56
Dependent Claim
17 words
The method of claim 51, wherein said solution comprises about 35% to about 40% by weight water.
Claim 57
Independent Claim
134 words
A method of exfoliating a phyllosilicate comprising: contacting the phyllosilicate, having adjacent phyllosilicate platelets and having a moisture content of at least about 7% by weight, with a polymerizable monomer-containing composition comprising at least about 2% by weight of said polymerizable monomer and polymerizing said polymerizable monomer while in contact with said phyllosilicate to form a water-soluble intercalant polymer in-situ, said water-soluble polymer present in an amount of at least about 16% based on the dry weight of the phyllosilicate, to achieve intercalation of said polymer between said adjacent phyllosilicate platelets, without a coupling agent selected from the group consisting of onium ion and silane coupling agents, in an amount sufficient to space said adjacent phyllosilicate platelets to a distance of at least about 10 Å; and separating the platelets of the intercalated phyllosilicate.
Claim 58
Independent Claim
134 words
A method of exfoliating a phyllosilicate comprising: contacting the phyllosilicate, having adjacent phyllosilicate platelets and having a moisture content of at least about 7% by weight, with a polymerizable monomer-containing composition comprising at least about 2% by weight of said polymerizable monomer and polymerizing said polymerizable monomer while in contact with said phyllosilicate to form a water-soluble intercalant polymer in-situ, said water-soluble polymer present in an amount of at least about 16% based on the dry weight of the phyllosilicate, to achieve intercalation of said polymer between said adjacent phyllosilicate platelets, without a coupling agent selected from the group consisting of onium ion and silane coupling agents, in an amount sufficient to space said adjacent phyllosilicate platelets to a distance of at least about 10 Å; and separating the platelets of the intercalated phyllosilicate.
Claim 59
Dependent Claim
110 words
An intercalate, capable of being exfoliated, formed by contacting a layered silicate material, having adjacent silicate platelets and having a moisture content of at least about 5% by weight, with polyvinylimine and water to form a mixture of said layered material in contact with an intercalate polymer composition, said intercalate polymer composition having a concentration of polyvinylimine of at least about 2% by weight polymer, to achieve sorption of the polyvinylimine between said adjacent silicate platelets of the layered silicate material to expand the spacing between a predominance of the adjacent platelets of said layered silicate material to at least about 10 Å, when measured after sorption of the polyvinylimine.
Claim 60
Dependent Claim
110 words
An intercalate, capable of being exfoliated, formed by contacting a layered silicate material, having adjacent silicate platelets and having a moisture content of at least about 5% by weight, with polyvinylimine and water to form a mixture of said layered material in contact with an intercalate polymer composition, said intercalate polymer composition having a concentration of polyvinylimine of at least about 2% by weight polymer, to achieve sorption of the polyvinylimine between said adjacent silicate platelets of the layered silicate material to expand the spacing between a predominance of the adjacent platelets of said layered silicate material to at least about 10 Å, when measured after sorption of the polyvinylimine.
Claim 61
Dependent Claim
27 words
An intercalate in accordance with claim 54, wherein the polyvinylimine intercalant polymer has a weight average molecular weight in the range of about 200 to about 40,000.
Claim 62
Independent Claim
103 words
A method of exfoliating a phyllosilicate comprising: contacting the phyllosilicate, having adjacent phyllosilicate platelets and having a moisture content of at least about 7% by weight, with an intercalant polymer-containing composition comprising at least about 2% by weight of a polymer and a carrier comprising about 5% to about 95% water, capable of dissolving said polymer, based on the total weight of said intercalant polymer-containing composition, to achieve intercalation of said polymer between said adjacent phyllosilicate platelets in an amount sufficient to space said adjacent phyllosilicate platelets a distance of at least about 10 Å; and separating the platelets of the intercalated phyllosilicate.
Claim 63
Independent Claim
103 words
A method of exfoliating a phyllosilicate comprising: contacting the phyllosilicate, having adjacent phyllosilicate platelets and having a moisture content of at least about 7% by weight, with an intercalant polymer-containing composition comprising at least about 2% by weight of a polymer and a carrier comprising about 5% to about 95% water, capable of dissolving said polymer, based on the total weight of said intercalant polymer-containing composition, to achieve intercalation of said polymer between said adjacent phyllosilicate platelets in an amount sufficient to space said adjacent phyllosilicate platelets a distance of at least about 10 Å; and separating the platelets of the intercalated phyllosilicate.
Claim 64
Dependent Claim
17 words
The method of claim 56, wherein said carrier comprises about 30% to about 40% by weight water.
Claim 65
Dependent Claim
18 words
The method of claim 57, wherein said water carrier comprises about 35% to about 40% by weight water.
Claim 66
Dependent Claim
31 words
The method of claim 56, wherein said carrier comprises about 5% to about 50% by weight water, based on the total weight of the intercalant polymer in said polymer-containing phyllosilicate-contacting composition.
Claim 67
Dependent Claim
158 words
A composite material comprising a matrix polymer selected from the group consisting of a thermoplastic polymer, a thermosetting polymer, and mixtures thereof, in an amount of about 40% to about 99.95% by weight of the composite material, and about 0.05% to about 60% by weight exfoliated platelets of a phyllosilicate material, said platelets derived from an intercalate formed by contacting a phyllosilicate, having adjacent phyllosilicate platelets and having a water content of at least about 7% by weight, with an intercalant polymer composition comprising an intercalant polymer and water and wherein the concentration of said intercalant polymer in said intercalant composition is at least about 5% by weight, thereby achieving sorption of the intercalant polymer between the adjacent platelets of the phyllosilicate to expand the spacing between a predominance of the adjacent phyllosilicate platelets to at least about 10 Å, when measured after sorption of the polymer, and thereafter exfoliating the intercalate into a predominance of single platelets.
Claim 68
Dependent Claim
158 words
A composite material comprising a matrix polymer selected from the group consisting of a thermoplastic polymer, a thermosetting polymer, and mixtures thereof, in an amount of about 40% to about 99.95% by weight of the composite material, and about 0.05% to about 60% by weight exfoliated platelets of a phyllosilicate material, said platelets derived from an intercalate formed by contacting a phyllosilicate, having adjacent phyllosilicate platelets and having a water content of at least about 7% by weight, with an intercalant polymer composition comprising an intercalant polymer and water and wherein the concentration of said intercalant polymer in said intercalant composition is at least about 5% by weight, thereby achieving sorption of the intercalant polymer between the adjacent platelets of the phyllosilicate to expand the spacing between a predominance of the adjacent phyllosilicate platelets to at least about 10 Å, when measured after sorption of the polymer, and thereafter exfoliating the intercalate into a predominance of single platelets.
Claim 69
Dependent Claim
25 words
A composite material in accordance with claim 60, wherein the concentration of intercalant polymer in said phyllosilicate-contacting composition is at least about 15% by weight.
Claim 70
Dependent Claim
25 words
A composite material in accordance with claim 61, wherein the concentration of intercalant polymer in said phyllosilicate-contacting composition is at least about 20% by weight.
Claim 71
Dependent Claim
25 words
A composite material in accordance with claim 62, wherein the concentration of intercalant polymer in said phyllosilicate-contacting composition is at least about 30% by weight.
Claim 72
Dependent Claim
29 words
A composite material in accordance with claim 63, wherein the concentration of intercalant polymer in said phyllosilicate-contacting composition in the range of about 50% to about 80% by weight.
Claim 73
Dependent Claim
29 words
A composite material in accordance with claim 63, wherein the concentration of intercalant polymer in said phyllosilicate-contacting composition in the range of about 50% to about 100% by weight.
Claim 74
Dependent Claim
34 words
A composite material in accordance with claim 60, wherein the concentration of intercalant polymer in the phyllosilicate-contacting composition is at least about 16% by weight, based on the dry weight of the phyllosilicate contacted.
Claim 75
Dependent Claim
39 words
A composite material in accordance with claim 66, wherein the concentration of intercalant polymer in the phyllosilicate-contacting composition is in the range of about 16% to about 70% by weight, based on the dry weight of the phyllosilicate contacted.
Claim 76
Dependent Claim
41 words
A composite material in accordance with claim 67, wherein the concentration of intercalant polymer in the phyllosilicate-contacting composition is in the range of about 16% to less than about 35% by weight, based on the dry weight of the phyllosilicate contacted.
Claim 77
Dependent Claim
41 words
A composite material in accordance with claim 67, wherein the concentration of intercalant polymer in the phyllosilicate-contacting composition is in the range of about 35% to less than about 55% by weight, based on the dry weight of the phyllosilicate contacted.
Claim 78
Dependent Claim
42 words
A composite material in accordance with claim 67, wherein the concentration of the intercalant polymer in the phyllosilicate-contacting composition is in the range of about 55% to less than about 70% by weight, based on the dry weight of the phyllosilicate contacted.
Claim 79
Dependent Claim
25 words
A composite material in accordance with claim 60, wherein the intercalant polymer is selected from the group consisting of polyvinyl pyrrolidone; polyvinyl alcohol; and polyvinylimine.
Claim 80
Dependent Claim
27 words
A composite material in accordance with claim 71, wherein the intercalant polymer is polyvinyl alcohol having less than about 5% by weight acetal substituents in the polymer.
Claim 81
Dependent Claim
27 words
A composite material in accordance with claim 72, wherein the intercalant polymer is polyvinyl alcohol having less than about 1% by weight acetal substituents in the polymer.
Claim 82
Dependent Claim
27 words
A composite material in accordance with claim 71, wherein the intercalant polymer has a weight average molecular weight in the range of about 100 to about 100,000.
Claim 83
Dependent Claim
27 words
A composite material in accordance with claim 71, wherein the intercalant polymer has a weight average molecular weight in the range of about 200 to about 40,000.
Claim 84
Dependent Claim
15 words
A composite material in accordance with claim 75, wherein the intercalant polymer is polyvinyl pyrrolidone.
Claim 85
Dependent Claim
52 words
A composite material in accordance with claim 60, wherein the matrix polymer is selected from the group consisting of a polyamide; polyvinyl alcohol; polyethylene terephthalate; polybutylene terephthalate; a polymer polymerized from a monomer selected from the group consisting of dihydroxyethyl terephthalate; dihydroxybutyl terephthalate; hydroxyethylmethyl terephthalate; hydroxybutylmethyl terephthalate; polycarbonate; polyvinylimine; and mixtures thereof.
Claim 86
Dependent Claim
42 words
A composite material in accordance with claim 60, wherein the matrix polymer is a mixture of a polymer of hydroxyethyl terephthalate with a polymer polymerized from a monomer selected from the group consisting of dihydroxyethyl terephthalate and dihydroxybutyl terephthalate, and mixtures thereof.
Claim 87
Dependent Claim
15 words
A composite material in accordance with claim 78, wherein the matrix polymer is polyethylene terephthalate.
Claim 88
Independent Claim
188 words
A method of manufacturing a composite material containing about 10% to about 99.95% by weight of a matrix polymer selected from the group consisting of a thermoplastic polymer, a thermosetting polymer, and mixtures thereof, and about 0.05% to about 60% by weight of exfoliated platelets of a phyllosilicate material, said platelets derived from an intercalated phyllosilicate having adjacent phyllosilicate platelets and having a water-soluble polymer intercalated between and electrostatically bonded to a phyllosilicate platelet comprising: contacting the phyllosilicate, having a moisture contact of about 5% by weight to about 30% by weight, with a water-soluble intercalant polymer in an aqueous solution comprising about 5% to about 95% by weight water, based on the total weight of said aqueous solution, to achieve intercalation of said polymer between said adjacent phyllosilicate platelets in an amount sufficient to space said adjacent phyllosilicate platelets a distance of at least about 10 Å; combining the intercalated phyllosilicate with said matrix polymer, and heating the matrix polymer sufficiently to provide for flow of said matrix polymer and exfoliation of said intercalated phyllosilicate into individual platelets; and dispersing said exfoliated platelets throughout said matrix polymer.
Claim 89
Independent Claim
188 words
A method of manufacturing a composite material containing about 10% to about 99.95% by weight of a matrix polymer selected from the group consisting of a thermoplastic polymer, a thermosetting polymer, and mixtures thereof, and about 0.05% to about 60% by weight of exfoliated platelets of a phyllosilicate material, said platelets derived from an intercalated phyllosilicate having adjacent phyllosilicate platelets and having a water-soluble polymer intercalated between and electrostatically bonded to a phyllosilicate platelet comprising: contacting the phyllosilicate, having a moisture contact of about 5% by weight to about 30% by weight, with a water-soluble intercalant polymer in an aqueous solution comprising about 5% to about 95% by weight water, based on the total weight of said aqueous solution, to achieve intercalation of said polymer between said adjacent phyllosilicate platelets in an amount sufficient to space said adjacent phyllosilicate platelets a distance of at least about 10 Å; combining the intercalated phyllosilicate with said matrix polymer, and heating the matrix polymer sufficiently to provide for flow of said matrix polymer and exfoliation of said intercalated phyllosilicate into individual platelets; and dispersing said exfoliated platelets throughout said matrix polymer.
Claim 90
Dependent Claim
15 words
The method of claim 80, wherein said solution comprises about 10% to about 90% water.
Claim 91
Dependent Claim
15 words
The method of claim 81, wherein said solution comprises about 30% to about 40% water.
Claim 92
Dependent Claim
17 words
The method of claim 82, wherein said solution comprises about 35% to about 40% by weight water.
References Cited (Backward Citations)
US4125411A
Cited
US3419517A
Cited
US3773708A
Cited
US4251576A
Cited
US3929678A
Cited
US4210572A
Cited
US4472538A
Cited
US4546145A
Cited
US4400485A
Cited
US4434075A
Cited
US4431755A
Cited
US4798766A
Cited
US4613542A
Cited
US4624982A
Cited
US4739007A
Cited
US4789403A
Cited
US5229451A
Cited
US4842651A
Cited
US4920171A
Cited
US4889885A
Cited
US4894411A
Cited
US4810734A
Cited
US5164440A
Cited
US5248720A
Cited
EP0358415A1
Cited
US5091462A
Cited
US5206284A
Cited
US5102948A
Cited
US5032546A
Cited
US5032547A
Cited
US5164460A
Cited
EP0479031A1
Cited
WO1993004118A1
Cited
US5385776A
Cited
US5326500A
Cited
US5340558A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-09-03 | 2000-03-04 | 2000-09-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-09-03 | 2004-03-04 | 2004-09-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-09-03 | 2008-03-04 | 2008-09-03 | $7700.00 | Window Closed / Lapsed |