Anionically modified organophilic clays and their preparation

Claim 2

An organophilic clay gellant comprising the reaction product of: a. a smectite-type clay having a cation exchange capacity of at least 75 milliequivalents per 100 grams of said clay; b. an organic anion in an amount ranging from 5 to 100 milliequivalents per 100 grams of said smectite-type clay, 100% active clay basis; and c. an organic cation having the formula ##STR9## wherein R 1 is selected from the group consisting of a β,γ-unsaturated alkyl group having less than 7 aliphatic carbon atoms, a hydroxyalkyl group having 2 to 6 aliphatic carbon atoms and mixtures thereof, R 2 is a long chain alkyl group having 12 to 60 carbon atoms, R 3 and R 4 are individually selected from the group consisting of a β,γ-unsaturated alkyl group having less than 7 aliphatic carbon atoms, a hydroxyalkyl group having 2 to 6 carbon atoms, an aralkyl group having 1 to 22 carbon atoms in the alkyl portion, an alkyl group having from 1 to 22 carbon atoms and mixtures thereof and X is selected from the group consisting of phosphorous and nitrogen, said organic cation being present in an amount sufficient to at least satisfy the cation exchange capacity of the smectite-type clay and the cationic activity of the organic anion, wherein the cation exchange sites of the smectite-type clay are substituted with the organic cation and wherein an organic cation-organic anion complex is intercalated with the clay.

Claim 3

The gellant of claim 1, wherein the β,γ-unsaturated alkyl group is selected from a group consisting of cyclic groups, acyclic alkyl groups having less than 7 carbon atoms, acyclic alkyl groups substituted with aromatic groups, and aromatic groups substituted with aliphatic groups.

Claim 4

The gellant of claim 1 wherein the hydroxyalkyl group is selected from a group consisting of cyclic groups and aliphatic groups having 2 to 6 carbon atoms with the hydroxy substitution on C 2 to C 6 .

Claim 5

The gellant of claim 2 wherein R 2 has from 12 to 22 carbon atoms.

Claim 6

The gellant of claim 4 wherein R 2 is along chain fatty acid group.

Claim 7

The gellant of claim 1 wherein the organic anion is derived from an organic acid having a pK A less than about 11.0.

Claim 8

The gellant of claim 1 wherein the smectite-type clay is selected from the group consisting of hectorite and sodium bentonite.

Claim 9

The gellant of claim 1 wherein the amount of said organic cation is from 80 to 200 milliequivalents per 100 grams of clay, 100% active clay basis.

Claim 10

The gellant of claim 1 wherein the amount of said organic cation is from 100 to 160 milliequivalents per 100 grams of clay, 100% active clay basis.

Claim 11

A process for preparing an organophilic clay gellant which comprises: a. preparing an aqueous slurry of smectite-type clay having a cation exchange capacity of at least 75 milliequivalents per 100 grams of clay, said clay ranging from about 1 to about 80% by weight of slurry; b. heating the slurry to a temperature between 20° C. and 100° C.; c. adding from about 5 to 100 milliequivalents of an organic anion per 100 grams of clay, 100% active clay basis and an organic cation compound, wherein said organic cation has the formula: ##STR10## wherein R 1 is selected from the group consisting of a β,γ-unsaturated alkyl group having less than 7 aliphatic carbon atoms, a hydroxyalkyl group having 2 to 6 aliphatic carbon atoms, and mixtures thereof; R 2 is a long chain alkyl group having 12 to 60 carbon atoms; R 3 and R 4 are individually selected from the group consisting of a β,γ-unsaturated alkyl group having less than 7 aliphatic carbon atoms, a hydroxyalkyl group having 2 to 6 aliphatic carbon atoms, an aralkyl group having 1 to 22 carbon atoms in the alkyl portion, an alkyl group having from 1 to 22 carbon atoms and mixtures thereof; X is selected from a group consisting of phosphorous and nitrogen; said organic cation compound is used in a sufficient amount to at least satisfy the cation exchange capacity of the smectite-type clay and the cationic activity of the organic anion while agitating the reaction solution; and d. reacting the mixture for a sufficient time to form a reaction product comprising an organic cation-organic anion complex which is intercalated with the smectite-type clay and the cation exchange sites of the smectite-type clay are substituted with the organic cation.

Claim 12

A process for preparing an organophilic clay gellant which comprises: a. preparing an aqueous slurry of smectite-type clay having a cation exchange capacity of at least 75 milliequivalents per 100 grams of clay, said clay ranging from about 1 to about 80% by weight of slurry; b. heating the slurry to a temperature between 20° C. and 100° C.; c. adding from about 5 to 100 milliequivalents of an organic anion per 100 grams of clay, 100% active clay basis and an organic cation compound, wherein said organic cation has the formula: ##STR10## wherein R 1 is selected from the group consisting of a β,γ-unsaturated alkyl group having less than 7 aliphatic carbon atoms, a hydroxyalkyl group having 2 to 6 aliphatic carbon atoms, and mixtures thereof; R 2 is a long chain alkyl group having 12 to 60 carbon atoms; R 3 and R 4 are individually selected from the group consisting of a β,γ-unsaturated alkyl group having less than 7 aliphatic carbon atoms, a hydroxyalkyl group having 2 to 6 aliphatic carbon atoms, an aralkyl group having 1 to 22 carbon atoms in the alkyl portion, an alkyl group having from 1 to 22 carbon atoms and mixtures thereof; X is selected from a group consisting of phosphorous and nitrogen; said organic cation compound is used in a sufficient amount to at least satisfy the cation exchange capacity of the smectite-type clay and the cationic activity of the organic anion while agitating the reaction solution; and d. reacting the mixture for a sufficient time to form a reaction product comprising an organic cation-organic anion complex which is intercalated with the smectite-type clay and the cation exchange sites of the smectite-type clay are substituted with the organic cation.

Claim 13

The process of claim 10 wherein the organic cation is selected from the group consisting of quaternary ammonium salts and phosphonium salts containing at least one lineal or branched alkyl group having 12 to 22 carbon atoms.

Claim 14

The process of claim 10 wherein the organic anion is derived from an organic acid having a pK A less than about 11.0.

Claim 15

The process of claim 10 wherein the smectite-type clay is selected from the group consisting of hectorite and sodium bentonite.

Claim 16

The process of claim 10 wherein the amount of said organic anion is from 10 to 50 milliequivalents per 100 grams of said clay, 100% active clay basis.

Claim 17

The process of claim 10 wherein the amount of said organic cation compound is from 80 to 200 milliequivalents per 100 grams of clay, 100% active clay basis.

Claim 18

The process of claim 10 wherein the organic anion is added to the smectite-type clay prior to the addition of the organic cation compound.

Claim 19

The process of claim 10 wherein the organic anion and organic cation compound are added to the smectite-type clay in the form of an organic cation-organic anion complex.