Nitridation of titanium, for use with tungsten filled contact holes
Assignee: Vanguard International Semiconductor Corp
•
Filing: 1995-10-27
•
Granted: 1996-09-03
•
Expires: 2015-10-27
Abstract
Abstract A process has been developed that allows small diameter contact holes to be filled with chemical vapor deposited tungsten, without tungsten peeling from the sides of the contact hole. The process consists of initially depositing an adhesive layer of titanium in the contact hole, followed by a rapid thermal anneal cycle, in an ammonia ambient, for purposes of creating a thin, uniform, barrier layer of titanium nitride. The titanium nitride protects the underlying titanium adhesion layer from the by-products introduced during the tungsten deposition, specifically the evolution of fluorine ions resulting from the decomposition of tungsten hexafluoride.
Inventors
- 👤 Ching-Ying Lee
- 👤 Shaw-Tzeng Hsia
- 👤 Haw Yen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 23:14
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/032; H10W20/047; H10W20/048; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10W20/033; H10W20/056
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
247 words
A method for fabricating a MOSFET device, on a semiconductor substrate, using a contact hole lined with adhesive and barrier layers, and filled with a metal, to provide electrical contact between an active device region in said semiconductor substrate, and an overlying interconnect metallization layer, comprising the steps of: providing device elements on said semiconductor substrate; depositing a dielectric layer on said semiconductor substrate, including depositing on said device elements; photolithographic processing to open a region in photoresist, exposing said dielectric layer, directly over a specific region of said device element; anisotropic etching of said dielectric layer, in the opened region in said photoresist, to create a contact hole to said specific region of said device element; ion implanting a first conductivity imparting dopant into said specific region of said device element, to create said active device region; surface cleaning of said active device region; deposition of an adhesive layer on said dielectric layer, on sides of said contact hole, and on a surface of said active device region; thermal annealing in an ammonia ambient to convert a surface of said adhesive layer to a first barrier layer; deposition of a second barrier layer on said first barrier layer; deposition of said metal, on said second barrier layer completely filling said contact hole; etchback of said metal, to remove said metal from all areas except in said contact hole; deposition of said interconnect metallization layer; and patterning of said interconnect metallization layer to form metal interconnect structure.
Claim 2
Independent Claim
247 words
A method for fabricating a MOSFET device, on a semiconductor substrate, using a contact hole lined with adhesive and barrier layers, and filled with a metal, to provide electrical contact between an active device region in said semiconductor substrate, and an overlying interconnect metallization layer, comprising the steps of: providing device elements on said semiconductor substrate; depositing a dielectric layer on said semiconductor substrate, including depositing on said device elements; photolithographic processing to open a region in photoresist, exposing said dielectric layer, directly over a specific region of said device element; anisotropic etching of said dielectric layer, in the opened region in said photoresist, to create a contact hole to said specific region of said device element; ion implanting a first conductivity imparting dopant into said specific region of said device element, to create said active device region; surface cleaning of said active device region; deposition of an adhesive layer on said dielectric layer, on sides of said contact hole, and on a surface of said active device region; thermal annealing in an ammonia ambient to convert a surface of said adhesive layer to a first barrier layer; deposition of a second barrier layer on said first barrier layer; deposition of said metal, on said second barrier layer completely filling said contact hole; etchback of said metal, to remove said metal from all areas except in said contact hole; deposition of said interconnect metallization layer; and patterning of said interconnect metallization layer to form metal interconnect structure.
Claim 3
Dependent Claim
20 words
The method of claim 1, wherein said device element on said semiconductor substrate, is an N type field effect transistor.
Claim 4
Dependent Claim
26 words
The method of claim 1, wherein said dielectric layer is silicon oxide, deposited using LPCVD or PECVD processing, to a thickness between 6000 and 14000 Angstroms.
Claim 5
Dependent Claim
36 words
The method of claim 1, wherein said contact hole is formed via anisotropic reactive ion etching, using CHF 3 +CF 4 +argon, where a diameter of said contact hole is between about 0.3 and 0.7 uM.
Claim 6
Dependent Claim
35 words
The method of claim 1, wherein said first conductivity imparting dopant is arsenic, ion implanted at an energy between about 20 and 50 Kev., at a dose between about 1E15 and 5E15 atoms/cm 2 .
Claim 7
Dependent Claim
41 words
The method of claim 1, wherein surface cleaning of said active device region is performed using a solution of water and hydrofluoric acid, at a temperature between about 20° and 25° C., for a time between about 75 and 105 seconds.
Claim 8
Dependent Claim
24 words
The method of claim 1, wherein said adhesive layer is titanium, deposited using r.f. sputtering, to a thickness between about 300 and 1000 Angstroms.
Claim 9
Dependent Claim
124 words
The method of claim 1, wherein thermal annealing of said adhesive layer is performed by; loading of wafers in thermal anneal furnace at a temperature between about 350°and 450° C., in a nitrogen flow of about 20 liters/min., ramp up and stabilization at a temperature between about 575° and 625° C., for between about 45 and 75 seconds in an ammonia flow between about 2 and 6 liters/min., another ramp up and stabilization step at a temperature between about 700° and 740° C., for between about 10 and 40 seconds in an ammonia flow between about 2 to 6 liters/min., and a ramp down and wafer unload in a nitrogen flow of about 20 liters/min., at a temperature between about 350° and 450° C.
Claim 10
Dependent Claim
27 words
The method of claim 1, wherein thermal annealing of said adhesive layer is performed in an ammonia ambient at a temperature between about 700 and 740° C.
Claim 11
Dependent Claim
48 words
The method of claim 1, wherein thermal annealing of said adhesive layers in an ammonia ambient, results in the formation of said first barrier layer, to a thickness between about 200 and 800 Angstroms, while leaving between about 100 and 500 Angstroms of underlying said adhesive layer, unreacted.
Claim 12
Dependent Claim
33 words
The method of claim 1, wherein thermal annealing results in the formation of a titanium disilicide layer, at the bottom of said contact hole, to a thickness between about 100 to 300 Angstroms.
Claim 13
Dependent Claim
37 words
The method of claim 1, wherein said metal is tungsten, deposited using LPCVD processing, at a temperature between about 400° and 500° C., to a thickness between about 5000 to 9000 Angstroms, using a tungsten hexafluoride source.
Claim 14
Independent Claim
299 words
A method for fabricating a MOSFET device, on semiconductor substrate, using a contact hole lined with titanium for adhesion purposes, titanium nitride for barrier purposes, and filled with tungsten, to provide electrical contact between an active device region and an overlying interconnect metallization, comprising the steps of: providing device elements on said semiconductor substrate; depositing a dielectric layer on said semiconductor substrate, including deposition on said device elements; photolithographic processing to open a region in photoresist, exposing said dielectric layer, directly over a specific region of said device element; anisotropic etching of said dielectric layers in opened region of said photoresist, to create a contact hole to said specific region of said device element; ion implanting a first conductivity imparting dopant, into said specific region, of said device element, to create a doped N type region; surface cleaning of said doped N type region; deposition of said titanium adhesion layer on said dielectric layer, on sides of said contact hole, and on said doped N type region; thermal annealing in an ammonia ambient to convert a surface of said titanium adhesion layer, to a said first titanium nitride barrier layer, while leaving a portion of underlying said titanium adhesion layer on sides of said contact hole, and forming a titanium disilicide layer at bottom of said contact hole, between overlying said first titanium nitride barrier layer and underlying said heavily doped N type region; depositing a second titanium nitride barrier layer, on said first titanium nitride barrier layer; deposition of said tungsten, on said second titanium nitride barrier layer, completely filling said contact hole; etchback of said tungsten, to remove said tungsten from all areas except in said contact hole; deposition of said interconnect metallization layer; and patterning of said interconnect metallization layer to form a metal interconnect structure.
Claim 15
Independent Claim
299 words
A method for fabricating a MOSFET device, on semiconductor substrate, using a contact hole lined with titanium for adhesion purposes, titanium nitride for barrier purposes, and filled with tungsten, to provide electrical contact between an active device region and an overlying interconnect metallization, comprising the steps of: providing device elements on said semiconductor substrate; depositing a dielectric layer on said semiconductor substrate, including deposition on said device elements; photolithographic processing to open a region in photoresist, exposing said dielectric layer, directly over a specific region of said device element; anisotropic etching of said dielectric layers in opened region of said photoresist, to create a contact hole to said specific region of said device element; ion implanting a first conductivity imparting dopant, into said specific region, of said device element, to create a doped N type region; surface cleaning of said doped N type region; deposition of said titanium adhesion layer on said dielectric layer, on sides of said contact hole, and on said doped N type region; thermal annealing in an ammonia ambient to convert a surface of said titanium adhesion layer, to a said first titanium nitride barrier layer, while leaving a portion of underlying said titanium adhesion layer on sides of said contact hole, and forming a titanium disilicide layer at bottom of said contact hole, between overlying said first titanium nitride barrier layer and underlying said heavily doped N type region; depositing a second titanium nitride barrier layer, on said first titanium nitride barrier layer; deposition of said tungsten, on said second titanium nitride barrier layer, completely filling said contact hole; etchback of said tungsten, to remove said tungsten from all areas except in said contact hole; deposition of said interconnect metallization layer; and patterning of said interconnect metallization layer to form a metal interconnect structure.
Claim 16
Dependent Claim
20 words
The method of claim 13, wherein said device element in said semiconductor substrates is an N type field effect transistor.
Claim 17
Dependent Claim
36 words
The method of claim 13, wherein said dielectric layer is silicon oxide, deposited using LPCVD or PECVD processing, at a temperature between about 400 and 800° C., to a thickness between about 6000 and 14000 Angstroms.
Claim 18
Dependent Claim
36 words
The method of claim 13, wherein said contact hole is formed via anisotropic reactive ion etching, using CHF 3 +CF 4 +argon, where the diameter of said contact hole is between about 0.3 and 0.7 uM
Claim 19
Dependent Claim
34 words
The method of claim 13, wherein the first conductivity imparting dopant is arsenic, ion implanted at energy between about 20 and 50 Kev., at a dose between about 1E15 and 5E15 atoms/cm 2 .
Claim 20
Dependent Claim
42 words
The method of claim 13, wherein surface cleaning of said doped N type region is performed using a solution of water and hydrofluoric acid, at a temperature between about 20° and 25° C., for a time between about 75 and 105 seconds.
Claim 21
Dependent Claim
24 words
The method of claim 13, wherein said titanium adhesion layer is deposited via r.f. sputtering, to a thickness between about 300 and 1000 Angstroms.
Claim 22
Dependent Claim
129 words
The method of claim 13, wherein thermal annealing, of said titanium adhesive layer, is performed by; wafer loading in thermal anneal furnace at a temperature between about 350° and 450° C., in a nitrogen flow of about 20 liters/min.; ramp up and stabilization at a temperature between about 575° and 625° C., for a time between about 45 to 75 seconds, in an ammonia flow between about 2 and 6 liters/min., another ramp up and stabilization step at a temperature between about 700° and 740° C., for a time between about 10 and 40 seconds, in an ammonia flow between about 2 and 6 liters/min., and a ramp down and wafer unload in a nitrogen flow of about 20 liters/min., at a temperature between about 350° and 450° C.
Claim 23
Dependent Claim
28 words
The method of claim 13, wherein thermal annealing of said titanium adhesive layer is performed in an ammonia ambient at a temperature between about 700° and 740° C.
Claim 24
Dependent Claim
50 words
The method of claim 13, wherein thermal anneal of said titanium adhesion layer, in an ammonia ambient, results in the formation of between about 200 and 800 Angstroms of said first titanium nitride barrier layer, while leaving between about 100 and 500 Angstroms of underlying said titanium adhesion layer, unreacted.
Claim 25
Dependent Claim
30 words
The method of claim 13, wherein thermal annealing results in the formation of between about 100 and 300 Angstroms of said titanium disilicide, at the bottom of said contact hole.
Claim 26
Dependent Claim
26 words
The method of claim 13, wherein said second titanium nitride barrier layer is deposited using r.f. sputtering, to a thickness between about 200 and 600 Angstroms.
Claim 27
Dependent Claim
36 words
The method of claim 13, wherein said tungsten is deposited using LPCVD processing, at a temperature between about 400° and 500° C., to a thickness between about 5000 and 9000 Angstroms, using a tungsten hexafluoride source.
References Cited (Backward Citations)
US4994410A
Cited
JPH02119129A
Cited
US5444018A
Cited
US5188979A
Cited
JPH0620997A
Cited
US5286675A
Cited
US5430328A
Cited
US5504038A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-09-03 | 2000-03-04 | 2000-09-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-09-03 | 2004-03-04 | 2004-09-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-09-03 | 2008-03-04 | 2008-09-03 | $7700.00 | Window Closed / Lapsed |