US5541253A
Expired / Lapsed
US
⏱️ 0.0 years remaining
High solids copolymer dispersion from a latex and its use in sealants
Assignee: Lubrizol Advanced Materials Inc
•
Filing: 1994-10-11
•
Granted: 1996-07-30
•
Expires: 2014-10-11
Abstract
Abstract A method for polymerizing predominantly one or more acrylate and/or vinyl acetate monomers in the presence of a latex results in high solids dispersions of polymer particles with lower viscosities than traditionally observed. A significant wt. % of added monomers can be present in large particles, having nonspherical shapes. Some of the original latex particles are retained during the polymerization and these increase the solids content and lower the viscosity by packing in the interstices between large particles. The total polymer solids content can easily be varied from 70 to 92 or more wt. % which are higher than achieved in any previously reported aqueous polymerizations. The viscosities at very high solids contents become paste-like but the materials still are stable to storage and further handling without breaking the dispersion into an agglomerated polymer portion and released water. The dispersions are useful to form sealants, membranes, etc., either with or without other additives. A preferred use is as an acrylate water-based caulking compound where the high solids and thixotropy of the dispersion allows for formation of a water-based caulk with low shrinkage.
Inventors
- 👤 James H. Dunaway
- 👤 Pamela K. Hernandez
- 👤 Gregory P. Bidinger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 12:59
CPC Classifications
C; C08; C08L; C08L33/00; C08L33/04; C08L51/00; C08L51/003; C08F; C08F265/00; C08F265/04; C08F265/06; C08F291/00; C08L31/00; C08L31/02; C08L31/04; C08L33/06; C09; C09D; C09D133/00; C09D133/04; C09D133/06; C08L2205/00; C08L2205/02; C08L2205/14; C08L2205/18
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
112 words
A high solids polymer dispersion, comprising; an aqueous dispersion being at least 77 percent by weight discrete polymer particles polymerized from monomers comprising at least 50 wt. % acrylate monomers having 4 to 16 carbon atoms and/or vinyl acetate: said dispersion having a particle size distribution with two or more modes, wherein one mode of said particle size distribution has particles of diameters between about 0.05 to 4 microns and another mode has particles of diameters between above 4 to about 100 microns and wherein said particles of diameters between 4 to about 100 microns are formed by polymerization of said acrylate or vinyl acetate monomers in the presence of a latex.
Claim 2
Dependent Claim
112 words
A high solids polymer dispersion, comprising; an aqueous dispersion being at least 77 percent by weight discrete polymer particles polymerized from monomers comprising at least 50 wt. % acrylate monomers having 4 to 16 carbon atoms and/or vinyl acetate: said dispersion having a particle size distribution with two or more modes, wherein one mode of said particle size distribution has particles of diameters between about 0.05 to 4 microns and another mode has particles of diameters between above 4 to about 100 microns and wherein said particles of diameters between 4 to about 100 microns are formed by polymerization of said acrylate or vinyl acetate monomers in the presence of a latex.
Claim 3
Dependent Claim
90 words
A high solids polymer dispersion according to claim 1, wherein said discrete polymer particles are from about 80 percent to about 95 percent by weight of said dispersion, wherein one said mode of said particle size distribution is between about 1.0 to about 3.5 microns, wherein said another mode of said particle size distribution has large particles from above 4 to about 60 microns, and wherein the particles above 4 microns have an average aspect ratio between the largest and smallest diameter of each large particle of at least 1.5.
Claim 4
Dependent Claim
54 words
A high solids polymer dispersion according to claim 2, wherein said monomers are at least 70 wt. % one or more acrylate monomers and/or vinyl acetate monomers, said acrylate monomers being of the structure ##STR1## where R 1 is H or methyl and R 2 is an alkyl of 1 to 12 carbon atoms.
Claim 5
Dependent Claim
18 words
A high solids polymer dispersion according to claim 3, wherein said average aspect ratio is at least 2.0.
Claim 6
Dependent Claim
101 words
A high solids polymer dispersion comprising; an aqueous dispersion being at least 77 weight percent discrete polymer particles polymerized from monomers being at least 50 weight percent of one or more acrylate monomers having from 4 to 16 carbon atoms and/or vinyl acetate, said dispersion having a particle size distribution, said particle size distribution having at least one mode in the particle size distribution between 0.05 and 0.7 μm and at least another mode from above 0.7 μm to 100 μm, and wherein the particle size distribution has at least 20 weight percent of particles greater than 1 μm in diameter.
Claim 7
Dependent Claim
101 words
A high solids polymer dispersion comprising; an aqueous dispersion being at least 77 weight percent discrete polymer particles polymerized from monomers being at least 50 weight percent of one or more acrylate monomers having from 4 to 16 carbon atoms and/or vinyl acetate, said dispersion having a particle size distribution, said particle size distribution having at least one mode in the particle size distribution between 0.05 and 0.7 μm and at least another mode from above 0.7 μm to 100 μm, and wherein the particle size distribution has at least 20 weight percent of particles greater than 1 μm in diameter.
Claim 8
Dependent Claim
44 words
A high solids polymer dispersion according to claim 5, wherein said discrete polymer particles are from about 80 to 92 weight percent of said dispersion and wherein said particles above 1 μm in diameter are at least 35 weight percent of the total particles.
Claim 9
Dependent Claim
27 words
A high solids polymer dispersion according to claim 6, wherein said particles above 1 μm in diameter are at least 50 weight percent of the total particles.
Claim 10
Dependent Claim
37 words
A high solids polymer dispersion according to claim 6, wherein the monomers of the polymer particles are at least 70 weight percent of said one or more acrylate monomers and/or said one or more vinyl ester monomers.
Claim 11
Dependent Claim
25 words
A high solids polymer dispersion according to claim 6, wherein at least 30 weight percent of the total particles are between 1 and 4 μm.
Claim 12
Dependent Claim
30 words
A high solids polymer dispersion according to claim 5, having from about 2 to about 20 weight percent of the particles having a particle diameter from 0.05 to 0.7 μm.
Claim 13
Dependent Claim
30 words
A high solids polymer dispersion according to claim 9, having from about 2 to about 20 weight percent of the particles having a particle diameter from 0.05 to 0.7 μm.
Claim 14
Dependent Claim
70 words
A high solids polymer dispersion according to claim 5, wherein said particle size distribution has at least one mode from above 0.7 to 4 μm and at least another mode from above 4 μm to 100 μm, wherein said particle size distribution has at least 20 weight percent of particles above 1 μm in diameter and at least 15 weight percent of the particles are above 4 μm in diameter.
Claim 15
Dependent Claim
39 words
A high solids polymer dispersion according to claim 12, wherein at least 35 weight percent of the particles are above 1 μm in diameter and at least 15 weight percent of the particles are above 4 μm in diameter.
Claim 16
Dependent Claim
39 words
A high solids polymer dispersion according to claim 13, wherein at least 50 weight percent of the particles are above 1 μm in diameter and at least 15 weight percent of the particles are above 4 μm in diameter.
Claim 17
Dependent Claim
26 words
A high solids polymer dispersion according to claim 13, wherein the discrete polymer particles are from about 80 to about 92 weight percent of said dispersion.
Claim 18
Dependent Claim
30 words
A high solids polymer dispersion according to claim 12, wherein the particles between 0.05 to 0.7 μm are from about 2 to about 20 weight percent of the total particles.
Claim 19
Dependent Claim
30 words
A high solids polymer dispersion according to claim 14, wherein the particles between 0.05 and 0.7 μm are from about 2 to about 20 weight percent of the total particles.
Claim 20
Dependent Claim
47 words
A high solids polymer dispersion according to claim 5, wherein dried films of said dispersion have two or more separate glass transition values separated by from 2° to 100° C. when measured by differential scanning calorimetry at a rate of temperature increase of 10° C. per minute.
Claim 21
Dependent Claim
47 words
A high solids polymer dispersion according to claim 9, wherein dried films of said dispersion have two or more separate glass transition values separated by from 2° to 100° C. when measured by differential scanning calorimetry at a rate of temperature increase of 10° C. per minute.
Claim 22
Dependent Claim
88 words
A high solids polymer dispersion comprising: at least about 80 weight percent discrete polymer particles being comprised of the reaction product from polymerizing unsaturated monomers in the presence of a latex, said unsaturated monomers being at least 50 weight percent of one or more acrylate monomers having from 4 to 16 carbon atoms and/or vinyl acetate, wherein said discrete polymer particles have a particle size distribution having at least 2 modes with one mode being less than 1 μm and one mode greater than 1 μm in diameter.
Claim 23
Dependent Claim
88 words
A high solids polymer dispersion comprising: at least about 80 weight percent discrete polymer particles being comprised of the reaction product from polymerizing unsaturated monomers in the presence of a latex, said unsaturated monomers being at least 50 weight percent of one or more acrylate monomers having from 4 to 16 carbon atoms and/or vinyl acetate, wherein said discrete polymer particles have a particle size distribution having at least 2 modes with one mode being less than 1 μm and one mode greater than 1 μm in diameter.
Claim 24
Dependent Claim
24 words
A high solids polymer dispersion according to claim 20, wherein at least 20 weight percent of said particles have a diameter above 1 μm.
Claim 25
Dependent Claim
82 words
A high solids polymer dispersion according to claim 20, wherein a dried film of said dispersion has at least two Tg values as measured by differential scanning calorimetry when heated at 10° C. per minute and said at least two Tg values vary by from 2° to 100° C., and one of said Tg values being characteristic of the dispersed polymer from the latex and one of said Tg values being characteristic of the discrete polymer particles formed from the added monomers.
Claim 26
Dependent Claim
156 words
A high solids dispersion of polymer particles comprising: large polymer particles being the reaction product of polymerizing free radically from one or more unsaturated monomers in a water based latex, said unsaturated monomers being at least 50 wt. % one or more acrylate monomers having from 4 to 16 carbon atoms and/or vinyl acetate, said large particles having particle diameters above 4 microns and wherein said large polymer particles have an average aspect ratio between a greatest and smallest diameter of each particle of at least 1.5, and residual polymer particles from said water based latex, said residual polymer particles having a weight average particle diameter of less than 4 microns and being the polymerization product of monomers, and wherein at least 50 wt. % of said monomers used to form said latex are said one or more acrylate and/or vinyl ester monomers, wherein said polymer particles are at least 77 wt. % of said dispersion.
Claim 27
Dependent Claim
156 words
A high solids dispersion of polymer particles comprising: large polymer particles being the reaction product of polymerizing free radically from one or more unsaturated monomers in a water based latex, said unsaturated monomers being at least 50 wt. % one or more acrylate monomers having from 4 to 16 carbon atoms and/or vinyl acetate, said large particles having particle diameters above 4 microns and wherein said large polymer particles have an average aspect ratio between a greatest and smallest diameter of each particle of at least 1.5, and residual polymer particles from said water based latex, said residual polymer particles having a weight average particle diameter of less than 4 microns and being the polymerization product of monomers, and wherein at least 50 wt. % of said monomers used to form said latex are said one or more acrylate and/or vinyl ester monomers, wherein said polymer particles are at least 77 wt. % of said dispersion.
Claim 28
Dependent Claim
48 words
A high solids dispersion according to claim 23, wherein the polymer particles have a particle size distribution, wherein said distribution is multimodal having at least one mode at a diameter of less than 3.5 microns and at least one mode at a diameter of greater than 4 microns.
Claim 29
Dependent Claim
32 words
A high solids dispersion according to claim 24, wherein the polymer particles are from about 80 to about 92 wt. % of said dispersion and said aspect ratio is at least 2.0.
Claim 30
Dependent Claim
72 words
A high solids dispersion according to claim 25, wherein the polymer particles are comprised of at least 70 wt. % acrylate repeat units from one or more acrylate monomers of the structure ##STR2## where R 1 is H or methyl and R 2 is an alkyl of 1 to 12 carbon atoms and wherein said particle size distribution has at least one mode at a particle diameter of less than 1 μm.
Claim 31
Dependent Claim
48 words
A high solids dispersion according to claim 25 wherein said latex is a water based latex, said latex includes from 0.1 to 10 wt. % unsaturated mono or dicarboxylic acid based on the polymer, and wherein the pH of the latex before polymerization is from 3 to 9.
Claim 32
Dependent Claim
60 words
A dispersion of polymer particles, comprising: an aqueous dispersion of at least 80 percent by weight of the particles, said particles comprising at least 50 wt. % repeat units from one or more acrylates and/or vinyl acetate monomers, said aqueous dispersion having a viscosity of less than 30,000 cps at 24° C., 20 rpm with a cone and plate viscometer.
Claim 33
Dependent Claim
60 words
A dispersion of polymer particles, comprising: an aqueous dispersion of at least 80 percent by weight of the particles, said particles comprising at least 50 wt. % repeat units from one or more acrylates and/or vinyl acetate monomers, said aqueous dispersion having a viscosity of less than 30,000 cps at 24° C., 20 rpm with a cone and plate viscometer.
Claim 34
Dependent Claim
37 words
A dispersion according to claim 28, wherein said polymer is derived from the in situ polymerization of monomers comprising at least 50 wt. % alkyl acrylates wherein the alkyl portion has from 1 to 12 carbon atoms.
Claim 35
Dependent Claim
30 words
A dispersion according to claim 29, wherein the Tg of said particles is less than 0° C., and wherein the viscosity of said aqueous dispersion is less than 20,000 cps.
References Cited (Backward Citations)
US2111266A
Cited
US3513121A
Cited
US3551374A
Cited
US3707585A
Cited
US3616166A
Cited
US4011388A
Cited
US4135043A
Cited
US4125700A
Cited
US4130523A
Cited
US4269959A
Cited
US4395500A
Cited
US4495318A
Cited
US4707515A
Cited
US4656318A
Cited
US4680200A
Cited
US4668730A
Cited
US4721748A
Cited
US4794065A
Cited
EP0259734A2
Cited
US4870143A
Cited
US4810763A
Cited
US5133992A
Cited
US5037880A
Cited
EP0439941A1
Cited
EP0515719A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-07-30 | 2000-01-29 | 2000-07-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-07-30 | 2004-01-29 | 2004-07-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-07-30 | 2008-01-29 | 2008-07-30 | $7700.00 | Window Closed / Lapsed |