US5538218A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Tire curing bladder with improved release from the tire innerliner
Assignee: Goodyear Tire and Rubber Co
•
Filing: 1994-09-28
•
Granted: 1996-07-23
•
Expires: 2014-09-28
Abstract
Abstract Expandable bladders for use in curing presses for hydrocarbon rubbers such as pneumatic tires are a crosslink elastomer comprising isobutylene repeat units and include graphite. A preferred isobutylene elastomer is a brominated copolymer of isobutylene and p-methylstyrene. The bladders have enhanced lubricity, low adhesion to tire innerliners, and lower hot tension set. The above enhancements allow hydrocarbon rubbers such as tires to be molded with fewer defects caused by abraded or deformed bladders. They also enhance the useful life of the bladder reducing the cost of tire curing.
Inventors
- 👤 George P. Patitsas
- 👤 Paul H. Sandstrom
- 👤 Bharat K. Kansupada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 15:05
CPC Classifications
B; B29; B29D; B29D30/00; B29D30/06; B29D30/0601; B29D30/0654; B29C; B29C33/00; B29C33/44; B29C33/48; B29C33/50; B29C33/505; B29C33/56; B29C33/60; B29C33/62; C; C08; C08L; C08L15/00; C08L15/02; B29D2030/0655; B29K; B29K2021/00; B29L; B29L2022/00; B29L2022/02; B29L2022/025
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
122 words
In a curing press for a hydrocarbon rubber composition which uses an expandable bladder to assist in shaping and curing said composition the improvement wherein said bladder consist essentially of a formulated rubber composition and from about 0.1 to about 30 parts by weight of graphite dispersed throughout said formulated rubber composition, said formulated rubber composition comprising one or more rubbery polymers including at least 50% by weight of one or more isobutylene rubbery polymers, wherein said formulated rubber composition after curing and after aging at 177° C. for 24 hrs has an elongation to break from 300 to 800%, and wherein said parts by weight are based on 100 parts by weight of the rubbery polymers in said formulated rubber composition.
Claim 2
Dependent Claim
122 words
In a curing press for a hydrocarbon rubber composition which uses an expandable bladder to assist in shaping and curing said composition the improvement wherein said bladder consist essentially of a formulated rubber composition and from about 0.1 to about 30 parts by weight of graphite dispersed throughout said formulated rubber composition, said formulated rubber composition comprising one or more rubbery polymers including at least 50% by weight of one or more isobutylene rubbery polymers, wherein said formulated rubber composition after curing and after aging at 177° C. for 24 hrs has an elongation to break from 300 to 800%, and wherein said parts by weight are based on 100 parts by weight of the rubbery polymers in said formulated rubber composition.
Claim 3
Dependent Claim
91 words
In a curing press according to claim 1, wherein the one or more isobutylene rubbery polymers are comprised of either one or more polymers of from 90 to 99 weight percent isobutylene and from 1 to 20 weight percent para-alkyl-styrene or one or more polymers of from 95 to 99 weight percent isobutylene and from 1 to 5 weight percent of at least one conjugated diene or combinations thereof and wherein said one or more isobutylene rubbery polymers are at least 75 weight percent of said rubbery polymers of said bladder.
Claim 4
Dependent Claim
77 words
In a curing press according to claim 1, wherein said expandable bladder is filled with a hot fluid during use wherein said graphite is present from about 0.5 to about 20 parts by weight, and wherein said at least 75 weight percent of said rubbery polymers of said bladder are comprised of one or more polymers of from 95 to 99 weight percent isobutylene and from 1 to 5 weight percent of at least one conjugated diene.
Claim 5
Dependent Claim
66 words
In a curing press according to claim 2, wherein said graphite is present from about 0.5 to about 20 parts by weight, and wherein said at least 75 weight percent of said rubbery polymers of said bladder is comprised of one or more copolymers of from 80 to 99 weight percent isobutylene and from 11 to 20 weight percent para-alkylstyrene and said copolymers are brominated polymers.
Claim 6
Dependent Claim
30 words
In a curing press according to claim 3, wherein said one or more isobutylene polymers comprise at least 80 weight percent of all the rubbery polymers in said expandable bladder.
Claim 7
Dependent Claim
34 words
In a curing press according to claim 4, wherein said one or more brominated polymers of isobutylene and para-methylstyrene are at least 80 weight percent of all the rubbery polymers in said expandable bladder.
Claim 8
Dependent Claim
21 words
In a curing press according to claim 6, wherein said formulated rubber composition was cured with a phenol-formaldehyde resin cure system.
Claim 9
Dependent Claim
21 words
In a curing press according to claim 5, wherein said formulated rubber composition was cured with a phenol-formaldehyde resin cure system.
Claim 10
Dependent Claim
137 words
An expandable curing bladder consisting essentially of a formulated rubber composition and from about 0.1 to about 30 parts by weight of graphite dispersed throughout said formulated rubber composition, said formulated rubber composition comprising: one or more rubbery polymers including one or more isobutylene rubbery polymers, wherein said isobutylene rubbery polymers are at least 50 weight percent isobutylene units, and are present as at least 50 weight percent of the rubbery polymers of said bladder and one or more curatives for said one or more isobutylene rubbery polymers wherein said parts by weight are based upon 100 parts by weight of said one or more rubbery polymers in said bladder and wherein said formulated rubber composition after curing and after aging at 177° C. for 24 hrs has an elongation at break of from 300% to 700%.
Claim 11
Dependent Claim
137 words
An expandable curing bladder consisting essentially of a formulated rubber composition and from about 0.1 to about 30 parts by weight of graphite dispersed throughout said formulated rubber composition, said formulated rubber composition comprising: one or more rubbery polymers including one or more isobutylene rubbery polymers, wherein said isobutylene rubbery polymers are at least 50 weight percent isobutylene units, and are present as at least 50 weight percent of the rubbery polymers of said bladder and one or more curatives for said one or more isobutylene rubbery polymers wherein said parts by weight are based upon 100 parts by weight of said one or more rubbery polymers in said bladder and wherein said formulated rubber composition after curing and after aging at 177° C. for 24 hrs has an elongation at break of from 300% to 700%.
Claim 12
Dependent Claim
57 words
An expandable curing bladder according to claim 9, wherein at least 75 weight percent of said one or more isobutylene polymers are one or more polymers comprised of from 80 to 99 weight percent isobutylene and from 1 to 20 weight percent para-methylstyrene and wherein said graphite is present from about 0.5 to about parts by weight.
Claim 13
Dependent Claim
49 words
An expandable curing bladder according to claim 9, wherein said one or more rubbery polymers of said expandable bladder are comprised of at least 75 weight percent polymers of from 95 to 99 weight percent isobutylene and from 1 to 5 weight percent of at least one conjugated diene.
Claim 14
Dependent Claim
20 words
An expandable curing bladder according to claim 10, wherein said one or more polymers of iso-butylene and para-methylstyrene are brominated.
Claim 15
Dependent Claim
26 words
An expandable curing bladder according to claim 12, wherein at least 90 weight percent of said graphite is capable of passing through a 325 mesh screen.
Claim 16
Dependent Claim
20 words
An expandable curing bladder according to claim 12, wherein said rubbery polymers are crosslinked with a phenol-formaldehyde resin cure system.
Claim 17
Independent Claim
237 words
A method of using an expandable rubber bladder to cure a hydrocarbon rubber, said method comprising: inserting an uncured rubber composition into a curing mold having an expandable rubber bladder positioned therein and one or more molding surfaces, wherein the expandable bladder consists essentially of a formulated rubber composition and from about 0.1 to about 30 parts by weight of graphite dispersed throughout said formulated rubber composition, said formulated rubber composition comprising: at least 50 parts by weight of one or more isobutylene polymers having at least 50 weight percent isobutylene units, optionally other rubbery polymers, and one or more curatives for said one or more isobutylene polymers, and wherein said parts by weight are based upon 100 parts by weight of said one or more isobutylene polymers and said optional rubbery polymers in said bladder and wherein said formulated rubber composition of said bladder after curing and aging at 177° C. for 24 hrs has an elongation at break of from 300 to 800%, closing the mold and expanding the bladder by application of heat and fluid in the internal portion of said bladder cavity to expand the bladder outwardly against an inner surface of the uncured hydrocarbon rubber to force said uncured hydrocarbon rubber against the one or more molding surfaces, curing the hydrocarbon rubber under conditions of heat and pressure, deflating said expandable bladder, and removing the cured hydrocarbon rubber from said curing mold.
Claim 18
Independent Claim
237 words
A method of using an expandable rubber bladder to cure a hydrocarbon rubber, said method comprising: inserting an uncured rubber composition into a curing mold having an expandable rubber bladder positioned therein and one or more molding surfaces, wherein the expandable bladder consists essentially of a formulated rubber composition and from about 0.1 to about 30 parts by weight of graphite dispersed throughout said formulated rubber composition, said formulated rubber composition comprising: at least 50 parts by weight of one or more isobutylene polymers having at least 50 weight percent isobutylene units, optionally other rubbery polymers, and one or more curatives for said one or more isobutylene polymers, and wherein said parts by weight are based upon 100 parts by weight of said one or more isobutylene polymers and said optional rubbery polymers in said bladder and wherein said formulated rubber composition of said bladder after curing and aging at 177° C. for 24 hrs has an elongation at break of from 300 to 800%, closing the mold and expanding the bladder by application of heat and fluid in the internal portion of said bladder cavity to expand the bladder outwardly against an inner surface of the uncured hydrocarbon rubber to force said uncured hydrocarbon rubber against the one or more molding surfaces, curing the hydrocarbon rubber under conditions of heat and pressure, deflating said expandable bladder, and removing the cured hydrocarbon rubber from said curing mold.
Claim 19
Dependent Claim
22 words
A method according to claim 15, wherein said graphite is present in amounts from about 0.5 to about 20 parts by weight.
Claim 20
Dependent Claim
62 words
A method according to claim 15, wherein 75 weight percent or more of said one or more isobutylene polymers and said optional other rubbery polymers are one or more copolymers comprised of from 80 top 99 weight percent isobutylene and from 1 to 20 weight percent para-methylstyrene, and wherein said graphite is present from about 0.5 to about 20 parts by weight.
Claim 21
Dependent Claim
19 words
A method according to claim 17, wherein said one or more copolymers comprised of isobutylene and para-methylstyrene are brominated.
Claim 22
Dependent Claim
16 words
A method according to claim 18, wherein said hydrocarbon rubber is cured into a pneumatic tire.
Claim 23
Dependent Claim
67 words
A method according to claim 15, wherein 75 weight percent or more of said one or more isobutylene polymers and said optional other rubbery polymers are one or more copolymers comprised of from 95 to 99 weight percent isobutylene and from 1 to 5 weight percent of at least one conjugated diene and wherein said graphite is present from about 0.5 to about 20 parts by weight.
Claim 24
Dependent Claim
25 words
In a curing press according to claim 6, wherein said bladder has a toroidal shape and said hydrocarbon rubber compositions are fiber reinforced pneumatic tires.
References Cited (Backward Citations)
US3967968A
Cited
US3932088A
Cited
US4310427A
Cited
US4333977A
Cited
US4407988A
Cited
US4863650A
Cited
EP0344021A2
Cited
US5063268A
Cited
US5238991A
Cited
US5162409A
Cited
US5162409B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-07-23 | 2000-01-22 | 2000-07-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-07-23 | 2004-01-22 | 2004-07-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-07-23 | 2008-01-22 | 2008-07-23 | $7700.00 | Window Closed / Lapsed |