US4863650A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for molding and vulcanizing tires and other rubber articles
Assignee: Rhein Chemie Rheinau GmbH
•
Filing: 1988-05-03
•
Granted: 1989-09-05
•
Expires: 2008-05-03
Abstract
Abstract Process for molding and vulcanizing tires and other rubber articles, in which in a press with the aid of a bladder negative shapes are pressed into the tire blank under high pressure and vulcanization is performed, the surface of the bladder having applied thereon a solvent which swells the surface, the swollen bladder being provided with a cross-linked, hardened, tightly adhering, elastic release agent film bonded to the bladder by chemical interactions before carrying out molding and vulcanization to prevent sticking of the molded and vulcanized tire to the bladder, the film comprising more than one thin coating each of which is produced by coating the bladder with an organic solvent solution comprising a mixture of a silicon release agent and a moisture or heat curable silicone rubber and curing the coated mixture through exposure to moisture or heat, and conducting at least 300 molding and vulcanizing cycles without recoating the bladder with the release agent film.
Inventors
- 👤 Winfried R. Kohler
- 👤 Herbert Wagner
- 👤 Wolfgang Fischer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 00:52
CPC Classifications
B; B29; B29C; B29C43/00; B29C43/32; B29C43/36; B29C43/3642; B29C33/00; B29C33/56; B29C33/60; B29C33/62; B29C33/64
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
168 words
Process for molding and vulcanizing tyres and other rubber articles, in which in a press with the aid of a bladder negative shapes are pressed into a tyre blank under high pressure and vulcanization is performed, comprising the steps of applying to the outside surface of the bladder a solvent which swells said surface, providing on the swollen outside surface of the bladder a cross-linked, hardened, tightly adhering, elastic release agent film bonded to the bladder by chemical interactions before molding and vulcanization are performed, and conducting at least 300 molding and vulcanizing cycles without recoating the bladder with the release agent film, the release agent film on the outside the bladder comprising more than one thin coating, each such coating produced by the steps of (a) coating the outside of the bladder with an organic solvent solution comprising a mixture of a silicone release agent and a moisture or heat curable silicone rubber and (b) exposing the coated mixture to moisture or heat to effect curing thereof.
Claim 2
Dependent Claim
168 words
Process for molding and vulcanizing tyres and other rubber articles, in which in a press with the aid of a bladder negative shapes are pressed into a tyre blank under high pressure and vulcanization is performed, comprising the steps of applying to the outside surface of the bladder a solvent which swells said surface, providing on the swollen outside surface of the bladder a cross-linked, hardened, tightly adhering, elastic release agent film bonded to the bladder by chemical interactions before molding and vulcanization are performed, and conducting at least 300 molding and vulcanizing cycles without recoating the bladder with the release agent film, the release agent film on the outside the bladder comprising more than one thin coating, each such coating produced by the steps of (a) coating the outside of the bladder with an organic solvent solution comprising a mixture of a silicone release agent and a moisture or heat curable silicone rubber and (b) exposing the coated mixture to moisture or heat to effect curing thereof.
Claim 3
Dependent Claim
19 words
Process according to claim 1 wherein the organic solvent solution contains a filler, a lubricant, or a combination thereof.
Claim 4
Dependent Claim
26 words
Process according to claim 1 wherein the organic solvent solution is also applied to the inside of the bladder to provide a release agent film thereon.
Claim 5
Dependent Claim
35 words
Process according to claim 1 wherein a lubricant is provided in at least one of the cured coatings or as a surface layer on top of the cured coatings produced in steps (a) and (b).
Claim 6
Dependent Claim
25 words
Process according to claim 1 wherein the release agent film on the outside of the bladder has a total thickness of 5 to 100 um.
Claim 7
Dependent Claim
25 words
Process according to claim 5, wherein the release agent film on the outside of the bladder has a total thickness of 20 to 60 um.
Claim 8
Dependent Claim
14 words
Process according to claim 4 wherein the lubricant comprises a coating-forming cross-linked silicone resin.
Claim 9
Dependent Claim
23 words
Process according to claim 3 wherein the release agent film on the inside of the bladder is produced by applying several thin coatings.
Claim 10
Dependent Claim
25 words
Process according to claim 3 wherein the release agent film on the inside of the bladder has a total thickness of 1 to 30 um.
Claim 11
Dependent Claim
25 words
Process according to claim 9 wherein the release agent film on the inside of the bladder has a total thickness of 2 to 10 um.
Claim 12
Dependent Claim
45 words
Process according to claim 1 wherein 2 to 10 thin coatings are applied to the outside of the bladder, each thin coating having a thickness of 1 to 20 um, to produce a release agent film having a total thickness of 2 to 50 um.
Claim 13
Dependent Claim
45 words
Process according to claim 11 wherein 3 to 6 thin coatings are applied to the outside of the bladder, each thin coating having a thickness of 1 to 5 um, to produce a release agent film having a total thickness of 5 to 30 um.
Claim 14
Dependent Claim
45 words
Process according to claim 3 wherein 1 to 5 thin coatings are applied to the inside of the bladder, each thin coating having a thickness of 1 to 20 um, to produce a release agent film having a total thickness of 1 to 30 um.
Claim 15
Dependent Claim
45 words
Process according to claim 13 wherein each thin coating applied to the inside of the bladder has a thickness of 1 to 5 um and the release agent film produced on the inside of the bladder has a total thickness of 2 to 10 um.
Claim 16
Dependent Claim
24 words
Process according to claim 1 where additionally a pure release agent layer is applied as an intermediate layer in between the several thin coatings.
References Cited (Backward Citations)
US3328482A
Cited
GB1158771A
Cited
US3549744A
Cited
US3525783A
Cited
GB1220381A
Cited
US3532624A
Cited
US3713851A
Cited
US3905823A
Cited
JPS51150270A
Cited
US4311737A
Cited
US4244912A
Cited
US4547544A
Cited
US4359340A
Cited
US4431452A
Cited
GB2088898A
Cited
JPS57181842A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-09-04 | 1993-03-06 | 1993-09-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-09-04 | 1997-03-06 | 1997-09-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-09-04 | 2001-03-06 | 2001-09-05 | $7700.00 | Window Closed / Lapsed |