Molding composition and molded product utilizing a specifically defined polymeric blend and phosphorus compound
Assignee: Polyplastics Co Ltd
•
Filing: 1994-11-09
•
Granted: 1996-05-07
•
Expires: 2014-11-09
Abstract
Abstract An improved synthetic resin composition is provided that consists essentially of 100 parts by weight of a resin component composed of 50 to 99 (preferably 50 to 90) parts by weight of a melt-processable polyester that does not form an anisotropic melt phase and 1 to 50 (preferably 10 to 50) parts by weight of a liquid crystal polyester that is capable of forming an anisotropic melt phase, to which has been added 0.01 to 0.5 part by weight of a phosphorus compound. The presence of the phosphorus compound has been found to facilitate the fibrillation of the liquid crystal polyester component during molding so as to form fibrils within the resulting molded article having an aspect ratio of 6 or more. The resulting molded article accordingly exhibits significantly enhanced mechanical properties.
Inventors
- 👤 Tomoyuki Aketa
- 👤 Takayuki Ishikawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 12:17
CPC Classifications
C; C08; C08L; C08L67/00; C08L67/02; C08L67/03; C08K; C08K5/00; C08K5/49; C08K5/51; C08K5/52; C08K5/527; C08L69/00; C08L2205/00; C08L2205/12; C08L2205/14; C08L2205/16; C08L67/04; C08L77/00; C08L77/12
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
105 words
An improved synthetic resin composition consisting essentially of 100 parts by weight of a resin component composed of 50 to 99 parts by weight of a melt-processable thermoplastic polyester resin (a) that does not form an anisotropic melt phase, and 1 to 50 parts by weight of a liquid crystal polyester resin (b) that is capable of forming an anisotropic melt phase, as well as 0.01 to 0.5 part by weight of a phosphite compound of pentaerythritol (c), with said liquid crystal polyester resin (b) being capable of forming fibrils having an aspect ratio of 6 or more during the molding of said resin composition.
Claim 2
Dependent Claim
105 words
An improved synthetic resin composition consisting essentially of 100 parts by weight of a resin component composed of 50 to 99 parts by weight of a melt-processable thermoplastic polyester resin (a) that does not form an anisotropic melt phase, and 1 to 50 parts by weight of a liquid crystal polyester resin (b) that is capable of forming an anisotropic melt phase, as well as 0.01 to 0.5 part by weight of a phosphite compound of pentaerythritol (c), with said liquid crystal polyester resin (b) being capable of forming fibrils having an aspect ratio of 6 or more during the molding of said resin composition.
Claim 3
Dependent Claim
27 words
An improved synthetic resin composition according to claim 1, wherein said phosphorus compound (c) is present in a concentration of approximately 0.05 to 0.3 part by weight.
Claim 4
Dependent Claim
21 words
An improved synthetic resin composition according to claim 1, wherein the weight ratio (c) to (a) is approximately 0.001 to 0.005:1.
Claim 5
Dependent Claim
34 words
An improved synthetic resin composition according to claim 1, wherein said melt-processable thermoplastic polyester resin (a) is selected from the group consisting of a polycarbonate resin, a polyalkylene terephthalate resin, and a polyarylate resin.
Claim 6
Dependent Claim
20 words
An improved synthetic resin composition according to claim 1, wherein said melt-processable thermoplastic polyester resin (a) is a polycarbonate resin.
Claim 7
Dependent Claim
20 words
An improved synthetic resin composition according to claim 2, wherein said melt-processable thermoplastic polyester resin (a) is a polycarbonate resin.
Claim 8
Dependent Claim
20 words
An improved synthetic resin composition according to claim 3, wherein said melt-processable thermoplastic polyester resin (a) is a polycarbonate resin.
Claim 9
Dependent Claim
22 words
An improved synthetic resin composition according to claim 1, wherein said melt-processable thermoplastic polyester resin (a) is polyethylene terephthalate and/or polybutylene terephthalate.
Claim 10
Dependent Claim
24 words
An improved synthetic resin composition according to claim 2, wherein said melt-processable thermoplastic polyester resin (a) is a polyethylene terephthalate and/or a polybutylene terephthalate.
Claim 11
Dependent Claim
24 words
An improved synthetic resin composition according to claim 3, wherein said melt-processable thermoplastic polyester resin (a) is a polyethylene terephthalate and/or a polybutylene terephthalate.
Claim 12
Dependent Claim
36 words
An improved synthetic resin composition according to claim 1, further consisting essentially of approximately 1 to 90 parts by weight of a thermoplastic resin not forming an anisotropic melt phase in addition to (a) and (b).
Claim 13
Dependent Claim
24 words
An improved synthetic resin composition according to claim 1, further consisting essentially of approximately 1 to 50 parts by weight of an inorganic filler.
Claim 14
Dependent Claim
52 words
An improved resin composition according to claim 1, wherein (a) is present in a concentration of approximately 50 to 90 parts by weight, (b) is present in a concentration of approximately 10 to 50 parts by weight, and (c) is present in a concentration of approximately 0.05 to 0.3 part by weight.
Claim 15
Dependent Claim
35 words
A molded article formed by the molding of the improved synthetic resin composition according to claim 1, wherein (b) is present therein in the form of fibrils having an aspect ratio of 6 or more.
Claim 16
Dependent Claim
48 words
A molded article formed by the molding of the improved synthetic resin composition according to claim 1 while at a temperature above the melting temperatures of (a) and (b) and wherein (b) is present therein in the form of fibrils having an aspect ratio of 6 or more.
References Cited (Backward Citations)
US2437046A
Cited
US3305520A
Cited
US4438236A
Cited
US4433083A
Cited
US4489190A
Cited
US4460735A
Cited
US4460736A
Cited
US4276397A
Cited
US4451611A
Cited
US4408022A
Cited
US4639504A
Cited
EP0180960A2
Cited
US4728698A
Cited
US4778858A
Cited
US4952663A
Cited
EP0411866A2
Cited
US5225488A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-05-07 | 1999-11-06 | 2000-05-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-05-07 | 2003-11-06 | 2004-05-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-05-07 | 2007-11-06 | 2008-05-07 | $7700.00 | Window Closed / Lapsed |