Process for forming blend of polyalkylene terephthalate and wholly aromatic polyester which exhibits an anisotropic melt phase
Assignee: Celanese Corp
•
Filing: 1981-12-15
•
Granted: 1984-05-29
•
Expires: 2001-12-15
Abstract
Abstract An improved process for producing a polymer blend which exhibits an anisotropic melt phase and is capable of forming shaped articles having satisfactory mechanical properties (e.g. tensile strength, flexural strength, and Izod impact strength) is provided. The process comprises the steps of (a) post-polymerizing a melt processable wholly aromatic polyester which is capable of forming an anisotropic melt phase apart from the blend and (b) subsequently intimately mixing together approximately 85 to 95 percent by weight of the wholly aromatic polyester and approximately 5 to 15 percent by weight of a polyalkylene terephthalate. Accordingly, the wholly aromatic polyester which is capable of forming an anisotropic melt phase serves as the continuous phase in the resulting blend. The post-polymerization step is conducted at a temperature and for a period of time sufficient to increase the inherent viscosity of the wholly aromatic polyester by at least approximately 50 percent, preferably by at least approximately 100 percent. Each of the shaped article mechanical properties identified above is improved over that of the composition in the absence of the polyalkylene terephthalate. The polyalkylene terephthalate is preferably polyethylene terephthalate.
Inventors
- 👤 David E. Cincotta
- 👤 Frank M. Berardinelli
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 14:58
CPC Classifications
C; C08; C08L; C08L67/00; C08G; C08G63/00; C08G63/02; C08G63/60; C08G63/605; C08L67/04
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
153 words
A process for producing a polymer blend which exhibits an anisotropic melt phase and is capable of forming shaped articles having satisfactory mechanical properties, said process comprising the steps of: (a) post-polymerizing a melt processable wholly aromatic polyester which is capable of forming an anisotropic melt phase apart from said blend, said post-polymerizing step being conducted at a temperature and for a period of time sufficient to increase the inherent viscosity of said wholly aromatic polyester by at least approximately 50 percent, and (b) subsequently intimately mixing together approximately 85 to 95 percent by weight of said wholly aromatic polyester and approximately 5 to 15 percent by weight of a polyalkylene terephthalate, wherein said resulting polymer blend is capable of forming shaped articles which exhibit a tensile strength, a flexural strength, and a notched Izod impact strength which each exceed that exhibited by the composition in the absence of the polyalkylene terephthalate component.
Claim 2
Dependent Claim
153 words
A process for producing a polymer blend which exhibits an anisotropic melt phase and is capable of forming shaped articles having satisfactory mechanical properties, said process comprising the steps of: (a) post-polymerizing a melt processable wholly aromatic polyester which is capable of forming an anisotropic melt phase apart from said blend, said post-polymerizing step being conducted at a temperature and for a period of time sufficient to increase the inherent viscosity of said wholly aromatic polyester by at least approximately 50 percent, and (b) subsequently intimately mixing together approximately 85 to 95 percent by weight of said wholly aromatic polyester and approximately 5 to 15 percent by weight of a polyalkylene terephthalate, wherein said resulting polymer blend is capable of forming shaped articles which exhibit a tensile strength, a flexural strength, and a notched Izod impact strength which each exceed that exhibited by the composition in the absence of the polyalkylene terephthalate component.
Claim 3
Dependent Claim
37 words
The process of claim 1 wherein said post-polymerizing step is conducted at a temperature and for a period of time sufficient to increase the inherent viscosity of said wholly aromatic polyester by at least approximately 100 percent.
Claim 4
Dependent Claim
39 words
The process of claim 1 wherein said wholly aromatic polyester prior to said post-polymerizing step exhibits an inherent viscosity of at least approximately 2.0 dl./g. when measured at a concentration of 0.1 weight/volume percent in pentafluorophenol at 60° C.
Claim 5
Dependent Claim
38 words
The process of claim 1 wherein said wholly aromatic polyester after said post-polymerizing step exhibits an inherent viscosity of at least approximately 7.0 dl./g. when measured at a concentration of 0.1 weight/volume percent in pentafluorophenol at 60° C.
Claim 6
Dependent Claim
46 words
The process of claim 1 wherein said post-polymerizing step is a solid phase polymerization conducted in a nonoxidizing atmosphere at a temperature within the range of approximately 250° C. to 300° C. for a period of time within the range of approximately 8 to 72 hours.
Claim 7
Dependent Claim
123 words
The process of claim 1 wherein said melt processable wholly aromatic polyester is capable of forming an anisotropic melt phase at a temperature below approximately 350° C. apart from the blend and consists essentially of the recurring moieties I and II which may include substitution of at least some of the hydrogen atoms present upon an aromatic ring wherein: ##STR5## with said optional substitution if present being selected from the group consisting of an alkyl group of 1 to 4 carbon atoms, an alkoxy group of 1 to 4 carbon atoms, halogen, and mixtures of the foregoing, and wherein said wholly aromatic polyester comprises approximately 10 to 90 mole percent of moiety I and approximately 10 to 90 mole percent of moiety II.
Claim 8
Dependent Claim
73 words
The process of claim 1 wherein said melt processable wholly aromatic polyester is capable of forming an anisotropic melt phase at a temperature below approximately 325° C. apart from the blend and consists essentially of the recurring moieties I, II, and III wherein: ##STR6## wherein said wholly aromatic polyester comprises approximately 30 to 70 mole percent of moiety I, and wherein each of said moieties of said polyester is free of ring substitution.
Claim 9
Dependent Claim
173 words
The process of claim 1 wherein said melt processable wholly aromatic polyester is capable of forming an anisotropic melt phase at a temperature below approximately 400° C. and consists essentially of the recurring moieties I, II, and III which may include substitution of at least some of the hydrogen atoms present upon an aromatic ring wherein: ##STR7## II is a dioxyaryl moiety of the formula --O--Ar--O--, where Ar is a divalent radical comprising at least one aromatic ring, and III is a dicarboxyaryl moiety of the formula ##STR8## where Ar' is a divalent radical comprising at least one aromatic ring, with said optional substitution if present being selected from the group consisting of an alkyl group of 1 to 4 carbon atoms, an alkoxy group of 1 to 4 carbon atoms, halogen, a phenyl group, and mixtures of the foregoing, and wherein said polyester comprises approximately 10 to 90 mole percent of moiety I, approximately 5 to 45 mole percent of moiety II, and approximately 5 to 45 mole percent of moiety III.
Claim 10
Dependent Claim
19 words
The process of claim 1 wherein the alkylene units of said polyalkylene terephthalate contain 2 to 4 carbon atoms.
Claim 11
Dependent Claim
12 words
The process of claim 9 wherein said polyalkylene terephthalate is polyethylene terephthalate.
Claim 12
Dependent Claim
32 words
The process of claim 1 wherein step (b) comprises intimately mixing together approximately 90 percent by weight of said wholly aromatic polyester and approximately 10 percent by weight of said polyalkylene terephthalate.
Claim 13
Dependent Claim
21 words
The process of claim 1 wherein said wholly aromatic polyester and said polyalkylene terephthalate are intimately mixed together by melt extrusion.
Claim 14
Dependent Claim
189 words
A process for producing a polymer blend which exhibits an anisotropic melt phase and is capable of forming shaped articles having satisfactory mechanical properties, said process comprising the steps of: (a) post polymerizing a melt processable wholly aromatic polyester which is capable of forming an anisotropic melt phase apart from said blend, said post-polymerizing step being conducted in the solid phase in a non-oxidizing atmosphere at a temperature within the range of approximately 250° C. to 300° C. and for a period of time within the range of approximately 8 to 72 hours so as to increase the inherent viscosity of said wholly aromatic polyester by at least approximately 100 percent, and (b) subsequently intimately mixing together approximately 90 percent by weight of said wholly aromatic polyester and approximately 10 percent by weight of a polyalkylene terephthalate in which the alkylene units contain 2 to 4 carbon atoms, wherein said resulting polymer blend is capable of forming shaped articles which exhibit a tensile strength, a flexural strength, and a notched Izod impact strength which each exceed that exhibited by the composition in the absence of the polyalkylene terephthalate component.
Claim 15
Dependent Claim
189 words
A process for producing a polymer blend which exhibits an anisotropic melt phase and is capable of forming shaped articles having satisfactory mechanical properties, said process comprising the steps of: (a) post polymerizing a melt processable wholly aromatic polyester which is capable of forming an anisotropic melt phase apart from said blend, said post-polymerizing step being conducted in the solid phase in a non-oxidizing atmosphere at a temperature within the range of approximately 250° C. to 300° C. and for a period of time within the range of approximately 8 to 72 hours so as to increase the inherent viscosity of said wholly aromatic polyester by at least approximately 100 percent, and (b) subsequently intimately mixing together approximately 90 percent by weight of said wholly aromatic polyester and approximately 10 percent by weight of a polyalkylene terephthalate in which the alkylene units contain 2 to 4 carbon atoms, wherein said resulting polymer blend is capable of forming shaped articles which exhibit a tensile strength, a flexural strength, and a notched Izod impact strength which each exceed that exhibited by the composition in the absence of the polyalkylene terephthalate component.
Claim 16
Dependent Claim
33 words
The process of claim 13 wherein said post-polymerizing step is conducted at a temperature within the range of approximately 265° C. to 280° C. for a period of time of approximatly 20 hours.
Claim 17
Dependent Claim
123 words
The process of claim 13 wherein said melt processable wholly aromatic polyester is capable of forming an anisotropic melt phase at a temperature below approximately 350° C. apart from the blend and consists essentially of the recurring moieties I and II which may include substitution of at least some of the hydrogen atoms present upon an aromatic ring wherein: ##STR9## with said optional substitution if present being selected from the group consisting of an alkyl group of 1 to 4 carbon atoms, an alkoxy group of 1 to 4 carbon atoms, halogen, and mixtures of the foregoing, and wherein said wholly aromatic polyester comprises approximately 10 to 90 mole percent of moiety I and approximately 10 to 90 mole percent of moiety II.
Claim 18
Dependent Claim
39 words
The process of claim 15 wherein said wholly aromatic polyester prior to said post-polymerizing step exhibits an inherent viscosity of at least approximately 5.0 dl./g. when measured at a concentration of 0.1 weight/volume percent in pentafluorophenol at 60° C.
Claim 19
Dependent Claim
73 words
The process of claim 13 wherein said melt processable wholly aromatic polyester is capable of forming an anisotropic melt phase at a temperature below approximately 325° C. apart from the blend and consists essentially of the recurring moieties I, II, and III wherein: ##STR10## wherein said wholly aromatic polyester comprises approximately 30 to 70 mole percent of moiety I, and wherein each of said moieties of said polyester is free of ring substitution.
Claim 20
Dependent Claim
39 words
The process of claim 17 wherein said wholly aromatic polyester prior to said post-polymerizing step exhibits an inherent viscosity of at least approximately 3.0 dl./g. when measured at a concentration of 0.1 weight/volume percent in pentafluorophenol at 60° C.
Claim 21
Dependent Claim
172 words
The process of claim 13 wherein said melt processable wholly aromatic polyester is capable of forming an anisotropic melt at a temperature below approximately 400° C. and consists essentially of the recurring moieties I, II, and III which may include substitution of at least some of the hydrogen atoms present upon an aromatic ring wherein: ##STR11## II is a dioxyaryl moiety of the formula --O--Ar--O--, where Ar is a divalent radical comprising at least one aromatic ring, and III is a dicarboxyaryl moiety of the formula ##STR12## where Ar' is a divalent radical comprising at least one aromatic ring, with said optional substitution if present being selected from the group consisting of an alkyl group of 1 to 4 carbon atoms, an alkoxy group of 1 to 4 carbon atoms, halogen, a phenyl group, and mixtures of the foregoing, and wherein said polyester comprises approximately 10 to 90 mole percent of moiety I, approximately 5 to 45 mole percent of moiety II, and approximately 5 to 45 mole percent of moiety III.
Claim 22
Dependent Claim
38 words
The process of claim 13 wherein said wholly aromatic polyester after said post-polymerizing step exhibits an inherent viscosity of at least approximately 7.0 dl./g. when measured at a concentration of 0.1 weight/volume percent in pentafluorophenol at 60° C.
Claim 23
Dependent Claim
12 words
The process of claim 13 wherein said polyalkylene terephthalate is polyethylene terephthalate.
Claim 24
Dependent Claim
21 words
The process of claim 13 wherein said wholly aromatic polyester and said polyalkylene terephthalate are intimately mixed together by melt extrusion.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-29 | 1987-11-28 | 1988-05-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-29 | 1991-11-28 | 1992-05-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-29 | 1995-11-28 | 1996-05-29 | $7700.00 | Window Closed / Lapsed |