Method for manufacturing a thermistor having a negative temperature coefficient in multi-layer technology
Assignee: Siemens AG
•
Filing: 1993-02-22
•
Granted: 1996-03-26
•
Expires: 2013-02-22
Abstract
Abstract In a method for manufacturing a thermistor having a negative temperature coefficient in multi-layer technology, a plurality of layers are produced of ceramic material by producing a suspension and then drawing out with a stripping technique to form an extremely thin film from which the individual ceramic material layers are formed. By a silk screening technique, metal coats are applied onto the ceramic metal layers, the metal coats containing at least one precious metal as a critical constituent selected from the group consisting of Hg, Au, Pd, and Pt. The metal layers extend from one side edge of the ceramic layer over the ceramic layer and stop short of and are spaced from the opposite side edge. The ceramic layers are stacked on top of one another, but with an alternating offset of the metal coats. A solderable metallization is applied at sides of the stack and is connected to every other coat at the respective sides.
Inventors
- 👤 Georg Fritsch
- 👤 Hans G. Schuster
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 23:07
CPC Classifications
H; H01; H01C; H01C1/00; H01C1/14; H01C1/1413; H01C7/00; H01C7/04; H01C7/041; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49082; Y10T29/49085
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
183 words
A method for manufacturing a multi-layer thermistor having a negative temperature coefficient, comprising the steps of: producing a plurality of layers formed of fine-particle ceramic material by first producing a suspension with an initial material and organic bonding materials, solvents, and softening agents and then subsequently drawing out with a stripping technique to form an extremely thin film from which the individual fine-particle ceramic material layers are formed; applying metal coats by a silk screening technique onto the fine-particle ceramic material layers, the metal coats containing at least one precious metal as a critical constituent and selected from the group consisting of Ag, Au, Pd, Pt, said metal coats extending from one side edge of each ceramic layer over the ceramic layer but stopping short of and being spaced from the opposite side edge; stacking the ceramic layers with the respective coats on top of one another but with an alternating offset of the metal coats; and pressing the stack, sintering the stack, and applying a solderable metallization at sides of the stack to connect to every other coat at the respective sides.
Claim 2
Independent Claim
183 words
A method for manufacturing a multi-layer thermistor having a negative temperature coefficient, comprising the steps of: producing a plurality of layers formed of fine-particle ceramic material by first producing a suspension with an initial material and organic bonding materials, solvents, and softening agents and then subsequently drawing out with a stripping technique to form an extremely thin film from which the individual fine-particle ceramic material layers are formed; applying metal coats by a silk screening technique onto the fine-particle ceramic material layers, the metal coats containing at least one precious metal as a critical constituent and selected from the group consisting of Ag, Au, Pd, Pt, said metal coats extending from one side edge of each ceramic layer over the ceramic layer but stopping short of and being spaced from the opposite side edge; stacking the ceramic layers with the respective coats on top of one another but with an alternating offset of the metal coats; and pressing the stack, sintering the stack, and applying a solderable metallization at sides of the stack to connect to every other coat at the respective sides.
Claim 3
Dependent Claim
26 words
A method according to claim 1 wherein the metal coats contain at least one element selected from the group Al, Pb as a further critical constituent.
Claim 4
Dependent Claim
28 words
A method according to claim 1 wherein the metal coats contain Pd and Ag as a critical constituent with a silver part of more than 50% by weight.
Claim 5
Dependent Claim
17 words
A method according to claim 3 wherein the silver part is between 70% and 80% by weight.
Claim 6
Dependent Claim
21 words
A method according to claim 3 wherein the metal coats are approximately in a range of 2 to 3 μm thick.
Claim 7
Independent Claim
190 words
A method for manufacturing a multi-layer thermistor having a negative temperature coefficient, comprising the steps of: producing a plurality of layers formed of fine-particle ceramic material by first producing a suspension with an initial material and organic bonding materials, solvents, and softening agents, and then subsequently drawing out with a stripping technique to form an extremely thin film from which the individual fine-particle ceramic material layers are formed; applying metal coats by a silk screening technique onto the fine-particle ceramic material layers, the metal coats of 2-μm thickness containing at least one precious metal as a critical constituent and selected from the group consisting of Ag, Au, Pd, Pt, said metal coats extending from one side edge of each ceramic layer over the ceramic layer but stopping short of and being spaced from the opposite side edge; stacking the ceramic layers with the respective coats on top of one another but with an alternating offset of the metal coats; and pressing the stack, tempering and expelling binder, sintering the stack, and applying a solderable metallization at sides of the stack to connect to every other coat at the respective sides.
Claim 8
Independent Claim
190 words
A method for manufacturing a multi-layer thermistor having a negative temperature coefficient, comprising the steps of: producing a plurality of layers formed of fine-particle ceramic material by first producing a suspension with an initial material and organic bonding materials, solvents, and softening agents, and then subsequently drawing out with a stripping technique to form an extremely thin film from which the individual fine-particle ceramic material layers are formed; applying metal coats by a silk screening technique onto the fine-particle ceramic material layers, the metal coats of 2-μm thickness containing at least one precious metal as a critical constituent and selected from the group consisting of Ag, Au, Pd, Pt, said metal coats extending from one side edge of each ceramic layer over the ceramic layer but stopping short of and being spaced from the opposite side edge; stacking the ceramic layers with the respective coats on top of one another but with an alternating offset of the metal coats; and pressing the stack, tempering and expelling binder, sintering the stack, and applying a solderable metallization at sides of the stack to connect to every other coat at the respective sides.
References Cited (Backward Citations)
US2886476A
Cited
DE2321478A1
Cited
GB1337929A
Cited
US4189760A
Cited
US4454495A
Cited
EP0189087A1
Cited
US4766409A
Cited
US4918421A
Cited
DE3725455A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-03-26 | 1999-09-25 | 2000-03-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-03-26 | 2003-09-25 | 2004-03-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-03-26 | 2007-09-25 | 2008-03-26 | $7700.00 | Window Closed / Lapsed |