Monolithic capacitor with non-noble metal electrodes and method of making the same
Assignee: Erie Technological Products Inc
•
Filing: 1975-03-31
•
Granted: 1980-02-19
•
Expires: 1995-03-31
Abstract
Abstract A monolithic ceramic capacitor having embedded electrodes formed by cosintering of ceramic dielectric layers and layers indifferent to the dielectric layers corresponding in area and position to the electrodes. The indifferent layers are converted to a conductive state, for example, by chemical conversion and used as such or are removed and replaced by metal or conductive material. One example in which the indifferent layers comprise nickel oxide involves stacking layers of green ceramic coated with nickel oxide in the desired electrode pattern, sintering the stacked layers to produce a monolith, reducing the nickel oxide in the monolith to metallic nickel in a hydrogen atmosphere at a temperature low enough to have minimal effect upon the dielectric properties of the ceramic and using the metallic nickel as reduced for the ceramic capacitor electrodes. In another example, after the reduction step (which may be at high temperature) the metallic nickel is dissolved, for example by sulfuric acid, the ceramic monolith is reoxidized by firing in an oxidizing atmosphere such as air, and the voids left by removal of the dissolved metallic nickel are provided with suitable electrodes. In still another example, in which the indifferent layers comprise oxidizable material such as carbon, the stacked layers are sintered in an inert atmosphere to produce a monolith of matured ceramic and the indifferent layers are removed by subsequent firing in an oxidizing atmosphere to produce the voids for receiving conductive electrode material.
Inventors
- 👤 Gilbert L. Marshall
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 11:03
CPC Classifications
H; H01; H01G; H01G4/00; H01G4/30; H01G4/302; Y; Y10; Y10T; Y10T29/00; Y10T29/43; Y10T29/435
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
73 words
A monolithic structure comprising: a sintered unitary body; 1. said body having a matrix of a dielectric ceramic composition and 2. a plurality of vertically spaced nonmetallic strata in said matrix, each stratum extending to one of a pair of edge regions of said body, alternate strata extending to the same edge region, said nonmetallic strata having been positioned in said matrix prior to the sintering of said body and comprising nickel oxide.
Claim 2
Dependent Claim
73 words
A monolithic structure comprising: a sintered unitary body; 1. said body having a matrix of a dielectric ceramic composition and 2. a plurality of vertically spaced nonmetallic strata in said matrix, each stratum extending to one of a pair of edge regions of said body, alternate strata extending to the same edge region, said nonmetallic strata having been positioned in said matrix prior to the sintering of said body and comprising nickel oxide.
Claim 3
Dependent Claim
136 words
An intermediate product comprising an as sintered monolith of ceramic dielectric material an one component and a solid non noble metallic oxide material as another component, said non noble material being in the positions and of the shapes and sizes required for electrodes in capacity relation to each other through portions of said dielectric material, said ceramic dielectric material and non noble material having been first positioned in said monolith and then cofired or sintered into said monolith, said ceramic having been matured by said sintering, said non noble material comprising a material which remains solid and in place and is indifferent to the ceramic during said sintering and is a solid metal oxide at the end of said sintering and is reducible in situ to the metallic state after said sintering to provide conductive electrodes.
Claim 4
Dependent Claim
136 words
An intermediate product comprising an as sintered monolith of ceramic dielectric material an one component and a solid non noble metallic oxide material as another component, said non noble material being in the positions and of the shapes and sizes required for electrodes in capacity relation to each other through portions of said dielectric material, said ceramic dielectric material and non noble material having been first positioned in said monolith and then cofired or sintered into said monolith, said ceramic having been matured by said sintering, said non noble material comprising a material which remains solid and in place and is indifferent to the ceramic during said sintering and is a solid metal oxide at the end of said sintering and is reducible in situ to the metallic state after said sintering to provide conductive electrodes.
Claim 5
Dependent Claim
95 words
A sintered monolith comprising, ceramic dielectric material and other material embedded in the monolith in the positions required for electrodes in capacity relation to each other through portions of said dielectric said ceramic and other material having been positioned in said monolith as discrete layers in the green state prior to sintering of said monolith and having been cosintered to mature the ceramic, said other material comprising nickel oxide which remains in place and is indifferent to the ceramic during said cosintering and is convertible to a conductive material by chemical reduction after said cosintering.
Claim 6
Dependent Claim
95 words
A sintered monolith comprising, ceramic dielectric material and other material embedded in the monolith in the positions required for electrodes in capacity relation to each other through portions of said dielectric said ceramic and other material having been positioned in said monolith as discrete layers in the green state prior to sintering of said monolith and having been cosintered to mature the ceramic, said other material comprising nickel oxide which remains in place and is indifferent to the ceramic during said cosintering and is convertible to a conductive material by chemical reduction after said cosintering.
Claim 7
Dependent Claim
31 words
The monolith of claim 3 in which after said sintering the nickel oxide present in the as sintered monolith is reducible in situ to the metallic state to provide capacitor electrodes.
Claim 8
Dependent Claim
111 words
A sintered monolith comprising ceramic dielectric material and other material embedded in the monolith in the positions required for electrodes in capacity relation to each other through protions of the dielectric, said ceramic and other material having been positioned in said monolith as discrete layers in the green state prior to sintering of said monolith and having been cosintered to mature the ceramic, said other material comprising nickel oxide which remains in place and is indifferent to the ceramic during said cosintering and is indifferent to the ceramic during said cosintering and is convertible to a conductive material after said cosintering by removing the nickel oxide and substituting conducting electrode material.
Claim 9
Dependent Claim
111 words
A sintered monolith comprising ceramic dielectric material and other material embedded in the monolith in the positions required for electrodes in capacity relation to each other through protions of the dielectric, said ceramic and other material having been positioned in said monolith as discrete layers in the green state prior to sintering of said monolith and having been cosintered to mature the ceramic, said other material comprising nickel oxide which remains in place and is indifferent to the ceramic during said cosintering and is indifferent to the ceramic during said cosintering and is convertible to a conductive material after said cosintering by removing the nickel oxide and substituting conducting electrode material.
Claim 10
Dependent Claim
27 words
The monolith of claim 5 in which the nickel oxide is reducible to the metallic state after said sintering and is then dissolvable to remove the same.
Claim 11
Independent Claim
128 words
The method of making a monolithic capacitor without high temperature noble metal electrodes which comprises the steps of superposing layers of green ceramic dielectric material and other material, the other material being in the positions required for electrodes in capacity relation to each other through portions of the dielectric and remaining in place and being indifferent to the dielectric material at the firing conditions to produce a sintered monolith, firing the superposed layers into a sintered monolith in which said other material constitutes discrete layers which are non conductive and comprises nickel oxide which is changed to conductive electrodes by subjecting the sintered monolith to a hydrogen atmosphere at temperatures reducing the nickel oxide to metallic nickel and below temperatures substantially affecting the dielectric properties of the ceramic.
Claim 12
Independent Claim
128 words
The method of making a monolithic capacitor without high temperature noble metal electrodes which comprises the steps of superposing layers of green ceramic dielectric material and other material, the other material being in the positions required for electrodes in capacity relation to each other through portions of the dielectric and remaining in place and being indifferent to the dielectric material at the firing conditions to produce a sintered monolith, firing the superposed layers into a sintered monolith in which said other material constitutes discrete layers which are non conductive and comprises nickel oxide which is changed to conductive electrodes by subjecting the sintered monolith to a hydrogen atmosphere at temperatures reducing the nickel oxide to metallic nickel and below temperatures substantially affecting the dielectric properties of the ceramic.
Claim 13
Independent Claim
99 words
The method of making a monolith capacitor without high temperature noble metal electrodes which comprises the steps of superposing layers of green ceramic dielectric material and combustible material, the combustible material being in the positions required for electrodes in capacity relation to each other through portions of the dielectric and remaining in place and being indifferent to the dielectric material at the firing conditions to produce a sintered monolith, firing the superposed layers into a monolith in a non oxidizing atmosphere, and thereafter changing the material to conductive electrodes by burning out the combustible material and substituting conductive material.
Claim 14
Independent Claim
99 words
The method of making a monolith capacitor without high temperature noble metal electrodes which comprises the steps of superposing layers of green ceramic dielectric material and combustible material, the combustible material being in the positions required for electrodes in capacity relation to each other through portions of the dielectric and remaining in place and being indifferent to the dielectric material at the firing conditions to produce a sintered monolith, firing the superposed layers into a monolith in a non oxidizing atmosphere, and thereafter changing the material to conductive electrodes by burning out the combustible material and substituting conductive material.
Claim 15
Dependent Claim
16 words
The method of claim 8 in which the firing atmosphere is inert to said combustible material.
Claim 16
Dependent Claim
12 words
The method of claim 8 in which said combustible material is carbon.
Claim 17
Dependent Claim
78 words
A sintered, unitary, ceramic body having a plurality of cosintered regions and comprising a plurality of regions of dielectric ceramic composition and at least one region of solid base metal oxide material which remains solid and in place and is indifferent to the ceramic during its sintering and by processing subsequent to said sintering is reducible in situ to the metallic state, the base metal oxide material extending to a region on the outer face of the body.
Claim 18
Dependent Claim
78 words
A sintered, unitary, ceramic body having a plurality of cosintered regions and comprising a plurality of regions of dielectric ceramic composition and at least one region of solid base metal oxide material which remains solid and in place and is indifferent to the ceramic during its sintering and by processing subsequent to said sintering is reducible in situ to the metallic state, the base metal oxide material extending to a region on the outer face of the body.
Claim 19
Independent Claim
88 words
A method of making a capacitor without high temperature noble metal electrodes which comprises the steps of superposing layers of green ceramic dielectric material and solid base metal oxide material, the base metal oxide material being in the position required for electrodes in capacity relation to each other through portions of the dielectric material and remaining solid and in place and being indifferent to the dielectric material at the firing conditions, firing the superposed layers into a monolith, and changing the base metal oxide material to conductive electrodes.
Claim 20
Independent Claim
88 words
A method of making a capacitor without high temperature noble metal electrodes which comprises the steps of superposing layers of green ceramic dielectric material and solid base metal oxide material, the base metal oxide material being in the position required for electrodes in capacity relation to each other through portions of the dielectric material and remaining solid and in place and being indifferent to the dielectric material at the firing conditions, firing the superposed layers into a monolith, and changing the base metal oxide material to conductive electrodes.
Claim 21
Dependent Claim
149 words
A process of providing electrodes or conductors in sintered ceramic bodies which comprises providing sheets of a finely divided insulating or dielectric ceramic composition bonded with a temporary binder, which composition forms a dense layer when fired to sintering temperature, introducing between the sheets a deposit of a combustible composition, the combustible composition being suspended in a vehicle which is eliminated during firing, the combustible composition developing a combustible layer when fired, consolidating a plurality of these sheets and intervening deposits whereby to obtain a self-sustaining body; heating this body to eliminate the vehicle and temporary binder, firing the body to sintering temperature in a non oxidizing atmosphere to produce a sintered monolithic body having regions of dense ceramic material and regions of combustible material, each such region extending to a region on an outer face of the monolithic body; and providing a conductive material in the combustible regions.
Claim 22
Dependent Claim
149 words
A process of providing electrodes or conductors in sintered ceramic bodies which comprises providing sheets of a finely divided insulating or dielectric ceramic composition bonded with a temporary binder, which composition forms a dense layer when fired to sintering temperature, introducing between the sheets a deposit of a combustible composition, the combustible composition being suspended in a vehicle which is eliminated during firing, the combustible composition developing a combustible layer when fired, consolidating a plurality of these sheets and intervening deposits whereby to obtain a self-sustaining body; heating this body to eliminate the vehicle and temporary binder, firing the body to sintering temperature in a non oxidizing atmosphere to produce a sintered monolithic body having regions of dense ceramic material and regions of combustible material, each such region extending to a region on an outer face of the monolithic body; and providing a conductive material in the combustible regions.
Claim 23
Dependent Claim
161 words
A process for forming a monolithic capacitor which comprises: (a) providing a plurality of thin leaves of finely divided ceramic dielectric composition bonded with a temporary binder, this composition forming a dense layer when fired to sintering temperature; (b) providing, between the leaves, layers of a combustible composition suspended in a vehicle, the combustible composition developing a combustible layer when fired in a non oxidizing atmosphere, the layers being so arranged and placed that alternate layers extend to one of two different portions of the leaves while being spaced from the other edge portions thereof; (c) forming a stack of the alternated leaves and layers; (d) heating the stack to eliminate the temporary binder and vehicle; (e) firing the self-sustaining stack to sintering temperature in a non oxidizing atmosphere so as to produce a monolithic body having alternate strata of a dense, dielectric, ceramic composition and of a combustible composition; and (f) providing a conductive material in the combustible composition strata.
Claim 24
Dependent Claim
161 words
A process for forming a monolithic capacitor which comprises: (a) providing a plurality of thin leaves of finely divided ceramic dielectric composition bonded with a temporary binder, this composition forming a dense layer when fired to sintering temperature; (b) providing, between the leaves, layers of a combustible composition suspended in a vehicle, the combustible composition developing a combustible layer when fired in a non oxidizing atmosphere, the layers being so arranged and placed that alternate layers extend to one of two different portions of the leaves while being spaced from the other edge portions thereof; (c) forming a stack of the alternated leaves and layers; (d) heating the stack to eliminate the temporary binder and vehicle; (e) firing the self-sustaining stack to sintering temperature in a non oxidizing atmosphere so as to produce a monolithic body having alternate strata of a dense, dielectric, ceramic composition and of a combustible composition; and (f) providing a conductive material in the combustible composition strata.
Claim 25
Independent Claim
128 words
The method of making a monolithic capacitor without high temperature noble metal electrodes which comprises the step of superposing layers of green ceramic dielectric material and other material, the other material being in the position required for electrodes in capacity relation to each other through portions of the dielectric and remaining in place and being indifferent to the dielectric material at the firing conditions to produce a sintered monolith, firing the superposed layers into a sintered monolith in which said other material constitutes discrete layers which are non conductive and comprises nickel oxide which is changed to conductive electrodes by subjecting the sintered monolith to a reducing atmosphere at temperatures reducing the nickel oxide to metallic nickel and below temperatures substantially affecting the dielectric properties of the ceramic.
Claim 26
Independent Claim
128 words
The method of making a monolithic capacitor without high temperature noble metal electrodes which comprises the step of superposing layers of green ceramic dielectric material and other material, the other material being in the position required for electrodes in capacity relation to each other through portions of the dielectric and remaining in place and being indifferent to the dielectric material at the firing conditions to produce a sintered monolith, firing the superposed layers into a sintered monolith in which said other material constitutes discrete layers which are non conductive and comprises nickel oxide which is changed to conductive electrodes by subjecting the sintered monolith to a reducing atmosphere at temperatures reducing the nickel oxide to metallic nickel and below temperatures substantially affecting the dielectric properties of the ceramic.
References Cited (Backward Citations)
US2919483A
Cited
US3390012A
Cited
US3838204A
Cited
US3561110A
Cited
US3534238A
Cited
US3645783A
Cited
US3679950A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-02-18 | 1983-08-20 | 1984-02-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-02-18 | 1987-08-20 | 1988-02-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-02-18 | 1991-08-20 | 1992-02-19 | $7700.00 | Window Closed / Lapsed |