Formation of microstructures using a preformed photoresist sheet
Assignee: Wisconsin Alumni Research Foundation
•
Filing: 1994-11-16
•
Granted: 1996-03-05
•
Expires: 2014-11-16
Abstract
Abstract In the formation of microstructures, a preformed sheet of photoresist, such as polymethylmethacrylate (PMMA), which is strain free, may be milled down before or after adherence to a substrate to a desired thickness. The photoresist is patterned by exposure through a mask to radiation, such as X-rays, and developed using a developer to remove the photoresist material which has been rendered susceptible to the developer. Micrometal structures may be formed by electroplating metal into the areas from which the photoresist has been removed. The photoresist itself may form useful microstructures, and can be removed from the substrate by utilizing a release layer between the substrate and the preformed sheet which can be removed by a remover which does not affect the photoresist. Multiple layers of patterned photoresist can be built up to allow complex three dimensional microstructures to be formed.
Inventors
- 👤 Henry Guckel
- 👤 Todd R. Christenson
- 👤 Kenneth Skrobis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 20:01
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/20; G03F7/2037; G03F7/2039; G03F7/26; G03F7/38; B; B81; B81C; B81C1/00; B81C1/00349; B81C1/0038; G03F7/0035; H; H10; H10P; H10P76/00; H10P76/20; H10P76/204; H10P76/2041; B81C2201/00; B81C2201/01; B81C2201/0101; B81C2201/0128; B81C2201/0156; B81C2201/0159; B81C2201/0174; B81C2201/019; B81C2201/03; B81C2201/032; Y; Y10; Y10S; Y10S430/00; Y10S430/167; Y10S430/168; Y10T; Y10T428/00; Y10T428/31504
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
90 words
A laminate including micromechanical structures therein comprising: two preformed sheets of photoresist material adhered together at one of the sides of each sheet, the side of each sheet of photoresist which is adhered to the other sheet having a pattern of voids therein which extend partially but not entirely through the sheet, the sheets of photoresist material being adhered together to form a pattern of voids between the sheets on the sides of the sheets where they are joined, each sheet of photoresist being about 3 mm thick or less.
Claim 2
Dependent Claim
90 words
A laminate including micromechanical structures therein comprising: two preformed sheets of photoresist material adhered together at one of the sides of each sheet, the side of each sheet of photoresist which is adhered to the other sheet having a pattern of voids therein which extend partially but not entirely through the sheet, the sheets of photoresist material being adhered together to form a pattern of voids between the sheets on the sides of the sheets where they are joined, each sheet of photoresist being about 3 mm thick or less.
Claim 3
Dependent Claim
22 words
The laminate of claim 1 further including a substrate having a surface to which one of the two photoresist sheets is adhered.
Claim 4
Dependent Claim
14 words
The laminate of claim 1 wherein the material of the photoresist sheets is PMMA.
Claim 5
Dependent Claim
67 words
A photoresist laminate having micromechanical structures comprising: two or more preformed sheets of photoresist material adhered together to form a laminate, each photoresist sheet being about 1 mm in thickness or less and each photoresist sheet having at least one surface thereof mechanically milled, and further wherein at least one surface of each photoresist sheet has a pattern of voids therein which extend entirely through each sheet.
Claim 6
Dependent Claim
67 words
A photoresist laminate having micromechanical structures comprising: two or more preformed sheets of photoresist material adhered together to form a laminate, each photoresist sheet being about 1 mm in thickness or less and each photoresist sheet having at least one surface thereof mechanically milled, and further wherein at least one surface of each photoresist sheet has a pattern of voids therein which extend entirely through each sheet.
Claim 7
Dependent Claim
57 words
The photoresist laminate of claim 4 including at least a third preformed sheet of photoresist having a thickness of about 1 mm or less adhered to one of the sheets, the third sheet of photoresist having a pattern of voids therein which extends entirely through the sheet, at least one surface of the third sheet mechanically milled.
Claim 8
Dependent Claim
21 words
The photoresist laminate of claim 4 including a substrate having a surface to which one of the photoresist sheets is adhered.
Claim 9
Dependent Claim
15 words
The photoresist laminate of claim 4 wherein the photoresist sheets are each formed of PMMA.
Claim 10
Dependent Claim
76 words
A micromechanical structure comprising: a free body of PMMA having a top surface and a bottom surface, at least one of the top and bottom surfaces being mechanically milled, the thickness of the body between the top and bottom surfaces being less than about 1 mm, the body formed of preformed PMMA with substantially no internal strain therein, and sidewalls for the body which are substantially perpendicular to the top and bottom surfaces of the body.
Claim 11
Dependent Claim
76 words
A micromechanical structure comprising: a free body of PMMA having a top surface and a bottom surface, at least one of the top and bottom surfaces being mechanically milled, the thickness of the body between the top and bottom surfaces being less than about 1 mm, the body formed of preformed PMMA with substantially no internal strain therein, and sidewalls for the body which are substantially perpendicular to the top and bottom surfaces of the body.
Claim 12
Dependent Claim
47 words
A laminated structure comprising: a substrate having a surface; a thin layer of low molecular weight PMMA on the surface of the substrate; and a preformed sheet of PMMA less than about 3 mm thick which is solvent bonded to the layer of low molecular weight PMMA.
Claim 13
Dependent Claim
47 words
A laminated structure comprising: a substrate having a surface; a thin layer of low molecular weight PMMA on the surface of the substrate; and a preformed sheet of PMMA less than about 3 mm thick which is solvent bonded to the layer of low molecular weight PMMA.
Claim 14
Dependent Claim
20 words
The laminated structure of claim 9 wherein the layer of low molecular weight PMMA is less than 5 μm thick.
Claim 15
Dependent Claim
19 words
The laminated structure of claim 9 wherein the low molecular weight layer has a molecular weight of about 496,000.
Claim 16
Dependent Claim
15 words
The laminated structure of claim 9 wherein the substrate is a preformed sheet of PMMA.
Claim 17
Dependent Claim
12 words
The laminated structure of claim 9 wherein the substrate is crystalline silicon.
Claim 18
Independent Claim
62 words
A method of forming a laminated structure comprising the steps of: spinning a thin layer of low molecular weight PMMA onto a substrate and curing the layer; wetting the layer of low molecular weight PMMA with MMA monomer; applying a preformed sheet of PMMA to the wetted layer to adhere the preformed sheet to the wetted layer and thus to the substrate.
Claim 19
Independent Claim
62 words
A method of forming a laminated structure comprising the steps of: spinning a thin layer of low molecular weight PMMA onto a substrate and curing the layer; wetting the layer of low molecular weight PMMA with MMA monomer; applying a preformed sheet of PMMA to the wetted layer to adhere the preformed sheet to the wetted layer and thus to the substrate.
Claim 20
Dependent Claim
14 words
The method of claim 14 wherein the substrate is a preformed sheet of PMMA.
Claim 21
Dependent Claim
20 words
The method of claim 14 wherein the layer of low molecular weight PMMA has a molecular weight of about 496K.
References Cited (Backward Citations)
US3449221A
Cited
US3535137A
Cited
US3886584A
Cited
US4035522A
Cited
US3984582A
Cited
US4108938A
Cited
US4107351A
Cited
US4422905A
Cited
US4351653A
Cited
US4541977A
Cited
US4493753A
Cited
US4563250A
Cited
US4563251A
Cited
EP0158357A2
Cited
US4703559A
Cited
US4705605A
Cited
US4693791A
Cited
US4694548A
Cited
US4698285A
Cited
US4661212A
Cited
US4780382A
Cited
US4797211A
Cited
US4738010A
Cited
EP0234553A2
Cited
US4784935A
Cited
US4872888A
Cited
US5189777A
Cited
US5357807A
Cited
US5206983A
Cited
US5327033A
Cited
US5190637A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-03-05 | 1999-09-04 | 2000-03-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-03-05 | 2003-09-04 | 2004-03-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-03-05 | 2007-09-04 | 2008-03-05 | $7700.00 | Window Closed / Lapsed |