Silicon on insulator with active buried regions
Assignee: University of California
•
Filing: 1993-10-18
•
Granted: 1996-01-30
•
Expires: 2013-10-18
Abstract
Abstract A method for forming patterned buried components, such as collectors, sources and drains, in silicon-on-insulator (SOI) devices. The method is carried out by epitaxially growing a suitable sequence of single or multiple etch stop layers ending with a thin silicon layer on a silicon substrate, masking the silicon such that the desired pattern is exposed, introducing dopant and activating in the thin silicon layer to form doped regions. Then, bonding the silicon layer to an insulator substrate, and removing the silicon substrate. The method additionally involves forming electrical contact regions in the thin silicon layer for the buried collectors.
Inventors
- 👤 Anthony M. McCarthy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 01:03
CPC Classifications
H; H10; H10W; H10W15/00; H10P; H10P50/00; H10P50/60; H10P50/64; H10P50/642; H10P50/644; H10P90/00; H10P90/19; H10P90/1904; H10P90/1906; H10P90/1914; H10W10/00; H10W10/10; H10W10/181; H10W15/01; H10W20/00; H10W20/01; H10W20/021; Y; Y10; Y10S; Y10S148/00; Y10S148/012; Y10S148/15; Y10S438/00; Y10S438/97
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
106 words
A method for forming at least one buried region in a silicon-on-insulator member, comprising: depositing at least one layer of silicon on a substrate; doping at least a selected area of the layer of silicon to form at least one buried region in an outer surface region of the silicon layer; bonding the silicon layer to an insulator substrate such that the at least one buried region is directly contiguous with a surface of the insulator substrate; and totally removing the substrate on which the layer of silicon was deposited; whereby the thus formed buried region is buried beneath an opposite surface of the silicon layer.
Claim 2
Independent Claim
106 words
A method for forming at least one buried region in a silicon-on-insulator member, comprising: depositing at least one layer of silicon on a substrate; doping at least a selected area of the layer of silicon to form at least one buried region in an outer surface region of the silicon layer; bonding the silicon layer to an insulator substrate such that the at least one buried region is directly contiguous with a surface of the insulator substrate; and totally removing the substrate on which the layer of silicon was deposited; whereby the thus formed buried region is buried beneath an opposite surface of the silicon layer.
Claim 3
Dependent Claim
24 words
The method of claim 1, additionally including forming at least one electric contact in the silicon layer so as to contact the buried region.
Claim 4
Dependent Claim
64 words
The method of claim 2, wherein the at least one electric contact is formed by: masking a selected area of the silicon layer so as to leave an area of the layer above the buried region exposed; directing pulsed laser energy onto the exposed area of the silicon layer causing same to be activated and doped; and removing the maskant from the silicon layer.
Claim 5
Dependent Claim
42 words
The method of claim 3, additionally including depositing a laser doped etch stop layer on the substrate prior to depositing the silicon layer thereon, and removing the etch stop layer following removal of the substrate on which the silicon layer was deposited.
Claim 6
Dependent Claim
26 words
The method of claim 4, additionally including forming the substrate on which the silicon layer was deposited from silicon, and forming the insulator substrate from glass.
Claim 7
Dependent Claim
42 words
The method of claim 4, wherein the pulsed laser energy is produced by an excimer laser having a wavelength of not greater than 350 nm, a pulse of 1-100 ns, and a power density sufficient to melt a surface of the silicon.
Claim 8
Dependent Claim
33 words
The method of claim 1, additionally including forming a layer of dielectric material on a surface of the insulator substrate or the silicon layer prior to bonding the silicon layer to that substrate.
Claim 9
Dependent Claim
39 words
The method of claim 1, additionally including depositing at least one each of alternating layers of laser doped etch stop material and silicon on the substrate, and masking the outer layer of silicon prior to forming the region therein.
Claim 10
Dependent Claim
30 words
The method of claim 8, additionally including providing the material to mask the selected areas of the layer of silicon from the group consisting of a metal and a dielectric.
Claim 11
Dependent Claim
16 words
The method of claim 1, additionally including providing a dopant environment from boron, phosphorous and arsenic.
Claim 12
Dependent Claim
44 words
The method of claim 3, additionally including providing the pulsed laser energy from an excimer laser having a wavelength less than 350 nm, power intensity sufficient to melt at least the surface of a silicon layer, and produces pulses in the 1-100 ns range.
Claim 13
Dependent Claim
108 words
A process for producing buried components formed in a layer of silicon bonded to a glass substrate, comprising: forming a doped etch stop layer on a silicon wafer; depositing a thin layer of silicon on the doped etch stop layer; providing the silicon layer with exposed and masked areas; introducing dopant into the silicon layer to form at least one doped region therein; bonding the silicon layer to a glass wafer such that the at least one doped region is located directly contiguous with the glass wafer; totally removing the silicon wafer; and etching away the doped etch stop layer, leaving a surface of the silicon layer exposed.
Claim 14
Dependent Claim
108 words
A process for producing buried components formed in a layer of silicon bonded to a glass substrate, comprising: forming a doped etch stop layer on a silicon wafer; depositing a thin layer of silicon on the doped etch stop layer; providing the silicon layer with exposed and masked areas; introducing dopant into the silicon layer to form at least one doped region therein; bonding the silicon layer to a glass wafer such that the at least one doped region is located directly contiguous with the glass wafer; totally removing the silicon wafer; and etching away the doped etch stop layer, leaving a surface of the silicon layer exposed.
Claim 15
Dependent Claim
31 words
The process of claim 12, additionally including smoothing the exposed surface of the silicon layer by scanning with an excimer laser causing melting and then recrystallization of the silicon layer surface.
Claim 16
Dependent Claim
26 words
The process of claim 12, additionally including forming in the silicon layer an electrical contact for selected components buried under the surface of the silicon layer.
Claim 17
Dependent Claim
58 words
The process of claim 14, wherein the electrical contact for a buried component is formed by: masking the silicon layer such that only the area of a desired electrical contact is exposed; directing pulsed excimer laser energy onto the exposed area of the silicon layer, causing activation and doping thereof; and removing the maskant from the silicon layer.
Claim 18
Dependent Claim
38 words
The process of claim 15, wherein masking of the silicon layer is carried out by depositing an oxide layer on the silicon layer, depositing a metal layer on the oxide layer, and patterning the oxide and metal layers.
Claim 19
Dependent Claim
34 words
The process of claim 12, wherein at least two etch stop layers and at least two silicon layers are formed on the silicon wafer, with the silicon layers alternating with the etch stop layers.
Claim 20
Dependent Claim
32 words
The process of claim 12, wherein forming the doped etch stop layer is carried out by irradiating a surface of the silicon wafer with pulsed excimer laser energy in a dopant atmosphere.
Claim 21
Dependent Claim
34 words
The process of claim 12, wherein introducing dopant into the silicon layer is carried out by directing pulsed excimer laser energy onto exposed areas of the silicon layer causing activation of the exposed areas.
References Cited (Backward Citations)
US3332137A
Cited
US3506424A
Cited
GB1222898A
Cited
US3602981A
Cited
US3944447A
Cited
US3959045A
Cited
JPS59188138A
Cited
US4599792A
Cited
US4601779A
Cited
US4968628A
Cited
US5013681A
Cited
US5071792A
Cited
US5110748A
Cited
US5244817A
Cited
US5234535A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-01-29 | 1999-07-31 | 2000-01-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-01-29 | 2003-07-31 | 2004-01-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-01-29 | 2007-07-31 | 2008-01-30 | $7700.00 | Window Closed / Lapsed |