Method of forming a silicon-on-insulator (SOI) material having a high degree of thickness uniformity
Assignee: Philips North America LLC
•
Filing: 1994-11-17
•
Granted: 1995-10-03
•
Expires: 2014-11-17
Abstract
Abstract A silicon-on-insulator (SOI) material is formed from a bonded silicon wafer structure which includes, in order, a silicon handler substrate, an insulating oxide layer, a silicon device layer, a highly-doped silicon etch stop layer, and a top silicon substrate. The bonded silicon wafer structure is etched in a first anisotropic etching step to remove the top silicon substrate and expose the etch stop layer. Subsequently, a second anisotropic etching step is performed to remove a major portion but less than all of the etch stop layer, with the second anisotropic etching step continuing only until a substantially maximum degree of thickness uniformity is obtained in a remaining portion of the etch stop layer. The remaining portion of the etch stop layer is then removed, to yield a silicon-on-insulator material having a high degree of thickness uniformity.
Inventors
- 👤 Richard H. Egloff
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 21:07
CPC Classifications
H; H10; H10P; H10P90/00; H10P90/19; H10P90/1904; H10P90/1906; H10P90/1914; H10D; H10D86/00; H10D86/01; H10D86/021; H10D86/0251; H10P50/00; H10P50/69; H10P50/691; H10W; H10W10/00; H10W10/10; H10W10/181; Y; Y10; Y10S; Y10S148/00; Y10S148/012; Y10S148/135
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
136 words
A method of forming a silicon-on-insulator (SOI) material from a bonded silicon wafer structure, which comprises: providing said bonded silicon wafer structure, which includes, in order, a silicon handler substrate, an insulating oxide layer, a silicon device layer, a highly-doped silicon etch stop layer, and a top silicon substrate; etching said bonded silicon wafer structure in a first anisotropic etching step to remove said top silicon substrate and expose said etch stop layer; then etching said bonded silicon wafer in a second anisotropic etching step to remove a major portion but less than all of said etch stop layer, said second anisotropic etching step continuing only until a substantially maximum degree of thickness uniformity is obtained in a remaining portion of said etch stop layer; and then removing the remaining portion of said etch stop layer.
Claim 2
Independent Claim
136 words
A method of forming a silicon-on-insulator (SOI) material from a bonded silicon wafer structure, which comprises: providing said bonded silicon wafer structure, which includes, in order, a silicon handler substrate, an insulating oxide layer, a silicon device layer, a highly-doped silicon etch stop layer, and a top silicon substrate; etching said bonded silicon wafer structure in a first anisotropic etching step to remove said top silicon substrate and expose said etch stop layer; then etching said bonded silicon wafer in a second anisotropic etching step to remove a major portion but less than all of said etch stop layer, said second anisotropic etching step continuing only until a substantially maximum degree of thickness uniformity is obtained in a remaining portion of said etch stop layer; and then removing the remaining portion of said etch stop layer.
Claim 3
Dependent Claim
47 words
A method of forming a silicon-on-insulator (SOI) material from a bonded silicon wafer structure as claimed in claim 1, wherein said second anisotropic etching step continues until the remaining portion of said etch stop layer has a thickness of between about 300 angstroms and about 1000 angstroms.
Claim 4
Dependent Claim
47 words
A method of forming a silicon-on-insulator (SOI) material from a bonded silicon wafer structure as claimed in claim 1, wherein said second anisotropic etching step continues until the remaining portion of said etch stop layer has a thickness of between about 500 angstroms and about 700 angstroms.
Claim 5
Dependent Claim
42 words
A method of forming a silicon-on-insulator (SOI) material from a bonded silicon wafer structure as claimed in claim 1, wherein said highly doped silicon etch stop layer is provided as a p-type layer doped with at least one of boron and germanium.
Claim 6
Dependent Claim
43 words
A method of forming a silicon-on-insulator (SOI) material from a bonded silicon wafer structure as claimed in claim 4, wherein said p-type layer is doped with both boron and germanium, the germanium doping concentration being about 6-8 times higher than the boron concentration.
Claim 7
Dependent Claim
30 words
A method of forming a silicon-on-insulator (SOI) material from a bonded silicon wafer structure as claimed in claim 4, wherein said silicon device layer is provided as a p-type layer.
Claim 8
Dependent Claim
42 words
A method of forming a silicon-on-insulator (SOI) material from a bonded silicon wafer structure as claimed in claim 1, wherein the remaining portion of the etch stop layer is removed by oxidizing said remaining portion and then etching the oxidized remaining portion.
Claim 9
Dependent Claim
35 words
A method of forming a silicon-on-insulator (SOI) material from a bonded silicon wafer structure as claimed in claim 1, wherein the remaining portion of the etch stop layer is removed by a local plasma etch.
References Cited (Backward Citations)
US4601779A
Cited
US4771016A
Cited
US5147808A
Cited
JPH0342814A
Cited
JPH03104276A
Cited
US5013681A
Cited
US5261999A
Cited
EP0520216A2
Cited
US5240883A
Cited
EP0561532A2
Cited
US5310451A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-10-02 | 1999-04-03 | 1999-10-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-10-02 | 2003-04-03 | 2003-10-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-10-02 | 2007-04-03 | 2007-10-03 | $7700.00 | Window Closed / Lapsed |