Shaped plastic light-polarizing lens and method of making same
Assignee: POLAROID EYEWEAR US LLC
•
Filing: 1993-09-14
•
Granted: 1995-07-18
•
Expires: 2013-09-14
Abstract
Abstract Plastic lenses having substantially no optical power and a light-polarizing layer therein are prepared by shaping composite laminate of the light-polarizing layer between opposed sheets of thermoplastic material by heating and pressing the laminate between opposed shaping molds (platens), the platens having predetermined radii of curvature for the production of a lens having substantially no optical power. Shaping is effected under conditions of heating and pressing sufficient to cause flow of the thermoplastic sheets and conformation thereof to the respective curvatures of the forming surfaces of the platens. The lenses are especially suited as sunglass lenses for spectacles.
Inventors
- 👤 William H. Dalzell
- 👤 Igor Loshak
- 👤 Nancy J. Gettens
- 👤 Carole L. G. McCarthy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 20:52
CPC Classifications
B; B29; B29D; B29D11/00; B29D11/0073; G; G02; G02B; G02B5/00; G02B5/30; B29D11/00009; G02B5/3025; G02B5/3033; G02C; G02C7/00; G02C7/12
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
236 words
A method of forming a plastic lens convex on one side and concave on the other and having its maximum thickness in the central region of said lens and diminishing gradually in thickness radially toward the periphery of said lens, said method comprising the steps of: providing a laminate comprising a layer of light-polarizing material disposed between and bonded to each of first and second opposed sheets of thermoplastic material; placing said laminate between opposed concave and convex platens for forming respectively convex and concave surfaces on said laminate, the radius of curvature (r 1 ) of said concave platen and the radius of curvature (r 2 ) of said convex platen each corresponding substantially to the relationship ##EQU5## wherein t represents the thickness of said laminate and n is the index of refraction; heating and pressing said platens together with said laminate therebetween, said heating and pressing being sufficient to deform said opposed sheets of thermoplastic material into a flowable condition and sufficient to conform each of said sheets to the respective forming surfaces of said concave and convex platens; said heating and pressing being sufficient to form said laminate into a shaped lens convex on one side and concave on the other, said lens having its maximum thickness in the central region thereof and diminishing gradually in thickness radially toward the periphery of said lens; and removing said shaped lens from between said platens.
Claim 2
Independent Claim
236 words
A method of forming a plastic lens convex on one side and concave on the other and having its maximum thickness in the central region of said lens and diminishing gradually in thickness radially toward the periphery of said lens, said method comprising the steps of: providing a laminate comprising a layer of light-polarizing material disposed between and bonded to each of first and second opposed sheets of thermoplastic material; placing said laminate between opposed concave and convex platens for forming respectively convex and concave surfaces on said laminate, the radius of curvature (r 1 ) of said concave platen and the radius of curvature (r 2 ) of said convex platen each corresponding substantially to the relationship ##EQU5## wherein t represents the thickness of said laminate and n is the index of refraction; heating and pressing said platens together with said laminate therebetween, said heating and pressing being sufficient to deform said opposed sheets of thermoplastic material into a flowable condition and sufficient to conform each of said sheets to the respective forming surfaces of said concave and convex platens; said heating and pressing being sufficient to form said laminate into a shaped lens convex on one side and concave on the other, said lens having its maximum thickness in the central region thereof and diminishing gradually in thickness radially toward the periphery of said lens; and removing said shaped lens from between said platens.
Claim 3
Dependent Claim
17 words
The method of claim 1 wherein said layer of light-polarizing material comprises a molecularly oriented dichroic material.
Claim 4
Dependent Claim
21 words
The method of claim 2 wherein said sheet of light-polarizing material comprises a stretched sheet of polyvinyl alcohol stained with iodine.
Claim 5
Dependent Claim
23 words
The method of claim 3 wherein said sheet of polyvinyl alcohol has a thickness in the range of about 0.0025 to 0.076 mm.
Claim 6
Dependent Claim
20 words
The method of claim 1 each of said first and second opposed sheets of thermoplastic material comprise an acrylic polymer.
Claim 7
Dependent Claim
16 words
The method of claim 5 wherein each of said sheets of acrylic polymer comprises poly(methyl methacrylate).
Claim 8
Dependent Claim
33 words
The method of claim 6 wherein the sheet formed by said concave platen has a thickness greater than about one and one-half times the thickness of the sheet formed by said convex platen.
Claim 9
Dependent Claim
28 words
The method of claim 7 wherein said laminate placed between said concave and convex platens is a lens blank cut from an endless web supply of said laminate.
Claim 10
Dependent Claim
22 words
The method of claim 8 wherein said lens blank placed between said platens has a thickness of about 1.27 mm or greater.
Claim 11
Dependent Claim
46 words
The method of claim 9 wherein said heating is conducted at a temperature of about 149° to 160° C. and said pressing together of said platens with the lens blank therebetween is conducted at a pressure of about 17.6 to 21.1 kg/cm 2 of lens area.
Claim 12
Dependent Claim
10 words
The plastic lens made by the method of claim 1.
References Cited (Backward Citations)
US2387308A
Cited
US2320375A
Cited
US2263249A
Cited
FR1080678A
Cited
DE1116383B
Cited
US3051054A
Cited
US3211047A
Cited
US3245315A
Cited
US3560076A
Cited
US3674587A
Cited
US3711417A
Cited
US3786119A
Cited
US3940304A
Cited
US3944346A
Cited
US4741611A
Cited
US4838673A
Cited
US4986648A
Cited
US5043405A
Cited
US4923758A
Cited
US5327180A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-07-17 | 1999-01-16 | 1999-07-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-07-17 | 2003-01-16 | 2003-07-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-07-17 | 2007-01-16 | 2007-07-18 | $7700.00 | Window Closed / Lapsed |